CN102618219A - Nanometer dustproof pretreating agent - Google Patents
Nanometer dustproof pretreating agent Download PDFInfo
- Publication number
- CN102618219A CN102618219A CN2012100573979A CN201210057397A CN102618219A CN 102618219 A CN102618219 A CN 102618219A CN 2012100573979 A CN2012100573979 A CN 2012100573979A CN 201210057397 A CN201210057397 A CN 201210057397A CN 102618219 A CN102618219 A CN 102618219A
- Authority
- CN
- China
- Prior art keywords
- solution
- pretreating agent
- nanometer
- tio
- wetting ability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A nanometer dustproof pretreating agent is prepared by mixing hydrophilic TiO2 solution serving as a base material and a C60 nanometer material serving as an addition agent. Specific ingredients of the hydrophilic TiO2 solution comprise butyl titanate, glacial acetic acid and absolute ethyl alcohol mixed solution, and the volume ratio of the ingredients is 1:1:1. Due to photocatalysis and photoinduction hydrophily of hydrophilic TiO2 and adhesion reducing characteristics of the C60 macromolecule nanometer material, carriers after treated by the pretreating agent are led to greatly reduce dust, particle and the like which can form adhesion effects in physical mode, chemical mode and the like when contacted with the carriers. The dust, the particle and the like are easy to break away from the carriers. The pretreated carriers are irradiated by light containing ultraviolet, and then impurities of steam, water mist and the like are easy to remove.
Description
Technical field
The present invention relates to the pretreating agent technical field, particularly a kind of interpolation C
60The nanometer that high molecule nano material the is prepared from pretreating agent that prevents dust.
Background technology
The a large amount of microparticle thing that exists in the air; These microparticle things usually can natural subsidence, adhere to various body surfaces; Cause serious harm for production work, perhaps adhere to glass surface, through a series of physics, chemical transformation like fields such as aerospace, food pharmaceutical, precision sizing, unicircuit; Make glass lose existing function and characteristic, bring certain influence for people's daily life.
Therefore need a kind of novel pretreating agent of development, this kind pretreating agent can carry out pre-treatment to various carriers, guarantees its effective efficiency and characteristic, and reduces the danger that causes because of dust, particle packing.
Summary of the invention
Defective in view of prior art exists the objective of the invention is to provide a kind of with wetting ability TiO
2Solution adds certain proportion C as base-material
60The nanometer that high molecule nano material the is prepared from pretreating agent that prevents dust.
For realizing above-mentioned purpose, the technical solution that the present invention adopted is:
A kind of nanometer pretreating agent that prevents dust is characterized in that: with wetting ability TiO
2Solution is as base-material, C
60Nano material is as additive, and both are mixed with and form.Said wetting ability TiO
2The concrete composition of solution is butyl(tetra)titanate, the Glacial acetic acid min. 99.5 mixing solutions with ethanol solution, and the composition volume ratio is 1:1:1.
Said wetting ability TiO
2The preparation method of solution slowly mixes for getting isopyknic butyl(tetra)titanate, Glacial acetic acid min. 99.5 and ethanol solution, fully stirs, and places after 48 hours, promptly obtains wetting ability TiO
2Solution.
Said C
60The adding proportion of high molecule nano material is different according to carrier, and its optimum proportion scope is to be 1:100-1:10000, disposes according to weight percent.
The present invention has the following advantages: the present invention is with wetting ability TiO
2Solution adds certain proportion C as base-material
60High molecule nano material is prepared from the dustproof pretreating agent of nanometer.Its wetting ability TiO
2Photocatalysis and photoinduction wetting ability, C in addition
60High molecule nano material has and weakens adherent characteristic and make carrier through after the processing of this pretreating agent; Can weaken dust, particle etc. greatly and contact the adhesiving effect that the back takes place with carrier, and make dust, particle etc. very easily come off from carrier with the formation of forms such as physics, chemistry; After containing ultraviolet rayed, impurity such as the aqueous vapor on the carrier, water smoke are easy to remove through pretreated carrier.
Embodiment
Embodiment below in conjunction with concrete explains the present invention, but embodiment of the present invention is not limited thereto.
Concrete preparation process of the present invention is following: get isopyknic butyl(tetra)titanate, Glacial acetic acid min. 99.5 and ethanol solution and slowly mix, fully stir the back and placed 48 hours, promptly obtain wetting ability TiO
2Solution, wetting ability TiO
2Solution is transparence.To wetting ability TiO
2Solution adds a certain proportion of C
60High molecule nano material obtains the dustproof pretreating agent of nanometer after fully stirring.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 99.995%; C
60High molecule nano material 0.005%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 99.991%; C
60High molecule nano material 0.009%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 99.99%; C
60High molecule nano material 0.01%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 99.95%; C
60High molecule nano material 0.05%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 99.9%; C
60High molecule nano material 0.1%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 99.5%; C
60High molecule nano material 0.5%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 99.2%; C
60High molecule nano material 0.8%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 99%; C
60High molecule nano material 1%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 98.8%; C
60High molecule nano material 1.2%.
Embodiment: a kind of nanometer pretreating agent that prevents dust, form by following weight percent configuration, it is characterized in that: wetting ability TiO
2Solution 98.5%; C
60High molecule nano material 1.5%.
In sum, its wetting ability of the present invention TiO
2Photocatalysis and photoinduction wetting ability, C in addition
60High molecule nano material has and weakens adherent characteristic and make carrier through after the processing of this pretreating agent; Can weaken dust, particle etc. greatly and contact the adhesiving effect that the back takes place with carrier, and make dust, particle etc. very easily come off from carrier with the formation of forms such as physics, chemistry; After containing ultraviolet rayed, impurity such as the aqueous vapor on the carrier, water smoke are easy to remove through pretreated carrier.
The pretreatment mode of carrier can adopt spraying, impregnating mode to handle.
Claims (3)
1. the dustproof pretreating agent of nanometer is characterized in that: with wetting ability TiO
2Solution is as base-material, C
60Nano material is as additive, and both are mixed with and form; Said wetting ability TiO
2The concrete composition of solution is butyl(tetra)titanate, the Glacial acetic acid min. 99.5 mixing solutions with ethanol solution, and the composition volume ratio is 1:1:1.
2. a kind of nanometer according to claim 1 pretreating agent that prevents dust is characterized in that: said wetting ability TiO
2The preparation method of solution slowly mixes for getting isopyknic butyl(tetra)titanate, Glacial acetic acid min. 99.5 and ethanol solution, fully stirs, and places after 48 hours, promptly obtains wetting ability TiO
2Solution.
3. a kind of nanometer according to claim 1 pretreating agent that prevents dust is characterized in that: said C
60The adding proportion of high molecule nano material is different according to carrier, and its optimum proportion scope is to be 1:100-1:10000, disposes according to weight percent.