CN102642421A - Preparation method and transfer printing method of film capable of being printed in transfer mode - Google Patents
Preparation method and transfer printing method of film capable of being printed in transfer mode Download PDFInfo
- Publication number
- CN102642421A CN102642421A CN2012101278585A CN201210127858A CN102642421A CN 102642421 A CN102642421 A CN 102642421A CN 2012101278585 A CN2012101278585 A CN 2012101278585A CN 201210127858 A CN201210127858 A CN 201210127858A CN 102642421 A CN102642421 A CN 102642421A
- Authority
- CN
- China
- Prior art keywords
- printing
- transfer
- film
- ink
- stock
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a film capable of being printed in transfer mode, which includes the following steps: printing transparent ink and color ink on a carrier film and preparing the film capable of being printed in transfer mode comprising a double layer structure of a carrier film base material layer and a printing layer. The ink comprises solvent base cellulose acetate butyrate transparent ink and/or solvent base chlorinated polypropylene transparent ink, and the color ink is solvent base polyurethane color ink. A transfer printing method of the film capable of being printed in transfer mode through the preparation method is further disclosed. The preparation method and the transfer printing method of the film capable of being printed in transfer mode can be used for preparing the film capable of being printed in transfer mode comprising the double layer structure of the carrier film base material layer and the printing layer and are simple in preparation process, few in work procedure, high in efficiency and low in cost. The preparation work procedures can meet the requirements for energy saving and emission reduction. Simultaneously, the film capable of being printed in transfer mode can utilize various printing materials in application, is simple in transfer printing work procedures, resolves the problem that the surface of irregular work pieces cannot be printed in transfer mode, and is wide in application.
Description
Technical field
But the present invention relates to the transfer film field, but relate in particular to a kind of preparation method and printing transferring method that comprises carrier film substrate layer and the double-deck transfer film of printing ink layer.
Background technology
To be called transfer printing to the printing process on the stock as conditional jumps such as the corresponding temperature of picture and text utilization on the film of intermediate carrier, pressure.According to the difference of employing method, transfer printing can be divided into hot transfer printing, water transfer printing, sublimation transfer, in-mold transfer printing, bat printing and cold wave transfer printing etc.
Transfer film of the prior art, the three-decker of generally being formed by transparent (or opaque) basalis, release layer and Hot melt glue film or induction glued membrane and one deck image layers.For example, the transfer film structure in Chinese patent ZL200510027809.4 is just by substrate layer, and strippable coating and printed layers are formed, because its strippable coating is the releasing agent or the nonabsorbable film of organosilicon series, the purposes limitation is bigger.
At present, transfer film both domestic and external has adopted strippable coating technology mostly, has also used materials such as releasing agent, wax.But no matter which kind of material strippable coating adopts, and the existence of strippable coating all can bring pollution and cause waste to environment.
Summary of the invention
Technical problem to be solved by this invention is, but a kind of preparation method of transfer film is provided, and the preparation process is simple, and operation is few, and efficient is high, and cost is low; This preparation section can reach the requirement of energy-saving and emission-reduction.
Another technical problem to be solved by this invention is, but a kind of printing transferring method of transfer film is provided, and in transfer printing is used, can use multiple printable fabric, transfer printing process is simple, solved the problem that the special-shaped workpiece surface can't transfer printing.
In order to solve the problems of the technologies described above, but embodiments of the invention provide a kind of preparation method of transfer film, may further comprise the steps:
The carrier film base material is placed on the continuous printing; Ink printing is constituted printed layers on carrier film; Comprise carrier film substrate layer and the double-deck transfer film of printed layers but process; Said printing ink comprises transparent ink and/or look China ink, and described transparent ink comprises solvent-borne type acetylbutyrylcellulose transparent ink and/or solvent-borne type chlorinated polypropylene transparent ink, and said look China ink is a solvent borne polyurethane look China ink;
Said transparent ink and look ink print in the step on the carrier film base material are: multilayer printing ink is printed in stack continuously on said carrier film base material; Wherein: ground floor printing ink is superimposed upon on the said carrier film base material; Second layer printing ink all or the part is superimposed upon on the said ground floor printing ink and stack one deck printing ink is until the required number of plies down, it is related that the maximum forme roller number of the number of plies of said stack printing ink and multicolour press is provided with;
The component percentage of said solvent-borne type acetylbutyrylcellulose transparent ink is: acetylbutyrylcellulose resin 5%-15%, levelling agent 0.1%-0.8%, butanone 65%-75%, xylenes 10%-30%.
Preferably, the component and the percentage of said solvent-borne type chlorinated polypropylene transparent ink are: chlorinated polypropylene polymer 10%-20%, adhesion promoter 5%-10%, delustering agent 1%-5%, toluene 50%-60%, butanone 15%-20%, silane coupler 1%-5%.
Preferably, said carrier film substrate layer comprises PET film base material layer or CPP film base material layer;
The thickness of said PET film base material layer is 12 microns ~ 30 microns, and the thickness of said CPP film base material layer is 30 microns ~ 50 microns.
But the invention also discloses a kind of printing transferring method of transfer film, may further comprise the steps:
Hot transfer printing is carried out on surface at stock, and said stock is processed by the arbitrary material in metal, melamine, nylon, pottery, glass, PP, PET, PS, PC, PVC, EVA and the ABS material;
But throw off the PET film base material layer or the CPP film base material layer on said transfer film surface.
Preferably, carry out in the hot transfer printing step on said surface at stock, and the temperature of heat transfer machine silica gel roller is 180 ℃ ~ 220 ℃, and the external air pressure of the cylinder of exerting pressure is 6 ~ 8kg/cm.
Preferably, described surface at stock is further comprising the steps of after carrying out in the hot transfer printing step:
The stock of accomplishing the transfer printing operation is toasted, and the baking temperature of described stock is 80 ~ 130 ℃, and stoving time is 15 ~ 30 minutes.
But the printing transferring method of another kind transfer film disclosed by the invention may further comprise the steps: glue or gluing are sprayed in the stock surface;
In the operating room of vacuum transfer interpreter and Packing Machine, but transfer film and stock are fitted through vacuumizing with pressing mode;
But throw off the substrate layer of the transfer film on stock surface.
Preferably, said in the step that the operating room of said vacuum transfer interpreter or Packing Machine vacuumizes, the negative pressure pressure of said operating room is-0.06 ~-0.1Mpa; In the step of pressurizeing, the positive pressure pressure of said operating room is 0.6Mpa ~ 1.0Mpa.
But the printing transferring method of the third transfer film disclosed by the invention may further comprise the steps:
But said transfer film printed layers placed up carries out plastics sucking moulding on the Packing Machine, obtain one group with the same or analogous plastic uptake film of product-forming, to cut said plastic uptake film be monomer and be placed in the said foaming mould; In said foaming mould, inject printable fabric, said printable fabric is through foaming and be fixed to stock, but said transfer film is fixed on the said stock; But throw off the substrate layer on said transfer film surface.
Preferably, the foaming of said printable fabric and time of being fixed to stock are 5 ~ 12 minutes.
But the preparation method of a kind of transfer film provided by the present invention and printing transferring method comprise carrier film substrate layer and the double-deck transfer film of printing ink layer but can process, and the preparation process is simple, and operation is few, and efficient is high, and cost is low; This preparation section can reach the requirement of energy-saving and emission-reduction.Simultaneously, but should transfer film in transfer printing is used, can use multiple printable fabric, transfer printing process is simple, has solved the problem that the special-shaped workpiece surface can't transfer printing, is widely used.
Description of drawings
In order to be illustrated more clearly in the embodiment of the invention or technical scheme of the prior art; To do to introduce simply to the accompanying drawing of required use in embodiment or the description of the Prior Art below; Obviously, the accompanying drawing in describing below only is some embodiments of the present invention, for those of ordinary skills; Under the prerequisite of not paying creative work, can also obtain other accompanying drawing according to these accompanying drawings.
But but Fig. 1 is the structural representation of the embodiment of the invention by the transfer film of preparation method embodiment one preparation of transfer film;
But but Fig. 2 is the structural representation of the embodiment of the invention by the printing ink layer of the transfer film of preparation method embodiment one preparation of transfer film;
But Fig. 3 is the side-looking structural representation that adopts India side formula in the intaglio plate among the preparation method of embodiment of the invention transfer film;
But but Fig. 4 is the structural representation of the embodiment of the invention by the transfer film of preparation method embodiment two preparations of transfer film;
But but Fig. 5 is the structural representation of the embodiment of the invention by the printing ink layer of the transfer film of preparation method embodiment two preparations of transfer film;
But Fig. 6 is the embodiment of the invention uses the structural representation that the transfer film printing transferring method carries out transfer printing embodiment three;
But being the embodiment of the invention, Fig. 7 uses the structural representation that on stock, sprays primer that the transfer film printing transferring method carries out transfer printing embodiment four;
But Fig. 8 is the embodiment of the invention uses the structural representation that the transfer film printing transferring method carries out the vacuum transfer interpreter transfer printing state one of transfer printing embodiment four;
But Fig. 9 is the embodiment of the invention uses the structural representation that the transfer film printing transferring method carries out the vacuum transfer interpreter transfer printing state two of transfer printing embodiment four;
But Figure 10 is the embodiment of the invention uses the structural representation that the transfer film printing transferring method carries out the vacuum transfer interpreter transfer printing state three of transfer printing embodiment four;
But Figure 11 is the embodiment of the invention uses the structural representation that the transfer film printing transferring method carries out the vacuum transfer interpreter transfer printing state four of transfer printing embodiment four;
But, Figure 12 uses the structural representation of transfer film transfer printing on stock that the transfer film printing transferring method carries out transfer printing embodiment four but being the embodiment of the invention;
But, Figure 13 uses the transfer film plastic uptake structural representation that the transfer film printing transferring method carries out transfer printing embodiment five but being the embodiment of the invention;
But, Figure 14 uses the transfer film behind the plastics sucking moulding that the transfer film printing transferring method carries out transfer printing embodiment five but being the embodiment of the invention;
But Figure 15 is the embodiment of the invention uses the foaming transfer printing structural representation that the transfer film printing transferring method carries out transfer printing embodiment five.
The specific embodiment
With reference to accompanying drawing the preferred embodiments of the present invention are described below.
Embodiment one: combine referring to Fig. 1-shown in Figure 5; But the preparation method of a kind of transfer film that the embodiment of the invention provides; But be used for preparation and comprise carrier film substrate layer and the double-deck transfer film of printing ink layer, may further comprise the steps: the carrier film base material is placed on the continuous printing, ink printing is constituted printed layers on carrier film; Comprise carrier film substrate layer and the double-deck transfer film of printed layers but process; Said printing ink comprises transparent ink and/or look China ink, and described transparent ink comprises solvent-borne type acetylbutyrylcellulose transparent ink and/or solvent-borne type chlorinated polypropylene transparent ink, and said look China ink is a solvent borne polyurethane look China ink;
During enforcement, carrier film can be used the polarity film, also can use nonpolar film, to preparation process did not influence.Wherein, Carrier film can be used PET (Polythylene terephthalate; Resin) film or CPP (polypropylene) film adopts above-mentioned two kinds of carrier film all can use solvent-borne type acetylbutyrylcellulose transparent ink and/or solvent-borne type chlorinated polypropylene transparent ink and solvent borne polyurethane look China ink to print respectively, and the equipment of printing can use the set type continuous printing; The mode of printing is to print in the intaglio plate, and finally forms printing ink layer.
Below form as carrier film with the PET film and to comprise that but carrier film substrate layer and the double-deck transfer film of printing ink layer are example, but the preparation method of transfer film of the present invention is described.In conjunction with referring to Fig. 1-shown in Figure 3.
Concrete; Use the mode printing transparent printing ink and the Se Mo on pet vector film 1 that print in the set type continuous printing intaglio plate; The thickness of employed pet vector film 1 is between 12 microns ~ 30 microns; Tack when this thickness can guarantee to print between multilayer ink lay and carrier film also is easier to the transfer printing of finished product transfer film.Printing many (N) layer printing ink can superpose during printing continuously on pet vector film 1; This process is: ground floor printing ink is superimposed upon on the said carrier film base material; Second layer printing ink all or the part be superimposed upon on the said ground floor printing ink, the rest may be inferred and stack down one deck printing ink until N layer printing ink, wherein; N is a natural number, between 1 and the maximum forme roller number of multicolour press between.As shown in Figure 3, but but by the structural representation of the printing ink layer of the transfer film of the preparation method embodiment of transfer film one preparation, the incidence relation in the number of plies that this figure can react stack printing ink and the diagram between the maximum forme roller number setting of multicolour press.
In the above-mentioned embodiment, ground floor printing ink adopts solvent-borne type acetylbutyrylcellulose transparent ink, and its component and percentage are: acetylbutyrylcellulose resin 5%-15%, levelling agent 0.1%-0.8%, butanone 65%-75%, xylenes 10%-30%.N layer printing ink adopts solvent-borne type chlorinated polypropylene transparent ink, and its component and percentage are: chlorinated polypropylene polymer 10%-20%, adhesion promoter 5%-10%, delustering agent 1%-5%, toluene 50%-60%, butanone 15%-20%, silane coupler 1%-5%; What the look China ink adopted is solvent borne polyurethane look China ink.
But the printed layers of the transfer film that makes according to above-mentioned preparation method has comprised the polychrome printing layer, but the decomposition texture sketch map of transfer film as shown in Figure 2 wherein, is printed polychrome printing layer 2.1-2.N on the pet vector film 1.But the transfer film through said method makes can carry out transfer printing through ordinary hot transfer interpreter or gilding press on stock, obtain corresponding pattern, the concrete follow-up explanation of transfer printing implementation process.
Embodiment two: in the another kind of embodiment, comprise carrier film substrate layer and the double-deck transfer film of printing ink layer but use the CPP film also to can be used as carrier film formation, but the transfer film structure of processing is referring to Fig. 4.The ground floor printing ink, the look China ink composition that adopt in the mode of printing that prints in the intaglio plate that is adopted among this embodiment, multilayer stack printing process and the printing are identical with above-mentioned embodiment with composition; Difference is; N layer printing ink also is the look China ink; And the thickness of CPP film base material layer is between 30 microns ~ 50 microns, and the tack when this thickness can guarantee to print between multilayer ink lay and carrier film also is easier to the transfer printing of finished product transfer film.But the printing ink layer of the transfer film that makes according to this kind preparation method has comprised the polychrome printing layer, but the decomposition texture sketch map of transfer film as shown in Figure 5 wherein, is printed polychrome printing layer 2.1-2.N on the CPP carrier film 3.But the transfer film through this kind embodiment makes can carry out transfer printing through vacuum transfer interpreter or Packing Machine on stock, and obtains corresponding pattern, the concrete follow-up explanation of transfer printing implementation process.
Implement the foregoing description one or two, comprise carrier film substrate layer and the double-deck transfer film of printing ink layer but can process, the preparation process is simple, and operation is few, and efficient is high, and cost is low.This preparation section meets the requirement of energy-saving and emission-reduction, and can on incrustation, use widely.
Embodiment three: but the invention discloses a kind of printing transferring method of the transfer film by above-mentioned preparation method preparation; May further comprise the steps: hot transfer printing is carried out on the surface at stock, and said stock is processed by the arbitrary material in metal, melamine, nylon, pottery, glass, PP, PET, PS, PC, PVC, EVA and the ABS material;
But throw off the PET film base material layer or the CPP film base material layer on said transfer film surface.
As shown in Figure 6, but carry out the structural representation of transfer printing embodiment three for the application transfer film printing transferring method of the embodiment of the invention.During practical implementation, but the transfer film of embodiment one preparation is placed on the stock 4, this stock has smooth excessiveness and carries cambered surface, moulds the fat material by melamine and processes.But a side of the printing ink layer 2 of attention transfer film is towards this cambered surface of undertaking the printing of in the enforcement; Use heat transfer machine or gilding press and cooperate corresponding stock anchor clamps, 180 ℃ ~ 220 ℃ of heat transfer machine silica gel roller temperature, under the condition of the external air pressure 6 ~ 8kg/cm of the cylinder of exerting pressure; Carry out hot transfer printing on stock 4 surfaces; And then, but throw off the PET film base material layer on transfer film surface, just can obtain exquisite printed patterns on stock 4 surfaces.
Preferred embodiment, after stock 4 is carried out hot transfer printing, also can toast stock 4, its effect is the adhesive force that strengthens carrier.The baking temperature of baking stock remains on 80 ~ 130 ℃, and the time of baking remained on 15 ~ 30 minutes.
, be suitable in by materials such as metal, melamine, nylon, pottery, glass, PP, PET, PS, PC, PVC, EVA and ABS, carrying out transfer printing because but carrier film substrate layer and the double-deck transfer film of printing ink layer of comprising of the present invention do not comprise peel ply.
Embodiment four: referring to Fig. 7-Figure 12, but the embodiment of the invention provides second kind of printing transferring method by the transfer film of above-mentioned preparation method's preparation, may further comprise the steps:
Glue or gluing are sprayed in the stock surface;
But the transfer film with embodiment 2 preparations in the operating room of vacuum transfer interpreter and Packing Machine places on the stock 5, but transfer film and stock are fitted through vacuumizing with pressing mode;
But throw off the CPP film base material layer of the transfer film on stock surface.Wherein, stock comprises the shaped face shape.
Preferably, said in the step that the operating room of said vacuum transfer interpreter or Packing Machine vacuumizes, the negative pressure pressure of said operating room is-0.06 ~-0.1Mpa; In the step of pressurizeing, the positive pressure pressure of said operating room is 0.6Mpa ~ 1.0Mpa.
In embodiment four, stock 5 is the pillow structures for abnormal shape, moulds the fat material by ABS and processes.As shown in Figure 7.In the enforcement, to stock 5 spraying adhesion glue, treat the glue dry tack free after, send into vacuum transfer interpreter operating room, but note keeping the printing-ink of transfer film to face down, and fixing in the mould operating room of vacuum transfer interpreter.As shown in Figure 8, each structure of vacuum transfer interpreter comprises transfer interpreter operating room epicoele 7, transfer interpreter operating room cavity of resorption 8, transfer printing electro-heat equipment 9, vacuum tank 10, compressed air reservoir 11, switching valve 12.But transfer film in transfer interpreter cavity of resorption 8 fixing after, the operating room that closes as shown in Figure 9, transfer interpreter operating room epicoele 7 vacuumizes with transfer interpreter operating room cavity of resorption 8 closed spaces simultaneously in the operating room, make reach negative pressure-0.06 ~-0.1Mpa/cm between.Meanwhile, the transfer printing electro-heat equipment 9 of vacuum transfer interpreter starts heating, and the preferred time of heating, heating and temperature control was at 140 ℃ ~ 200 ℃, like Figure 10 and shown in Figure 11 at 5 ~ 15 seconds.
The mould jack-up stock of vacuum transfer interpreter, switching pressurized air gets into operating room's epicoele, and air pressure remains on 0.6 ~ 0.8Mpa/cm, but transfer film is adjacent to stock 5 immediately, and printed layers 3 can be bonding with the stock glue layer, referring to Figure 12.But throw off the CPP film base material layer on transfer film surface, just can obtain corresponding printed patterns on the surface of stock.
But using the transfer apparatus that the transfer film printing transferring method carries out transfer printing among this embodiment is other equipment that can remove the vacuum transfer interpreter, like Packing Machine.Using Packing Machine, to carry out the process and the above-mentioned implementation process of transfer printing roughly the same, repeats no more.Transfer printing is carried out, the transfer printing effect stability in the surface of multiple shaped objects such as this kind transfer printing mode can be on the plane, curved surface, shaped face.
Embodiment five: but the present invention implement five a kind of transfer film by above-mentioned preparation method preparation also is provided printing transferring method; May further comprise the steps: carry out plastics sucking moulding on the Packing Machine up but the transfer film printed layers of embodiment two preparation placed; Obtain one group and the same or analogous plastic uptake film of product-forming, the shape of said plastic uptake film and the shape of foaming mould are suitable;
To cut said plastic uptake film be monomer and be placed in the said foaming mould;
In said foaming mould, inject printable fabric, said printable fabric is through foaming and be fixed to stock, but said transfer film is fixed on the said stock;
But throw off the CPP film base material layer on said transfer film surface.
Preferably, but the plastics sucking moulding transfer film form in the step of a plurality of plastic uptake films, the plastic uptake temperature is 160 ℃ ~ 200 ℃, be 5 ~ 8 seconds heat time heating time, vacuum time is 2 ~ 5 seconds;
In foaming mould in the step of injection printable fabric, printable fabric foaming and the time that is fixed to stock are 5 ~ 12 minutes.
During practical implementation, referring to Figure 13-Figure 15.But the transfer film that embodiment two is prepared; The mode that makes progress with printing-ink face 3 places Packing Machine 12 to carry out plastics sucking moulding; Adsorption mould is used die, and the temperature of plastic uptake remains on 160 ℃ ~ 200 ℃, and the time of heating was controlled at 5 ~ 8 seconds; Vacuum time is 2 ~ 5 seconds, can obtain one group of a plurality of and same or analogous plastic uptake film of product-forming.Use suitable blanking knife model, one group of a plurality of plastic uptake film stamping-out is become the plastic uptake film of a plurality of monomer plastic uptake films or a plurality of little combinations.Subsequently, stamping-out is good plastic uptake Membrane cover is in PU foaming mould 6,14; Add foaming component materials 15; Through foaming in 5 ~ 12 minutes and shaping time, take out foaming product, but transfer film is adjacent on the foaming object; But throw off the CPP film base material layer on transfer film surface, just can obtain corresponding printed patterns on the surface of stock.
But the preparation method of the transfer film of embodiment of the present invention embodiment and printing transferring method comprise carrier film substrate layer and the double-deck transfer film of printing ink layer but can process, and the preparation process is simple, and operation is few, and efficient is high, and cost is low.This preparation section can reach the requirement of energy-saving and emission-reduction; Simultaneously, but should transfer film in transfer printing is used, can use multiple printable fabric, transfer printing process is simple, has solved the problem that the special-shaped workpiece surface can't transfer printing, is widely used.
Above disclosedly be merely preferred embodiment of the present invention, can not limit the present invention's interest field certainly with this, the equivalent variations of therefore doing according to claim of the present invention still belongs to the scope that the present invention is contained.
Claims (10)
1. but the preparation method of a transfer film is characterized in that, may further comprise the steps:
The carrier film base material is placed on the continuous printing; Ink printing is constituted printed layers on carrier film; Comprise carrier film substrate layer and the double-deck transfer film of printed layers but process; Said printing ink comprises transparent ink and/or look China ink, and described transparent ink comprises solvent-borne type acetylbutyrylcellulose transparent ink and/or solvent-borne type chlorinated polypropylene transparent ink, and said look China ink is a solvent borne polyurethane look China ink;
Said transparent ink and look ink print in the step on the carrier film base material are: multilayer printing ink is printed in stack continuously on said carrier film base material; Wherein: ground floor printing ink is superimposed upon on the said carrier film base material; Second layer printing ink all or the part is superimposed upon on the said ground floor printing ink and stack one deck printing ink is until the required number of plies down, it is related that the maximum forme roller number of the number of plies of said stack printing ink and multicolour press is provided with;
The component percentage of said solvent-borne type acetylbutyrylcellulose transparent ink is: acetylbutyrylcellulose resin 5%-15%, levelling agent 0.1%-0.8%, butanone 65%-75%, xylenes 10%-30%.
2. but the preparation method of transfer film as claimed in claim 1; It is characterized in that the component percentage of said solvent-borne type chlorinated polypropylene transparent ink is: chlorinated polypropylene polymer 10%-20%, adhesion promoter 5%-10%; Delustering agent 1%-5%; Toluene 50%-60%, butanone 15%-20%, silane coupler 1%-5%.
3. but according to claim 1 or claim 2 the preparation method of transfer film is characterized in that said carrier film substrate layer comprises PET film base material layer or CPP film base material layer;
The thickness of said PET film base material layer is 12 microns ~ 30 microns, and the thickness of said CPP film base material layer is 30 microns ~ 50 microns.
4. but the printing transferring method by the transfer film of each preparation of claim 1-3 is characterized in that, may further comprise the steps:
Hot transfer printing is carried out on surface at stock, and said stock is processed by the arbitrary material in metal, melamine, nylon, pottery, glass, PP, PET, PS, PC, PVC, EVA and the ABS material;
But throw off the PET film base material layer or the CPP film base material layer on said transfer film surface.
5. but the printing transferring method of transfer film as claimed in claim 4 is characterized in that, carry out in the hot transfer printing step on said surface at stock, and the temperature of heat transfer machine silica gel roller is 180 ℃ ~ 220 ℃, and the external air pressure of the cylinder of exerting pressure is 6 ~ 8kg/cm.
6. but the printing transferring method of transfer film as claimed in claim 5 is characterized in that, described surface at stock is further comprising the steps of after carrying out in the hot transfer printing step:
The stock of accomplishing the transfer printing operation is toasted, and the baking temperature of described stock is 80 ~ 130 ℃, and stoving time is 15 ~ 30 minutes.
7. but the printing transferring method by the transfer film of each preparation of claim 1-3 is characterized in that, may further comprise the steps:
Glue or gluing are sprayed in the stock surface;
In the operating room of vacuum transfer interpreter and Packing Machine, but transfer film and stock are fitted through vacuumizing with pressing mode;
But throw off the substrate layer of the transfer film on stock surface.
8. but the printing transferring method of transfer film as claimed in claim 7 is characterized in that, in the step that the operating room of said vacuum transfer interpreter or Packing Machine vacuumizes, the negative pressure pressure of said operating room is-0.06 ~-0.1Mpa;
In the said step of pressurizeing, the positive pressure pressure of said operating room is 0.6Mpa ~ 1.0Mpa.
9. but the printing transferring method by the transfer film of each preparation of claim 1-3 is characterized in that, may further comprise the steps:
But said transfer film printed layers placed up carries out plastics sucking moulding on the Packing Machine, obtain one group with the same or analogous plastic uptake film of product-forming, to cut said plastic uptake film be monomer and be placed in the said foaming mould;
In said foaming mould, inject printable fabric, said printable fabric is through foaming and be fixed to stock, but said transfer film is fixed on the said stock;
But throw off the substrate layer on said transfer film surface.
10. but the printing transferring method of transfer film as claimed in claim 9 is characterized in that,
In said foaming mould in the step of injection printable fabric, foaming of said printable fabric and the time that is fixed to stock are 5 ~ 12 minutes.