CN102643051A - 一种耐腐蚀的化工建筑胶 - Google Patents

一种耐腐蚀的化工建筑胶 Download PDF

Info

Publication number
CN102643051A
CN102643051A CN2012100412712A CN201210041271A CN102643051A CN 102643051 A CN102643051 A CN 102643051A CN 2012100412712 A CN2012100412712 A CN 2012100412712A CN 201210041271 A CN201210041271 A CN 201210041271A CN 102643051 A CN102643051 A CN 102643051A
Authority
CN
China
Prior art keywords
parts
corrosion
building glue
chemical building
resistant chemical
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100412712A
Other languages
English (en)
Inventor
黄波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Nashuo Technology Co Ltd
Original Assignee
Chengdu Nashuo Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Nashuo Technology Co Ltd filed Critical Chengdu Nashuo Technology Co Ltd
Priority to CN2012100412712A priority Critical patent/CN102643051A/zh
Publication of CN102643051A publication Critical patent/CN102643051A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐腐蚀的化工建筑胶，属于化工产品领域，解决现有的建筑胶不同程度的存在粘接强度不够、耐酸耐碱性不够容易老化的问题。其重量配比为：环氧树脂100～150份，糠醛树脂40～60份，丙酮2～20份，乙二胺10～15份，氧化铝5～10份，石英粉150～200份。适用于化工建筑防腐,耐酸、耐碱池,瓷板、瓷砖的粘接及填缝。

Description

一种耐腐蚀的化工建筑胶
技术领域
本发明属于化工产品领域，具体涉及一种耐腐蚀的化工建筑胶。 
背景技术
建筑胶应用于建筑行业的每一个工序，乃至每一种材料。它可概分为以下几个方面：(1)应用于各种建筑施工；(2)室内外装饰、装修中的应用；(3)各种建筑的密封用 包括门窗、大板墙、伸缩缝、接缝、特种建筑等；(4)建筑物维修、改造、加固与补强中应用；(5)各类交通设施与水利工程的加固和维修；(6)广泛应用于复合建材的生产质轻、强度高、功能多是复合建材发展的方向；(7)与水泥混合制成各种高性能混凝土,这类应用可提供高性能的建筑用基本材料，解决传统材料达不到高强、快干等特种要求的许多难题；(8)建筑胶还可用于道路标志、水坝防漏、军事工程应急维修，以及堵漏等诸多方面。 
化工建筑上用的建筑胶由于其使用环境的特殊，对建筑胶的要求更高，但市售的建筑胶不同程度的存在粘接强度不够、耐酸耐碱性不够容易老化的问题。 
发明内容
本发明要解决的技术问题是现有的建筑胶不同程度的存在粘接强度不够、耐酸耐碱性不够容易老化的问题。 
本发明的技术方案为：一种耐腐蚀的化工建筑胶，其重量配比为： 
环氧树脂100～150份
糠醛树脂40～60份
丙酮2～20份
乙二胺10～15份
氧化铝 5～10份
石英粉150～200份。
优选地，所述重量配比为： 
环氧树脂120份
糠醛树脂50份
丙酮15份
乙二胺12份
氧化铝 8份
石英粉180份。
本发明的耐腐蚀的化工建筑胶的制备方法为： 
a、按照配比将环氧树脂与糠醛树脂混合均匀,加热至41℃；
b、按照配比加入丙酮、乙二胺,搅拌均匀；
c、按照配比加入氧化镁和石英粉即得成品。
本发明与现有技术相比具有如下优点： 
1、本发明的化工建筑胶粘接强度高, 胶合压缩强度达到150.2MPa，拉伸强度达到l4.1MPa。
2、本发明的化工建筑胶专为化工建筑配制，耐腐蚀性能好，适用于化工建筑防腐，耐酸、耐碱池，瓷板、瓷砖的粘接及填缝。 
具体实施方式
提供以下的描述以助于全面理解由权利要求及其等同物限定的本发明的示例性实施例。以下描述包括各种特定细节以助于理解，但这些仅被认为是示例性的。因此，本领域的普通技术人员将认识到，在不脱离本发明的范围和精神的情况下可对在此描述的实施例做出各种改变和修改。另外，为了清楚和简洁，省略了已知功能和结构的描述。  
实施例1 
取100kg环氧树脂和40kg糠醛树脂混合均匀,加热至41℃；然后加入2kg丙酮和10kg乙二胺搅拌均匀；最后加入5kg氧化铝粉末和150kg石英粉即得成品。
强度检测：胶合压缩强度达到138.3MPa，拉伸强度达到13.8MPa。 
实施例2 
取150kg环氧树脂和60kg糠醛树脂混合均匀,加热至41℃；然后加入20kg丙酮和15kg乙二胺搅拌均匀；最后加入10kg氧化铝粉末和200kg石英粉即得成品。
强度检测：胶合压缩强度达到143.6MPa，拉伸强度达到l3.4MPa。 
实施例3 
取120kg环氧树脂和50kg糠醛树脂混合均匀,加热至41℃；然后加入15kg丙酮和12kg乙二胺搅拌均匀；最后加入8kg氧化铝粉末和180kg石英粉即得成品。
强度检测：胶合压缩强度达到150.2MPa，拉伸强度达到l4.1MPa。 

Claims (2)

1.一种耐腐蚀的化工建筑胶，其特征在于，其重量配比为：
环氧树脂100～150份
糠醛树脂40～60份
丙酮2～20份
乙二胺10～15份
氧化铝 5～10份
石英粉150～200份。
2.根据权利要求1所述的一种耐腐蚀的化工建筑胶，其特征在于：所述重量配比为：
环氧树脂120份
糠醛树脂50份
丙酮15份    
乙二胺12份
氧化铝 8份
石英粉180份。
CN2012100412712A 2012-02-23 2012-02-23 一种耐腐蚀的化工建筑胶 Pending CN102643051A (zh)