CN102676114A - 一种多用途封瓶口胶及其制备方法 - Google Patents
一种多用途封瓶口胶及其制备方法 Download PDFInfo
- Publication number
- CN102676114A CN102676114A CN2012101646784A CN201210164678A CN102676114A CN 102676114 A CN102676114 A CN 102676114A CN 2012101646784 A CN2012101646784 A CN 2012101646784A CN 201210164678 A CN201210164678 A CN 201210164678A CN 102676114 A CN102676114 A CN 102676114A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- bottleneck
- nitrocellulose
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种多用途封瓶口胶，它包括如下重量份数的组分：乙醇 2～5份、乙醚1～6份、硝酸纤维素5～10份、甘油10～25份、水80～100份、骨胶120～150份、颜料10～30份。本发明的多用途封瓶口胶，原料简单，价格低廉，韧性强，胶膜不易脆裂，环保无毒，所封的瓶口美观，坚固。本发明制造工艺简单，易于实现。
Description
技术领域
本发明涉及化工领域，尤其涉及一种多用途封瓶口胶。
背景技术
封瓶口胶主要是用于瓶口密封，现有技术中封瓶口胶各种各样，但是存在韧性较差，封口后胶膜易脆裂，所封的瓶口不够美观，坚固，同时由于封瓶口胶采用的原料有些有毒、有味、可能造成污染，所以容易影响盛装的瓶内物的质量。
发明内容
本发明正是为了克服上述不足，所要解决的技术问题是提供一种韧性强、胶膜不易脆裂，环保的多用途封瓶口胶。
本发明还要解决的技术问题是提供上述多用途封瓶口胶的制备方法。
为解决上述技术问题，本发明所采用的技术方案如下：
一种多用途封瓶口胶，它包括如下重量份数的组分：
乙醇 2～5份
乙醚 1～6份
硝酸纤维素 5～10份
甘油 10～25份
水 80～100份
骨胶 120～150份
颜料 10～30份。
作为优选配方，上述多用途封瓶口胶，它包括如下重量份数的组分：
乙醇 3份
乙醚 4份
硝酸纤维素 8份
甘油 18份
水 90份
骨胶 135份
颜料 20份。
制备上述多用途封瓶口胶的方法，包括如下步骤：
1、按配方量将硝酸纤维素加入到乙醇、乙醚的混合溶液中，溶解均匀备用；
2、按配方量将甘油和水混合，再加入骨胶，步骤1中的备用溶液，然后加热溶化；
3、向步骤2中的溶化液中加入配方量的颜料搅拌均匀，即为所述的多用途封瓶口胶。
有益效果：本发明的多用途封瓶口胶，原料简单，价格低廉，韧性强，胶膜不易脆裂，环保无毒，所封的瓶口美观，坚固，可用于密封各种酒瓶、饮料瓶、调料瓶等。本发明制造工艺简单，易于实现。
具体实施方式
实施例1：
一种多用途封瓶口胶，它包括如下重量份数的组分：
乙醇 3份
乙醚 4份
硝酸纤维素 8份
甘油 18份
水 90份
骨胶 135份
颜料 20份。
制备上述多用途封瓶口胶的方法，包括如下步骤：
1、按配方量将硝酸纤维素加入到乙醇、乙醚的混合溶液中，溶解均匀备用；
2、按配方量将甘油和水混合，再加入骨胶，步骤1中的备用溶液，然后加热溶化；
3、向步骤2中的溶化液中加入配方量的颜料搅拌均匀，即为所述的多用途封瓶口胶。
实施例2：
一种多用途封瓶口胶，它包括如下重量份数的组分：
乙醇 2份
乙醚 1份
硝酸纤维素 5份
甘油 10份
水 80份
骨胶 120份
颜料 10份。
制备上述多用途封瓶口胶的方法，包括如下步骤：
1、按配方量将硝酸纤维素加入到乙醇、乙醚的混合溶液中，溶解均匀备用；
2、按配方量将甘油和水混合，再加入骨胶，步骤1中的备用溶液，然后加热溶化；
3、向步骤2中的溶化液中加入配方量的颜料搅拌均匀，即为所述的多用途封瓶口胶。
实施例3：
一种多用途封瓶口胶，它包括如下重量份数的组分：
乙醇 5份
乙醚 6份
硝酸纤维素 10份
甘油 25份
水 100份
骨胶 150份
颜料 30份。
制备上述多用途封瓶口胶的方法，包括如下步骤：
1、按配方量将硝酸纤维素加入到乙醇、乙醚的混合溶液中，溶解均匀备用；
2、按配方量将甘油和水混合，再加入骨胶，步骤1中的备用溶液，然后加热溶化；
3、向步骤2中的溶化液中加入配方量的颜料搅拌均匀，即为所述的多用途封瓶口胶。
上述实施例只为说明本发明的技术构思及特点，其目的是让熟悉该技术领域的技术人员能够了解本发明的内容并据以实施，并不能以此来限制本发明的保护范围。凡根据本发明精神实质所作出的等同变换或修饰，都应涵盖在本发明的保护范围之内。
Claims (3)
1.一种多用途封瓶口胶，其特征在于它包括如下重量份数的组分：
乙醇 2～5份
乙醚 1～6份
硝酸纤维素 5～10份
甘油 10～25份
水 80～100份
骨胶 120～150份
颜料 10～30份。
2.根据权利要求1所述的多用途封瓶口胶，其特征在于它包括如下重量份数的组分：
乙醇 3份
乙醚 4份
硝酸纤维素 8份
甘油 18份
水 90份
骨胶 135份
颜料 20份。
3.一种制备权利要求1所述的多用途封瓶口胶的方法，其特征在于包括如下步骤：
（1）、按配方量将硝酸纤维素加入到乙醇、乙醚的混合溶液中，溶解均匀备用；
（2）、按配方量将甘油和水混合，再加入骨胶，步骤（1）中的备用溶液，然后加热溶化；
（3）、向步骤（2）中的溶化液中加入配方量的颜料搅拌均匀，即为所述的多用途封瓶口胶。