CN102675699B - Fully-synthesized engineering tread rubber and formula thereof - Google Patents
Fully-synthesized engineering tread rubber and formula thereof Download PDFInfo
- Publication number
- CN102675699B CN102675699B CN201110064241.9A CN201110064241A CN102675699B CN 102675699 B CN102675699 B CN 102675699B CN 201110064241 A CN201110064241 A CN 201110064241A CN 102675699 B CN102675699 B CN 102675699B
- Authority
- CN
- China
- Prior art keywords
- rubber
- formula
- agent
- engineering
- synthesized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to tread rubber, in particular to fully-synthesized engineering tread rubber and a formula thereof, which belong to the technical field of rubber processing. In the formula, the entire raw rubber system is made from styrene butadiene rubber according to the practical characteristics of an engineering mechanical tire and the performance analysis of various types of synthesized rubber, and zinc oxide, stearic acid, an anti-aging agent RD and the like are added. As proved by the tests of a blending process, a winding process and a vulcanizing process, the engineering tread formula is low in cost, various comprehensive properties are higher than those of an original natural rubber formula, and the wearing resistance, scratching resistance and wear resistance of the engineering mechanical tire are improved greatly.
Description
Technical field
The present invention relates to a kind of tire sealant, be specifically related to a kind of complete synthesis engineering tread rubber and formula thereof, belong to Rubber processing technical field.
Background technology
At present, domestic project machinery tire tread glue adopts natural rubber mostly, but natural rubber resource is few, and price is high.
Summary of the invention
The object of the invention is for overcoming above-mentioned the deficiencies in the prior art part, a kind of complete synthesis engineering tread rubber and formula thereof are provided, this formula is according to the practical feature of off-the-road tyre and various elastomeric performance analysis, determine that the rubber system in formula all adopts universal divinyl rubber, be equipped with again zinc oxide, stearic acid, anti-aging agent RD etc., by comprising calendering process, winding process, the testing and verification of sulfuration process, this project tyre surface formula not only cost is low, and every over-all properties is all higher than former natural rubber formulations, the resistance to of off-the-road tyre gnaws, scratch-resistant, wear resistance improves greatly.
The technical solution adopted for the present invention to solve the technical problems is: a kind of complete synthesis engineering tread rubber and formula thereof, it is characterized in that: this tread rubber comprises one section of glue and finished composition, and wherein the formula of one section of glue and weight part are: universal divinyl rubber 100, zinc oxide 4-6, stearic acid 2-4, anti-aging agent RD 1.5-2, antioxidant 4020 1.5-2, protection wax 1.5-2, in super carbon black N22050-60, aromatic hydrocarbon oil 5-6, binder resin 7-9, homogeneous phase agent 2-4; The formula of finished composition and weight part are: rubber master batch 174.5-180, sulphur 2.5-3, accelerant NOBS 1-2, anti-scorching agent CTP 0.3-1.
Described binder resin is NH-80 binder resin, and described homogeneous phase agent is the agent of JF10 homogeneous phase.
Rubber master batch in described finished composition formula is one section of glue.
Advantage of the present invention is: this project tread glue formula is reasonable, rubber system all adopts styrene-butadiene rubber(SBR), be equipped with again zinc oxide, stearic acid, anti-aging agent RD etc., by comprising the testing and verification of calendering process, winding process, sulfuration process, this project tyre surface formula not only cost is low, and every over-all properties is all higher than former natural rubber formulations, off-the-road tyre resistance to gnaw, scratch-resistant, wear resistance improves greatly.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail:
Embodiment 1,
The formula of one section of glue and weight part are: universal divinyl rubber 100, zinc oxide 4, stearic acid 2, anti-aging agent RD 1.5, antioxidant 4020 1.5, protection wax 1.5, in super carbon black N220 50, aromatic hydrocarbon oil 5, binder resin 7, homogeneous phase agent 2; The formula of finished composition and weight part are: rubber master batch 174.5, sulphur 2.5, accelerant NOBS 1, anti-scorching agent CTP 0.3.
Described binder resin is NH-80 binder resin, and described homogeneous phase agent is the agent of JF10 homogeneous phase.
Rubber master batch in described finished composition formula is one section of glue.
Embodiment 2,
The formula of one section of glue and weight part are: universal divinyl rubber 100, zinc oxide 6, stearic acid 4, anti-aging agent RD 2, antioxidant 4020 2, protection wax 2, in super carbon black N22060, aromatic hydrocarbon oil 6, binder resin 9, homogeneous phase agent 4; The formula of finished composition and weight part are: rubber master batch 178, sulphur 3, accelerant NOBS 2, anti-scorching agent CTP 1.
Described binder resin is NH-80 binder resin, and described homogeneous phase agent is the agent of JF10 homogeneous phase.
Rubber master batch in described finished composition formula is one section of glue.
Claims (1)
1. a complete synthesis engineering tread rubber, it is characterized in that: this tread rubber comprises one section of glue and finished composition, and wherein the formula of one section of glue and weight part are: universal divinyl rubber 100, zinc oxide 4-6, stearic acid 2-4, anti-aging agent RD 1.5-2, antioxidant 4020 1.5-2, protection wax 1.5-2, in super carbon black N220 50-60, aromatic hydrocarbon oil 5-6, binder resin 7-9, homogeneous phase agent 2-4; The formula of finished composition and weight part are: rubber master batch 174.5-180, sulphur 2.5-3, accelerant NOBS 1-2, anti-scorching agent CTP 0.3-1; Described binder resin is NH-80 binder resin, and described homogeneous phase agent is the agent of JF10 homogeneous phase, and described rubber master batch is one section of glue.