CN102786715A - Silicon fire retardant and manufacture method of silicon fire retardant - Google Patents
Silicon fire retardant and manufacture method of silicon fire retardant Download PDFInfo
- Publication number
- CN102786715A CN102786715A CN2012102840207A CN201210284020A CN102786715A CN 102786715 A CN102786715 A CN 102786715A CN 2012102840207 A CN2012102840207 A CN 2012102840207A CN 201210284020 A CN201210284020 A CN 201210284020A CN 102786715 A CN102786715 A CN 102786715A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire retardant
- silicon
- rubber
- marinco
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of chemical engineering, in particular to a silicon fire retardant and a manufacture method of the silicon fire retardant. The silicon fire retardant is formed by mixing the following ingredients in parts by weight: 3 to 6 parts of magnesium hydrate, 3 to 6 parts of antimonous oxide and 1 to 2 parts of silicon dioxide. The fineness of the raw materials cannot be smaller than 325 meshes, the fire retardant has the advantages that the fire retardant effect is good, the surface smoothness and the intensity of products cannot be reduced, and the pollution is avoided, and the manufacture method has the advantage that the process is simple.
Description
Technical field
The present invention relates to chemical technology field, specifically establish and relate to a kind of silicon-series five-retardant and method of manufacture thereof.
Background technology
The development in recent years impetus is better, and market potential is bigger.Though the most frequently used halogenated flame retardant has the unrivaled high efficiency of other fire retardant series in the fire retardant, it is very important to environment and people's harm.Environmental issue is the focus that auxiliary agent development and application merchant pays close attention to, so adjusting the product structure of fire retardant both at home and abroad always, strengthens the exploitation dynamics of efficient and environment-friendly type fire retardant.
Summary of the invention
The object of the invention is exactly to above-mentioned shortcoming, and fire retardant---a kind of silicon-series five-retardant of a kind of good flame retardation effect, enhancing product strength is provided, and the present invention also provides the method for manufacture of this silicon-series five-retardant.
Technical scheme of the present invention is achieved in that a kind of silicon-series five-retardant, comprises by weight being 3-6 parts of Marinco Hs and 3-6 parts of Antimony Trioxide: 99.5Mins.
In order to reach flame retardant effect preferably, it has also increased by 1-2 parts silicon-dioxide.
Best is: a kind of silicon-series five-retardant comprises by weight being that 5 parts of Marinco Hs, 4 parts of Antimony Trioxide: 99.5Mins, 1.5 parts silicon-dioxide mix.
The method of manufacture of silicon-series five-retardant of the present invention is achieved in that above-mentioned raw materials mixed together and gets final product.
Be preferably, the fineness of above-mentioned raw materials should be not less than 325 orders.
The invention has the beneficial effects as follows: such fire retardant has good flame retardation effect, the intensity that can not reduce product, free of contamination advantage.Such method of manufacture has advantage of simple technology.
Embodiment
Below in conjunction with embodiment the present invention is done further description.
Embodiment 1
Directly get the rubber of processing rubber is burnt on spirit lamp, rubber had combustion phenomena in 2 minutes.
Embodiment 2
Get Marinco H 300 grams, Antimony Trioxide: 99.5Min 300 gram powder, be mixed and made into mixture.
Said mixture is got 100 grams, join in the 2000 gram rubber raw materials and process the rubber that contains this mixture, rubber is burnt on spirit lamp, can not burn in 3 minutes.
Embodiment 3
Get Marinco H 300 grams, Antimony Trioxide: 99.5Min 600 gram powder, be mixed and made into mixture.
Said mixture is got 100 grams, join in the 2000 gram rubber raw materials and process the rubber that contains this mixture, rubber is burnt on spirit lamp, can not burn in 4 minutes.
Embodiment 4
Get Marinco H 600 grams, Antimony Trioxide: 99.5Min 300 gram powder, be mixed and made into mixture.
Said mixture is got 100 grams, join in the 2000 gram rubber raw materials and process the rubber that contains this mixture, rubber is burnt on spirit lamp, can not burn in 3 minutes.
Embodiment 5
Get Marinco H 300 grams, Antimony Trioxide: 99.5Min 300, silica 1 00 gram powder, be mixed and made into mixture.
Said mixture is got 100 grams, join in the 2000 gram rubber raw materials and process the rubber that contains this mixture, rubber is burnt on spirit lamp, can not burn in 4 minutes.
Embodiment 6
Get Marinco H 300 grams, Antimony Trioxide: 99.5Min 300, silicon-dioxide 200 gram powder, be mixed and made into mixture.
Said mixture is got 100 grams, join in the 2000 gram rubber raw materials and process the rubber that contains this mixture, rubber is burnt on spirit lamp, can not burn the unaffected rubber performance of rubber intensity, no bad smell in 5 minutes.
Embodiment 7
Get Marinco H 600 grams, Antimony Trioxide: 99.5Min 600, silica 1 00 gram powder, be mixed and made into mixture.
Said mixture is got 100 grams, join in the 2000 gram rubber raw materials and process the rubber that contains this mixture, rubber is burnt on spirit lamp, can not burn the unaffected rubber performance of rubber intensity, no bad smell in 5 minutes.
Embodiment 8
Get Marinco H 500 grams, Antimony Trioxide: 99.5Min 300, silica 1 50 gram powder, be mixed and made into mixture.
Said mixture is got 100 grams, join in the 2000 gram rubber raw materials and process the rubber that contains this mixture, rubber is burnt on spirit lamp, can not burn the unaffected rubber performance of rubber intensity, no bad smell in 5.5 minutes.
Above-mentioned experiment is repeated, and the result finds that Marinco H, Antimony Trioxide: 99.5Min, SiO 2 powder fineness are thin more, and flame retardant effect is good more, is more or less the same after reaching 325 orders and during 325 orders.
Claims (6)
1. a silicon-series five-retardant comprises by weight being 3-6 parts of Marinco Hs and 3-6 parts of Antimony Trioxide: 99.5Mins.
2. fire retardant according to claim 1 is characterized in that: it has also increased by 1-2 parts silicon-dioxide.
3. fire retardant according to claim 2 is characterized in that: comprise by weight being 5 parts of Marinco Hs, 4 parts of Antimony Trioxide: 99.5Mins, 1.5 parts silicon-dioxide.
4. method of making silicon-series five-retardant is with by weight being that 3-6 parts of Marinco Hs and 3-6 parts of Antimony Trioxide: 99.5Mins mix and get final product together.
5. the method for manufacturing silicon-series five-retardant according to claim 4 is with by weight being that 5 parts of Marinco Hs, 4 parts of Antimony Trioxide: 99.5Mins, 1.5 parts silicon-dioxide mix and gets final product together.
6. the method for manufacturing silicon-series five-retardant according to claim 5, the fineness of described Marinco H, Antimony Trioxide: 99.5Min, silica material should be not less than 325 orders.