CN102675869A - 一种弹性好的pa6-gf10hb的配方 - Google Patents
一种弹性好的pa6-gf10hb的配方 Download PDFInfo
- Publication number
- CN102675869A CN102675869A CN2012101590172A CN201210159017A CN102675869A CN 102675869 A CN102675869 A CN 102675869A CN 2012101590172 A CN2012101590172 A CN 2012101590172A CN 201210159017 A CN201210159017 A CN 201210159017A CN 102675869 A CN102675869 A CN 102675869A
- Authority
- CN
- China
- Prior art keywords
- gf10hb
- accounts
- polycaprolactam
- elasticity
- aluminum oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明揭示了一种弹性好的PA6-GF10HB的配方,包括聚已内酰胺、改性剂、填充剂和助剂,所述改性剂为三元乙丙橡胶,填充剂为氧化铝粉,助剂为山梨醇,各成分重量配比为聚已内酰胺占87%-89%,三元乙丙橡胶占9%-10%,氧化铝粉占1.5%-2%,山梨醇占0.5%-1%,使制得的弹性好的PA6-GF10HB具有较高的吸湿性,弹性好,耐碱性优良,耐紫外线和日光的效果。
Description
技术领域
本发明涉及一种塑料配方,具体涉及一种弹性好的PA6-GF10HB的配方。
背景技术
由于尼龙具有很多的特性,因此,在汽车、电气设备、机械部构、交通器材、纺织、造纸机械等方面得到广泛应用。随着汽车的小型化、电子电气设备的高性能化、机械设备轻量化的进程加快,对尼龙的需求将更高更大。特别是尼龙作为结构性材料,对其强度、耐热性、耐寒性等方面提出了很高的要求。尼龙的固有缺点也是限制其应用的重要因素,特别是对于PA6、PA66两大品种来说,与PA46、PAl2等品种比具有很强的价格优势,虽某些性能不能满足相关行业发展的要求。因此,必须针对某一应用领域,通过改性,提高其某些性能,来扩大其应用领域。 由于PA强极性的特点,吸湿性强,尺寸稳定性差,但可以通过改性来改善。
尼龙作为工程塑料中最大最重要的品种,具有很强的生命力,主要在于它改性后实现高性能化,其次是汽车、电器、通讯、电子、机械等产业自身对产品高性能的要求越来越强烈,相关产业的飞速发展,促进了工程塑料高性能化的进程,改性尼龙未来发展趋势如下。 ①高强度高刚性尼龙的市场需求量越来越大,新的增强材料如无机晶须增强、碳纤维增强PA将成为重要的品种,主要是用于汽车发动机部件,机械部件以及航空设备部件。②尼龙合金化将成为改性工程塑料发展的主流。尼龙合金化是实现尼龙高性能的重要途径,也是提高尼龙性能的主要手段。通过掺混其他高聚物,来改善尼龙的吸水性,提高制品的尺寸稳定性,以及低温脆性、耐热性和耐磨性。从而,适用车种不同要求的用途。③纳米尼龙的制造技术与应用将得到迅速发展。纳米尼龙的优点在于其热性能、力学性能、阻燃性、阻隔性比纯尼龙高,而制造成本与普通尼龙相当。因而,具有很大的竞争力。 ④用于电子、电气、电器的阻燃尼龙与日俱增,绿色化阻燃尼龙越来越受到市场的重视。⑤抗静电、导电尼龙以及磁性尼龙将成为电子设备、矿山机械、纺织机械的首选材料。⑥加工助剂的研究与应用,将推动改性尼龙的功能化、高性能化的进程。⑦综合技术的应用,产品的精细化是推动其产业发展的动力。
发明内容
本发明的目的在于提供具有较高的吸湿性,弹性好,耐碱性优良,耐紫外线和日光效果的一种弹性好的PA6-GF10HB的配方。
本发明的技术方案是:一种弹性好的PA6-GF10HB的配方,包括聚已内酰胺、改性剂、填充剂和助剂,所述改性剂为三元乙丙橡胶,填充剂为氧化铝粉,助剂为山梨醇,各成分重量配比为聚已内酰胺占87%-89%,三元乙丙橡胶占9%-10%,氧化铝粉占1.5%-2%,山梨醇占0.5%-1%。
在本发明一个较佳实施例中,所述三元乙丙橡胶包括乙烯,丙烯和二烯烃。
在本发明一个较佳实施例中,所述弹性好的PA6-GF10HB的配方各成分重量配比为聚已内酰胺占87%,三元乙丙橡胶占10%,氧化铝粉占2%,山梨醇占1%。
本发明的一种弹性好的PA6-GF10HB的配方,具有较高的吸湿性,弹性好,耐碱性优良,耐紫外线和日光的效果。
具体实施方式
下面结合对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
在一实施例中,一种弹性好的PA6-GF10HB的配方,包括聚已内酰胺、改性剂、填充剂和助剂,所述改性剂为三元乙丙橡胶,填充剂为氧化铝粉,助剂为山梨醇,各成分重量配比为聚已内酰胺占87%-89%,三元乙丙橡胶占9%-10%,氧化铝粉占1.5%-2%,山梨醇占0.5%-1%,所述三元乙丙橡胶包括乙烯,丙烯和二烯烃。
进一步说明,样品测试是在样品室放置24小时,样品室温度保持在23℃,相对湿度在50℃下:
测试项目 | 单位 | 测试方法 | 实测数据 |
溶融指数 | g/10min | D1238 | |
密度 | g/cm3 | D792 | 1.26 |
缺口冲击强度 | J/M | D256 | 144 |
抗弯强度 | mpa | D790 | 99.49 |
弯曲摸量 | mpa | D790 | 3828.24 |
拉伸强度 | mpa | D638 | 67.76 |
断裂伸长率 | % | D638 | 19.1 |
所述弹性好的PA6-GF10HB的配方各成分重量配比为聚已内酰胺占87%,三元乙丙橡胶占10%,氧化铝粉占2%,山梨醇占1%,根据不同需求可按照不同比例进行调试,从而达到不同的使用效果,而聚已内酰胺具有较高的吸湿性,三元乙丙橡胶具有弹性好,氧化铝粉具有耐碱性优良,而山梨醇起到耐紫外线和日光的效果,本发明提供一种弹性好的PA6-GF10HB的配方,具有较高的吸湿性,弹性好,耐碱性优良,耐紫外线和日光的效果。
本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (3)
1.一种弹性好的PA6-GF10HB的配方,其特征在于:包括聚已内酰胺、改性剂、填充剂和助剂,所述改性剂为三元乙丙橡胶,填充剂为氧化铝粉,助剂为山梨醇,各成分重量配比为聚已内酰胺占87%-89%,三元乙丙橡胶占9%-10%,氧化铝粉占1.5%-2%,山梨醇占0.5%-1%。
2.根据权利要求1所述的弹性好的PA6-GF10HB的配方,其特征在于:所述三元乙丙橡胶包括乙烯,丙烯和二烯烃。
3.根据权利要求1所述的弹性好的PA6-GF10HB的配方,其特征在于:所述弹性好的PA6-GF10HB的配方各成分重量配比为聚已内酰胺占87%,三元乙丙橡胶占10%,氧化铝粉占2%,山梨醇占1%。