CN102774104B - Die directly plates composite package film and preparation method thereof of windowing - Google Patents
Die directly plates composite package film and preparation method thereof of windowing Download PDFInfo
- Publication number
- CN102774104B CN102774104B CN201210203722.8A CN201210203722A CN102774104B CN 102774104 B CN102774104 B CN 102774104B CN 201210203722 A CN201210203722 A CN 201210203722A CN 102774104 B CN102774104 B CN 102774104B
- Authority
- CN
- China
- Prior art keywords
- layer
- film
- aluminizing
- compound
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses die and directly plate composite package film and preparation method thereof of windowing, described packaging film is respectively printing from outside to inside, Biaxially oriented polypropylene layer of aluminizing, biaxial tension PETG layer, compound curtain coating polypropylene layer.The present invention compared with prior art, has transparency high, and printed patterns is accurately clear, the feature that deflection is good.
Description
Technical field
The invention belongs to composite package film and preparation method thereof, belong to composite package film and preparation method thereof of windowing especially.
Background technology
Existing common packaging film of aluminizing, be that all parts of face have aluminizer to hide, content cannot well be shown.
Summary of the invention
1st technical problem to be solved by this invention is to provide a kind ofly well can show that the die of content directly plates composite package film of windowing.
2nd technical problem to be solved by this invention is the preparation method of above-mentioned composite membrane.
The technical scheme of technical solution problem of the present invention is: die directly plates composite package film of windowing, and is respectively printing from outside to inside, Biaxially oriented polypropylene layer of aluminizing, biaxial tension PETG layer, compound curtain coating polypropylene layer;
Described printing, Biaxially oriented polypropylene layer of aluminizing are provided with the blank portion of demonstration package film content.
Preferred composite package film is 28 μm of printings, μm biaxial tension PETG layer/40, Biaxially oriented polypropylene layer/12 μm compound curtain coating polypropylene layer of aluminizing;
Described compound curtain coating polypropylene layer is respectively corona layer, sandwich layer, hot sealing layer from outside to inside.
In order to improve the polyacrylic deflection of compound curtain coating, described sandwich layer is HOPP and nucleation intensity strengthening agent blending extrusion, and the weight ratio of HOPP and nucleation intensity strengthening agent is 100:1-10.
In order to improve the polyacrylic transparency of compound curtain coating, also can add trimesic acid in the core, the weight ratio of HOPP and trimesic acid is 100:1-10.
Preparation method of the present invention comprises the following steps:
A) print, the preparation section of bidirectional stretching polypropylene film of aluminizing:
B) preparation section of compound cast polypropylene film;
C) compound working procedure
D) cutting process is divided;
Described a) to print, the preparation section of bidirectional stretching polypropylene film of aluminizing, comprise following operation:
In bidirectional stretching polypropylene film printed design pattern operation, blank parts coating water soluble varnish, the remainder of showing content is being needed to apply high temperature resistant gloss oil operation, operation of aluminizing, wash aluminium operation.
Described high temperature resistant gloss oil is the high temperature resistant gloss oil of X-A18 type of Shantou Feng Hua company.
Described water soluble varnish is the DM-515 type water soluble varnish of Shantou Feng Hua company.
Due in printing process, a part of high temperature resistant gloss oil is coated in above printing zone ink, and need aluminize on gloss oil surface.Therefore below demand fulfillment, some requires:
1) reactionless with look ink, ink of checking colors does not dissolve.
2) in process of aluminizing, temperature is very high, and therefore this gloss oil will have good high-temperature resistant result, can effectively protect printing-ink not corroded by aluminum vapor in evaporate process.
3) strong with ink adheres power, also there is good adhesive force with aluminium coated, ensure washing the good appearance of aluminium process.For above-mentioned requirements, have selected the high temperature resistant gloss oil of X-A18 type of Shantou maple China.
Water soluble varnish is coated in the blank space without printing zone, washing in aluminium process, it washed away together with attached superincumbent aluminium lamination.Therefore below demand fulfillment, some requires:
1) combine fully with film itself, densification, can not have and lose a little, or the problem such as particle line.
2) good water solubility, meeting water can completely fast peel away with film.
3) gloss oil good leveling property, easily evenly coating.
To above-mentioned requirements, have selected the DM-515 type water soluble varnish of Shantou maple China.
The present invention compared with prior art, has transparency high, and printed patterns is accurately clear, the feature that deflection is good.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention.
Fig. 2 is the structural representation of compound curtain coating polypropylene layer of the present invention.
Fig. 3 is the process chart of preparation method of the present invention.
In Fig. 1,2,1 for printing, Biaxially oriented polypropylene layer of aluminizing, 2 for biaxial tension PETG layer, 3 be compound curtain coating polypropylene layer; 4 be corona layer, 5 be sandwich layer, 6 for hot sealing layer.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in detail.
Bidirectional stretching polypropylene film of the present invention (28BOPP)
The key technical indexes:
Biaxial tension pet film (PET film)
The key technical indexes: table (2)
Embodiment 1:
Die directly plates the preparation method of composite package film of windowing, and comprises the following steps,
A) print, the preparation section of bidirectional stretching polypropylene film of aluminizing:
In bidirectional stretching polypropylene film printed design pattern operation, blank parts coating water soluble varnish, the remainder of showing content is being needed to apply high temperature resistant gloss oil operation, operation of aluminizing, wash aluminium operation.
Described washes in aluminium operation, and described live-roller is drive roll, and washing aluminium liquid is water.
Described high temperature resistant gloss oil is the high temperature resistant gloss oil of X-A18 type of Shantou Feng Hua company.
Described water soluble varnish is the DM-515 type water soluble varnish of Shantou Feng Hua company.
B) preparation section of compound cast polypropylene film;
Corona layer: homopolymerization PP (FC801MX)
Sandwich layer: 95% homopolymerization PP (FC801)+nucleation intensity strengthening agent 5%(FIS600)
Hot sealing layer: ternary polymerization PP (FL7632L)+opening agent (AB10S)+slipping agent (SL07PP)
FC801MX: degree of crystallinity is high, deflection is good, and processability is good, anti-stick company, easy surface corona process.For three-layer co-extruded middle corona layer in this resin.Ash is few, and impurity is few, and film-formation result is good.
FC801: degree of crystallinity is high, deflection is good, and processability is good, the slipping agent containing certain amount, and this resin is used for three-layer co-extruded sandwich layer.
FL7632L: ternary polymerization pp, fusing point is low, anti-stick company, and smoothness is good, and salivation processability is good.For third layer, play good low-temperature heat-sealing effect.
AB10S: opening agent, effective ingredient uniform particle sizes, Kekelé structure count is good.
SL07PP: slipping agent, good heat resistance, can not stick together between the caudacoria of interpolation, makes film have lower coefficient of friction.
FIS600: nucleation intensity strengthening agent.Add nucleation intensity strengthening agent, polypropylene film degree of crystallinity is improved and reduces geode particle diameter again simultaneously, light transmittance is improved.The raising of degree of crystallinity makes the deflection of film significantly improve, and the transparency that geode particle diameter reduces film just obviously increases.
C) compound working procedure: the printing prepared, bidirectional stretching polypropylene film of aluminizing, compound cast polypropylene film and PET film are carried out dry type compound, obtain composite package film, it be 28 μm of printings from outside to inside, μm biaxial tension PETG layer/40, Biaxially oriented polypropylene layer/12 μm compound curtain coating polypropylene layer of aluminizing;
D) cutting process is divided;
Film prepared by embodiment 1 is respectively printing from outside to inside, Biaxially oriented polypropylene layer 1 of aluminizing, biaxial tension PETG layer 2, compound curtain coating polypropylene layer 3; Described compound curtain coating polypropylene layer 3 is respectively corona layer 4, sandwich layer 5, hot sealing layer 6 from outside to inside.
Embodiment 2:
Except in the preparation section of b) compound cast polypropylene film, the material of sandwich layer is: 96% homopolymerization PP (FC801)+nucleation intensity strengthening agent 3%(FIS600) outward, all the other are identical with embodiment 1.
Embodiment 3:
Except in the preparation section of b) compound cast polypropylene film, the material of sandwich layer is: 98% homopolymerization PP (FC801)+nucleation intensity strengthening agent 1%(FIS600) outside+trimesic acid 1%, all the other are identical with embodiment 1.
The technical indicator of the composite membrane that embodiment 1-3 is made is as follows:
Claims (3)
1. die directly plates composite package film of windowing, and is respectively printing from outside to inside, Biaxially oriented polypropylene layer of aluminizing, biaxial tension PETG layer, compound curtain coating polypropylene layer;
Described compound curtain coating polypropylene layer is respectively corona layer, sandwich layer, hot sealing layer from outside to inside,
Described sandwich layer is HOPP and nucleation intensity strengthening agent blending extrusion, and the weight ratio of HOPP and nucleation intensity strengthening agent is 100: 1-10, adds trimesic acid in the core, and the weight ratio of HOPP and trimesic acid is 100: 1-10;
Described printing, Biaxially oriented polypropylene layer of aluminizing are provided with the blank portion of demonstration package film content.
2. directly plate composite package film of windowing according to the die described in claim 1, it is characterized in that: described composite package film is 28 μm of printings, Biaxially oriented polypropylene layer of aluminizing, 12 μm of biaxial tension PETG layers, 40 μm of compound curtain coating polypropylene layers.
3. die according to claim 1 directly plates the preparation method of composite package film of windowing, and comprises the following steps:
A) print, the preparation section of bidirectional stretching polypropylene film of aluminizing:
B) preparation section of compound cast polypropylene film;
C) compound working procedure, carries out dry type compound by the printing prepared, bidirectional stretching polypropylene film of aluminizing, compound cast polypropylene film and biaxial tension pet film, obtains composite package film;
D) cutting process is divided;
Described a) to print, the preparation section of bidirectional stretching polypropylene film of aluminizing, comprise following operation:
In bidirectional stretching polypropylene film printed design pattern operation, blank parts coating water soluble varnish, the remainder of showing content is being needed to apply high temperature resistant gloss oil operation, operation of aluminizing, wash aluminium operation;
Described high temperature resistant gloss oil is the high temperature resistant gloss oil of X-A18 type of Shantou Feng Hua company;
Described water soluble varnish is the DM-515 type water soluble varnish of Shantou Feng Hua company.