CN103587163A - Method for locally printing plate aluminum on package film - Google Patents
Method for locally printing plate aluminum on package film Download PDFInfo
- Publication number
- CN103587163A CN103587163A CN201310544378.3A CN201310544378A CN103587163A CN 103587163 A CN103587163 A CN 103587163A CN 201310544378 A CN201310544378 A CN 201310544378A CN 103587163 A CN103587163 A CN 103587163A
- Authority
- CN
- China
- Prior art keywords
- printing
- base
- wash
- aluminium
- pet
- Prior art date
Abstract
Description
Technical field
The present invention relates to packaging film print field, refer to especially a kind of method of packaging film local printing of aluminized.
Background technology
Aluminized complex film is by the metallized films such as VMPET, VMBOPP, VMCPP or VMPE and the compound and flexible packing material of a kind of barrier having had with aluminium gloss of forming of transparent plastic film, it has good metallic luster, good barrier property, convenience, the advantage such as inexpensive and is widely used in the external packing of food, health products, medicine, cosmetics, especially on dry, dilated food.
The alkali cleaning product of aluminizing: at the face of the aluminizing printed patterns of the base material of aluminizing (as VMBOPP, VMPET etc.); non-washing in aluminium place protected ink; after alkali cleaning; after the aluminium lamination and alkali oxidation reaction at not upper protection ink place; aluminium lamination is washed off, becomes transparent window, thereby solves the object that the packaging product of aluminizing can local be seen content; impel consumer's desire to buy, very attractive in appearance again.The alkali cleaning product shortcoming of aluminizing: 1. can shade after printed patterns alkali cleaning, pattern is brightless is just not attractive in appearance yet.When 2. printing occurs that cutter line, version dirt etc. are abnormal, during alkali cleaning, aluminium lamination does not wash clean, and scrappage is high.3. the material such as alkali and aluminium oxide is attached to packaging bag, unhelpful to health.4. after alkali cleaning, generate aluminium oxide, contaminated environment.
Summary of the invention
The present invention proposes a kind of method of packaging film local printing of aluminized, has solved the problems such as printed patterns obfuscation in prior art, not environmental protection, yields be low.
Technical scheme of the present invention is achieved in that
A method for packaging film local printing of aluminized, comprising:
A) in the corona surface picture and text printing of base material, wherein said base material is transparent or semitransparent film;
B) dry afterwards; Then carry out full version and aluminize, be dipped in water and wash afterwards, washing post-drying;
C) the compound at least transparent material layer of the printing surface of the described base material after oven dry, the washing product of must aluminizing.
As preferred technical scheme, described printing is intaglio printing.
As preferred technical scheme, described base material is biaxially oriented polyester film (PET), bidirectional stretching polypropylene film (BOPP), cast polypropylene film (CPP) and polyethylene film (PE).
As preferred technical scheme, described base material is plastic sheeting.
As preferred technical scheme, described picture and text printing is polychrome printing, and wherein having at least of the same colour is colorless ink, washes aluminum window port part for washing ink.
As preferred technical scheme, described dry temperature is 55-65 ℃.
As preferred technical scheme, described washing is used is the water of 18-25 ℃.Washing will guarantee to wash the complete of aluminium, and guarantee transparency is high.
As preferred technical scheme, the temperature of described oven dry is 60-80 ℃.
As preferred technical scheme, described complex method is that glue bonding dry type composite algorithm or heat posted are bonding.
As preferred technical scheme, the common structure of described washing product is BOPP/ aluminium/PE, BOPP/ aluminium/CPP, PET/ aluminium/PE, PET/ aluminium/CPP, BOPP/ aluminium/PET/PE, PET/ aluminium/PET/PE, BOPP/ aluminium/PET/CPP or the PET/ aluminium/PET/CPP that aluminizes/wash that aluminizes/wash that aluminizes/wash that aluminizes/wash that aluminizes/wash that aluminizes/wash that aluminizes/wash that aluminizes/wash.
Beneficial effect
The product printed patterns that the inventive method makes is full, light.Do not exist and wash the sordid problem of aluminium, bad scrappage is little.The non-cohesive any alkaline matter of packaging bag and alkaline oxygenated material, environmental protection, aluminium scrap easily reclaims.
The specific embodiment
Below the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only the present invention's part embodiment, rather than whole embodiment.Embodiment based in the present invention, those of ordinary skills, not making all other embodiment that obtain under creative work prerequisite, belong to the scope of protection of the invention.
The present invention be take the conventional aluminizer of those skilled in the art and is carried out the preparation of laminating production as base material, the present invention is not particularly limited described aluminum plating process, for the base material of aluminizing well known to those skilled in the art, as biaxially oriented polyester film (PET), bidirectional stretching polypropylene film (BOPP), cast polypropylene film (CPP) and polyethylene film (PE) etc.The present invention is not particularly limited the source of described base material, can directly buy from the market, also can be according to the method well known to those skilled in the art preparation of aluminizing.The present invention is not particularly limited described thickness of aluminizing, and those skilled in the art can select to determine according to the purposes of target aluminized complex film.The base material using in the present invention can be directly to buy from the market the product after corona, or on the base material of buying, to carry out sided corona treatment be all feasible.Base material in following embodiment is all the material after the sided corona treatment of directly buying.
Preparation before printing:
Design
1. first determine it is intaglio printing.
2. according to client's intention, layout reserve part and transparent window portion (washing aluminum portions).
3. color separation: carry out color separation according to the designing requirement of pattern, as colors such as black, blueness, redness, yellow, whites, can not color separation too many, must meet the requirement of printery's production equipment, as printed the equipment of ten colors, color separation can not a more than ten color.
Typesetting
1. determine printing material, as BOPP, PET etc.
2. determine printing surface, inner seal.
3. according to the requirement of typography and pattern reproduction, the sequencing of row's print color is process color order.
4. the door width of consideration production efficiency, printing equipment and girth, bag number, stipulate printing plate cylinder typesetting quantity: longitudinal several, laterally several.
Plate-making
1. according to technological requirement, pipe cutting-scraping-copper facing-scraping-engraving-chromium plating-scrape-check.
2. printing draw a design-be up to the standards-is put into production.
Embodiment 1
A method for packaging film local printing of aluminized, structure: the BOPP/ aluminium/PET/PE that aluminizes/wash
Comprise:
A) select intaglio printing, in the corona surface picture and text printing of BOPP base material, wherein having of the same colour is colorless ink, washes aluminum window port part for washing ink.Base material is transparent or semitransparent film.
B) dry at 55-65 ℃ afterwards; Then carry out full version and aluminize, be dipped in water and wash afterwards, washing off with the aluminium lamination of washing ink on base material, become transparent window, the temperature of water is 18-25 ℃ (normal-temperature water), must guarantee to wash the complete of aluminium in the time of washing, and guarantee transparency is high like this.After washing, setting at least three group oven for drying, then rollings within the scope of 60-80 ℃ of staged temperature.
C) the compound PET of glue for the printing surface of the base material after oven dry, at the compound PE of glue for skin of PET, the washing product of must aluminizing.Glue is two-component polyurethane adhesive.
To aluminize washing product producing through bag operation, obtain packaging bag.
This product printed patterns is full, light.Do not exist and wash the sordid problem of aluminium, bad scrappage is little.The non-cohesive any alkaline matter of packaging bag and alkaline oxygenated material, environmental protection, aluminium scrap easily reclaims.
Embodiment 2
A method for packaging film local printing of aluminized, structure: the PET/ aluminium/PET/CPP that aluminizes/wash
Comprise:
A) select intaglio printing, in the corona surface picture and text printing of PET base material, wherein having of the same colour is colorless ink, washes aluminum window port part for washing ink.Base material is transparent or semitransparent film.
B) dry at 55-65 afterwards; Then carry out full version and aluminize, be dipped in water and wash afterwards, washing off with the aluminium lamination of washing ink on base material, become transparent window, the temperature of water is 18-25 ℃ (being normal-temperature water), must guarantee to wash the complete of aluminium in the time of washing, and guarantee transparency is high like this.After washing, setting at least three group oven for drying, then rollings within the scope of 60-80 ℃ of staged temperature.
C) the compound PET of glue for the printing surface of the base material after oven dry, at the compound PE of glue for skin of PET, the washing product of must aluminizing.Glue is two-component polyurethane adhesive.
To aluminize washing product producing through bag operation, obtain packaging bag.
This product printed patterns is full, light.Do not exist and wash the sordid problem of aluminium, bad scrappage is little.The non-cohesive any alkaline matter of packaging bag and alkaline oxygenated material, environmental protection, aluminium scrap easily reclaims.
Embodiment 3
A method for packaging film local printing of aluminized, the structure BOPP/ aluminium/PE that aluminizes/wash
Comprise:
A) select intaglio printing, in the corona surface picture and text printing of BOPP base material, wherein having of the same colour is colorless ink, washes aluminum window port part for washing ink.Base material is transparent or semitransparent film;
B) dry at 55-65 ℃ afterwards; Then carry out full version and aluminize, be dipped in water and wash afterwards, washing off with the aluminium lamination of washing ink on base material, become transparent window, the temperature of water is 18-25 ℃ (being normal-temperature water), must guarantee to wash the complete of aluminium in the time of washing, and guarantee transparency is high like this.After washing, setting at least three group oven for drying, then rollings within the scope of 60-80 ℃ of staged temperature;
C) the compound PE of glue for the printing surface of the base material after oven dry, the washing product of must aluminizing.Glue is two-component polyurethane adhesive.
To aluminize washing product through bag operation, obtain packaging bag.
This product printed patterns is full, light.Do not exist and wash the sordid problem of aluminium, bad scrappage is little.The non-cohesive any alkaline matter of packaging bag and alkaline oxygenated material, environmental protection, aluminium scrap easily reclaims.
The foregoing is only preferred embodiment of the present invention, in order to limit the present invention, within the spirit and principles in the present invention not all, any modification of doing, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (10)