CN102807740A - 一种聚酯型引拨件 - Google Patents

一种聚酯型引拨件 Download PDF

Info

Publication number
CN102807740A
CN102807740A CN2012102789408A CN201210278940A CN102807740A CN 102807740 A CN102807740 A CN 102807740A CN 2012102789408 A CN2012102789408 A CN 2012102789408A CN 201210278940 A CN201210278940 A CN 201210278940A CN 102807740 A CN102807740 A CN 102807740A
Authority
CN
China
Prior art keywords
polyester type
draws
solventfree resin
vibrin
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102789408A
Other languages
English (en)
Other versions
CN102807740B (zh
Inventor
高禄生
易江洲
李孟德
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Heng Yuan green wood Science and Technology Co., Ltd.
Original Assignee
HENGYANG HENGYUAN ELECTRICAL MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HENGYANG HENGYUAN ELECTRICAL MATERIAL CO Ltd filed Critical HENGYANG HENGYUAN ELECTRICAL MATERIAL CO Ltd
Priority to CN201210278940.8A priority Critical patent/CN102807740B/zh
Publication of CN102807740A publication Critical patent/CN102807740A/zh
Application granted granted Critical
Publication of CN102807740B publication Critical patent/CN102807740B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种聚酯型引拨件，由玻璃纤维体积含量78-82%和无溶剂树脂体积含量18-22%组成，固化温度为：一区：115℃；二区：145℃；三区：130℃；拉挤速度为：0.2-0.3m/min。无溶剂树脂体积组成如下：聚酯树脂（浅色）95-105份、氢氧化铝20-30份、过氧化二苯甲酰1.5-2.5份、125脱模剂2-2.6份。本发明的聚酯型引拨件具有良好的介电性能和极高的机械强度。

Description

一种聚酯型引拨件
技术领域
本发明属于绝缘材料领域，具体的涉及一种聚酯型引拨件。
背景技术
玻璃纤维具有一系列的优越性能，如轻质、高强、耐高温、耐腐蚀、吸声、保温、吸湿性低、伸长小、电绝缘性能好、价廉及原料易得等优点，因此被认为是优良的增强材料。在电气、机械、冶金、石油、化工、汽车、造船、飞机、冷藏、建筑以及国防工业中得到了广泛应用。玻璃纤维配合树脂赋予形状以后可以成为优良之结构用材。玻璃纤维增强聚酯具有重量轻、强度高、抗冲击、良好的耐化学腐蚀性能和电气绝缘性能等特点。
引拨件是由无碱玻璃纤维丝作为增强材料，浸渍无溶剂树脂，在专用模具上一拉挤成型工艺连续烘焙，固化成具有恒定截面形状的制品，如圆杆、方棒、槽楔、工字梁、槽形件等，及其其他复杂形状的制品，它具有极高的机械强度和良好的介电性能。
发明内容
本发明的目的在于提供一种聚酯型引拨件。
为了实现本发明的目的，本发明所采用的技术方案如下：
一种聚酯型引拨件，其特征在于，由下列体积含量的组分组成：
无溶剂树脂        22-18%；
玻璃纤维          78-82%；
所述无溶剂树脂的主要成分为聚酯树脂（浅色）、氢氧化铝、过氧化二苯甲酰和125脱模剂。
所述无溶剂树脂各组分的重量份组成是：
聚酯树脂（浅色）    95-105份；
氢氧化铝            20-30份；
过氧化二苯甲酰      1.5-2.5份；
125脱模剂           2-2.6份。
所述无溶剂树脂的混合工艺是：先把聚酯树脂和氢氧化铝混合搅拌5分钟，再加入过氧化二苯甲酰和125脱模剂搅拌均匀。
本发明聚酯型引拨件是由玻璃纤维作为增强剂材料，浸渍无溶剂树脂，在专用模具上一拉挤成型工艺连续烘焙，固化成型，固化温度为：一区：115℃；二区：145℃；三区：130℃；拉挤速度为：0.2-0.3m/min。
本发明的聚酯型引拨件具有良好的介电性能和极高的机械强度。
具体实施方式
下面结合实施例详细说明本发明的技术内容，但本发明不限于以下实施例。
实施例1
1.配方
本实施例无溶剂树脂的组成如下：
聚酯树脂（浅色）    100kg；
氢氧化铝            20kg；
过氧化二苯甲酰      2kg；
125脱模剂           2kg。
2.混合工艺
先把聚酯树脂和氢氧化铝按以上重量混合搅拌5分钟，再加入过氧化二苯甲酰和125脱模剂搅拌均匀。
实施例2
2.配方
本实施例无溶剂树脂的组成如下：
聚酯树脂（浅色）    105kg；
氢氧化铝            25kg；
过氧化二苯甲酰      2.3kg；
125脱模剂           2.5kg。
2.混合工艺
先把聚酯树脂和氢氧化铝按以上重量混合搅拌5分钟，再加入过氧化二苯甲酰和125脱模剂搅拌均匀。
实施例3
本实施例聚酯型引拨件的组成及其拉挤工艺条件如下
玻璃纤维        78L
无溶剂树脂      22L
固化温度为：一区：115℃；二区：145℃；三区：130℃；
拉挤速度为：0.2-0.3m/min。
本实施例的聚酯型引拨件的技术指标见表1。
实施例4
本实施例聚酯型引拨件的组成及其拉挤工艺条件如下
玻璃纤维    80L
无溶剂树脂  20L
固化温度为：一区：115℃；二区：145℃；三区：130℃；
拉挤速度为：0.2-0.3m/min。
本实施例的聚酯型引拨件的技术指标见表1。
实施例5
本实施例聚酯型引拨件的组成及其拉挤工艺条件如下
玻璃纤维    82L
无溶剂树脂  18L
固化温度为：一区：115℃；二区：145℃；三区：130℃；
拉挤速度为：0.2-0.3m/min。
本实施例的聚酯型引拨件的技术指标见表1。0
表1
  检验项目   实施例3   实施例4   实施例5
  密度（g/cm3）   2.0   1.9   2.0
  吸水率（%）   0.15   0.16   0.16
  沿面耐电压(12kv/mm电极间距30mm)   通过   通过   通过
  绝缘电阻（Ω）   1.0×1013   1.0×1013   1.0×1014
  弯曲强度（MPa）   250   300   290
  压缩强度（轴向）（Mpa）   240   260   275
  热变形温度（℃）   160   175   170

Claims (4)

1.一种聚酯型引拨件，其特征在于，由下列体积含量的组分组成：
无溶剂树脂    22-18%；
玻璃纤维      78-82%；
所述无溶剂树脂的主要成分为聚酯树脂（浅色）、氢氧化铝、过氧化二苯甲酰和125脱模剂。
2.根据权利要求1所述的聚酯型引拨件，其特征在于，所述无溶剂树脂各组分的重量份组成是：
聚酯树脂（浅色）        95-105份；
氢氧化铝                 20-30份；
过氧化二苯甲酰         1.5-2.5份；
125脱模剂                2-2.6份。
3.根据权利要求2所述的聚酯型引拨件，其特征在于，所述无溶剂树脂的混合工艺是：先把聚酯树脂和氢氧化铝混合搅拌5分钟，再加入过氧化二苯甲酰和125脱模剂搅拌均匀。
4.根据权利要求1所述的聚酯型引拨件，其特征在于，由玻璃纤维作为增强剂材料，浸渍无溶剂树脂，在专用模具上一拉挤成型工艺连续烘焙，固化成型，固化温度为：一区：115℃；二区：145℃；三区：130℃；拉挤速度为：0.2-0.3m/min。
CN201210278940.8A 2012-08-07 2012-08-07 一种聚酯型引拨件 Active CN102807740B (zh)