CN102797123A - Silk drying and dehumidifying method after real silk impregnation - Google Patents

Abstract

The invention provides a silk drying and dehumidifying method after real silk impregnation. The silk drying and dehumidifying method is characterized in that mulberry reeled silks are dried and dehumidified by using a dehumidifier. The strengths of the silks dried by the method cannot be damaged; the time taken by drying is obviously reduced; working efficiency is increased; and silk quality is improved.

Description

Baking silk dehumanization method behind the real silk dipping

Technical field

The present invention relates to the baking silk dehumanization method behind the real silk dipping in a kind of silk production.

Background technology

Dipping is the special procedure of silk broadcloth product before preparatory construction, is commonly called as immersion, silk damping.Its purpose mainly is that to make assistant for immersing ooze people's mulberry silk inner, improves the brute force and the extension at break of raw silk, removes the outside part silk gum of real silk, eliminates " hard or angle " in the silk reeling process, makes wire body soft, obtains weavy grain effect preferably; Strand obtains lubricant, disappears quiet dose in dipping, increase the lubricity of strand in process and disappear static stability.For guaranteeing the dipping effect of real silk, the regain of dehydration back silk is 100%, therefore also must dry by the fire silk and remove moisture content, controls to subsequent processing and produces required technology regain.

Usually the baking silk has nature to dry, or the drying room oven dry, or three kinds of drying machine oven dry, and the regain of silk is bigger to the preparation processing characteristics influence of real silk, and general organizine is controlled at 9%～13%, and tram is controlled at 11%～17%.Naturally dry the better softness of silk, regain is even between silk and the silk, but floor space is big, efficient is low; The drying room bake out temperature is between 40～60 ~ C, and dry efficiency is better, be that adopt in most silk mills, but drying room is bigger, and the temperature of each point and relative temperature are difficult to be consistent all around, thereby is difficult to guarantee that the regain of silk is consistent; High, little, the rapid draing of floor space of drying machine drying efficiency, but wire body is prone to harden, the baking oven next door is bigger with the ectonexine regain difference of middle hank knotting and hank knotting.Thereby back two kinds of methods must be placed on the silk after the baking bag inner equilibrium moisture regain 2～3 days, have postponed the process time of operation.Therefore manufacturing enterprise just needed a kind of both can the minimizing to dry by the fire the silk time, did not injure the wire body brute force again as far as possible, can make the regain of silk reach consistent baking silk method again.

Summary of the invention

The present invention has researched and developed the novel baking silk method behind a kind of real silk dipping, and purpose is: provide a kind of and both can reduce the baking silk time, do not injure the wire body brute force again as far as possible, can make the regain of silk reach consistent baking silk method again.

This technical scheme:

Baking silk dehumanization method behind a kind of real silk dipping is characterized in that: use dehumidifier that the silkworm hank knotting is dried by the fire a dehumidification treatments.

Said dehumidifier is industrial dehumidifier.

The invention has the beneficial effects as follows: the brute force through silk after this method drying can not injured, and the time required for drying also obviously reduces, and has improved the quality of operating efficiency and silk.

The specific embodiment

Below in conjunction with embodiment the present invention is described further.

At first hank knotting is hung on the guide frame that dries in the air in the drying room equably, confined space and open dehumidifier then, design temperature, humidity are closed dehumidifier after 72 hours-84 hours and are promptly reached effect on moisture extraction and reach the technology regain.The power of dehumidifier and moisture removal are confirmed based on pending silk amount and storage area size.

The said technology of this technology is compared with prior art: the silk with equal number is used diverse ways, the contrast of processing time and effect.

Claims (2)

1. the baking silk dehumanization method after a real silk floods is characterized in that: use dehumidifier that the silkworm hank knotting is dried by the fire a dehumidification treatments.

2. the baking silk dehumanization method behind a kind of real silk dipping as claimed in claim 1, it is characterized in that: said dehumidifier is industrial dehumidifier.