CN102728577B - Method for improving surface tension of glass plastic accessory - Google Patents
Method for improving surface tension of glass plastic accessory Download PDFInfo
- Publication number
- CN102728577B CN102728577B CN201210205774.9A CN201210205774A CN102728577B CN 102728577 B CN102728577 B CN 102728577B CN 201210205774 A CN201210205774 A CN 201210205774A CN 102728577 B CN102728577 B CN 102728577B
- Authority
- CN
- China
- Prior art keywords
- glass plastic
- heating
- glass
- deionized water
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a method for improving surface tension of a glass plastic accessory in the technical field of glass production. The method for improving the surface tension of the glass plastic accessory comprises the following steps of: 1) adding deionized water (3) into a heating container (1) for heating the glass plastic accessory; 2) before the glass plastic accessory (2) is put into the heating container (1), heating the deionized water (3), and then putting the glass plastic accessory (2) into the heating container (1) for hot boiling; and 3) continuously heating the deionized water (3) in the heating container (1) for 20 to 60 minutes. By adopting the technical scheme, under the condition that the material of the glass plastic accessory is not damaged, residual release agent or grease on the surface of the plastic accessory can be well removed, an optimal cleaning effect is achieved, and the thermal stability of the glass plastic accessory in a bonding technology is improved. Meanwhile, adverse effects of chemical reagents adopted in the prior art on human body and environment can be avoided, and an environment-friendly effect is achieved.
Description
Technical field
The invention belongs to field of glass production technology, more particularly, relate to a kind of process that improves glass plastic attachment surface tension force.
Background technology
For improving the surface tension of glass plastic annex, improve the stability of glass plastic annex in technique for sticking, need clean glass plastic parts surface.In prior art, be to adopt butanone or alcohol to soak, dry processing to glass plastic annex.Existing this method but, chemical reagent use amount is larger, and cost is higher, and discarded butanone or alcohol have negative effect to human body, environment, are unfavorable for environmental protection.Meanwhile, even if segment glass plastic accessory is after being used butanone or alcohol-pickled processing, still processes to fall material surface releasing agent, grease, thereby affect the stability of glass plastic annex in barbola work.
Summary of the invention
Technical problem to be solved by this invention is: for the deficiencies in the prior art, provide a kind of and can avoid the negative effect to human body, environment of chemical reagent in glass plastic accessory adhering, improve the process of the raising glass plastic attachment surface tension force of glass plastic attachment surface tension force simultaneously.
Solve above-described technical problem, the technical scheme that the present invention takes is:
The present invention is a kind of process that improves glass plastic attachment surface tension force, and the step of the process of described raising glass plastic attachment surface tension force is:
1) to adding deionized water for heating in the heating container of glass plastic annex;
2) in heating container, put into before glass plastic annex, add hot deionized water, then put into glass plastic annex and carry out heat and boil;
3) to the deionized water continuous heating 20-60min in heating container.
Described glass plastic annex is carried out to heat while boiling, different glass plastic annexes should be in batches glass container heat boil or in different glass containers heat boil.
Glass plastic annex is carried out to heat while boiling, when each heat is boiled, change deionized water.
In heating container, put into before glass plastic annex, the temperature of the ion that anhydrates is heated between 90 ℃-100 ℃.
During to deionized water continuous heating in heating container, the heating-up temperature of deionized water is remained between 90 ℃-100 ℃.
During to deionized water continuous heating in heating container, the heat time is controlled between 30-40min, and described glass plastic annex heat is dried glass plastic annex, and then glass plastic annex is carried out to subsequent job after having boiled.
The structure that described heating container is set to heat by Electric heating.
Adopt technical scheme of the present invention, can obtain following beneficial effect:
The process of raising glass plastic attachment surface tension force of the present invention, do not destroying in glass plastic annex material situation, use high warm process of boiling, not only can better remove releasing agent, the grease of working of plastics remained on surface, reach best cleaning effect, improve the stability of glass plastic annex in technique for sticking.Meanwhile, the process that adopts heat to boil, can avoid the negative effect of available technology adopting chemical reagent to human body, environment, reaches the effect of environmental protection.
Accompanying drawing explanation
The expressed content of each accompanying drawing of this description and the mark in figure are made to brief description below:
Fig. 1 is for improving the structural representation of the heating container of glass plastic attachment surface tension force;
Fig. 2 is the process chart of the process of raising glass plastic attachment surface tension force of the present invention;
Mark in figure: 1, heating container; 2, glass plastic annex; 3, deionized water.
The specific embodiment
Contrast accompanying drawing below, by the description to embodiment, the specific embodiment of the present invention is described in further detail as the effect of the mutual alignment between the shape of each related member, structure, each several part and annexation, each several part and operation principle etc.:
As shown in accompanying drawing 1, accompanying drawing 2, the present invention is a kind of process that improves glass plastic attachment surface tension force, and the step of the process of described raising glass plastic attachment surface tension force is:
1) to adding deionized water 3 for heating in the heating container 1 of glass plastic annex;
2) in heating container 1, put into before glass plastic annex 2, add hot deionized water 3, then put into glass plastic annex 2 and carry out heat and boil;
3) to the deionized water 3 continuous heating 20-60min in heating container 1.
Described glass plastic annex 2 is carried out to heat while boiling, different glass plastic annexes 2 should be in batches glass container 1 heat boil or in different glass container 1 heat boil.
Glass plastic annex 2 is carried out to heat while boiling, when each heat is boiled, change deionized water 3.The deionized water that each heat must more renew while boiling, the glass plastic annex of unlike material can not mix and carries out poach simultaneously, because the heat of mixing is boiled, will greatly affect the stability of glass plastic annex in technique for sticking.
In heating container 1, put into before glass plastic annex 2, the temperature of the ion 3 that anhydrates is heated between 90 ℃-100 ℃.
During to deionized water 3 continuous heating in heating container 1, the heating-up temperature of deionized water 3 is remained between 90 ℃-100 ℃.
During to deionized water 3 continuous heating in heating container 1, the heat time is controlled between 30-40min, and described glass plastic annex 2 heat are dried glass plastic annex 2 after having boiled, and then glass plastic annex 2 is carried out to subsequent job.
The structure that described heating container 1 is set to heat by Electric heating.
The process of raising glass plastic attachment surface tension force of the present invention, do not destroying in glass plastic annex material situation, use high warm process of boiling, not only can better remove releasing agent, the grease of working of plastics remained on surface, reach best cleaning effect, improve the stability of glass plastic annex in technique for sticking.Meanwhile, the process that adopts heat to boil, can avoid the negative effect of available technology adopting chemical reagent to human body, environment, reaches the effect of environmental protection.
By reference to the accompanying drawings the present invention has been carried out to exemplary description above; obviously the concrete realization of the present invention is not subject to the restrictions described above; as long as the various improvement that adopted method design of the present invention and technical scheme to carry out; or without improving, design of the present invention and technical scheme are directly applied to other occasions, all in protection scope of the present invention.
Claims (3)
1. improve a process for glass plastic attachment surface tension force, the step of the process of described raising glass plastic attachment surface tension force is:
1) to adding deionized water (3) for heating in the heating container (1) of glass plastic annex;
2) front to putting into glass plastic annex (2) in heating container (1), add hot deionized water (3), then put into glass plastic annex (2) and carry out heat and boil;
3) to deionized water (3) continuous heating 20-60min in heating container (1);
Described glass plastic annex (2) is carried out to heat while boiling, different glass plastic annexes (2) should be in batches glass container (1) heat boil or in different glass container (1) heat boil;
Glass plastic annex (2) is carried out to heat while boiling, when each heat is boiled, change deionized water (3);
Front to putting into glass plastic annex (2) in heating container (1), the temperature of deionized water (3) is heated between 90 ℃-100 ℃;
It is characterized in that: during to deionized water (3) continuous heating in heating container (1), the heating-up temperature of deionized water (3) is remained between 90 ℃-100 ℃;
Described glass plastic annex (2) heat is dried glass plastic annex (2), and then glass plastic annex (2) is carried out to subsequent job after having boiled.
2. the process of raising glass plastic attachment surface tension force according to claim 1, is characterized in that: the structure that described heating container (1) is set to heat by Electric heating.
3. the process of raising glass plastic attachment surface tension force according to claim 2, is characterized in that: during to deionized water (3) continuous heating in heating container (1), the heat time is controlled between 30-40min.