CN102643988B - 一种用离子液体从废弃印刷线路板中浸出金属铜的方法 - Google Patents

一种用离子液体从废弃印刷线路板中浸出金属铜的方法 Download PDF

Info

Publication number
CN102643988B
CN102643988B CN2012101074446A CN201210107444A CN102643988B CN 102643988 B CN102643988 B CN 102643988B CN 2012101074446 A CN2012101074446 A CN 2012101074446A CN 201210107444 A CN201210107444 A CN 201210107444A CN 102643988 B CN102643988 B CN 102643988B
Authority
CN
China
Prior art keywords
ionic liquid
printed circuit
circuit board
butyl
aqueous solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2012101074446A
Other languages
English (en)
Other versions
CN102643988A (zh
Inventor
陈梦君
陈海焱
段涛
谌书
黄金秀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Southwest Jiaotong University
Southwest University of Science and Technology
Original Assignee
Southwest University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Southwest University of Science and Technology filed Critical Southwest University of Science and Technology
Priority to CN2012101074446A priority Critical patent/CN102643988B/zh
Publication of CN102643988A publication Critical patent/CN102643988A/zh
Application granted granted Critical
Publication of CN102643988B publication Critical patent/CN102643988B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用离子液体从废弃印刷线路板中浸出金属铜的方法，将废弃印刷线路板切成小块，用万能粉碎机进行粉碎，筛分，选用粒径在0.25-0.5mm的样品，烘干；称取样品于锥形瓶中，加入30％的双氧水，再加入浓度为10-80％的离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液，使固液比为1g∶7-55mL，其中双氧水和离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液体积比为1∶1.5-6，加盖于20-80℃的恒温水浴震荡箱中浸出1-24h，振荡频率为50-250转/分钟；将所得浸出液抽滤、洗涤、定容，测铜含量。本发明用离子液体1-丁基-3-甲基咪唑硫酸氢盐作为浸出剂，浸出废弃印刷线路板中的铜，铜含量达到90-95％。

Description

一种用离子液体从废弃印刷线路板中浸出金属铜的方法
技术领域
本发明涉及一种从废弃印刷线路板中浸出金属铜的方法，属于电子废弃物资源化处理和有价金属回收领域。
背景技术
印刷线路板(Printed Circuit Boards，PCBs)是电子电器产品中的基本构件，广泛应用于信息、通讯、消费性电子等领域。随着电子工业的发展，作为电子产品的重要组成部分，印刷线路板的数量在急剧增加，随之被淘汰的数量也在不断增加。废弃印刷线路板(Waste Printed Circuit Boards，WPCBs)正在成为电子废弃物的主要来源之一，其中含有卤化阻燃剂和重金属(铅、镉、汞等)等有毒有害物质，如处理不当，会对环境产生严重危害。另一方面，废弃印刷线路板中含有大量的贵金属(金、钯、银等)、贱金属(铜、铁、铝等)、树脂等可重复利用的资源，如果采用适当的处理技术回收其中的有价资源，具有极其重要的资源经济效益。废弃印刷线路板中铜的含量高达20％左右，从冶金的角度出发，其品味甚至比一般矿山要高，是可以重复利用的重要资源。当前我国已成为世界上第一大金属铜消费国，约占全球消费量的20％，但我国的铜矿资源难以满足自身经济持续快速发展的需要。因此，寻找一种经济、高效的绿色处理方式，从废弃印刷线路板中回收金属铜显得尤为重要。
目前，国内外对废弃印刷线路板的资源化处理方法大致可分为机械法、火法冶金、生物法和湿法冶金。机械处理法二次污染较轻，但得到的多是金属富集体，需进行进一步分离提纯，通常作为湿法和其他处理方法的预处理。火法冶金对所处理的废弃物形态要求较低，且金属的回收率较高，但在焚烧过程中易产生有毒气体二噁英及呋喃，会造成严重的环境污染，且部分金属的回收率相当低。生物法从废弃印刷线路板中浸取金等贵金属，具有工艺简单、费用低、操作方便、清洁等优点，但是浸取时间长，浸取率较低，而且由于目前可利用的菌种相当有限，菌种的培养又比较困难，因此目前生物法还处于研究阶段。湿法冶金处理过程中，金属的回收率较高，生产周期短，采用湿法技术最终可获得高纯度的金属单质。但湿法冶金也存在设备的腐蚀和试剂消耗量大的问题。因此，该技术的未来研究趋势应该是在整个回收工艺过程中考虑循环使用浸出剂，或采用环境友好型试剂作为浸出剂。离子液体作为一种新型绿色溶剂，具有其独特的理化性能，非常适合作为分离提纯的溶剂。
离子液体(Ionic Liquid，ILs)，也称室温离子液体(Room Temperature Ionic Liquid，RTILs)，是一种绿色有机溶剂。它是由一种有机阳离子和一种无机或有机的阴离子组成的盐，在室温时为液体。与传统溶剂相比，离子液体表现出其独特的物理化学性质：可忽略的蒸汽压、不挥发、较大的稳定温度范围、较好的化学稳定性以及较宽的电化学窗口，并且能够溶解有机物、无机物和聚合物等物质，是很多化学反应的优良溶剂。
发明内容
本发明的目的在于克服传统湿法冶金技术存在的不足，提供一种用新型绿色溶剂作为浸出剂，从废弃印刷线路板中高效浸出金属铜的方法。
本发明是通过以下步骤实现的：
一种用离子液体从废弃印刷线路板中浸出金属铜的方法，将废弃印刷线路板切成小块，用万能粉碎机进行粉碎，筛分，选用粒径在0.25-0.5mm的样品，烘干；称取样品于锥形瓶中，加入30％的双氧水，再加入浓度为10-80％的离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液，使固液比为1g∶7-55mL，其中双氧水和离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液体积比为1∶1.5-6，加盖于20-80℃的恒温水浴震荡箱中浸出1-24h，振荡频率为50-250转/分钟；将所得浸出液抽滤、洗涤、定容，测铜含量。
本发明用离子液体——1-丁基-3-甲基咪唑硫酸氢盐作为浸出剂，浸出废弃印刷线路板中的铜，铜含量达到90-95％。
具体实施方式
以下结合具体实施例，对本发明进行详细说明。
实施例一：首先用高速切割机将废弃印刷线路板切成小于50mm×50mm的小块，然后用万能粉碎机进行粉碎，最后用国家标准筛筛分，选用粒径在0.25-0.5mm的样品，烘干；称取1g样品于锥形瓶中，加入5mL30％的双氧水，再加入15mL浓度为60％的离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液，固液比为1g∶20mL，加盖于20℃的恒温水浴震荡箱中浸出2h，振荡频率为50转/分钟；将所得浸出液抽滤、洗涤、定容，测得铜含量为92.3％。
实施例二：首先用高速切割机将废弃印刷线路板切成小于50mm×50mm的小块，然后用万能粉碎机进行粉碎，最后用国家标准筛筛分，选用粒径在0.25-0.5mm的样品，烘干；称取1g样品于锥形瓶中，加入10mL30％的双氧水，再加入15mL浓度为10％的离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液，固液比为1g∶25mL，加盖于50℃的恒温水浴震荡箱中浸出2h，振荡频率为150转/分钟；将所得浸出液抽滤、洗涤、定容，测得铜含量为94.6％。
实施例三：首先用高速切割机将废弃印刷线路板切成小于50mm×50mm的小块，然后用万能粉碎机进行粉碎，最后用国家标准筛筛分，选用粒径在0.25-0.5mm的样品，烘干；称取1g样品于锥形瓶中，加入5mL30％的双氧水，再加入15mL浓度为20％的离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液，固液比为1g∶20mL，加盖于60℃的恒温水浴震荡箱中浸出2h，振荡频率为250转/分钟；将所得浸出液抽滤、洗涤、定容，测得铜含量为94.0％。
实施例四：首先用高速切割机将废弃印刷线路板切成小于50mm×50mm的小块，然后用万能粉碎机进行粉碎，最后用国家标准筛筛分，选用粒径在0.25-0.5mm的样品，烘干；称取1g样品于锥形瓶中，加入5mL30％的双氧水，再加入30mL浓度为10％的离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液，固液比为1g∶35mL，加盖于80℃的恒温水浴震荡箱中浸出2h，振荡频率为250转/分钟；将所得浸出液抽滤、洗涤、定容，测得铜含量为95.2％。
实施例五：首先用高速切割机将废弃印刷线路板切成小于50mm×50mm的小块，然后用万能粉碎机进行粉碎，最后用国家标准筛筛分，选用粒径在0.25-0.5mm的样品，烘干；称取1g样品于锥形瓶中，加入5mL30％的双氧水，再加入15mL浓度为10％的离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液，固液比为1g∶20mL，加盖于50℃的恒温水浴震荡箱中浸出12h，振荡频率为250转/分钟；将所得浸出液抽滤、洗涤、定容，测得铜含量为90.0％。
应当理解的是，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，而所有这些改进和变换都应属于本发明所附权利要求的保护范围。

Claims (1)

1.一种用离子液体从废弃印刷线路板中浸出金属铜的方法，其特征在于，将废弃印刷线路板切成小块，用万能粉碎机进行粉碎，筛分，选用粒径在0.25-0.5mm的样品，烘干；称取样品于锥形瓶中，加入浓度为30％的双氧水，再加入浓度为10-80％的离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液，使固液比为1g∶7-55mL，其中双氧水和离子液体1-丁基-3-甲基咪唑硫酸氢盐水溶液体积比为1∶1.5-6，加盖于20-80℃的恒温水浴震荡箱中浸出1-24h，震荡频率为50-250转/分钟；将所得浸出液抽滤、洗涤、定容，测铜含量。
CN2012101074446A 2012-04-13 2012-04-13 一种用离子液体从废弃印刷线路板中浸出金属铜的方法 Expired - Fee Related CN102643988B (zh)