CN102689351B - 一种带台阶吊臂的制备方法 - Google Patents

一种带台阶吊臂的制备方法 Download PDF

Info

Publication number
CN102689351B
CN102689351B CN201210181402.7A CN201210181402A CN102689351B CN 102689351 B CN102689351 B CN 102689351B CN 201210181402 A CN201210181402 A CN 201210181402A CN 102689351 B CN102689351 B CN 102689351B
Authority
CN
China
Prior art keywords
preparation
step arm
dry
pressure
pressing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210181402.7A
Other languages
English (en)
Other versions
CN102689351A (zh
Inventor
陶岳雨
陶近翁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI COMPANION PRECISION CERAMICS CO Ltd
Original Assignee
SHANGHAI COMPANION PRECISION CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI COMPANION PRECISION CERAMICS CO Ltd filed Critical SHANGHAI COMPANION PRECISION CERAMICS CO Ltd
Priority to CN201210181402.7A priority Critical patent/CN102689351B/zh
Publication of CN102689351A publication Critical patent/CN102689351A/zh
Application granted granted Critical
Publication of CN102689351B publication Critical patent/CN102689351B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种带台阶吊臂的制备方法，包括：（1）采用氧化铝进行配料，使用起缓冲作用的装置进行干压成型，得到成型坯体；（2）将上述成型坯体进行冷等静压，然后经过烧结和精加工，得到带台阶吊臂。本发明解决了台阶结构件的干压成型问题，生产效率高，成品率高，可实现规模化生产，产品结构无异常变形，密度达到98%以上，具有良好的应用前景。

Description

一种带台阶吊臂的制备方法
技术领域
本发明属于半导体搬运精密陶瓷的制备领域，特别涉及一种带台阶吊臂的制备方法。
背景技术
精密陶瓷主要用于制作电路基片、线圈骨架、电子管插座、高压绝缘瓷、火箭的前锥体等。也可制成用于浇制合金的高气孔率精密铸造型芯。还可用作抗震性好的高温材料。精密陶瓷工艺是以热固性塑料（如硅酮树脂）为黏合剂，按一定比例加入陶瓷粉料，混匀后用注塑机成型或流延法成型。然后，经高温烧结成制品。根据原材料性质的不同和制品性能、形状、尺寸的差异，选择不同的黏合剂和成型方法，可制成表面光滑、气孔率低的电子陶瓷和结构陶瓷制品。
结合生产效率和产品的要求，采用干压成型进行精密陶瓷制品的生产是在满足产品质量前提下的高效生产方式，带有台阶的结构件由于在干压成型过程中在台阶和其他结构间产生压力差，从而造成结构上的密度不均匀性，造成成型失败或者在烧结过程中产生裂纹和变形等各种缺陷。
发明内容
本发明所要解决的技术问题是提供一种带台阶吊臂的制备方法，该方法解决了台阶结构结构件的干压成型问题，生产效率高，成品率高，可实现规模化生产，产品结构无异常变形，密度达到98%以上，具有良好的应用前景。
本发明的一种带台阶吊臂的制备方法，包括：
（1）采用氧化铝进行配料，使用起缓冲作用的装置进行干压成型，得到成型坯体；
（2）将上述成型坯体进行冷等静压，然后经过烧结和精加工，得到带台阶吊臂。
所述步骤（1）中的氧化铝为纯度≥99.7%的氧化铝。
所述步骤（1）中的干压成型的工艺参数为压力100-150MPa，双向加压，保压1-3分钟。
所述步骤（2）中的冷等静压的工艺参数为压力200-300MPa，保压3-5分钟。
所述步骤（2）中的烧结的温度为1650-1800℃，保温时间为2-4小时。
本发明采用在台阶结构以外使用缓冲装置，使得在干压成型过程中初期台阶处承受先期压力，而其余部分由于缓冲结构的存在不承受直接的压力，从而使得台阶处先实现一定程度的致密化，模具到达一定位置后，台阶和其余部分承受比先期大的同等压力，从而使得各部分不会由于台阶的存在产生过大的压力差，达到均匀致密化的程度。
成型后的坯体经冷等静压进一步使得产品的密度均匀性达到一致，烧结后，产品结构无异常变形，密度达到98%以上，生产效率高。
有益效果
本发明解决了台阶结构结构件的干压成型问题，生产效率高，成品率高，可实现规模化生产，产品结构无异常变形，密度达到98%以上，具有良好的应用前景。
附图说明
图1为本发明制得的带台阶吊臂的俯视图；
图2为本发明制得的带台阶吊臂的侧视图。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围。
实施例1
（1）采用纯度≥99.7%的氧化铝进行配料，使用起缓冲作用的装置进行干压成型，压力100MPa，双向加压，保压1分钟，得到成型坯体；
（2）将上述成型坯体进行冷等静压，压力200MPa，保压3分钟，然后经过1650℃烧结2小时和精加工，得到带台阶吊臂（如图1、2所示）。
实施例2
（1）采用纯度≥99.7%的氧化铝进行配料，使用起缓冲作用的装置进行干压成型，压力150MPa，双向加压，保压3分钟，得到成型坯体；
（2）将上述成型坯体进行冷等静压，压力300MPa，保压5分钟，然后经过1800℃烧结4小时和精加工，得到带台阶吊臂。

Claims (5)

1.一种带台阶吊臂的制备方法，包括：
(1)采用氧化铝进行配料，在台阶结构以外的其余部分使用起缓冲作用的装置进行干压成型，得到成型坯体；
(2)将上述成型坯体进行冷等静压，然后经过烧结和精加工，得到带台阶吊臂。
2.根据权利要求1所述的一种带台阶吊臂的制备方法，其特征在于：所述步骤(1)中的氧化铝为纯度≥99.7％的氧化铝。
3.根据权利要求1所述的一种带台阶吊臂的制备方法，其特征在于：所述步骤(1)中的干压成型的工艺参数为压力100-150MPa，双向加压，保压1-3分钟。
4.根据权利要求1所述的一种带台阶吊臂的制备方法，其特征在于：所述步骤(2)中的冷等静压的工艺参数为压力200-300MPa，保压3-5分钟。
5.根据权利要求1所述的一种带台阶吊臂的制备方法，其特征在于：所述步骤(2)中的烧结的温度为1650-1800℃，保温时间为2-4小时。
CN201210181402.7A 2012-06-04 2012-06-04 一种带台阶吊臂的制备方法 Active CN102689351B (zh)