CN102756245A - 一种环保型高密度耐磨链条销轴及其制造方法 - Google Patents
一种环保型高密度耐磨链条销轴及其制造方法 Download PDFInfo
- Publication number
- CN102756245A CN102756245A CN2012102635630A CN201210263563A CN102756245A CN 102756245 A CN102756245 A CN 102756245A CN 2012102635630 A CN2012102635630 A CN 2012102635630A CN 201210263563 A CN201210263563 A CN 201210263563A CN 102756245 A CN102756245 A CN 102756245A
- Authority
- CN
- China
- Prior art keywords
- environment
- bearing pin
- friendly type
- heating
- type high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型高密度耐磨链条销轴及其制造方法,包括如下步骤:(1)备料:用切轴机将圆柱型合金钢切割成规定长度的工件A;(2)高频加热:将工件A进行高频加热,加热温度800℃-900℃;(3)压锻:将步骤(2)所得工件放入压锻模具内,以30-40吨压力进行压锻:(4)常规热处理:将步骤(3)所得工件脱模后进行常规热处理。该方法避免了传统研磨制造方法中水和砂的使用,减少了水资源浪费和环境污染,更为环保,并且其抗拉耐磨性能和硬度有所提高,增加了链条销轴的使用寿命。
Description
技术领域
本发明涉及一种链条销轴。
背景技术
传统的汽车、摩托车链条销轴的加工方法是:先将圆柱形合金钢切断,然后加入砂和水进行研磨,研磨出的销轴是两端具有圆角的圆柱体。这种研磨加工方法每加工500KG销轴要耗费200KG砂及500KG水,用水量较大且排放大量砂浆污染环境。
发明内容
本发明的目的是提供一种不使用水和砂,环境污染小的链条销轴加工方法。
为解决上述技术问题,本发明包括如下步骤:
(1)备料:用切轴机将圆柱型合金钢切割成规定长度的工件A;
(2)高频加热:将工件A进行高频加热,加热温度800°C-900°C;
(3)压锻:将步骤(2)所得工件放入压锻模具内,以30-40吨压力进行压锻;
(4)常规热处理:将步骤(3)所得工件脱模后进行常规热处理。
优选地,其步骤(1)所述的规定长度为工件经过步骤(3)后的1.05-1.1倍。
优选地,其步骤(3)所述压锻模具的内腔为两端有倒角的圆柱体。
优选地,所述倒角为45°-55°。
优选地,其步骤(4)所述的常规热处理包括步骤:(1)淬火,加热温度930°C-950°C,加热时间45分钟;(2)回火,加热温度320°C-350°C,加热时间50分钟,常温下冷却。
由上述方法制造的一种链条销轴是两端有倒角的圆柱体。
优选地,所述链条销轴是两端有倒角的圆柱体,所述倒角为45°-55°。
本发明利用热压锻的方法制造链条销轴,避免了水和砂的使用,减少了环境污染和资源浪费,更加环保。并且热压断可以在一定程度上增加链条销轴密度,提高链条销轴的抗拉耐磨性能和硬度,传统方法制造的销轴硬度为HRC79-81,本发明最终产品的硬度为HRC82-85,其使用寿命增加5%-10%。
附图说明
图1是本发明的主视图。
具体实施方式
下面结合具体实施例对本发明做进一步说明:
实施例1:
材料30CrMnTi,HRB77,材料切割为压锻后长度的1.05倍; 800°C高频加热;放入模具以30吨压力压锻;淬火,加热温度930°C,加热时间45分钟;回火,加热温度330°C,加热时间50分钟,常温下冷却。最终硬度为HRC82。使用寿命(以使用里程计算)增加5%。
实施例2:
材料30CrMnTi,HRB77,材料切割为压锻后长度的1.07倍; 850°C高频加热;放入模具以35吨压力压锻;淬火,加热温度930°C,加热时间45分钟;回火,加热温度330°C,加热时间50分钟,常温下冷却。最终硬度为HRC84。使用寿命(以使用里程计算)增加10%。
实施例3:
材料20CrMnMo,HRB77,材料切割为压锻后长度的1.10倍; 900°C高频加热;放入模具以40吨压力压锻;淬火,加热温度930°C,加热时间45分钟;回火,加热温度330°C,加热时间50分钟,常温下冷却。最终硬度为HRC85。使用寿命(以使用里程计算)增加10%。
制造出的链条销轴如图1所示,为两端有倒角的圆柱体,其压锻模具的内腔形状与链条销轴相同,所述倒角A为45°-55°。
以上已将本发明做一详细说明,以上所述,仅为本发明之较佳实施例而已,当不能限定本发明实施范围,即凡依本申请范围所作均等变化与修饰,皆应仍属本发明涵盖范围内。
Claims (8)
1.一种环保型高密度耐磨链条销轴及其制造方法,该方法包括如下步骤:
备料:用切轴机将圆柱型合金钢切割成规定长度的工件A;
高频加热:将工件A进行高频加热,加热温度800°C-900°C;
压锻:将步骤(2)所得工件放入压锻模具内,以30-40吨压力进行压锻;
常规热处理:将步骤(3)所得工件脱模后进行常规热处理。
2.如权利要求1所述的一种环保型高密度耐磨链条销轴及其制造方法,其特征在于:其步骤(1)所述的规定长度为最终成品长度1.05-1.1倍。
3.如权利要求1所述的一种环保型高密度耐磨链条销轴及其制造方法,其特征在于:其步骤(3)所述压锻模具的内腔为两端有倒角的圆柱体。
4.如权利要求3所述的一种环保型高密度耐磨链条销轴及其制造方法,其特征在于:所述倒角为45°-55°。
5.如权利要求1所述的一种环保型高密度耐磨链条销轴及其制造方法,其特征在于:其步骤(4)所述的常规热处理包括步骤:(1)淬火,加热温度930°-950°,加热时间45分钟;(2)回火,加热温度320°-350°,加热时间50分钟,常温下冷却。
6.一种环保型高密度耐磨链条销轴,其特征在于:它是根据权利要求1-5任意一项所述方法制造的。
7.如权利要求6所述的一种环保型高密度耐磨链条销轴,其特征在于:所述链条销轴是两端有倒角的圆柱体。
8.如权利要求7所述的一种环保型高密度耐磨链条销轴,其特征在于:所述倒角为45°-55°。