CN102660175B - Multifunctional environmental-friendly writing paint and production method thereof - Google Patents
Multifunctional environmental-friendly writing paint and production method thereof Download PDFInfo
- Publication number
- CN102660175B CN102660175B CN201210165172.5A CN201210165172A CN102660175B CN 102660175 B CN102660175 B CN 102660175B CN 201210165172 A CN201210165172 A CN 201210165172A CN 102660175 B CN102660175 B CN 102660175B
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- polystyrene foamed
- lysate
- write
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a multifunctional environmental-friendly writing paint and a production method thereof. The multifunctional environmental-friendly writing paint is prepared from the following raw materials in parts by weight: 60-80 parts of PS (polystyrene) lysate, 10-20 parts of polystyrene foamed plastic, 0-5 parts of surface active agent, 1-5 parts of dispersing agent and 5-10 parts of vegetable oil. The production method comprises the following step of: firstly carrying out thermal cracking on the polystyrene foamed plastic at 400-450 DEG C through a reaction kettle to obtain the PS lysate, dissolving the polystyrene foamed plastic in the PS lysate to obtain a PS mixed glue solution, mixing pigment, the surface active agent, the dispersing agent and the vegetable oil with the PS mixed glue solution, fully and uniformly mixing at normal temperature, grinding and filtering to obtain the multifunctional environmental-friendly writing paint. The multifunctional environmental-friendly writing paint has excellent infiltration capacity, does not contain any organic solvent, is not easy to volatilize when not used for writing and ensures that a painting pen writes smoothly for the second time, the adhesive force of paint is very strong; and through the multifunctional environmental-friendly writing paint and the production method thereof, disclosed by the invention, the waste is recycled, the production cost is low, and the effect of environment protection is achieved.
Description
Technical field
The present invention relates to a kind of paint, specifically, be to provide a kind of painting pen specialized paint and production method thereof.
Background technology
Painting pen has been widely used in daily life and production, is mainly used in mark and repairs damaged paint etc.The fluency that painting pen is write is closely related with the paint quality using.Existing painting pen does not generally have specialized paint, how containing organic solvent, easily volatilize, and fluent writing degree is not high when use, need in the time writing, constantly rock pen container or a nib, uses very inconvenient.
Summary of the invention
The object of the present invention is to provide a kind of multi-functional environment-protection to write paint and production method thereof, it has good penetrating power, is not easy volatilization while not writing, fluent writing, and also production cost is low, is conducive to protection of the environment.
Embodiment of the present invention are: a kind of multi-functional environment-protection is write paint, it is characterized in that, formed by the raw material mixed preparing that comprises following weight part: 60 ~ 80 parts of PS lysates, 10 ~ 20 parts of polystyrene foamed plasticss, 0 ~ 5 part, tensio-active agent, 1-5 parts of dispersion agents, 5 ~ 10 parts of vegetables oil, described PS lysate is to be formed 400-450 DEG C of thermo-cracking through reactor by polystyrene foamed plastics.
Optimize, formed by the raw material mixed preparing that comprises following weight part: 65 parts of PS lysates, 15 parts of polystyrene foamed plasticss, 2 parts, tensio-active agent, 3 parts of dispersion agents, 8 parts of vegetables oil.
Described surface activity agent is the one in sodium oleate, Witconol 2301.
Described dispersion agent is any one in NUOSPERSE657, DISPONER9250 and ethylene glycol.
Described vegetables oil is one or both in Viscotrol C, Oleum Gossypii semen.
Production method of the present invention is: first polystyrene foamed plastics is obtained to PS lysate through reactor 400-450 DEG C of thermo-cracking, polystyrene foamed plastics is dissolved in PS lysate, obtain PS mixed glue solution, again pigment, tensio-active agent, dispersion agent, vegetables oil are admixed in PS mixed glue solution, stir at normal temperatures, make through grinding, filtering.
Polystyrene foamed plastics used in the present invention is waste old polystyrene foamed plastic.
Addition and the kind of pigment of the present invention are selected according to actual needs.
The present invention has excellent penetrating power, because not containing organic solvent, while not writing, be not easy volatilization, make nib under any condition, all keep moisture state, ensure painting pen smoothness in the time again writing, thereby overcome other painting pen, in the time writing, need rock pen container or pause use inconvenience written and that bring; This PASS is extremely strong, can write in any body surfaces such as iron and steel, ceramic tile, glass, timber, wrapping material by special painting pen.Production technique of the present invention is reasonable, and cost is low, and to reclaim waste old polystyrene foamed plastic as main raw material, recycling economy, is conducive to environment protection.
Embodiment
Embodiment 1:
Preparation raw material is: PS lysate 65kg, and waste old polystyrene foamed plastic 15kg, Witconol 2301 2kg,
nUOSPERSE6573kg, Viscotrol C 8kg.Compound method is: first by waste old polystyrene foamed plastic through reactor 400-450 DEG C of thermo-cracking, obtain PS lysate, waste old polystyrene foamed plastic is dissolved in PS lysate, obtain PS mixed glue solution, again pigment, Witconol 2301, NUOSPERSE6573, Viscotrol C are admixed in PS mixed glue solution, stir at normal temperatures, make through grinding, filtering.The pigment adding is selected addition and kind according to actual needs.
Embodiment 2:
Preparation raw material is: PS lysate 60kg, and polystyrene foamed plastics 20kg,
dISPONER92501kg, Oleum Gossypii semen 10kg.Compound method is: first by waste old polystyrene foamed plastic through reactor 400-450 DEG C of thermo-cracking, obtain PS lysate, waste old polystyrene foamed plastic is dissolved in PS lysate, obtain PS mixed glue solution, then by pigment,
dISPONER9250, Oleum Gossypii semen admixes in PS mixed glue solution, stirs at normal temperatures, make through grinding, filtering.The pigment adding is selected addition and kind according to actual needs.
Embodiment 3:
Preparation raw material is: PS lysate 80kg, polystyrene foamed plastics 10kg, Witconol 2301 5kg, ethylene glycol 1kg, Oleum Gossypii semen 10kg.Compound method is: first by waste old polystyrene foamed plastic through reactor 400-450 DEG C of thermo-cracking, obtain PS lysate, waste old polystyrene foamed plastic is dissolved in PS lysate, obtain PS mixed glue solution, again by pigment, Witconol 2301, ethylene glycol, Oleum Gossypii semen is admixed in PS mixed glue solution, stirs at normal temperatures, makes through grinding, filtering.The pigment adding is selected addition and kind according to actual needs.
Embodiment 1 is preferred version.
Claims (7)
1. a multi-functional environment-protection is write paint, it is characterized in that, formed by the raw material mixed preparing that comprises following weight part: 60 ~ 80 parts of PS lysates, 10 ~ 20 parts of polystyrene foamed plasticss, 0 ~ 5 part, tensio-active agent, 1-5 parts of dispersion agents, 5 ~ 10 parts of vegetables oil, described PS lysate is to be formed 400-450 DEG C of thermo-cracking through reactor by polystyrene foamed plastics.
2. multi-functional environment-protection according to claim 1 is write paint, it is characterized in that, is formed by the raw material mixed preparing that comprises following weight part: 65 parts of PS lysates, 15 parts of polystyrene foamed plasticss, 2 parts, tensio-active agent, 3 parts of dispersion agents, 8 parts of vegetables oil.
3. multi-functional environment-protection according to claim 1 and 2 is write paint, it is characterized in that, described surface activity agent is the one in sodium oleate, Witconol 2301.
4. multi-functional environment-protection according to claim 1 and 2 is write paint, it is characterized in that, described dispersion agent is any one in NUOSPERSE657, DISPONER9250 and ethylene glycol.
5. multi-functional environment-protection according to claim 1 and 2 is write paint, it is characterized in that, described vegetables oil is one or both in Viscotrol C, Oleum Gossypii semen.
6. the production method that multi-functional environment-protection as claimed in claim 1 is write paint, it is characterized in that, first polystyrene foamed plastics is obtained to PS lysate through reactor 400-450 DEG C of thermo-cracking, polystyrene foamed plastics is dissolved in PS lysate, and obtain PS mixed glue solution, again pigment, tensio-active agent, dispersion agent, vegetables oil are admixed in PS mixed glue solution, stirred at normal temperatures, make through grinding, filtering.
7. multi-functional environment-protection according to claim 6 is write the production method of paint, it is characterized in that, described polystyrene foamed plastics is waste old polystyrene foamed plastic.