CN102731164B - Anti-skid glaze for floor tiles - Google Patents
Anti-skid glaze for floor tiles Download PDFInfo
- Publication number
- CN102731164B CN102731164B CN 201210214230 CN201210214230A CN102731164B CN 102731164 B CN102731164 B CN 102731164B CN 201210214230 CN201210214230 CN 201210214230 CN 201210214230 A CN201210214230 A CN 201210214230A CN 102731164 B CN102731164 B CN 102731164B
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- floor tile
- skid
- floor tiles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses an anti-skid glaze for floor tiles. The anti-skid glaze is prepared from the following raw materials, by weight, 20-40 parts of stalactite, 10-30 parts of aluminate, 20-40 parts of ZnSO3, 20-40 parts of NbO2, 3-12 parts of SnO2, 3-12 parts of Cu2O, 30-40 parts of OsO2, 2-6 parts of Sc2O3, 5-10 parts of borax, and 20-40 parts of clay. The anti-skid glaze for the floor tiles in the present invention has good viscosity and good anti-skid property, and is a novel special anti-skid glaze for the floor tiles and with a wide application range.
Description
Technical field
The present invention relates to a kind of enamel, be specifically related to a kind of anti-skidding glaze for floor tile.
Background technology
Floor tile is the ground decoration such as widespread use and family, hotel, office space, attractive in appearance, easy to clean, but the floor tile surface flatness of prior art is higher, especially when there is water on ground, surface is very smooth, and frictional force is little, and people are when the walking of floor tile surface, easily fall down, therefore, necessary on the basis of prior art design research and development a kind of anti-skidding, viscosity is large, the floor tile surface glaze that is difficult for slipping.
Summary of the invention
Goal of the invention: technical problem to be solved by this invention is to overcome the deficiencies in the prior art, provides a kind of component proportioning scientific and reasonable, and viscosity is large, non-skid property good, is exclusively used in the anti-skidding glaze on floor tile surface.
Technical scheme: for solving above technical problem, the present invention takes following technical scheme:
A kind of anti-skidding glaze for floor tile, it is made by the raw material of following parts by weight:
20 ~ 40 parts, Stalactitum, 10 ~ 30 parts of aluminates, ZnSO
320 ~ 40 parts, NbO
220 ~ 40 parts, SnO
23 ~ 12 parts, Cu
23 ~ 12 parts of O, OsO
230 ~ 40 parts, Sc
2o
32 ~ 6 parts, 5 ~ 10 parts of boraxs, 20 ~ 40 parts of clays.
As preferred version, the above-described anti-skidding glaze for floor tile, it is made by the raw material of following parts by weight:
20 ~ 30 parts, Stalactitum, 10 ~ 20 parts of aluminates, ZnSO
320 ~ 30 parts, NbO
220 ~ 30 parts, SnO
25 ~ 10 parts, Cu
25 ~ 10 parts of O, OsO
230 ~ 35 parts, Sc
2o
33 ~ 5 parts, 5 ~ 8 parts of boraxs, 20 ~ 30 parts of clays.
As more preferably scheme, the above-described anti-skidding glaze for floor tile, it is made by the raw material of following parts by weight:
35 parts, Stalactitum, 20 parts of aluminates, ZnSO
330 parts, NbO
230 parts, SnO
28 parts, Cu
210 parts of O, OsO
235 parts, Sc
2o
35 parts, 8 parts of boraxs, 30 parts of clays.
As preferred version, the above-described anti-skidding glaze for floor tile, described aluminate is potassium aluminate or sodium aluminate.
The present invention is directed to the deficiency that the prior art floor tile shows that slickness is large, through great many of experiments, filter out and can increase glaze viscosity, increase frictional force, anti-skidding ground brick glaze, the anti-skidding glaze for floor tile provided by the invention, superior performance, have wide range of applications.
Beneficial effect: compared to the prior art the anti-skidding glaze for floor tile provided by the invention has following advantage:
Anti-skidding glaze for floor tile provided by the invention, the best that optimizes ceramic anti-skidding glaze according to great many of experiments forms, and experimental result shows that the each component proportioning is scientific and reasonable, and the ground brick glaze viscosity prepared is large, non-skid property is good, can be widely used in the decoration of family, hotel.
Embodiment
Below in conjunction with specific embodiment, further illustrate the present invention, should understand these embodiment only is not used in and limits the scope of the invention for the present invention is described, after having read the present invention, those skilled in the art all fall within the application's claims limited range to the modification of the various equivalent form of values of the present invention.
Embodiment 1
A kind of anti-skidding glaze for floor tile, it is made by the raw material of following parts by weight:
40 parts, Stalactitum, 30 parts of sodium aluminates, ZnSO
340 parts, NbO
240 parts, SnO
212 parts, Cu
212 parts of O, OsO
240 parts, Sc
2o
36 parts, 10 parts of boraxs, 40 parts of clays.
Embodiment 2
A kind of anti-skidding glaze for floor tile, it is made by the raw material of following parts by weight:
20 parts, Stalactitum, 10 parts of sodium aluminates, ZnSO
320 parts, NbO
220 parts, SnO
23 parts, Cu
23 parts of O, OsO
230 parts, Sc
2o
32 parts, 5 parts of boraxs, 20 parts of clays.
Embodiment 3
A kind of anti-skidding glaze for floor tile, it is made by the raw material of following parts by weight:
30 parts, Stalactitum, 20 parts of aluminates, ZnSO
330 parts, NbO
230 parts, SnO
210 parts, Cu
210 parts of O, OsO
235 parts, Sc
2o
35 parts, 8 parts of boraxs, 30 parts of clays.
Embodiment 4
A kind of anti-skidding glaze for floor tile, it is made by the raw material of following parts by weight:
35 parts, Stalactitum, 20 parts of aluminates, ZnSO
330 parts, NbO
230 parts, SnO
28 parts, Cu
210 parts of O, OsO
235 parts, Sc
2o
35 parts, 8 parts of boraxs, 30 parts of clays.
The anti-skidding glaze that is exclusively used in floor tile provided by the invention, can greatly reduce the probability slipped, and especially, when there is water on the floor tile surface, viscosity is larger, and slippery is low, is a kind of novel ground brick glaze with good application prospect.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. the anti-skidding glaze for floor tile, is characterized in that, it is made by the raw material of following parts by weight:
20 ~ 40 parts, Stalactitum, 10 ~ 30 parts of aluminates, ZnSO
320 ~ 40 parts, NbO
220 ~ 40 parts, SnO
23 ~ 12 parts, Cu
23 ~ 12 parts of O, OsO
230 ~ 40 parts, Sc
2o
32 ~ 6 parts, 5 ~ 10 parts of boraxs, 20 ~ 40 parts of clays.
2. the anti-skidding glaze for floor tile according to claim 1, is characterized in that, it is made by the raw material of following parts by weight:
20 ~ 30 parts, Stalactitum, 10 ~ 20 parts of aluminates, ZnSO
320 ~ 30 parts, NbO
220 ~ 30 parts, SnO
25 ~ 10 parts, Cu
25 ~ 10 parts of O, OsO
230 ~ 35 parts, Sc
2o
33 ~ 5 parts, 5 ~ 8 parts of boraxs, 20 ~ 30 parts of clays.
3. the anti-skidding glaze for floor tile according to claim 1, is characterized in that, it is made by the raw material of following parts by weight:
35 parts, Stalactitum, 20 parts of aluminates, ZnSO
330 parts, NbO
230 parts, SnO
28 parts, Cu
210 parts of O, OsO
235 parts, Sc
2o
35 parts, 8 parts of boraxs, 30 parts of clays.
4. according to the described anti-skidding glaze for floor tile of claims 1 to 3 any one, it is characterized in that, described aluminate is potassium aluminate or sodium aluminate.