CN102747617B - Wrinkling printing adhesive and printing process thereof - Google Patents
Wrinkling printing adhesive and printing process thereof Download PDFInfo
- Publication number
- CN102747617B CN102747617B CN201210258889.4A CN201210258889A CN102747617B CN 102747617 B CN102747617 B CN 102747617B CN 201210258889 A CN201210258889 A CN 201210258889A CN 102747617 B CN102747617 B CN 102747617B
- Authority
- CN
- China
- Prior art keywords
- wrinkling
- fabric
- weight
- printing
- weight portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a wrinkling printing adhesive which is prepared from the following components in part by weight: 20 to 40 parts by weight of phenolic compound, 20 to 40 parts by weight of solid pulp, 4 to 6 parts by weight of thickener, 1 to 5 parts by weight of emulsifier MP, 1 to 10 parts by weight of color paste and a right amount of water. The wrinkling printing adhesive provided by the invention is printed on a fabric by a printing process; after the fabric is roasted at a high temperature of 150 to 180 DEG C, the fabric with a unique stereoscopic pattern can be obtained; the wrinkling printing adhesive has the advantages of good wrinkling performance, water-based environmental-friendliness, no pollution and the like and can be widely applied to the fields of textile, garments and the like; the pattern of the fabric has strong concave-convex feeling; and after the fabric is washed for twenty times, the concave-convex wrinkles are not deformed.
Description
Technical field
The present invention relates to a kind of printing adhesive of chemical technology field adhesive, particularly a kind of wrinkling performance.
Technical background
Along with socioeconomic development, people require constantly changing and improving for style, pattern and the style of fabric and clothes, the particularly raising of people's living standard, and life taste has very big lifting.Not only require comfort level high for garment material, health care is strong, the original function of more main is clothes: the image of beautify people, improves people's external packing quality.Popular stamp mode has ROTARY SCREAM PRINTING, PLATE SCREAM PRINTING, rat stamp and digit printing etc. both at home and abroad at present, and colorful, color is gorgeous, has met the different demands of people to fashion, personalization.But these stamp mode third dimensions are not strong, see for a long time these designs and varieties, easily produce visual fatigue.The wrinkling stereoscopic printing of chemical fibre becomes the direction that people pursue, and stereoscopic printing not only color is complete, and third dimension is strong, gives the sensation of a kind of youthful vigor of people.Mostly adopt in the market oiliness creping adhesives to produce Crinkled face fabric, but there is the shortcoming of contaminated air, not environmental protection in this series products, is difficult to meet the requirement of existing production.
Summary of the invention
The object of the invention is for the deficiencies in the prior art, provide that one has that wrinkling performance is good, aqueous, environmental protective, pollution-free, cost is low, the simple wrinkling printing adhesive of production technology.
Object of the present invention realizes by following technical solution:
A kind of wrinkling printing adhesive, it is characterized in that: the component that comprises following parts by weight is prepared from: the thickener of the aldehydes matter of 20-40 weight portion, the stereoplasm of 20-40 weight portion, 4-6 weight portion, the emulsifying agent MP of 1-5 weight portion, the mill base of 1-10 weight portion and appropriate water, described aldehydes matter is O-methoxy phenol, 2-methoxyl group-4-methylphenol, catechol, 1, at least one in 3-benzenediol, described stereoplasm is polyacrylate aqueous emulsion, polyurethanes aqueous emulsion or acroleic acid polyurethane copolymerization aqueous emulsion.
Further, described thickener is agent for polyacrylic acid thickening.
Another object of the present invention is to provide a kind of wrinkling printing technology, comprises the steps:
(1) adopt printing technology to be printed on fabric described wrinkling printing adhesive;
(2), without the fabric after stamp being baked and makes cockline under tension force, baking temperature is controlled at 150-180 DEG C.
The present invention has following beneficial effect:
Wrinkling printing adhesive of the present invention has that wrinkling performance is strong, water-based, environmental protection, the advantage such as pollution-free, belongs to resource-conserving product, with low cost, can mix with other raw materials simultaneously, and be a kind of desirable printing adhesive product.
Wrinkling principle of the present invention is: can make the nylon generation chemical reaction in aldehydes matter and the fabric in wrinkling printing adhesive baking without tension force under condition of technique, thereby make web contraction form concavo-convex wrinkle; Stereoplasm in wrinkling printing adhesive can make aldehydes matter better be combined with fabric; The technological process of production of the present invention is short, and technique is simple, aqueous, environmental protective, pollution-free, and cost-saving and energy consumption, and the advantage such as after stamp, to have wrinkling third dimension strong for product, and flower type is plentiful, and color is beautiful, can be widely used in weaving, garment industry, and market prospects are wide.
Detailed description of the invention
Embodiment mono-
A preparation for wrinkling printing adhesive, comprises the steps: that (1) is by the polyacrylate aqueous emulsion stirring and dissolving at normal temperatures of the water of the catechol of 40 weight portions, 29 weight portions and 20 weight portions, mixing speed 300rpm; (2) in above-mentioned solution, add the emulsifying agent MP of 1 weight portion and the mill base of 5 weight portions, then add the agent for polyacrylic acid thickening of 5 weight portions, high-speed stirred is even, reaches 2.5 × 10 to viscosity
4mPas(adopts NDJ-4 rotation viscometer, No. 4 rotors, 6 revs/min of measurements).Agent for polyacrylic acid thickening is the printing thickening agent PTF that Guangzhou Zhuo Hou Chemical Industry Science Co., Ltd produces.
Embodiment bis-
A preparation for wrinkling printing adhesive, comprises the steps: that (1) is by the polyacrylate aqueous emulsion stirring and dissolving at normal temperatures of the water of the catechol of 20 weight portions, 20 weight portions and 40 weight portions, mixing speed 300rpm; (2) in above-mentioned solution, add the emulsifying agent MP of 1 weight portion and the mill base of 6 weight portions, then add the agent for polyacrylic acid thickening of 4 weight portions, high-speed stirred is even, reaches 2.5 × 10 to viscosity
4mPas(adopts NDJ-4 rotation viscometer, No. 4 rotors, 6 revs/min of measurements).Agent for polyacrylic acid thickening is the printing thickening agent PTF that Guangzhou Zhuo Hou Chemical Industry Science Co., Ltd produces.
A kind of wrinkling printing technology, comprises the steps: that (1) adopts ROTARY SCREAM PRINTING technique to be printed on fabric arbitrary described wrinkling printing adhesive in claims 1 to 3; (2), without the fabric after stamp being baked and makes fabric face form concavo-convex wrinkle under tension force, baking temperature is controlled at 150-180 DEG C.
Above-mentioned fabric flower type concave-convex sense is strong, wash 20 times after concavo-convex wrinkle indeformable.
The above, be only preferred embodiment of the present invention, therefore can not limit scope of the invention process with this, the equivalence of doing according to the present patent application the scope of the claims and description changes and modifies, and all should still remain within the scope of the patent.
Claims (3)
1. a wrinkling printing adhesive, it is characterized in that: the component that comprises following parts by weight is prepared from: the thickener of the aldehydes matter of 20-40 weight portion, the stereoplasm of 20-40 weight portion, 4-6 weight portion, the emulsifying agent MP of 1-5 weight portion, the mill base of 1-10 weight portion and appropriate water, described aldehydes matter is O-methoxy phenol, 2-methoxyl group-4-methylphenol, catechol, 1, at least one in 3-benzenediol, described stereoplasm is polyacrylate aqueous emulsion, polyurethanes aqueous emulsion or acroleic acid polyurethane copolymerization aqueous emulsion.
2. the wrinkling printing adhesive of one according to claim 1, is characterized in that: described thickener is agent for polyacrylic acid thickening.
3. a wrinkling printing technology, comprises the steps:
(1) adopt printing technology to be printed on fabric the wrinkling printing adhesive described in claim 1 or 2, described fabric contains nylon;
(2), without the fabric after stamp being baked and makes cockline under tension force, baking temperature is controlled at 150-180 DEG C.