CN102689155A

CN102689155A - Liquid die forging and rolling compound formation method for aluminum alloy irregular-section large ring piece

Info

Publication number: CN102689155A
Application number: CN2012102004883A
Authority: CN
Inventors: 李路; 王放; 陈志谦; 于文斌
Original assignee: Southwest University
Current assignee: Southwest University
Priority date: 2012-06-18
Filing date: 2012-06-18
Publication date: 2012-09-26
Anticipated expiration: 2032-06-18
Also published as: CN102689155B

Abstract

The invention discloses a liquid die forging and rolling compound formation method for an aluminum alloy irregular-section large ring piece. The method comprises the following steps of: smelting, performing liquid die forging, homogenizing, performing afterheat isothermal rolling, performing thermal treatment and finishing, wherein the step of performing liquid die forging comprises the following substeps of: fixing a liquid die forging mold on an indirect extrusion casting machine, pouring a quantitative amount of aluminum alloy solution obtained through smelting into the liquid die forging mold at the pouring temperature of between 650 and 730 DEG C, pressurizing at the speed of 35 to 40 mm/s, filling for 1 to 6 seconds at the specific pressure of 100 to 200 MPa, keeping the pressure for 35 to 60 seconds, and thus obtaining a similarly final section ring blank; and the step of performing afterheat isothermal rolling comprises the following substeps of: cooling the homogenized similarly final section ring blank to the temperature of between 430 and 480 DEG C, and performing afterheat isothermal rolling on a radial shaft compound ring rolling machine. According to the liquid die forging and rolling compound formation method for the stainless steel irregular-section large ring piece, the flow of a blank preparation process for an aluminum alloy ring piece can be simplified, the cost can be reduced, and the production efficiency can be improved; and furthermore, the microstructure state of the aluminum alloy ring piece can be effectively improved, and the comprehensive mechanical performance is improved.

Description

The rolling combined shaping method of liquid forging of the different cross section of aluminium alloy large ring

Technical field

The present invention relates to a kind of short flow process and shape method, the concrete rolling combined shaping method of liquid forging that relates to the different cross section of a kind of aluminium alloy large ring with major diameter metal ring of complex section.

Background technology

Along with the develop rapidly of China's aerospace industry, the high thrust carrier rocket is badly in need of the large-size complex-cross-section aluminium alloy rings of 5 meters higher levels of diameter.So-called complex section ring; Be meant that ring axial direction sectional area size difference is big, ring cross-wise direction shape and size change greatly and inner surface and all comparatively complicated ferrule piece of external surface shape; It is the important step that can high thrust carrier rocket project successful, is the crucial connector of carrier rocket.The requirement that special environment for use has proposed intimate harshness to the dimensional accuracy and the comprehensive mechanical property of ring: require part to have high-precision appearance and size on the one hand; Avoid follow-up machine to add shaping, the serious ring serviceability that reduces when wasting a large amount of manpower and materials; Require part to have excellent structural state on the other hand to reach the requirement of comprehensive mechanical property.

At present, hot rolling system (be also referred to as heat and roll over expansion) and machine cut processing associating completion are adopted in the preparation of complex section ring usually.This technology rolls out the ring base of square-section based on the shaping ingot blank, through machine cut needed complex section is processed in the square-section again.The main process flow process is: smelting → cogging → blanking → jumping-up → punching → hot rolling system → heat treatment → machining.There is the problem of the following aspects in this technology:

1) flow process is tediously long, and operation is various, and production efficiency is low;

2) roll over the ring expansion base and need the punching preparation, and final cross sectional shape need guarantee that stock utilization is low through the unnecessary dressing of cutting;

3) mechanical processing process cuts off metal streamline, causes the ring comprehensive mechanical property to descend;

4) preparation process needs repeated heating, causes crystal grain thick, and surface oxidation is serious, and energy loss is big.

Publication number is the method that the Chinese patent of CN 101817134A discloses a kind of ferrule piece short-flow casting and rolling composite forming; Though it is short that the method for this ferrule piece short-flow casting and rolling composite forming satisfies production procedure to a certain extent; Save the beneficial effect of the energy, material and manpower; But this method adopts centrifugal casting ring base, can't satisfy the processing request of complex section ring, and the comprehensive mechanical property of producing the ferrule piece that obtains does not also reach the instructions for use like carrier rocket.

Given this; The present invention is intended to explore the rolling combined shaping method of liquid forging of the different cross section of a kind of aluminium alloy large ring; The rolling combined shaping method of liquid forging of the different cross section of this aluminium alloy large ring not only can simplify aluminium alloy rings the blank-making technology flow process, reduce cost and enhance productivity; But also can effectively improve the microstructure state of aluminium alloy rings, improve comprehensive mechanical property.

Summary of the invention

The technical problem that the present invention will solve is the rolling combined shaping method of liquid forging that proposes the different cross section of a kind of aluminium alloy large ring; The rolling combined shaping method of liquid forging of the different cross section of this aluminium alloy large ring not only can simplify aluminium alloy rings the blank-making technology flow process, reduce cost and enhance productivity; But also can effectively improve the microstructure state of aluminium alloy rings, improve comprehensive mechanical property.

Realize above-mentioned technical purpose, the rolling combined shaping method of liquid forging of the different cross section of aluminium alloy of the present invention large ring comprises melting → liquid forging → homogenising → waste heat ausrolling → heat treatment → finishing;

Said liquid forging is: after being fixed in liquid-state forging die on the indirect extrusion casting machine; The aluminium alloy solution that melting is obtained quantitatively is poured in the liquid-state forging die, and pouring temperature is 650-730 ℃, and pressing speed is 35-40 mm/s; Filling time 1-6 s; Specific pressure is 100-200 MPa, and under this pressure pressurize 35-60 s, obtain nearly whole cross section ring base;

Said waste heat ausrolling is: when the temperature of the near whole cross section ring base after homogenising is reduced to 430-480 ℃, on the compound machine for rolling ring of footpath axle, carry out ausrolling.

Further; After being fixed in said liquid-state forging die on the indirect extrusion casting machine, when being preheated to 150-200 ℃, in the liquid-state forging die die cavity, evenly spray one deck releasing agent; Coating layer thickness 10-20 micron continues the preheating liquid-state forging die to 250-300 ℃;

Further, said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.5-0.6V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when the external diameter that encircles base and finished product ring differed 30-50 mm, axial roll was lifted;

Further, the rolling mould and the blank temperature difference are ± 10 ℃;

Further, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping;

Further, the raw material selection fine aluminium ingot of smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy, and fine aluminium ingot, pure spelter and MAG block all need remove before use the surface oxide skin and dirt, put into electric furnace after the cleaning and toast, remove contained steam;

Further; The cavity shape of said liquid-state forging die is similar with the shape of ring; When the design of liquid-state forging die; A side of choosing simple shape on the inside/outside cross section is as positioning reference plane; And the shape that roll contacts with nearly whole cross section ring base during according to the waste heat ausrolling is provided with the die cavity of liquid-state forging die, and the closed size of liquid-state forging die die cavity is compared with the final sectional dimension of ring: the radial dimension of liquid-state forging die is greater than the radial dimension of ring, and the axial dimension of liquid-state forging die is less than the radial dimension of ring;

Further, the rolling of said waste heat ausrolling is expanded than>=1.4, the endoporus degree of eccentricity≤3 of the near whole cross section ring base after rolling °, the core bore dia>=330mm of the near whole cross section ring base that liquid forging obtains.

Beneficial effect of the present invention is:

The rolling combined shaping method of the liquid forging of the different cross section of aluminium alloy of the present invention large ring adopts the technological process of melting → liquid forging → homogenising → waste heat ausrolling → heat treatment → finishing; This method is smelting aluminium alloy solution at first; Adopt liquid forging process to obtain nearly whole cross section ring base subsequently; And the direct rolling forming of waste heat that utilizes the ring base to solidify, compare with traditional handicraft, have the following advantages:

1) lacks flow process, effectively enhance productivity;

2) no punching operation, the complex section of aluminium alloy rings relies on liquid-state forging die and roll pass common guarantee, significantly improves stock utilization, realizes near-net forming;

3) liquid forging-ring base structural state significantly is superior to conventional cast ring base, is aided with follow-up hot rolling and processes the forging attitude modification that shape can fully guarantee to encircle the base material, obtains the tissue of fine and closely woven and homogenising.

4) finishing procedure effectively guarantees ring sectional dimension and surface accuracy, and the problem of avoiding machined to cause the ring streamline to cut off significantly improves comprehensive mechanical property;

5) blank need not repeated heating, and energy-saving and emission-reduction realize green manufacturing.

Therefore, the rolling combined shaping method of liquid forging of the different cross section of aluminium alloy of the present invention large ring is effectively simplified blank-making technology, and shortened process reduces cost, and boosts productivity and economic benefit, has huge development potentiality and broad prospect for its application.

The specific embodiment

Be elaborated below in conjunction with the rolling combined shaping method of liquid forging of specific embodiment to the different cross section of aluminium alloy of the present invention large ring.

First embodiment

The rolling combined shaping method of liquid forging of the different cross section of the aluminium alloy of present embodiment large ring comprises the steps, the aluminium alloy of present embodiment is 6082 aluminium alloys:

1) melting: 6082 aluminium alloys are pressed the composition proportion melting in melting furnace, melting was left standstill 25 minutes after accomplishing; Concrete, the raw material selection fine aluminium ingot of present embodiment smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; Fine aluminium ingot, pure spelter and MAG block are all used sand papering before use, remove the oxide skin and the dirt on surface, in clear water, clean then, put into electric furnace after the cleaning and toast, and remove contained steam.

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 650 ℃, and pressing speed is 35 mm/s; Filling time 6 s; Specific pressure is 100 MPa, and under this pressure pressurize 60 s, obtain nearly whole cross section ring base; Specific pressure is meant that liquid metal cools off the unit pressure of bearing under pressure, the amount that quantitatively is the required aluminium alloy solution of the rolling different cross section of liquid forging large ring as herein described.Preferably, be fixed in liquid-state forging die on the indirect extrusion casting machine after, when being preheated to 150 ℃; In the liquid-state forging die die cavity, evenly spray one deck releasing agent; 18 microns of coating layer thicknesses continue preheating liquid-state forging die to 250 ℃, and the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

Adopt liquid forging to process nearly whole cross section ring base, make aluminium alloy crystallization, shaping and produce a small amount of plastic deformation under pressure, obtain dense internal organization, crystal grain is tiny, the high-quality liquid forging part of any surface finish.Liquid forging has following process characteristic: 1) liquid forging can be eliminated the inner pore of foundry goods, shrinkage cavity and defective such as loose, produces local plastic deformation, makes foundry goods dense structure; 2) liquid metal is shaped under pressure and solidifies, and foundry goods and die cavity wall are fitted closely, thereby the liquid forging part has higher surface smoothness and dimensional accuracy, and its rank can reach the level of die casting; 3) the liquid forging part is in process of setting, and each position is in compressive stress state, helps the feeding of foundry goods and prevents the generation of casting crack; 4) liquid forging process is fit to the complicated ring base in preparation cross section very much, can effectively reduce cost, and improves the stock utilization of ring.The liquid forging technology also has advantages such as technology is simple, foundry goods good mechanical property, production efficiency is high, cost is relatively low.

3) homogenising: insulation 6 h after nearly whole cross section ring base is cooled to 550 ℃;

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 450 ℃; Adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 450 ℃, and the rolling mould of present embodiment and the blank temperature difference are 0 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.6V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 50 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

5) heat treatment: the ring base that obtains through the waste heat ausrolling is incubated 1 h down at 525 ℃, and heating up behind the quenching-in water 165 ℃ is incubated 12 h again;

6) finishing.

Further; The cavity shape of liquid-state forging die is similar with the shape of ring; When the design of liquid-state forging die, a side of choosing simple shape on the inside/outside cross section is as positioning reference plane, and the shape that roll contacts with nearly whole cross section ring base during according to the waste heat ausrolling is provided with the die cavity of liquid-state forging die; Effectively avoid blank cross sectional shape complicacy to cause rolling initial stage ring base to contact, cause skidding or the problem of malocclusion with point/line between the roll.The closed size of liquid-state forging die die cavity is compared with the final sectional dimension of ring: the radial dimension of liquid-state forging die is greater than the radial dimension of ring, and the axial dimension of liquid-state forging die is less than the radial dimension of ring, and concrete size expands than confirms according to rolling over.

Further, the rolling of waste heat ausrolling is expanded than >=1.4, and the rolling of present embodiment is expanded than=1.4, has tangible circumferential fibers to guarantee final ring.The near whole cross section ring base endoporus degree of eccentricity of the endoporus degree of eccentricity≤3 ° present embodiment of the near whole cross section ring base after the controlled rolling is 1 °, guarantees terminal ring base geometric accuracy and weight precision, and the core bore dia>=330mm of base is encircled in the near whole cross section that liquid forging obtains.

The rolling combined shaping method of the liquid forging of the different cross section of the aluminium alloy of present embodiment large ring adopts the technological process of melting → liquid forging → homogenising → waste heat ausrolling → heat treatment → finishing; This method is smelting aluminium alloy solution at first; Adopt liquid forging process to obtain nearly whole cross section ring base subsequently; And the direct rolling forming of waste heat that utilizes the ring base to solidify, compare with traditional handicraft, have the following advantages:

1) lacks flow process, effectively enhance productivity;

3) finishing procedure effectively guarantees ring sectional dimension and surface accuracy, and the problem of avoiding machined to cause the ring streamline to cut off significantly improves comprehensive mechanical property;

4) blank need not repeated heating, and energy-saving and emission-reduction realize green manufacturing.

Second embodiment

The rolling combined shaping method of liquid forging of the different cross section of the aluminium alloy of present embodiment large ring comprises the steps that the aluminium alloy of present embodiment is 6082 aluminium alloys:

1) melting: 6082 aluminium alloys are pressed the composition proportion melting in melting furnace, melting was left standstill 30 minutes after accomplishing; Concrete, the raw material selection fine aluminium ingot of present embodiment smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; Fine aluminium ingot, pure spelter and MAG block are all used sand papering before use, remove the oxide skin and the dirt on surface, in clear water, clean then, put into electric furnace after the cleaning and toast, and remove contained steam.

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 680 ℃, and pressing speed is 40 mm/s; Filling time 1 s; Specific pressure is 150 MPa, and under this pressure pressurize 35s, obtain nearly whole cross section ring base.Preferably; After being fixed in liquid-state forging die on the indirect extrusion casting machine; When being preheated to 200 ℃, in the liquid-state forging die die cavity, evenly spray one deck releasing agent, 10 microns of coating layer thicknesses; Continue preheating liquid-state forging die to 300 ℃, the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

3) homogenising: nearly whole cross section ring base is cooled to 550 ℃ of insulation 6 h;

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 480 ℃; Adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 470 ℃, and the rolling mould of present embodiment and the blank temperature difference are-10 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.55V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 30 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

6) finishing.

Further; The cavity shape of liquid-state forging die is similar with the shape of ring; When the design of liquid-state forging die, a side of choosing simple shape on the inside/outside cross section is as positioning reference plane, and the shape that roll contacts with nearly whole cross section ring base during according to the waste heat ausrolling is provided with the die cavity of liquid-state forging die; Effectively avoid blank cross sectional shape complicacy to cause rolling initial stage ring base to contact, cause skidding or the problem of malocclusion with point/line between the roll.The closed size of liquid-state forging die die cavity is compared with the final sectional dimension of ring: the radial dimension of liquid-state forging die is greater than the radial dimension of ring, and the axial dimension of liquid-state forging die is less than the radial dimension of ring.

Further, the rolling of waste heat ausrolling is expanded than >=1.4, and the rolling of present embodiment is expanded than=3, has tangible circumferential fibers to guarantee final ring.The near whole cross section ring base endoporus degree of eccentricity of the endoporus degree of eccentricity≤3 ° present embodiment of the near whole cross section ring base after the controlled rolling is 2 °, guarantees terminal ring base geometric accuracy and weight precision, and the core bore dia>=330mm of base is encircled in the near whole cross section that liquid forging obtains.

1) lacks flow process, effectively enhance productivity;

The 3rd embodiment

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 670 ℃, and pressing speed is 38 mm/s; Filling time 3 s; Specific pressure is 130MPa, and under this pressure pressurize 40 s, obtain nearly whole cross section ring base; Preferably, be fixed in liquid-state forging die on the indirect extrusion casting machine after, when being preheated to 180 ℃; In the liquid-state forging die die cavity, evenly spray one deck releasing agent; 20 microns of coating layer thicknesses continue preheating liquid-state forging die to 270 ℃, and the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 465 ℃; Adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 475 ℃, and the rolling mould of present embodiment and the blank temperature difference are 10 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.6V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 40 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

6) finishing.

Further, the rolling of waste heat ausrolling is expanded than >=1.4, and the rolling of present embodiment is expanded than=2, has tangible circumferential fibers to guarantee final ring.The endoporus degree of eccentricity≤3 of the near whole cross section ring base after the controlled rolling °, the near whole cross section ring base endoporus degree of eccentricity of present embodiment is 3 °, guarantees terminal ring base geometric accuracy and weight precision, the core bore dia>=330mm of base is encircled in the near whole cross section that liquid forging obtains.

1) lacks flow process, effectively enhance productivity;

The 4th embodiment

The rolling combined shaping method of liquid forging of the different cross section of the aluminium alloy of present embodiment large ring comprises the steps, the aluminium alloy of present embodiment is 7050 aluminium alloys:

1) melting: 7050 aluminium alloys are pressed the composition proportion melting in melting furnace, melting was left standstill 25 minutes after accomplishing; Concrete, the raw material selection fine aluminium ingot of present embodiment smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; Fine aluminium ingot, pure spelter and MAG block are all used sand papering before use, remove the oxide skin and the dirt on surface, in clear water, clean then, put into electric furnace after the cleaning and toast, and remove contained steam.

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 700 ℃, and pressing speed is 35 mm/s; Filling time 6 s; Specific pressure is 160 MPa, and under this pressure pressurize 45 s, obtain nearly whole cross section ring base; Specific pressure is meant that liquid metal cools off the unit pressure of bearing under pressure, the amount that quantitatively is the required aluminium alloy solution of the rolling different cross section of liquid forging large ring as herein described.Preferably, be fixed in liquid-state forging die on the indirect extrusion casting machine after, when being preheated to 150 ℃; In the liquid-state forging die die cavity, evenly spray one deck releasing agent; 18 microns of coating layer thicknesses continue preheating liquid-state forging die to 250 ℃, and the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

3) homogenising: after nearly whole cross section ring base is cooled to 430 ℃, be incubated 18 h, be warmed up to 467 ℃ of insulation 12 h subsequently;

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 430 ℃; Adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 430 ℃, and the rolling mould of present embodiment and the blank temperature difference are 0 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.6V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 50 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

5) heat treatment: the ring base that obtains through the waste heat ausrolling is incubated 40 min at 470 ℃, is warming up to 485 ℃ of insulation 40 min then, is incubated 12 h down at 135 ℃ after the cold-water quench, is warming up to 170 ℃ of insulation 2 h again, is cooled to 135 ℃ at last and is incubated 12 h;

6) finishing.

1) lacks flow process, effectively enhance productivity;

The 5th embodiment

1) melting: 7050 aluminium alloys are pressed the composition proportion melting in melting furnace, melting was left standstill 30 minutes after accomplishing; Concrete, the raw material selection fine aluminium ingot of present embodiment smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; Fine aluminium ingot, pure spelter and MAG block are all used sand papering before use, remove the oxide skin and the dirt on surface, in clear water, clean then, put into electric furnace after the cleaning and toast, and remove contained steam.

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 730 ℃, and pressing speed is 40 mm/s; Filling time 1 s; Specific pressure is 200 MPa, and under this pressure pressurize 35s, obtain nearly whole cross section ring base.Preferably; After being fixed in liquid-state forging die on the indirect extrusion casting machine; When being preheated to 200 ℃, in the liquid-state forging die die cavity, evenly spray one deck releasing agent, 10 microns of coating layer thicknesses; Continue preheating liquid-state forging die to 300 ℃, the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 440 ℃; Adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 430 ℃, and the rolling mould of present embodiment and the blank temperature difference are-10 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.55V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 30 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

6) finishing.

1) lacks flow process, effectively enhance productivity;

The 6th embodiment

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 710 ℃, and pressing speed is 38 mm/s; Filling time 3 s; Specific pressure is 170MPa, and under this pressure pressurize 40 s, obtain nearly whole cross section ring base; Preferably, be fixed in liquid-state forging die on the indirect extrusion casting machine after, when being preheated to 180 ℃; In the liquid-state forging die die cavity, evenly spray one deck releasing agent; 20 microns of coating layer thicknesses continue preheating liquid-state forging die to 270 ℃, and the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

3) homogenising: nearly whole cross section ring base is cooled to 430 ℃ of insulation 18 h, is warmed up to 467 ℃ of insulation 12 h subsequently;

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 435 ℃; Adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 445 ℃, and the rolling mould of present embodiment and the blank temperature difference are 10 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.6V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 40 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

6) finishing.

1) lacks flow process, effectively enhance productivity;

The 7th embodiment

The rolling combined shaping method of liquid forging of the different cross section of the aluminium alloy of present embodiment large ring comprises the steps, the aluminium alloy of present embodiment is 7075 aluminium alloys:

1) melting: after the completion of 7075 aluminium alloy smeltings, under 725 ℃ temperature, left standstill 25 minutes; Concrete, the raw material selection fine aluminium ingot of present embodiment smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; Fine aluminium ingot, pure spelter and MAG block are all used sand papering before use, remove the oxide skin and the dirt on surface, in clear water, clean then, put into electric furnace after the cleaning and toast, and remove contained steam.

In the fusion process, when the melting furnace temperature rises to 310 ℃, earlier the fine aluminium ingot is added melting furnace; Temperature is elevated to 770 ℃ in stove, treat that aluminium ingot melts basically after, add intermediate alloy, and sprinkle coverture; When temperature drops to 745 ℃; The center, molten bath that the MAG block and the pure spelter that are preheating to 200 ℃ are pressed into melting furnace; And add 1.7% the grain refiner that 1.5% refining agent that consumption is an aluminium liquid weight and consumption are aluminium liquid weight; With bell jar refining agent and grain refiner are pressed into apart from the melting furnace crucible bottom 100 mm degree of depth, and stir, alloy was carried out the refining refinement 30 minutes with the stirring rod of abundant preheating; In the time of 730 ℃, aluminum alloy melt is carried out degasification, ventilated 6 minutes with high pure nitrogen or argon gas; Leave standstill after 25 minutes and to add 0.3% the deslagging agent that consumption is an aluminium liquid weight; Adopt porous ceramic plate to the aluminum alloy melt filter cleaner; And change alloy melt over to resistance and leave standstill stove; Keep the aluminium alloy melt temperature at 730 ℃, carry out the secondary degasification, under 725 ℃ temperature, left standstill 25 minutes at last to reduce the influence of air content and dregginess to tissue.The intermediate alloy of present embodiment adopts the composition of AlCu50 and AlCr2.The coverture of present embodiment is the composition of NaCl and KCl, and the weight ratio of said NaCl and KCl is 1:1.

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 685 ℃, and pressing speed is 38mm/s; Filling time 4s; Specific pressure is 160 MPa, and under this pressure pressurize 42 s, obtain nearly whole cross section ring base; Specific pressure is meant that liquid metal cools off the unit pressure of bearing under pressure, the amount that quantitatively is the required aluminium alloy solution of the rolling different cross section of liquid forging large ring as herein described.Preferably, be fixed in liquid-state forging die on the indirect extrusion casting machine after, when being preheated to 150 ℃; In the liquid-state forging die die cavity, evenly spray one deck releasing agent; 18 microns of coating layer thicknesses continue preheating liquid-state forging die to 250 ℃, and the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

3) homogenising: when nearly whole cross section 7075 aluminum alloy ring bases are cooled to 462 ℃, be incubated 6 h;

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 450 ℃, adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 450 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.6V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 50 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

5) heat treatment: the ring base is at 460 ℃ of insulation 2 h, and cold-water quench is warming up to 170 ℃ of insulation 8h subsequently behind 110 ℃ of insulation 6h;

6) finishing.

Further, the chemical composition of 7075 aluminium alloys of present embodiment (wt. %): Si:0.06, Fe:0.16, Cu:1.50, Mn:0.05, Mg:2.57, Cr:0.21, Ti:0.02, Zn:5.85, all the other are Al.

1) lacks flow process, effectively enhance productivity;

The 8th embodiment

The rolling combined shaping method of liquid forging of the different cross section of the aluminium alloy of present embodiment large ring comprises the steps that the aluminium alloy of present embodiment is 7075 aluminium alloys:

1) melting: after the completion of 7075 aluminium alloy smeltings, under 730 ℃ temperature, left standstill 30 minutes; Concrete, the raw material selection fine aluminium ingot of present embodiment smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; Fine aluminium ingot, pure spelter and MAG block are all used sand papering before use, remove the oxide skin and the dirt on surface, in clear water, clean then, put into electric furnace after the cleaning and toast, and remove contained steam.

In the fusion process, when the melting furnace temperature rises to 320 ℃, earlier the fine aluminium ingot is added melting furnace; Temperature is elevated to 760 ℃ in stove, treat that aluminium ingot melts basically after, add intermediate alloy, and sprinkle coverture; When temperature drops to 740 ℃; The center, molten bath that the MAG block and the pure spelter that are preheating to 250 ℃ are pressed into melting furnace; And add 2% the grain refiner that 1% refining agent that consumption is an aluminium liquid weight and consumption are aluminium liquid weight; With bell jar refining agent and grain refiner are pressed into apart from the melting furnace crucible bottom 100 mm degree of depth, and stir, alloy was carried out the refining refinement 10 minutes with the stirring rod of abundant preheating; In the time of 735 ℃, aluminum alloy melt is carried out degasification, ventilated 8 minutes with high pure nitrogen or argon gas; Leave standstill after 20 minutes and to add 0.2% the deslagging agent that consumption is an aluminium liquid weight; Adopt porous ceramic plate to the aluminum alloy melt filter cleaner; And change alloy melt over to resistance and leave standstill stove; Keep the aluminium alloy melt temperature at 730 ℃, carry out the secondary degasification, under 730 ℃ temperature, left standstill 30 minutes at last to reduce the influence of air content and dregginess to tissue.The intermediate alloy of present embodiment adopts the composition of AlCu50 and AlCr2.The coverture of present embodiment is the composition of NaCl and KCl, and the weight ratio of said NaCl and KCl is 1:1.

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 680 ℃, and pressing speed is 35 mm/s; Filling time 3s; Specific pressure is 180 MPa, and under this pressure pressurize 35s, obtain nearly whole cross section ring base.Preferably; After being fixed in liquid-state forging die on the indirect extrusion casting machine; When being preheated to 150 ℃, in the liquid-state forging die die cavity, evenly spray one deck releasing agent, 10 microns of coating layer thicknesses; Continue preheating liquid-state forging die to 230 ℃, the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

3) homogenising: when nearly whole cross-sectional aluminum alloy ring base is cooled to 440 ℃, be incubated 24 h;

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 440 ℃, adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 430 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.55V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 30 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

5) heat treatment: the ring base is at 477 ℃ of insulation 1 h, and cold-water quench is warming up to 180 ℃ of insulation 6h subsequently behind 100 ℃ of insulation 8h;

6) finishing.

Further, the chemical composition of described 7075 aluminium alloys of present embodiment (wt. %): Si:0.08, Fe:0.18, Cu:1.50, Mn:0.05, Mg:2.58, Cr:0.25, Ti:0.05, Zn:5.65, all the other are Al.

1) lacks flow process, effectively enhance productivity;

The 9th embodiment

1) melting: after the completion of 7075 aluminium alloy smeltings, under 720 ℃ temperature, left standstill 25 minutes; Concrete, the raw material selection fine aluminium ingot of present embodiment smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; Fine aluminium ingot, pure spelter and MAG block are all used sand papering before use, remove the oxide skin and the dirt on surface, in clear water, clean then, put into electric furnace after the cleaning and toast, and remove contained steam.

In the fusion process, when the melting furnace temperature rises to 300 ℃, earlier the fine aluminium ingot is added melting furnace; Temperature is elevated to 780 ℃ in stove, treat that aluminium ingot melts basically after, add intermediate alloy, and sprinkle coverture; When temperature drops to 750 ℃; The center, molten bath that the MAG block and the pure spelter that are preheating to 200 ℃ are pressed into melting furnace; And add 1.5% the grain refiner that 2% refining agent that consumption is an aluminium liquid weight and consumption are aluminium liquid weight; With bell jar refining agent and grain refiner are pressed into apart from the melting furnace crucible bottom 100 mm degree of depth, and stir, alloy was carried out the refining refinement 40 minutes with the stirring rod of abundant preheating; In the time of 733 ℃, aluminum alloy melt is carried out degasification, ventilated 5 minutes with high pure nitrogen or argon gas; Leave standstill after 10 minutes and to add 0.1% the deslagging agent that consumption is an aluminium liquid weight; Adopt porous ceramic plate to the aluminum alloy melt filter cleaner; And change alloy melt over to resistance and leave standstill stove; Keep the aluminium alloy melt temperature at 730 ℃, carry out the secondary degasification, under 720 ℃ temperature, left standstill 25 minutes at last to reduce the influence of air content and dregginess to tissue.The intermediate alloy of present embodiment adopts the composition of AlCu50 and AlCr2.The coverture of present embodiment is the composition of NaCl and KCl, and the weight ratio of said NaCl and KCl is 1:1.

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 700 ℃, and pressing speed is 40 mm/s; Filling time 1s; Specific pressure is 170MPa, and under this pressure pressurize 45 s, obtain nearly whole cross section ring base; Preferably, be fixed in liquid-state forging die on the indirect extrusion casting machine after, when being preheated to 100 ℃; In the liquid-state forging die die cavity, evenly spray one deck releasing agent; 20 microns of coating layer thicknesses continue preheating liquid-state forging die to 250 ℃, and the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

3) homogenising: when nearly whole cross-sectional aluminum alloy ring base is cooled to 470 ℃, be incubated 10 h;

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 460 ℃, adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 460 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.6V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 40 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

5) heat treatment: the ring base is at 465 ℃ of insulation 1.5 h, and cold-water quench is warming up to 175 ℃ of insulation 7h subsequently behind 105 ℃ of insulation 7h;

6) finishing.

Further, the chemical composition of described 7075 aluminium alloys of present embodiment (wt. %): Si:0.10, Fe:0.20, Cu:1.52, Mn:0.08, Mg:2.75, Cr:0.22, Ti:0.07, Zn:5.90, all the other are Al.

1) lacks flow process, effectively enhance productivity;

The tenth embodiment

1) melting: after the completion of 7075 aluminium alloy smeltings, under 730 ℃ temperature, left standstill 20 minutes; Concrete, the raw material selection fine aluminium ingot of present embodiment smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; Fine aluminium ingot, pure spelter and MAG block are all used sand papering before use, remove the oxide skin and the dirt on surface, in clear water, clean then, put into electric furnace after the cleaning and toast, and remove contained steam.

In the fusion process, when the melting furnace temperature rises to 310 ℃, earlier the fine aluminium ingot is added melting furnace; Temperature is elevated to 770 ℃ in stove, treat that aluminium ingot melts basically after, add intermediate alloy, and sprinkle coverture; When temperature drops to 745 ℃; The center, molten bath that the MAG block and the pure spelter that are preheating to 300 ℃ are pressed into melting furnace; And add 1% the grain refiner that 1.5% refining agent that consumption is an aluminium liquid weight and consumption are aluminium liquid weight; With bell jar refining agent and grain refiner are pressed into apart from the melting furnace crucible bottom 100 mm degree of depth, and stir, alloy was carried out the refining refinement 20 minutes with the stirring rod of abundant preheating; In the time of 730 ℃, aluminum alloy melt is carried out degasification, ventilated 10 minutes with high pure nitrogen or argon gas; Leave standstill after 30 minutes and to add 0.3% the deslagging agent that consumption is an aluminium liquid weight; Adopt porous ceramic plate to the aluminum alloy melt filter cleaner; And change alloy melt over to resistance and leave standstill stove; Keep the aluminium alloy melt temperature at 730 ℃, carry out the secondary degasification, under 730 ℃ temperature, left standstill 20 minutes at last to reduce the influence of air content and dregginess to tissue.The intermediate alloy of present embodiment adopts the composition of AlCu50 and AlCr2.The coverture of present embodiment is the composition of NaCl and KCl, and the weight ratio of said NaCl and KCl is 1:1.

2) liquid forging: after being fixed in liquid-state forging die on the indirect extrusion casting machine; With the 1st) aluminium alloy solution that obtains in the step quantitatively is poured in the liquid-state forging die, and pouring temperature is 690 ℃, and pressing speed is 37mm/s; Filling time 6s; Specific pressure is 200MPa, and under this pressure pressurize 38 s, obtain nearly whole cross section ring base.Preferably; After being fixed in liquid-state forging die on the indirect extrusion casting machine; When being preheated to 120 ℃, in the liquid-state forging die die cavity, evenly spray one deck releasing agent, 15 microns of coating layer thicknesses; Continue preheating liquid-state forging die to 240 ℃, the spraying releasing agent can make things convenient for the liquid-state forging die demoulding.

3) homogenising: when nearly whole cross-sectional aluminum alloy ring base is cooled to 455 ℃, be incubated 12 h;

4) waste heat ausrolling: the waste heat after the employing homogenising cools to rolling temperature and directly implements hot rolling system process; And do not need post bake; When nearly whole cross section ring base is cooled to 450 ℃, adopt on the compound machine for rolling ring of footpath axle and carry out ausrolling, rolling mold temperature is 460 ℃.Said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.5V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when external diameter and the finished product ring that encircles base when nearly whole cross section differed 45 mm, axial roll was lifted; Preferably, the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

5) heat treatment: the ring base is at 470 ℃ of insulation 1 h, and cold-water quench is warming up to 170 ℃ of insulation 8h subsequently behind 110 ℃ of insulation 6h;

6) finishing.

Further, the chemical composition of described 7075 aluminium alloys of present embodiment (wt. %): Si:0.05, Fe:0.18, Cu:1.68, Mn:0.08, Mg:2.38, Cr:0.19, Ti:0.03, Zn:5.88, all the other are Al.

Further, the rolling of waste heat ausrolling is expanded than >=1.4, and the rolling of present embodiment is expanded than=1.5, has tangible circumferential fibers to guarantee final ring.The endoporus degree of eccentricity≤3 of the near whole cross section ring base after the controlled rolling °, the near whole cross section ring base endoporus degree of eccentricity of present embodiment is 3 °, guarantees terminal ring base geometric accuracy and weight precision, the core bore dia>=330mm of base is encircled in the near whole cross section that liquid forging obtains.

1) lacks flow process, effectively enhance productivity;

Explanation is at last; Above embodiment is only unrestricted in order to technical scheme of the present invention to be described; Although with reference to preferred embodiment the present invention is specified, those of ordinary skill in the art should be appreciated that and can make amendment or be equal to replacement technical scheme of the present invention; And not breaking away from the aim and the scope of technical scheme of the present invention, it all should be encompassed in the middle of the claim scope of the present invention.

Claims

1. the rolling combined shaping method of liquid forging of the different cross section of an aluminium alloy large ring is characterized in that: comprise melting → liquid forging → homogenising → waste heat ausrolling → heat treatment → finishing;

2. the rolling combined shaping method of liquid forging of the different cross section of aluminium alloy according to claim 1 large ring; It is characterized in that: after being fixed in said liquid-state forging die on the indirect extrusion casting machine; When being preheated to 150-200 ℃; In the liquid-state forging die die cavity, evenly spray one deck releasing agent, coating layer thickness 10-20 micron continues the preheating liquid-state forging die to 250-300 ℃.

3. the rolling combined shaping method of liquid forging of the different cross section of aluminium alloy according to claim 1 large ring; It is characterized in that: said waste heat ausrolling comprises quick rolling expansion stage, stable rolling expansion stage, slows down and roll over the expansion stage and become the rounding shape stage, and the said quick rolling expansion stage is rolled over the axial feed velocity V of expansion during the stage with stablizing _AxiallyWith radial feed speed V _RadiallySatisfy V _Axially=0.5-0.6V _Radially, said deceleration is rolled over the expansion stage and is become rounding shape during the stage, and the not feeding of awl roller of the compound machine for rolling ring of footpath axle is only rollingly spreaded owing to what radial rolling caused, and when the external diameter that encircles base and finished product ring differed 30-50 mm, axial roll was lifted.

4. the rolling combined shaping method of aluminium alloy according to claim 3 different cross section large ring liquid forging, it is characterized in that: the rolling mould and the blank temperature difference are ± 10 ℃.

5. the rolling combined shaping method of liquid forging of the different cross section of aluminium alloy according to claim 3 large ring is characterized in that: the radial feeds of the compound machine for rolling ring of footpath axle are selected to forge and are passed through the desired minimum amount of feeding and the smaller value between the maximum amount of feeding that pass allowed of nipping.

6. the rolling combined shaping method of liquid forging of the different cross section of aluminium alloy according to claim 1 large ring; It is characterized in that: the raw material selection fine aluminium ingot of smelting aluminium alloy, pure spelter, MAG block, copper billet and intermediate alloy; And fine aluminium ingot, pure spelter and MAG block all need be removed the oxide skin and the dirt on surface before use; Put into electric furnace after the cleaning and toast, remove contained steam.

7. according to the rolling combined shaping method of liquid forging of each different cross section of described aluminium alloy large ring of claim 1-6; It is characterized in that: the cavity shape of said liquid-state forging die is similar with the shape of ring; When the design of liquid-state forging die; A side of choosing simple shape on the inside/outside cross section is as positioning reference plane; And the shape that roll contacts with nearly whole cross section ring base during according to the waste heat ausrolling is provided with the die cavity of liquid-state forging die; And the closed size of liquid-state forging die die cavity is compared with the final sectional dimension of ring: the radial dimension of liquid-state forging die is greater than the radial dimension of ring, and the axial dimension of liquid-state forging die is less than the radial dimension of ring.

8. the rolling combined shaping method of liquid forging of the different cross section of aluminium alloy according to claim 1 large ring; It is characterized in that: the rolling of said waste heat ausrolling is expanded than>=1.4; The endoporus degree of eccentricity≤3 of the near whole cross section ring base after rolling °, the core bore dia>=330mm of the near whole cross section ring base that liquid forging obtains.