CN102732101B - 一种自粘性保偏光纤用涂料 - Google Patents
一种自粘性保偏光纤用涂料 Download PDFInfo
- Publication number
- CN102732101B CN102732101B CN201210221500.9A CN201210221500A CN102732101B CN 102732101 B CN102732101 B CN 102732101B CN 201210221500 A CN201210221500 A CN 201210221500A CN 102732101 B CN102732101 B CN 102732101B
- Authority
- CN
- China
- Prior art keywords
- polarization maintaining
- maintaining optical
- molecular weight
- self
- filmogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种自粘性保偏光纤用涂料，其特征是它由成膜物质和增塑剂组成；成膜物质与增塑剂的重量比为：成膜物质：增塑剂？=？1：0.1～1：0.4；其中成膜物质为：低密度聚乙烯、聚氯乙烯、聚丙烯、热塑性丙烯酸树脂或热塑性聚氨酯树脂；增塑剂为邻苯二甲酸二丁酯或邻苯二甲酸二辛酯。本发明具有能使光纤环制作时间短、效率高、制作方便的优点。
Description
技术领域
本发明涉及一种保偏光纤用涂料，尤其涉及一种自粘性保偏光纤用涂料。
背景技术
保偏光纤其横截面结构由外到里分别是：基管层、应力作用区和芯层，应力作用区和芯层设置在基管层中；而光纤陀螺的基本元器件是光纤环圈，它由保偏光纤直接绕制在事先设计好的骨架上，通过施胶固化使光纤环达到抗振、长期稳定的状态。构成全固态的光纤环线圈，提高光纤陀螺的稳定性。施胶的方法有多种，目前比较常用的是刷胶、带胶、喷胶和浸渍。前三种方法都是在绕环过程中进行的，效率较低，一致性也难以保证。浸渍是绕环后进行的，将光纤环放置在一个密封的容器中，抽真空，在一定的负压条件下，将事先准备好的胶浸渍到光纤环中，产品一致性比前三种方法有改善，但胶浸渍速度慢、光纤环制作时间长、工艺复杂等。
发明内容
针对上述缺点，本发明的目的在于提供一种自粘性保偏光纤用涂料，其可以保偏光纤在制作光纤环时制作时间短、效率高、制作方便。
本发明的技术内容为：一种自粘性保偏光纤用涂料，其特征是它由成膜物质和增塑剂组成；成膜物质与增塑剂的重量比为：成膜物质：增塑剂 = 1：0.1～1：0.4；
其中成膜物质为：低密度聚乙烯、聚氯乙烯、聚丙烯、热塑性丙烯酸树脂或热塑性聚氨酯树脂；低密度聚乙烯的分子量为10000～20000；聚氯乙烯的分子量为30000～40000；聚丙烯的分子量为10000～20000；热塑性丙烯酸树脂的分子量为20000～30000；热塑性聚氨酯树脂的分子量为20000～30000，热塑性聚氨酯树脂的Tg=50～80℃；
增塑剂为邻苯二甲酸二丁酯或邻苯二甲酸二辛酯。
本发明所具有的优点是： 将发明的自粘性保偏光纤用涂料涂覆到保偏光纤后，再将保偏光纤绕制成光纤环后只须在一定的温度下进行加热烘干即刻，由此使光纤环制作时间短、效率高、制作方便。
具体实施例
实施例1：将分子量为15000的低密度聚乙烯100g与邻苯二甲酸二丁酯10 g加热熔融并混合均匀后即得自粘性保偏光纤用涂料。
实施例2：将分子量为30000的聚氯乙烯100g与邻苯二甲酸二辛酯15g加热熔融并混合均匀后即得自粘性保偏光纤用涂料。
实施例3：将分子量为20000的聚丙烯100g与邻苯二甲酸二辛酯40 g加热熔融并混合均匀后即得自粘性保偏光纤用涂料。
实施例4：将分子量为20000、Tg=60℃的热塑性丙烯酸树脂100g与邻苯二甲酸二丁酯10 g加热熔融并混合均匀后即得自粘性保偏光纤用涂料。
实施例5：将分子量为20000、Tg=70℃的热塑性聚氨酯树脂100g与邻苯二甲酸二丁酯10 g加热熔融并混合均匀后即得自粘性保偏光纤用涂料。
Claims (1)
1.一种自粘性保偏光纤用涂料，其特征是它由成膜物质和增塑剂组成；成膜物质与增塑剂的重量比为：成膜物质：增塑剂 = 1：0.1～1：0.4；
其中增塑剂为邻苯二甲酸二丁酯时，成膜物质为热塑性丙烯酸树脂或热塑性聚氨酯树脂；增塑剂为邻苯二甲酸二辛酯时，成膜物质为低密度聚乙烯、聚氯乙烯、聚丙烯、热塑性丙烯酸树脂或热塑性聚氨酯树脂；上述低密度聚乙烯的分子量为10000～20000；聚氯乙烯的分子量为30000～40000；聚丙烯的分子量为10000～20000；热塑性丙烯酸树脂的分子量为20000～30000；热塑性聚氨酯树脂的分子量为20000～30000，热塑性聚氨酯树脂的Tg=50～80℃。