CN102795789A - Violet film-coated glass - Google Patents
Violet film-coated glass Download PDFInfo
- Publication number
- CN102795789A CN102795789A CN2012101594830A CN201210159483A CN102795789A CN 102795789 A CN102795789 A CN 102795789A CN 2012101594830 A CN2012101594830 A CN 2012101594830A CN 201210159483 A CN201210159483 A CN 201210159483A CN 102795789 A CN102795789 A CN 102795789A
- Authority
- CN
- China
- Prior art keywords
- layer
- coated glass
- tio
- coated
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses violet film-coated glass. The structure of a film layer is sequentially formed by white glass, TiOxNy, TiOxNy, TiOxNy and SST. The violet film-coated glass can adopt a unique TiOxNy film layer so as to obtain the film-coated glass which is reflected to have a violet color. The violet film-coated glass has a gorgeous color and is low in cost, green and environment-friendly, has stable production process parameters and is convenient to be widely popularized.
Description
Technical field
The present invention relates to a kind of special coated glass, especially relate to a kind of violaceous decoration film coating glass that is reflected into
Background technology
The coated glass kind is a lot of in the market, but the reflection colour of coated glass is light color mostly, can not satisfy interior finish market to dazzling the color demand of pursuing.Interior finish now uses stained glass to be mostly the production of printing ink method, and this method produces this height of stained glass, yields poorly, and production process can not satisfy the needs of environmental protection.
The coated glass of magnetron sputtering method production is on the fine float glass, to be coated with compound layer, metal level, compound layer uniformly.Absorption, interference through different retes form distinct colors.
General compound layer is at present: ZnO
x, SnO
x, TiO
x, TiN
x, SSTO
x, SiN
x, metal level is: Ti, SST, Cr, NiCr.
But the coated glass color with above rete is produced is too shallow, even the thickness of suitable adjustment compound rete can have the dark colour coated glass.Cost is too high, does not have marketable value.
For these reasons, be necessary to develop a kind of reflection colour and dazzle coloured silk, the coated glass that can be used for interior finish that cost is low.
Summary of the invention
The objective of the invention is to, adopt the working method of particular compound rete configuration, satisfy and dazzle color color and VT coated glass with low cost.
In order to achieve the above object, the present invention proposes following technical scheme:
A kind of VT coated glass, the structure of this coated glass is: the first layer glass substrate, the second layer are the compound TiO that is plated on the glass substrate
xN
y, the 3rd layer for being plated on the compound TiO on the second layer
xN
y, the 4th layer for being plated on the compound TiO on the 3rd layer
xN
y, layer 5 is the metal SST that is plated on the 4th layer.
The first layer is the fine float glass
The second layer is to contain an amount of O
2And N
2TiO
xN
y
The 3rd layer is to contain an amount of O
2And N
2TiO
xN
y
The 4th layer is to contain an amount of O
2And N
2TiO
xN
y
Be coated with second layer TiO with No. 1 target
xN
y20-25nm
Plating second layer TiO with No. 2 targets
xN
yBe coated with the 3rd layer of TiO on the rete
xN
y20-25nm
Plating the 3rd layer of TiO with No. 3 targets
xN
yBe coated with the 4th layer of TiO on the rete
xN
y20-25nm
Plating the 4th layer of TiO with No. 4 targets
xN
yBe coated with layer 5 SST45-55nm on the rete
Description of drawings
Fig. 1 is a VT coated glass film layer structure synoptic diagram of the present invention
Fig. 2 is a VT coated glass film layer structure synoptic diagram of the present invention (sectional elevation)
Fig. 3 is a VT coated glass manufacturing flow chart of the present invention
Specific embodiments
Form by five layers like Fig. 1, the VT coated glass structure shown in 2, comprise the first layer glass, second layer TiO
xN
y, the 3rd layer of TiO
xN
y, the 4th layer of TiO
xN
y, layer 5 SST.
The present invention is extracted into 5.0 * 10 to vacuum magnetic control film coating equipment vacuum
-4Pa feeds Ar, O then
2, N
2, three kinds of gases, make vacuum tightness 3.0 * 10
-1During Pa, give the energising of Ti target.Make the Ti target stablize sputter at power 45KW.
Using three kinds of Ar in the gas among the present invention is working gass, sputters out the Ti material.
Use three kinds of O in the gas among the present invention
2, N
2Be reactant gases, generate TiO with the Ti reaction that is sputtered out
xN
y
The 3rd layer of TiO of step 2
xN
yBe coated with, feed Ar, O
2, N
2, three kinds of gas Ar: O
2: N
2Ratio is 5: 1: 7, and power uses 40-45KW to be coated with thicknesses of layers to be 20-25nm.
The 4th layer of TiO of step 3
xN
yBe coated with, feed Ar, O
2, N
2, three kinds of gas Ar: O
2: N
2Ratio is 5: 1: 7, and power uses 40-45KW to be coated with thicknesses of layers to be 20-25nm.
The manufacturing process of VT coated glass as shown in Figure 3:
Floatingization of high-quality white glass cleans through cleaning machine and is dry, send like coating chamber through the white glass behind the cleaning-drying.
Be coated with second layer TiO with No. 1 target
xN
y20-25nm
Plating second layer TiO with No. 2 targets
xN
yBe coated with the 3rd layer of TiO on the rete
xN
y20-25nm
Plating the 3rd layer of TiO with No. 3 targets
xN
yBe coated with the 4th layer of TiO on the rete
xN
y20-25nm
Plating the 4th layer of TiO with No. 4 targets
xN
yBe coated with layer 5 SST45-55nm on the rete
Four tunics are coated with after the completion through detecting qualified back packing warehouse-in.
This VT coated glass glass surface reflection colour is to dazzle color pansy, can be good at satisfying the needs of upholstery to color.
The above embodiment has only expressed embodiment of the present invention, and it describes comparatively concrete and detailed, but can not therefore be interpreted as the restriction to claim of the present invention.Should be pointed out that for the person of ordinary skill of the art under the prerequisite that does not break away from the present invention's design, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with accompanying claims.
Claims (5)
1. VT coated glass is characterized in that: the rete of this coated glass the upper layer of the white glass of the first layer from bottom to top structure be followed successively by: TiO
xN
y, TiO
xN
y, TiO
xN
y, SST.
2. VT coated glass as claimed in claim 1 is characterized in that, said second layer TiO
xN
yThicknesses of layers is 20-25nm.
3. VT coated glass as claimed in claim 1 is characterized in that, said the 3rd layer of TiO
xN
yThicknesses of layers is 20-25nm.
4. VT coated glass as claimed in claim 1 is characterized in that, said the 4th layer of TiO
xN
yThicknesses of layers is 20-25nm.
5. VT coated glass as claimed in claim 1 is characterized in that, said layer 5 TiO
xN
yThicknesses of layers is 45-55nm.