CN102775723A - 高弯曲强度酚醛模塑料 - Google Patents

高弯曲强度酚醛模塑料 Download PDF

Info

Publication number
CN102775723A
CN102775723A CN2012101858792A CN201210185879A CN102775723A CN 102775723 A CN102775723 A CN 102775723A CN 2012101858792 A CN2012101858792 A CN 2012101858792A CN 201210185879 A CN201210185879 A CN 201210185879A CN 102775723 A CN102775723 A CN 102775723A
Authority
CN
China
Prior art keywords
moulding compound
parts
bending strength
high bending
compound according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101858792A
Other languages
English (en)
Other versions
CN102775723B (zh
Inventor
邱维
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI XINHEXIN SYNTHETIC MATERIALS CO Ltd
Original Assignee
GUANGXI XINHEXIN SYNTHETIC MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI XINHEXIN SYNTHETIC MATERIALS CO Ltd filed Critical GUANGXI XINHEXIN SYNTHETIC MATERIALS CO Ltd
Priority to CN201210185879.2A priority Critical patent/CN102775723B/zh
Publication of CN102775723A publication Critical patent/CN102775723A/zh
Application granted granted Critical
Publication of CN102775723B publication Critical patent/CN102775723B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高弯曲强度的酚醛模塑料。其特点是按重量份比，包含以下组分：酚醛树脂：100份，热固性酚醛树脂：60-100份，纳米橡胶：1-10份，固化剂：5-30份，固化促进剂：1-10份，脱模剂：0.5-3份，陶瓷粉填料：5-20份，其他矿物填料：50-80份，增强纤维：60-150份；将上述配方中的组分混合均匀，在85-140度反应3-5分钟，冷却，粉碎成颗粒。其优点是得到的酚醛模塑料具有良好的弯曲强度，弯曲强度（MPa）150以上。

Description

高弯曲强度酚醛模塑料
技术领域
本发明属于酚醛模塑料领域，具体涉及一种高弯曲强度的酚醛模塑料。
技术背景
酚醛模塑料又称电木粉，是人类历史上开发应用较早的合成材料，它具备有廉价、绝缘性能好、耐热性好、尺寸稳定好、硬度高等特点，广泛应用与电子、电动工具、汽车等工业领域。由于其硬度较高，而易脆，所以其弯曲强度一般较低，本发明旨在于提供一种较高强度的酚醛摸塑料。
发明内容
本发明的目的在于实现一种较高弯曲强度的酚醛模塑料。
本发明为一种较高弯曲强度酚醛模塑料，该塑料按重量份比，包含以下组分：
酚醛树脂：              100份
热固性酚醛树脂：      60-100份
纳米橡胶：              1-10份
固化剂：                5-30份
固化促进剂：            1-10份
脱模剂：                0.5-3份
陶瓷粉填料：             5-20份
其他矿物填料：          50-80份
增强纤维：             60-150份
更具体的技术方案包括：
本发明所述的酚醛树脂是指热塑性酚醛树脂。
本发明所述的热固性酚醛树脂是指液态或者固态的热固性酚醛树脂。
本发明所述的纳米橡胶是指丁腈纳米橡胶。
本发明所述的固化剂是六次甲基四胺、多聚甲醛一种或者两种混合。
本发明所述的固化促进剂是指氧化钙、氧化镁、氧化锌、氢氧化钙、氢氧化镁一种或至少任意两种混合。
本发明所述的脱模剂是指硬脂酸、硬脂酸钙、硬脂酸锌、硬脂酸镁等一种或至少任意两种混合。
本发明所述的陶瓷粉填料是指100目以上的陶瓷粉。
本发明所述的其他矿物填料是指滑石粉、氢氧化铝、碳酸钙、云母粉等一种或至少任意两种混合。
本发明所述的增强纤维是玻璃纤维。
本发明的优点是得到的酚醛模塑料具有良好的弯曲强度，弯曲强度（MPa）150 以上。
具体实施方式
实施例1：
酚醛树脂：                     100份
热固性酚醛树脂                  60份
丁腈纳米橡胶             　　    1份
六次甲基四胺            　　     5份
氧化钙     　　                  1份
硬脂酸           　　          0.5份
陶瓷粉             　　          5份
滑石粉         　　             50份
玻璃纤维          　　          60份
实施例2：
酚醛树脂：                     100份
热固性酚醛树脂                  70份
丁腈纳米橡胶       　　          3份
六次甲基四胺       　　         10份
氧化钙         　　              2份
硬脂酸         　　            0.5份
陶瓷粉       　　                8份
滑石粉          　　            55份
玻璃纤维     　　               75份
实施例3：
酚醛树脂：                     100份
热固性酚醛树脂                  80份
丁腈纳米橡胶   　　              5份
六次甲基四胺    　　            15份
氧化钙         　　              6份
硬脂酸  　　                   0.5份
陶瓷粉   　　                   10份
滑石粉   　　                   60份
玻璃纤维  　　                 100份
实施例4：
酚醛树脂：                     100份
热固性酚醛树脂                  90份
丁腈纳米橡胶     　　            7份
六次甲基四胺      　　          20份
氧化钙   　　                    8份
硬脂酸     　　                0.5份
陶瓷粉    　　                  15份
滑石粉     　　                 70份
玻璃纤维        　　           125份
实施例5：
酚醛树脂：                     100份
热固性酚醛树脂                  100份
丁腈纳米橡胶   　　             10份
六次甲基四胺        　　        30份
氧化钙            　　          10份
硬脂酸      　　               0.5份
陶瓷粉    　　                  20份
滑石粉   　　                   80份
玻璃纤维    　　                150份。
　　按以上实例1-5的组分混合均匀，在前辊为90度，后辊为135度的混炼机反应3-5分钟制成片状，冷却，用粉碎机粉碎，以3mm筛网过筛，得到该酚醛模塑料颗粒。把该酚醛模塑料颗粒在温度参数为170到175度，压力参数为20MPa压力成型机压注成型，在相应的模具中成型得到80*10*4的式样条，经烘箱150度烘1小时，170度烘2小时，190度烘3小时后处理条件处理后，按GB/T9341在万能试验机测得其弯曲强度。
  实施例1 实施例2 实施例3 实施例4 实施例5
弯曲强度MPa 170 151 165 185 163
 其弯曲强度都远高于普通酚醛模塑料的弯曲强度（70到120MPa）。

Claims (10)

1.一种高弯曲强度酚醛模塑料，其特征在于主要由含有重量份比的原料组成：
酚醛树脂：              100份
热固性酚醛树脂：      60-100份
纳米橡胶：              1-10份
固化剂：                5-30份
固化促进剂：            1-10份
脱模剂：                0.5-3份
陶瓷粉填料：             5-20份
其他矿物填料：          50-80份
增强纤维：             60-150份
将上述配方中的组分混合均匀，在85-140度反应3-5分钟，冷却，粉碎成颗粒。
2.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的酚醛树脂是指热塑性酚醛树脂。
3.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的热固性酚醛树脂是指液态或者固态的热固性酚醛树脂。
4.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的纳米橡胶是指丁腈纳米橡胶。
5.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的固化剂是六次甲基四胺、多聚甲醛之一种或者两种混合。
6.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的固化促进剂是指氧化钙、氧化镁、氧化锌、氢氧化钙、氢氧化镁之一种或至少任意两种混合。
7.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的脱模剂是指硬脂酸、硬脂酸钙、硬脂酸锌、硬脂酸镁之一种或者至少任意两种混合。
8.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的陶瓷粉填料是指100目以上的陶瓷粉。
9.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的其他矿物填料是指滑石粉、氢氧化铝、碳酸钙、云母粉之一种或者至少任意两种混合。
10.根据权利要求1所述的高弯曲强度酚醛模塑料，其特征在于所述的增强纤维是玻璃纤维。
CN201210185879.2A 2012-06-07 2012-06-07 高弯曲强度酚醛模塑料 Active CN102775723B (zh)