CN102732895A - 一种水溶性缓蚀剂及其制备方法 - Google Patents

一种水溶性缓蚀剂及其制备方法 Download PDF

Info

Publication number
CN102732895A
CN102732895A CN2012102198075A CN201210219807A CN102732895A CN 102732895 A CN102732895 A CN 102732895A CN 2012102198075 A CN2012102198075 A CN 2012102198075A CN 201210219807 A CN201210219807 A CN 201210219807A CN 102732895 A CN102732895 A CN 102732895A
Authority
CN
China
Prior art keywords
water
preparation
corrosion inhibitor
inhibiter
rust inhibitor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102198075A
Other languages
English (en)
Inventor
张士钊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012102198075A priority Critical patent/CN102732895A/zh
Publication of CN102732895A publication Critical patent/CN102732895A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种水溶性缓蚀剂及其制备方法，属于金属腐蚀抑制领域。它是由下述重量份的原料制成：二乙烯三胺10-20、次氯酸钠5-10、水溶性咪唑啉5-10、缓蚀剂助剂5-8、乙醇10-20和去离子水15-20，本发明提供的水溶性缓蚀剂为液体产品，无毒，无污染，适用性强，缓蚀效果好；且生产原料易得，生产简便易行。

Description

一种水溶性缓蚀剂及其制备方法
技术领域
本发明涉及一种水溶性缓蚀剂及其制备方法，属于金属腐蚀抑制领域。
背景技术
缓蚀剂是一种在低浓度下能阻止或减缓金属在环境介质中腐蚀的物质。缓蚀剂又叫作阻蚀剂、阻化剂或腐蚀抑制剂等。缓蚀剂保护技术已经发展为一项重要的防腐蚀技术，广泛用在石油、冶金、化工、机械制造、动力和运输等部门。
缓蚀作用的吸附理论认为缓蚀剂分子与金属表面由于有静电引力和分子间作用力而发生物理吸附。有的缓蚀剂分子还可以和金属表面形成化学键而发生化学吸附。缓蚀剂分子吸附在金属表面，形成了连续的吸附层，把腐蚀介质与金属表面隔离开，从而起到抑制腐蚀的作用。
然而缓蚀剂也存在局限性：缓蚀剂对材料—环境体系有极强的针对性，要针对不同的体系通过实验室及现场的试验选择缓蚀剂的配方和有关参数；并且具有一定的污染性。
发明内容
本发明的目的在于提供一种适用性强且缓蚀效率高的水溶性缓蚀剂，本发明还提供了该水溶性缓蚀剂的制备方法。
本发明的技术方案是：一种水溶性缓蚀剂，是由下述重量份的原料制成：
Figure BDA00001828129200011
Figure BDA00001828129200021
所述的缓蚀剂助剂为醋酸锌或钼酸钠。
一种水溶性缓蚀剂的制备方法，包括如下步骤：
（1）、称取上述重量份的原料备用；
（2）、常压下，向反应容器中依次加入去离子水和次氯酸钠，升温至50-60℃，至次氯酸钠完全溶解；
（3）、向上述反应液中加入二乙烯三胺、水溶性咪唑啉、缓蚀剂助剂和乙醇，在温度为70-80℃条件下，搅拌反应3-5h，冷却至室温，过滤后即得该产品。
本发明的有益效果是：本发明提供的水溶性缓蚀剂为液体产品，无毒，无污染，适用性强，缓蚀效果好；且生产原料易得，生产简便易行。
具体实施方式
为了更好地理解本发明，下面结合实施例进一步阐明本发明的内容，但本发明的内容不仅仅局限于下面的实施例，实施例不应视作对本发明保护范围的限定。
实施例1
配比:
Figure BDA00001828129200022
Figure BDA00001828129200031
制备方法，包括如下步骤：
（1）、称取上述重量份的原料备用；
（2）、常压下，向反应容器中依次加入去离子水和次氯酸钠，升温至50-60℃，至次氯酸钠完全溶解；
（3）、向上述反应液中加入二乙烯三胺、水溶性咪唑啉、缓蚀剂助剂和乙醇，在温度为70-80℃条件下，搅拌反应3-5h，冷却至室温，过滤后即得该产品。
实施例2
配比:
制备方法同实施例1。
实施例3
配比:
Figure BDA00001828129200033
制备方法同实施例1。

Claims (3)

1.一种水溶性缓蚀剂，其特征是，由下述重量份的原料制成：
Figure FDA00001828129100011
2.根据权利要求1所述的水溶性缓蚀剂，其特征是，所述的缓蚀剂助剂为醋酸锌或钼酸钠。
3.如权利要求1所述的一种水溶性缓蚀剂的制备方法，其特征是，包括如下步骤：
（1）、称取上述重量份的原料备用；
（2）、常压下，向反应容器中依次加入去离子水和次氯酸钠，升温至50-60℃，至次氯酸钠完全溶解；
（3）、向上述反应液中加入二乙烯三胺、水溶性咪唑啉、缓蚀剂助剂和乙醇，在温度为70-80℃条件下，搅拌反应3-5h，冷却至室温，过滤后即得该产品。
CN2012102198075A 2012-06-29 2012-06-29 一种水溶性缓蚀剂及其制备方法 Pending CN102732895A (zh)