CN102757854A - 一种采用硬质合金刀具或被加工件为硬质合金的切削液 - Google Patents
一种采用硬质合金刀具或被加工件为硬质合金的切削液 Download PDFInfo
- Publication number
- CN102757854A CN102757854A CN2012101771248A CN201210177124A CN102757854A CN 102757854 A CN102757854 A CN 102757854A CN 2012101771248 A CN2012101771248 A CN 2012101771248A CN 201210177124 A CN201210177124 A CN 201210177124A CN 102757854 A CN102757854 A CN 102757854A
- Authority
- CN
- China
- Prior art keywords
- cutting fluid
- methyl
- acid ester
- wimet
- sulphosuccinic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种采用硬质合金刀具或被加工件为硬质合金的切削液,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺24-26%,硼酸5-7%,聚氧乙烯十八烷基磷酸酯3-5%,聚氧乙烯苯基磷酸酯5-7%,酚醚磷酸酯6-8%,邻苯二甲酸二丁酯2-4%,苯甲酸钠2-4%,丙三醇2-4%,异塞唑啉酮0.4-0.6%,苯并三氮唑0.6-0.8%,壬基酚聚氧乙烯醚0.3-0.5%,甲基硅油0.6-1.0%,去离子水余量。
Description
技术领域
本发明涉及金属切削加工技术领域,尤其涉及一种采用硬质合金刀具或被加工件为硬质合金的切削液。
背景技术
水基金属切削液可分为可溶性油(乳化液)、半合成切削液(微乳化液)和全合成切削液三种。与可溶性油及半合成切削液相比,全合成切削液不含矿物油,其各组分如防锈剂、极压抗磨添加剂、表面活性剂、防腐剂和消泡剂等多种添加剂均溶于水,稀释液呈透明状或半透明状。全合成型切削液冷却效果好、加工场所清洁、产品性能稳定,是一类应用范围广泛的金属加工液。
但全合成型切削液中通常含有三乙醇胺,三乙醇胺作为全合成切削液的重要添加剂,有助于切削液浸润、渗透于磨(切)削界面,充分发挥全合成切削液的清洗、润滑和防锈作用。但是,三乙醇胺等氨类添加剂对碳化钨钴等硬质合金中的钴有浸出作用(参见Pat.Brutto.Water hazard.Cutting ToolEngineering,1996,(12):50;参见张秀玲,高筠.含三乙醇胺磨削液对硬质合金刀具的危害.硬质合金,2000,17(4):231-232)。而金属钴是碳化钨钴等硬质合金的粘结剂,如果在使用硬质合金刀具或对硬质合金进行磨削加工时,碳化钨钴硬质合金中的钴元素被浸出,一方面直接影响着硬质合金的坚韧性和抗震性等性能,另一方面导致碳化钨钴硬质合金制品的表面出现彩色条纹,直接影响制品的外观。
在使用硬质合金刀具或对硬质合金进行磨削加工的场合,为了避免全合成切削液对钨钴或钛钴等硬质合金中的钴的浸出作用,国内学者将油酸三乙醇胺代替三乙醇胺,这样可部分降低全合成切削液对合金中钴的浸出作用,但仍不能完全抑制钴元素的浸出(参见:张好强.硬质合金刀具钴元素浸出机理及对策研究,河北理工大学硕士学位论文,2005年)。
因此,现有技术中的切削液不适于采用硬质合金刀具加工,或不适于对硬质合金进行切削加工。
发明内容
本发明的目的在于提出一种采用硬质合金刀具或被加工件为硬质合金的切削液,该切削液适于采用硬质合金刀具进行的切削加工,也适于被加工件涉及硬质合金的切削加工。
为达此目的,本发明采用以下技术方案:
一种采用硬质合金刀具或被加工件为硬质合金的切削液,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺24-26%,硼酸5-7%,聚氧乙烯十八烷基磷酸酯3-5%,聚氧乙烯苯基磷酸酯5-7%,酚醚磷酸酯6-8%,邻苯二甲酸二丁酯2-4%,苯甲酸钠2-4%,丙三醇2-4%,异塞唑啉酮0.4-0.6%,苯并三氮唑0.6-0.8%,壬基酚聚氧乙烯醚0.3-0.5%,甲基硅油0.6-1.0%,去离子水余量。
优选,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺24.5-25.5%,硼酸5.5-6.5%,聚氧乙烯十八烷基磷酸酯3.5-4.5%,聚氧乙烯苯基磷酸酯5.5-6.5%,酚醚磷酸酯6.5-7.5%,邻苯二甲酸二丁酯2.5-3.5%,苯甲酸钠2.5-3.5%,丙三醇2.5-3.5%,异塞唑啉酮0.45-0.55%,苯并三氮唑0.65-0.75%,壬基酚聚氧乙烯醚0.35-0.45%,甲基硅油0.7-0.9%,去离子水余量。
最优选,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺25%,硼酸6.0%,聚氧乙烯十八烷基磷酸酯4.0%,聚氧乙烯苯基磷酸酯6.0%,酚醚磷酸酯7.0%,邻苯二甲酸二丁酯3.0%,苯甲酸钠3.0%,丙三醇3.0%,异塞唑啉酮0.50%,苯并三氮唑0.70%,壬基酚聚氧乙烯醚0.40%,甲基硅油0.80%,去离子水余量。
本发明的组成机理为:不采用三乙醇胺,而是采用2-氨基-2-甲基-1-丙醇胺抑制钴的析出,并在此基础上,复配硼酸、聚氧乙烯十八烷基磷酸酯、聚氧乙烯苯基磷酸酯、酚醚磷酸酯、邻苯二甲酸二丁酯等各种添加剂,采用苯甲酸钠作为防锈成分,在适量复配其它添加剂,并在大量实验基础上确定了各个组份的添加比例,使得各组份之间达到协同作用效果,使得切削液除了具有抑制钴析出的作用外,还兼具普通切削液所要求的润滑,防锈,冷却和清洗作用。
与现有技术相比本发明具有如下突出的优点及有益效果:
1)本发明的切削液能够防止钴析出,适用于采用硬质合金刀具进行的切削加工,也适于被加工件涉及硬质合金的切削加工。
2)本发明的切削液在使用时润滑,防锈,冷却和清洗效果突出,完全满足使用需求。
3)本发明的切削液绿色环保,所采用的原料成本低,使用寿命长。
具体实施方式
实施例一
一种采用硬质合金刀具或被加工件为硬质合金的切削液,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺24%,硼酸7%,聚氧乙烯十八烷基磷酸酯3%,聚氧乙烯苯基磷酸酯7%,酚醚磷酸酯6%,邻苯二甲酸二丁酯4%,苯甲酸钠2%,丙三醇4%,异塞唑啉酮0.4%,苯并三氮唑0.8%,壬基酚聚氧乙烯醚0.3%,甲基硅油1.0%,去离子水余量。
实施例二
一种采用硬质合金刀具或被加工件为硬质合金的切削液,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺26%,硼酸5%,聚氧乙烯十八烷基磷酸酯5%,聚氧乙烯苯基磷酸酯5%,酚醚磷酸酯8%,邻苯二甲酸二丁酯2%,苯甲酸钠4%,丙三醇2%,异塞唑啉酮0.6%,苯并三氮唑0.6%,壬基酚聚氧乙烯醚0.5%,甲基硅油0.6%,去离子水余量。
实施例三
一种采用硬质合金刀具或被加工件为硬质合金的切削液,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺24.5%,硼酸6.5%,聚氧乙烯十八烷基磷酸酯3.5%,聚氧乙烯苯基磷酸酯6.5%,酚醚磷酸酯6.5%,邻苯二甲酸二丁酯3.5%,苯甲酸钠2.5%,丙三醇3.5%,异塞唑啉酮0.45%,苯并三氮唑0.75%,壬基酚聚氧乙烯醚0.35%,甲基硅油0.9%,去离子水余量。
实施例四
一种采用硬质合金刀具或被加工件为硬质合金的切削液,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺25.5%,硼酸5.5%,聚氧乙烯十八烷基磷酸酯4.5%,聚氧乙烯苯基磷酸酯5.5%,酚醚磷酸酯7.5%,邻苯二甲酸二丁酯2.5%,苯甲酸钠3.5%,丙三醇2.5%,异塞唑啉酮0.55%,苯并三氮唑0.65%,壬基酚聚氧乙烯醚0.45%,甲基硅油0.7%,去离子水余量。
实施例五
一种采用硬质合金刀具或被加工件为硬质合金的切削液,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺25%,硼酸6%,聚氧乙烯十八烷基磷酸酯4%,聚氧乙烯苯基磷酸酯6%,酚醚磷酸酯7%,邻苯二甲酸二丁酯3%,苯甲酸钠3%,丙三醇3%,异塞唑啉酮0.5%,苯并三氮唑0.7%,壬基酚聚氧乙烯醚0.4%,甲基硅油0.8%,去离子水余量。
Claims (3)
1.一种采用硬质合金刀具或被加工件为硬质合金的切削液,其特征在于,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺24-26%,硼酸5-7%,聚氧乙烯十八烷基磷酸酯3-5%,聚氧乙烯苯基磷酸酯5-7%,酚醚磷酸酯6-8%,邻苯二甲酸二丁酯2-4%,苯甲酸钠2-4%,丙三醇2-4%,异塞唑啉酮0.4-0.6%,苯并三氮唑0.6-0.8%,壬基酚聚氧乙烯醚0.3-0.5%,甲基硅油0.6-1.0%,去离子水余量。
2.如权利要求1所述的一种采用硬质合金刀具或被加工件为硬质合金的切削液,其特征在于,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺24.5-25.5%,硼酸5.5-6.5%,聚氧乙烯十八烷基磷酸酯3.5-4.5%,聚氧乙烯苯基磷酸酯5.5-6.5%,酚醚磷酸酯6.5-7.5%,邻苯二甲酸二丁酯2.5-3.5%,苯甲酸钠2.5-3.5%,丙三醇2.5-3.5%,异塞唑啉酮0.45-0.55%,苯并三氮唑0.65-0.75%,壬基酚聚氧乙烯醚0.35-0.45%,甲基硅油0.7-0.9%,去离子水余量。
3.如权利要求2一种采用硬质合金刀具或被加工件为硬质合金的切削液,其特征在于,所述切削液按重量百分比由下述组份组成:2-氨基-2-甲基-1-丙醇胺25%,硼酸6.0%,聚氧乙烯十八烷基磷酸酯4.0%,聚氧乙烯苯基磷酸酯6.0%,酚醚磷酸酯7.0%,邻苯二甲酸二丁酯3.0%,苯甲酸钠3.0%,丙三醇3.0%,异塞唑啉酮0.50%,苯并三氮唑0.70%,壬基酚聚氧乙烯醚0.40%,甲基硅油0.80%,去离子水余量。