CN102718559A - 一种有色含铅熔块 - Google Patents
一种有色含铅熔块 Download PDFInfo
- Publication number
- CN102718559A CN102718559A CN2012101899063A CN201210189906A CN102718559A CN 102718559 A CN102718559 A CN 102718559A CN 2012101899063 A CN2012101899063 A CN 2012101899063A CN 201210189906 A CN201210189906 A CN 201210189906A CN 102718559 A CN102718559 A CN 102718559A
- Authority
- CN
- China
- Prior art keywords
- parts
- frit
- pbo
- weight
- sio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种制备陶瓷用的有色含铅熔块,它由下列重量份数的原料制成:SiO2 20~30份、Al2O3 1~5份、PbO 30~40份、Fe2O3 20~30份、碱金属1至5份。本发明提供的有色含铅熔块,各组份配比科学合理,烧制工艺简单,釉面光泽度高、釉浆性能好,烧成性能,适用范围广泛。
Description
技术领域
本发明涉及一种陶瓷用的含铅熔块,具体涉及一种陶瓷用的有色含铅熔块。
背景技术
随着工业技术的发展,陶瓷具有高致密性、耐高温、不易变形、耐磨性能优、绝缘性能好、可成型性强,装饰效果好的优点,已广泛在日用品、建筑材料、艺术品等领域广泛应用,陶瓷用的的重要原料熔块是配中、低温釉的重要原料。但现有技术的熔块存在熔化温度高,熔块颜色不均匀、制备的釉面光滑度不佳等缺点,因此,很有必要在现有技术的基础之上,研发设计一种熔化温度适中,熔块颜色分布均匀,釉面光泽度高的有色含铅熔块。
发明内容
发明目的:本发明所要解决的技术问题是克服现有技术的不足,提供一种熔块颜色分布均匀,釉面光泽度高、釉浆性能好,烧成性能好有色含铅熔块。
技术方案:为解决以上技术问题,本发明采取如下技术方案:
一种有色含铅熔块,它由下列重量份数的原料制成:
SiO2 20~30份、Al2O3 1~5份、PbO 30~40份、Fe2O3 20~30份、碱金属1至5份。
作为优选方案,以上所述的有色含铅熔块,它由下列重量份数的原料制成:
SiO2 20~25份、Al2O3 3~5份、PbO 30~35份、Fe2O3 20~25份、碱金属3~5份。
作为更优选方案,以上所述的有色含铅熔块,它由下列重量份数的原料制成:
SiO2 20份、Al2O3 3份、PbO 30份、Fe2O3 20份、碱金属3份。
作为优选方案,以上所述的有色含铅熔块,所述的碱金属为Na2O或K2O。
本发明提供的有色含铅熔块,性能优越,具体产品参数为:
热膨胀系数83、变换点(度)500、膨胀软化点(度)545、烧结点(度)560、软化点(度)870、球点(度)950、半球点(度)970。
有益效果:本发明提供的有色含铅熔块和现有技术相比具有如下优点:
本发明提供的有色含铅熔块,根据大量实验优选熔块的最佳组成,各组份配比科学合理,烧制工艺简单,并且熔块颜色分布均匀,釉面光泽度高、釉浆性能好,烧成性能,适用范围广泛。
具体实施方式
下面结合具体实施例,进一步阐明本发明,应理解这些实施例仅用于说明本发明而不用于限制本发明的范围,在阅读了本发明之后,本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
实施例1
一种有色含铅熔块,它由下列重量份数的原料制成:
SiO2 30份、Al2O3 5份、PbO 40份、Fe2O3 30份、Na2O 5份。
实施例2
一种有色含铅熔块,它由下列重量份数的原料制成:
SiO2 20份、Al2O3 1份、PbO 30份、Fe2O3 20份、Na2O 1份。
实施例3
一种有色含铅熔块,它由下列重量份数的原料制成:
SiO2 25份、Al2O3 5份、PbO 35份、Fe2O3 25份、K2O 5份。
实施例4
一种有色含铅熔块,它由下列重量份数的原料制成:
SiO2 20份、Al2O3 3份、PbO 30份、Fe2O3 20份、碱金属3份。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (4)
1.一种有色含铅熔块,其特征在于,它由下列重量份数的原料制成:
SiO2 20~30份、Al2O3 1~5份、PbO 30~40份、Fe2O3 20~30份、碱金属1至5份。
2.根据权利要求1所述的有色含铅熔块,其特征在于,它由下列重量份数的原料制成:
SiO2 20~25份、Al2O3 3~5份、PbO 30~35份、Fe2O3 20~25份、碱金属3~5份。
3.根据权利要求1所述的有色含铅熔块,其特征在于,它由下列重量份数的原料制成:
SiO2 20份、Al2O3 3份、PbO 30份、Fe2O3 20份、碱金属3份。
4.根据权利要求1至3任一项所述的有色含铅熔块,其特征在于,所述的碱金属为Na2O或K2O。