CN102755198A - 具高链接力的口腔牙材结构 - Google Patents
具高链接力的口腔牙材结构 Download PDFInfo
- Publication number
- CN102755198A CN102755198A CN2011101083864A CN201110108386A CN102755198A CN 102755198 A CN102755198 A CN 102755198A CN 2011101083864 A CN2011101083864 A CN 2011101083864A CN 201110108386 A CN201110108386 A CN 201110108386A CN 102755198 A CN102755198 A CN 102755198A
- Authority
- CN
- China
- Prior art keywords
- metal base
- oral cavity
- tool
- equipment structure
- ceramic film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明为一种具高链接力的口腔牙材结构，用以结合在牙床上，口腔牙材结构包括金属基座、利用大气电浆熔射的陶瓷膜层、及牙科瓷层，金属基座套合在牙床上，陶瓷膜层喷镀在金属基座的表面，牙科瓷层则是烧结在陶瓷膜层上，以此增加金属基座及牙科瓷层之间的链接力，并避免金属基座的外露及金属离子释出的问题。
Description
技术领域
本发明与口腔内部牙材结构有关，特别是有关于一种金属链接力高的牙材结构。
背景技术
传统上，用于口腔内牙齿修复(dental restoration)的假牙(denture teeth)结构大多是以铸造作业(casting operation)或利用计算机数值控制(Computer NumericalControl，CNC)加工方式来形成构成牙冠及/或牙桥(crown and bridgeprosthodontics)等结构的牙材基座。
请参考图1，是显示现有一假牙结构1a，其结合在一牙床2a上，该假牙结构1a包含一金属基座(metal coping)10a及烧结在该金属基座10a上的一牙科瓷(dental porcelain)部20a。由于利用铸造方式所形成的该金属基座10a表面极为光滑，导致该金属基座10a及该牙科瓷部20a的结合力差。因此，在烧结该牙科瓷部20a之前，该金属基座10a的表面通常会施以喷砂工序，据以增加该金属基座10a及该牙科瓷部20a之间的结合力。
然而，利用上述工序所制成的假牙结构，其精密度差，常需经过多次校正及加工修改，不但费时、费工，且成本高。再者，现有假牙结构1a在使用一段时间后，因该金属基座10a及该牙科瓷部20a的链接强度差，造成该金属基座10a释出部分离子至人体内，恐产生致癌风险；此外，现有的假牙结构1a经过长时间的使用磨耗后，其金属基座10a会外露并氧化，不但影响强度，更造成外观上的不美观。
发明内容
本发明的一目的，在于提供一种具高链接力的口腔牙材结构，以增加金属基座及牙科瓷层之间的链接力。
本发明的另一目的，在于提供一种具高链接力的口腔牙材结构，以避免金属基座外露，增加口腔牙材的美观性。
本发明的又一目的，在于提供一种具高链接力的口腔牙材结构，以防止金属基座的离子释出至人体，减少口腔牙材对人体健康的危害。
本发明的再一目的，在于提供一种具高链接力的口腔牙材结构，其使口腔牙材结构的整体结构更为轻薄，但仍具有足够的强度，有助于假牙的精准对位，以减少在牙齿修复过程中该牙床的修磨量，降低患者的不适。
为了达成上述目的，本发明提供一种具高链接力的口腔牙材结构，用以结合在一牙床上，该具高链接力的口腔牙材结构包括一金属基座、利用大气电浆熔射的一陶瓷膜层、及一牙科瓷层，金属基座套合在牙床上，金属基座包含套合在牙床的内表面及相对于内表面的外表面，陶瓷膜层喷镀在金属基座的表面，牙科瓷层烧结在陶瓷膜层上。
相较于现有技术，本发明是利用大气电浆熔射的加工方式在金属基座表面喷镀一陶瓷膜层，该陶瓷膜层是选自氧化锆(ZrO2)、氧化铝及氢氧磷灰石(hydroxyapatite，HA)所组成的群组中的其中一种所构成，通过该陶瓷膜层来提高金属基座及牙科瓷层之间的链接力，使口腔牙材的整体结构更为轻薄，但仍具有足够的强度，有助于假牙的精准对位，以减少牙床的修磨量，降低患者的不适；再者，因陶瓷膜层可完全包覆金属基座，故可有效隔绝金属基座与外界空气接触，降低金属基座的氧化问题，防止金属基座外露而影响美观性，更可阻止金属基座氧化时而释出金属离子，避免对人体健康的危害，增加使用上的实用性及安全性。
附图说明
图1为现有一假牙结构；
图2为本发明具高链接力的口腔牙材结构的示意图；
图3为本发明具高链接力的口腔牙材结构的剖视图；
图3A为图3中A处的局部放大图；
图4为本发明具高链接力的口腔牙材结构的使用示意图；
图5为本发明具高链接力的口腔牙材结构第二实施例的结构示意图；
图6为本发明具高链接力的口腔牙材结构第二实施例的剖视图。
【主要组件符号说明】
1a 假牙结构 2a 牙床
10a 金属基座 20a 牙科瓷部
1 口腔牙材结构 2 牙床
10 金属基座 100 套置空间
101 内表面 102 外表面
15 黏着剂 20 陶瓷膜层
30 牙科瓷层
1’ 口腔牙材结构 20’ 陶瓷膜层
具体实施方式
有关本发明的详细说明及技术内容，配合附图说明如下，然而附图仅提供参考与说明用，并非用来对本发明加以限制。
请参照图2至图4，分别为本发明具高链接力的口腔牙材结构的示意图、剖视图及使用示意图；本发明的具高链接力的口腔牙材结构1是用以结合在一牙床2上，该具高链接力的口腔牙材结构包括一金属基座10、及利用大气电浆熔射的一陶瓷膜层20。
该金属基座10的材质为一般用于口腔牙材的金属，其可由镍、铬、钛、铂、钯、铜、锌、黄金、银等金属或组合(合金)所构成。该金属基座10成型有一套置空间100，该套置空间100的大小对应欲结合的该牙床2外型，以套合在该牙床2上。
该金属基座10包含套合在该牙床2上的一内表面101及相对于该内表面101的一外表面102，其中，该金属基座10的内表面101还涂布有一黏着剂15，该金属基座10及该牙床2之间以该黏着剂15而相互结合，即，该黏着剂15涂布在该牙床2及该金属基座10之间。
该陶瓷膜层20是选自氧化锆(ZrO2)、氧化铝及氢氧磷灰石(hydroxyapatite，HA)所组成的群组中的其中一种所构成。该陶瓷膜层20为一致密性高的涂层，其是利用大气电浆熔射的加工方式喷镀在该金属基座10的外表面102而形成一白色薄层，该陶瓷膜层20可提供更佳的金属基座10颜色遮蔽，且该陶瓷膜层20因完全遮蔽该金属基座10的表面而形成一良好的扩散障碍层(diffusionbarrier)，可有效完全隔绝该金属基座10与外界空气接触，以降低随着时间与使用磨耗后该金属基座10的氧化问题，进而防止日后该金属基座10外露而影响美观性，避免该金属基座10的金属离子氧化对人体健康的危害。
该大气电浆熔射是利用氩、氢、氮、氦中的其中一种或一种以上的气体离子化之后产生电弧，再将陶瓷粉末注入电弧的火焰中心，使其融熔并通过高压的该气体，高速喷覆于该金属基座10而形成该陶瓷膜层20，据此，应用于牙冠或牙桥(crown/bridge prosthodontics)结构的口腔牙材的基底即制作完成。
当该口腔牙材结构1应用在牙冠(crown)制作时，该陶瓷膜层20的表面另烧结有一牙科瓷层30。该牙科瓷层30为陶瓷材料中的一种，其是以硅土(silica，SiO2)为主，并混以适量的石英(quartz)、长石(feldspar)等其它所需的氧化物，经过多次的加工程序形成粉末，待混合适量容易后再予以涂抹在金属基座上(堆瓷)，最后再经过烧结而形成该牙科瓷层30。
该陶瓷膜层20经烧结过程后产生强度，以此可有效降低该牙科瓷层30与金属基座10的厚度需求，使该口腔牙材结构1的整体更为轻薄，但仍具有足够的强度。再者，当该口腔牙材结构1的厚度较薄时，有助于假牙的精准对位，以减少使用的黏着剂15的剂量及该牙床2的修磨量，降低患者在牙齿修复过程中的不适。
从图3中的局部放大图图3A中可看出，该陶瓷膜层20的表面粗糙不平，以提供该陶瓷膜层20及该牙科瓷层30之间良好的机械固持力，提高两者之间的链接力，并增加该口腔牙材结构1的整体强度。本实施例中，该陶瓷膜层20是利用大气电浆熔射的加工方式而喷镀在该金属基座10的外表面102，另外，该陶瓷膜层20的较佳厚度在0.5mm以下。
请继续参照图5及图6，为本发明具高链接力的口腔牙材结构的第二实施例；本实施例与第一实施例大致相同，口腔牙材结构1’包含一金属基座10及一陶瓷膜层20’及一牙科瓷层30。本实施例中与第一实施例不同之处在于该陶瓷膜层20’是喷镀在该金属基座10的内表面101及外表面102，即，该陶瓷膜层20’完全包覆该金属基座10，提供该金属基座10更完整的包覆性，且因该陶瓷膜层20的表面粗糙不平，不但可提高该陶瓷膜层20及该牙科瓷层30之间的链接力，更可增加该金属基座10及该牙床2之间的结合力。
以上所述仅为本发明的较佳实施例，非用以限定本发明的专利范围，其它运用本发明的专利精神的等效变化，均应属本发明的专利范围。
Claims (8)
1.一种具高链接力的口腔牙材结构，用以结合在一牙床上，其特征在于，该具高链接力的口腔牙材结构包括：
一金属基座，套合在所述牙床上，该金属基座包含套合在所述牙床的一内表面及相对于该内表面的一外表面；
利用大气电浆熔射的一陶瓷膜层，喷镀在该金属基座的表面；以及
一牙科瓷层，烧结在该陶瓷膜层上。
2.如权利要求1所述的具高链接力的口腔牙材结构，其特征在于，还包括一黏着剂，该黏着剂涂布在所述牙床及该金属基座之间。
3.如权利要求1所述的具高链接力的口腔牙材结构，其特征在于，该陶瓷膜层是选自氧化锆、氧化铝及氢氧磷灰石所组成的群组中的其中一种所构成。
4.如权利要求1所述的具高链接力的口腔牙材结构，其特征在于，该陶瓷膜层喷镀在该外表面。
5.如权利要求1所述的具高链接力的口腔牙材结构，其特征在于，该陶瓷膜层喷镀在该外表面及该内表面，以完全包覆该金属基座。
6.如权利要求1所述的具高链接力的口腔牙材结构，其特征在于，该陶瓷膜层的表面粗糙不平。
7.如权利要求1所述的具高链接力的口腔牙材结构，其特征在于，该大气电浆熔射是利用氩、氢、氮、氦中的其中一种或一种以上的气体离子化之后产生电弧，再将陶瓷粉末注入电弧的火焰中心，使其融熔并通过高压的该气体，高速喷覆于该金属基座而形成该陶瓷膜层。
8.如权利要求1所述的具高链接力的口腔牙材结构，其特征在于，该金属基座是选自镍、铬、钛、铂、钯、铜、锌、黄金、银的组合或其中一种所构成。