CN102631117A - 抑菌紫砂壶及其制造方法 - Google Patents
抑菌紫砂壶及其制造方法 Download PDFInfo
- Publication number
- CN102631117A CN102631117A CN201210121409XA CN201210121409A CN102631117A CN 102631117 A CN102631117 A CN 102631117A CN 201210121409X A CN201210121409X A CN 201210121409XA CN 201210121409 A CN201210121409 A CN 201210121409A CN 102631117 A CN102631117 A CN 102631117A
- Authority
- CN
- China
- Prior art keywords
- dark
- red enameled
- enameled pottery
- micropore
- pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抑菌紫砂壶及其制造方法,所述抑菌紫砂壶的内腔器壁呈微孔状态,且微孔裸露,微孔中有AgO固体颗粒,其制造方法为:先采用浓度为0.15mol/L的硝酸银溶液涂覆在紫砂壶的内表面器壁上,使其渗入微孔中,再将其烘干;然后将浓度为0.6mol/L~5.6mol/L的氢氧化钠溶液或氢氧化钾溶液涂覆在紫砂壶的内表面器壁上,使其渗入微孔中;然后在25℃~55℃温度条件下向紫砂壶内部通入浓度不小于15mg/L的O3气体,通入臭氧气体的时间为1~8h;最后洗净内腔表面再烘干即制成抑菌紫砂壶。本发明抗菌紫砂壶有很好的抗菌性能,用该紫砂壶盛装凉茶能延长保质期。
Description
技术领域
本发明涉及抑菌紫砂壶及其制造方法。
背景技术
紫砂壶或紫砂杯是一种传统的优质泡茶用具,也是一种陶瓷器皿,其器壁上分布着无数的细小微孔,因未上釉,故透气不透水。然而,正是这些细小微孔,很容易藏纳细菌,当用于盛装凉茶时,微孔中的细菌就会进到茶水中,在人们饮用这种凉茶时这些细菌就被直接喝入人体内,对人体健康十分有害。紫砂杯如放置一段时间不用,必须用吹风机吹干,否则就会发现杯内壁发霉。杯内壁之所以会发霉,就是细菌大量繁殖的结果。
所以,如能对紫砂杯的杯体进行改性,使杯体本身对人体无毒无害,也不会产生异味,同时又能够抑制细菌繁殖或杀灭细菌,则将是一个很有意义的技术进步。
发明内容
本发明所要解决的技术问题是提供一种抑菌紫砂壶,该紫砂壶的器壁具有杀菌或抑菌功能,用于盛装诸如饮用水、茶、饮料等食用液体。
为了解决上述技术问题,本发明所提供的技术方案是:一种抑菌紫砂壶,紫砂壶的器壁呈微孔状态,且微孔裸露,即器壁表面没有上釉,微孔中含有AgO固体。
所述紫砂壶的壶体侧部设有水嘴和手把,壶体与水嘴的结合部设有出水小孔,顶部的开口处设有壶盖,壶盖上设有通气孔,所述壶体、水嘴和手把均采用紫砂为主要原料。
本发明还提供在紫砂壶器壁的微孔中生成AgO固体颗粒的方法,其包括:
步骤1.用50℃~100℃的洁净热水洗净紫砂壶的内外表面,再烘干,所述紫砂壶的器壁呈微孔状态,且微孔裸露;
步骤2.配制浓度为0.15mol/L的硝酸银溶液;
步骤3.配置浓度为0.6mol/L~5.6mol/L的氢氧化钠溶液或氢氧化钾溶液;
步骤4.将配置好的硝酸银溶液在搅拌状态下倒入紫砂壶内,静置1~20分钟,使硝酸银溶液从壶体内表面和水嘴内表面向其内部的微孔渗透,然后将硝酸银溶液倒出,再烘干;
步骤5.将配置好的所述氢氧化钠溶液倒入所述紫砂壶内;
步骤6.然后在25℃~55℃温度条件下,向紫砂壶内部通入浓度不小于15mg/L的O3气体,通入臭氧气体的时间为1~8小时;
步骤7.最后用洁净水清洗紫砂壶内表面,然后烘干。
由于所述紫砂壶的器壁呈微孔状态,且微孔裸露,在向紫砂壶内壁涂覆溶液时,能够将微孔内的空气从紫砂壶外壁的微孔中挤出,所以,能够使更多的溶液渗入到紫砂壶器壁的微孔中,从而能够在微孔中生成更多的AgO固体,增强抑菌或杀菌功能。
上述方法能够在紫砂壶器壁的微孔中直接生成Ag4O4固体颗粒,颗粒尺寸为纳米级,Ag4O4可简写为AgO,反应方程式如下:
4AgNO3+4NaOH+2O3→Ag4O4↓+2O2+4NaNO3+2H2O
或者4AgNO3+4KOH+2O3→Ag4O4↓+2O2+4KNO3+2H2O
因上述反应是在紫砂壶器壁的内表面和器壁的微孔中同时进行,所以在紫砂壶器壁的内表面和器壁的微孔中都会有AgO固体产生。在清洗紫砂壶内表面时只能将表面上的AgO清洗掉,而微孔中的AgO固体则不能被清洗掉,必定仍将保持在微孔中;同时NaNO3或者KNO3都能够以离子的形式溶解在水中,所以在清洗紫砂壶内表面时,这些盐类物质都会很容易地被清洗干净,不会对紫砂壶造成污染。
AgO是一种对多种致病细菌和病毒,如粪链球菌、革兰氏阴阳菌、大肠杆菌、金黄色葡萄球菌、艾滋病毒等有很好杀灭效果的固体物质。此外,AgO在100℃以下,化学性质稳定,不易分解,而紫砂壶所盛装的饮用水,通常其最高温度都不会超过95℃,所以完全可以满足使用要求。
本发明具有如下有益效果:
1.本发明抑菌紫砂壶有很好的抗菌性能,用该紫砂壶盛装凉茶能延长保质期。
2.本发明抑菌紫砂壶的制备方法能够将价值较高的硝酸银溶液得到几乎100%地利用,而其它价值较低的药品也能够几乎100%地利用,所以本发明所述的方法成本低,有助于本技术的推广应用。
附图说明
为了使本发明的内容更容易被清楚地理解,下面根据具体实施例并结合附图,对本发明作进一步详细的说明,其中
图1为本发明的实施例1的结构示意图。
附图中的标号为:
AgO固体颗粒1、出水小孔2、壶嘴内表面3、壶体内表面4、水嘴5、壶体外表面6、通气孔7、壶盖8、手把9。
具体实施方式
实施例1
一种抗菌紫砂壶,壶体的侧部设有水嘴5和手把9,壶体与水嘴5的结合部设有出水小孔2,顶部的开口处设有壶盖8,壶盖8上设有通气孔7,壶体、水嘴5和手把9均采用紫砂为主要原料,其成形和烧制后保持微孔裸露状态,即不上釉,然后采用化学方法在微孔中生成AgO固体颗粒1,所述化学方法包括如下步骤:
步骤1.用60℃~80℃的洁净热水洗净壶体内表面4和壶体外表面6,再烘干,所述紫砂壶的器壁呈微孔状态,且微孔裸露;
步骤2.配制浓度为0.15mol/L的硝酸银溶液;
步骤3.配置浓度为3mol/L的氢氧化钠溶液;
步骤4.将配置好的硝酸银溶液在搅拌状态下倒入紫砂壶内,静置1~20分钟,使硝酸银溶液从壶体内表面4和水嘴内表面3向其内部的微孔渗透,然后将硝酸银溶液倒出,再烘干;
步骤5.将配置好的所述氢氧化钠溶液倒入所述紫砂壶内;
步骤6.然后在50℃温度条件下,向紫砂壶内部通入浓度不小于15mg/L的O3气体,通入臭氧气体的时间为1~8小时;
步骤7.用洁净水清洗紫砂壶内表面,然后烘干,即制成抑菌紫砂壶。
上述方法能够在紫砂壶器壁的微孔中直接生成AgO固体颗粒。
分别向按实施例1方法制得的抑菌紫砂壶和普通紫砂壶中加入凉茶,盖上相应的紫砂壶盖,并将两者均放置在恒温箱中,将温度保持在35℃,静置24小时后,再分别检测两种紫砂壶中凉茶的菌落总数,结果如下表:
试验表明,抑菌紫砂壶中凉茶的菌落总数实测值远小于标准规定的限值,这说明本发明方法制备的抑菌紫砂壶的抑菌效果显著。其抑菌机理是:凉茶中如果存在细菌,则由于凉茶是液体,总是存在分子热运动,在分子热运动的作用下会促使细菌迁移到紫砂壶的器壁上,此外,细菌是活的生物体,本身也会迁移到紫砂壶的器壁上,并进入器壁的微孔中,由于器壁的微孔中存在AgO固体颗粒,细菌碰到AgO固体颗粒就会被杀死,所以无法在微孔中生存和繁殖,因而,凉茶中的细菌数量就被有效抑制。
而普通紫砂壶,因没有抑菌功能,空气中的细菌一旦从紫砂壶壶盖的透气孔中或从壶盖和壶体之间的间隙中进入紫砂壶,细菌就进入到壶内的凉茶中,而凉茶中含有可供细菌繁殖所需的大量营养物,所以凉茶中的细菌越来越多是必然的。
所以,用本发明方法制备的紫砂壶,即使用于盛装凉茶,也能保证凉茶较长时间不会变质,从而能够保证紫砂壶用户的饮茶卫生健康。
以上公开的仅为本发明的具体实施例,但是,本发明并非局限于此,任何本领域的技术人员能思之的变化都应涵盖在本发明的权利要求范围中。
Claims (3)
1.抑菌紫砂壶,其特征在于:抑菌紫砂壶的器壁呈微孔状态,且微孔裸露,微孔中含有AgO固体。
2.按照权利要求1所述的抑菌紫砂壶,其特征在于:壶体的侧部设有水嘴和手把,壶体与水嘴的结合部设有出水小孔,顶部的开口处设有壶盖,壶盖上设有通气孔,所述壶体、水嘴和手把均采用紫砂为主要原料。
3.按照权利要求1或2所述的抑菌紫砂壶,其特征在于在紫砂壶器壁的微孔中生成AgO固体颗粒的方法步骤为:
步骤1.用50℃~100℃的洁净热水洗净紫砂壶的内外表面,再烘干,所述紫砂壶的器壁呈微孔状态,且微孔裸露;
步骤2.配制浓度为0.15mol/L的硝酸银溶液;
步骤3.配置浓度为0.6mol/L~5.6mol/L的氢氧化钠溶液或氢氧化钾溶液;
步骤4.将配置好的硝酸银溶液在搅拌状态下倒入紫砂壶内,静置1~20分钟,使硝酸银溶液从壶体内表面和水嘴内表面向其内部的微孔渗透,然后将硝酸银溶液倒出,再烘干;
步骤5.将配置好的所述氢氧化钠溶液倒入所述紫砂壶内;
步骤6.然后在25℃~55℃温度条件下,向紫砂壶内部通入浓度不小于15mg/L的O3气体,通入臭氧气体的时间为1~8小时;
步骤7.最后再用洁净水清洗紫砂壶内表面,然后烘干。