CN102690629A - 速焊自愈型灌缝胶及其使用方法 - Google Patents
速焊自愈型灌缝胶及其使用方法 Download PDFInfo
- Publication number
- CN102690629A CN102690629A CN2011100762270A CN201110076227A CN102690629A CN 102690629 A CN102690629 A CN 102690629A CN 2011100762270 A CN2011100762270 A CN 2011100762270A CN 201110076227 A CN201110076227 A CN 201110076227A CN 102690629 A CN102690629 A CN 102690629A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- crack
- self
- crack pouring
- pitches
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种速焊自愈型灌缝胶及其使用方法，包括100号沥青、10号沥青、胶粉、SBS橡胶改性石油沥青、萜烯树酯、APAO无定型烯烃共聚物、稀土、滑石粉。其使用方法是：将灌缝胶用刀割成胶条，将胶条塞入裂缝中，用燃气喷枪加热灌入缝隙中，再用油灰刀刮平，最后撒细沙覆盖。本发明粘度大，弹性高，耐低温，自愈性好，回粘性好，耐磨性强，抗撕裂性好，工序简单，易携带，投资小，成本低，灌缝后凝固时间十分钟左右，即可开放交通，效率高，操作方便，在使用过程中不会对大气和路面造成污染，灌缝质量好，节省灌缝材料，材料可反复加热，能延长养护周期，减少养护次数，使用寿命长，可节省能源、人力及成本。可广泛应用于路面裂缝修补过程中。
Description
技术领域 本发明涉及一种速焊自愈型灌缝胶及其使用方法，可广泛应用于路面裂缝修补过程中。
背景技术 路面裂缝是沥青混凝土路面最为常见的病害之一，在诸多道路病害中，属于危害较为严重的一种。如果不及时处理，在车辆载荷的作用下，再加上雨水的渗入，使裂缝进一步发展，最终形成龟裂，大大降低了路面的使用品质，而且增加了后期养护成本。因此，为了提高路面的路况质量，减少路面病害，加强路面预防性养护，必须加强路面早期横纵裂缝的防治。
传统的灌缝胶及其施工工艺方法，一般需要大型笨重的灌缝设备和热施工，而且需要喷吹除尘工序，投资大，成本高，效率低，胶粘结剂浪费严重。
发明内容 为了克服上述缺点，本发明的目的在于提供一种粘度大、弹性高、耐低温、自愈性好、回粘性好、耐磨性强、抗撕裂性好、工序简单、易携带、投资小、成本低、效率高、操作方便、灌缝质量好、节省灌缝材料、使用寿命长的速焊自愈型灌缝胶及其使用方法。
为了达到上述目的，本发明速焊自愈型灌缝胶，包括100号沥青、10号沥青、胶粉、SBS橡胶改性石油沥青、萜烯树酯、APAO无定型烯烃共聚物、稀土、滑石粉；各组分重量百分数为：
100号沥青 25％～40％，
10号沥青 20％～35％，
胶粉 9％～15％，
SBS橡胶改性石油沥青 4％～8％，
萜烯树酯 0.4％～0.6％，
APAO无定型烯烃共聚物 0.4％～0.6％，
稀土 4％～8％，
滑石粉 13％～19％；
按上述各组分重量百分数，将100号、10号沥青升温脱水，温度保持在220℃～230℃时加胶粉，保温1小时加后加SBS橡胶改性石油沥青，熔化时间2小时，溶化后添加用胶体磨研磨后的APAO无定型烯烃共聚物、稀土、萜烯树酯，最后加滑石粉搅拌均匀，温度保持140℃～160℃放灌、冷却、成形。
本发明速焊自愈型灌缝胶，其使用方法是：将速焊自愈型灌缝胶用刀割成胶条，然后将胶条塞入裂缝中，用路面焊缝机燃气喷枪对准缝隙中的胶条加热灌入缝隙中，再用油灰刀刮平，最后撒细沙覆盖。
本发明速焊自愈型灌缝胶，所说的胶粉，可使灌缝胶粘接强度高，耐水性能强。所说的SBS橡胶改性石油沥青，可使灌缝胶的气密性、低温柔性、耐化学腐蚀性、耐光、耐臭氧性、耐候性和耐燃性得到大大改善。所说的萜烯树酯，为增粘剂，又是热熔材料的改良剂，无毒、无臭、耐辐射、抗结晶性能，对氧、热、光较稳定，对各种合成物质有良好的相溶性，耐稀酸、稀碱，增粘性强，电绝缘性强，不溶于水及乙醇。所说的APAO无定型烯烃共聚物，容易和沥青混合，而且分散性好，能与大量无机填料混合，对水完全无反应，抗水解，对酸碱和还原剂有抵抗性，良好的耐热性，耐塞性，使其低温时柔软，高温时不软化和流淌，是灌缝胶的良好改性剂。所说的稀土，是一种催化剂，具有活性高、选择性好的优点，可用于石油沥青催化裂化过程。所说的滑石粉，可以作为强化改质填充剂，有润滑、抗粘、耐火、抗酸、绝缘、化学性不活泼、遮盖力良好、光泽好、吸附力强的特点，对电和热都有良好的绝缘性，低膨胀和收缩力，分散性高，遮盖力强，吸油和疏水性好，滑腻度大，摩擦系数小，化学性质稳定，防水，抗酸、碱侵蚀。
本发明速焊自愈型灌缝胶，粘度大，弹性高，耐低温，自愈性好，回粘性好，耐磨性强，耐磨耗寿命为普通路面的2～3倍，而且有抗撕裂性，夏季高温路面不会晒软，冬季路面不脆裂收缩，保持较好弹性，减少路面裂缝。因此，使用寿命长。
本发明速焊自愈型灌缝胶，在满足温度、加热时间、保温时间条件的前提下，只要按要求添加各组分，然后搅拌均匀即可，易于成形。
本发明速焊自愈型灌缝胶的使用方法，使路面修补养护效率增加5倍，焊缝胶的胶条厚一般为1cm～1.5cm，投料方便，易熔化。有利于施工现场根据裂缝的大小切割成胶条，将胶条往裂缝中一塞，路面焊缝机燃气喷枪火焰一燎，瞬间就可将裂缝焊死。随时开放交通，不会对交通造成任何影响。焊缝胶条受热面积大，容易熔化，可迅速填充到缝隙中，节省燃料。清洁施工，低碳运作，工人劳动强度低，工作效率高出五倍以上，并且对仰缝、立缝的施工更加方便。
本发明速焊自愈型灌缝胶的使用方法，通过使用燃气喷枪，在喷枪气压和熔化胶条重力的双重作用下，有效填充路面裂缝，操作方便，灌缝质量好，节省灌缝材料。
本发明速焊自愈型灌缝胶的使用方法，通过燃气喷枪的气压，可吹掉裂缝周围的灰尘，省去喷吹除尘工序。因喷枪设备简单，易携带，投资小，不需要投资较大的现场加热的灌缝机设备，成本小，效率高，不会浪费胶粘结剂。
综上所述，本发明速焊自愈型灌缝胶及其使用方法，粘度大，弹性高，耐低温，自愈性好，回粘性好，耐磨性强，抗撕裂性好，工序简单，易携带，投资小，成本低，灌缝后凝固时间十分钟左右，即可开放交通，效率高，操作方便，在使用过程中不会对大气和路面造成污染，灌缝质量好，节省灌缝材料，材料可反复加热，能延长养护周期，减少养护次数，使用寿命长，可节省能源、人力及成本。
具体实施方式
实施例1：
本发明速焊自愈型灌缝胶，包括100号沥青、10号沥青、胶粉、SBS橡胶改性石油沥青、萜烯树酯、APAO无定型烯烃共聚物、稀土、滑石粉；各组分重量百分数为：
100号沥青 32％，
10号沥青 27％，
胶粉 12％，
SBS橡胶改性石油沥青 6％，
萜烯树酯 0.5％，
APAO无定型烯烃共聚物 0.5％，
稀土 6％，
滑石粉 16％；
按上述各组分重量百分数，将100号、10号沥青升温脱水，温度保持在225℃时加胶粉，保温1小时加后加SBS橡胶改性石油沥青，熔化时间2小时，溶化后添加用胶体磨研磨后的APAO无定型烯烃共聚物、稀土、萜烯树酯，最后加滑石粉搅拌均匀，温度保持150℃放灌、冷却、成形。
本发明速焊自愈型灌缝胶，其使用方法是：将速焊自愈型灌缝胶用刀割成胶条，然后将胶条塞入裂缝中，用路面焊缝机燃气喷枪对准缝隙中的胶条加热灌入缝隙中，再用油灰刀刮平，最后撒细沙覆盖。
实施例2：
本发明速焊自愈型灌缝胶，包括100号沥青、10号沥青、胶粉、SBS橡胶改性石油沥青、萜烯树酯、APAO无定型烯烃共聚物、稀土、滑石粉；各组分重量百分数为：
100号沥青 25％，
10号沥青 35％，
胶粉 12％，
SBS橡胶改性石油沥青 5％，
萜烯树酯 0.4％，
APAO无定型烯烃共聚物 0.6％，
稀土 5％，
滑石粉 17％；
按上述各组分重量百分数，将100号、10号沥青升温脱水，温度保持在220℃时加胶粉，保温1小时加后加SBS橡胶改性石油沥青，熔化时间2小时，溶化后添加用胶体磨研磨后的APAO无定型烯烃共聚物、稀土、萜烯树酯，最后加滑石粉搅拌均匀，温度保持140℃放灌、冷却、成形。
本发明速焊自愈型灌缝胶，其使用方法是：将速焊自愈型灌缝胶用刀割成胶条，然后将胶条塞入裂缝中，用路面焊缝机燃气喷枪对准缝隙中的胶条加热灌入缝隙中，再用油灰刀刮平，最后撒细沙覆盖。
实施例3：
本发明速焊自愈型灌缝胶，包括100号沥青、10号沥青、胶粉、SBS橡胶改性石油沥青、萜烯树酯、APAO无定型烯烃共聚物、稀土、滑石粉；各组分重量百分数为：
100号沥青 40％，
10号沥青 20％，
胶粉 10％，
SBS橡胶改性石油沥青 8％，
萜烯树酯 0.6％，
APAO无定型烯烃共聚物 0.4％，
稀土 7％，
滑石粉 14％；
按上述各组分重量百分数，将100号、10号沥青升温脱水，温度保持在230℃时加胶粉，保温1小时加后加SBS橡胶改性石油沥青，熔化时间2小时，溶化后添加用胶体磨研磨后的APAO无定型烯烃共聚物、稀土、萜烯树酯，最后加滑石粉搅拌均匀，温度保持160℃放灌、冷却、成形。
本发明速焊自愈型灌缝胶，其使用方法是：将速焊自愈型灌缝胶用刀割成胶条，然后将胶条塞入裂缝中，用路面焊缝机燃气喷枪对准缝隙中的胶条加热灌入缝隙中，再用油灰刀刮平，最后撒细沙覆盖。
Claims (3)
1.一种速焊自愈型灌缝胶，其特征在于，包括100号沥青、10号沥青、胶粉、SBS橡胶改性石油沥青、萜烯树酯、APAO无定型烯烃共聚物、稀土、滑石粉；各组分重量百分数为：
100号沥青 25％～40％，
10号沥青 20％～35％，
胶粉 9％～15％，
SBS橡胶改性石油沥青 4％～8％，
萜烯树酯 0.4％～0.6％，
APAO无定型烯烃共聚物 0.4％～0.6％，
稀土 4％～8％，
滑石粉 13％～19％；
按上述各组分重量百分数，将100号、10号沥青升温脱水，温度保持在220℃～230℃时加胶粉，保温1小时加后加SBS橡胶改性石油沥青，熔化时间2小时，溶化后添加用胶体磨研磨后的APAO无定型烯烃共聚物、稀土、萜烯树酯，最后加滑石粉搅拌均匀，温度保持140℃～160℃放灌、冷却、成形。
2.根据权利要求1所述的速焊自愈型灌缝胶，其特征在于，所说的各组分重量百分数为：
100号沥青 32％，
10号沥青 27％，
胶粉 12％，
SBS橡胶改性石油沥青 6％，
萜烯树酯 0.5％，
APAO无定型烯烃共聚物 0.5％，
稀土 6％，
滑石粉 16％。
3.一种权利要求1所述的速焊自愈型灌缝胶的使用方法，其特征在于，其使用方法是：将速焊自愈型灌缝胶用刀割成胶条，然后将胶条塞入裂缝中，用路面焊缝机燃气喷枪对准缝隙中的胶条加热灌入缝隙中，再用油灰刀刮平，最后撒细沙覆盖。