CN102617099B - 一种纯天然建筑内墙涂料 - Google Patents

一种纯天然建筑内墙涂料 Download PDF

Info

Publication number
CN102617099B
CN102617099B CN 201210079959 CN201210079959A CN102617099B CN 102617099 B CN102617099 B CN 102617099B CN 201210079959 CN201210079959 CN 201210079959 CN 201210079959 A CN201210079959 A CN 201210079959A CN 102617099 B CN102617099 B CN 102617099B
Authority
CN
China
Prior art keywords
parts
building interior
natural
water
interior paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201210079959
Other languages
English (en)
Other versions
CN102617099A (zh
Inventor
陶祖岐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI KANGSHUN ENERGY-SAVING MATERIAL TECHNOLOGY CO LTD
Original Assignee
WUXI KANGSHUN ENERGY-SAVING MATERIAL TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI KANGSHUN ENERGY-SAVING MATERIAL TECHNOLOGY CO LTD filed Critical WUXI KANGSHUN ENERGY-SAVING MATERIAL TECHNOLOGY CO LTD
Priority to CN 201210079959 priority Critical patent/CN102617099B/zh
Publication of CN102617099A publication Critical patent/CN102617099A/zh
Application granted granted Critical
Publication of CN102617099B publication Critical patent/CN102617099B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种纯天然建筑内墙涂料，由以下重量份的原料混合而成：白水泥50～130份，石灰膏250～400份，明矾4.2～6.9份，老土10～20份，橡胶树汁0.1～0.8份，水60～90份；具体制备步骤为：首先将老土、明矾粉碎，然后将白水泥、石灰膏混合，投入搅拌机中，再将粉碎好的老土、明矾依次投入，均匀搅拌，再加入橡胶树汁均匀搅拌，最后搅拌出料后的混干固体状再经过加水的步骤，调制成纯天然建筑内墙涂料成品。本发明具有良好的技术性能，成本低，所用原材料天然无毒无危害，能够节约资源，保护环境，可广泛应用于各类建筑的内墙涂饰工程。

Description

一种纯天然建筑内墙涂料
技术领域
本发明涉及建筑内墙的涂饰工程技术领域，尤其是涉及一种采用天然材料制备的建筑内墙涂料。
背景技术
用于建筑物或构筑物内墙面装饰的建筑涂料称为内墙涂料。内墙涂料有一些不同于外墙涂料的特征要求：首先，内墙涂料直接涂装于建筑物或构筑物的内表面，与人们的生活或工作关系更为密切。从这一意义上讲，内墙涂料的装饰效果（例如涂膜手感、平整度和质感等）会 受到人们更多的关注；第二，内墙涂料会对室内环境产生较大的影响，应当具有适当的透气性和吸湿性，完全不透气、不吸湿的涂膜会造成墙面的结露，不利于室内环境的改善和居住舒适性的提高；第三，内墙涂料中不能含有有毒、有害物质，否则会对环境和健康造成危害。当然，从对性能的严格要求来说，内墙涂料最好还能够防止霉菌在涂膜上的滋生，另外，虽然内墙涂料不要求具有像外墙涂料那样高的物理力学性能和耐候性能，但也必须具有适当的耐水性、耐碱性和耐擦洗性。现有的内墙涂料主要原料为化工原料，含有少量的甲醛、醇醚类有机溶剂，稳定性差，耐水性差，表面污染物易使涂膜产生缩孔。
发明内容
针对现有技术存在的上述问题，本申请人提供了一种纯天然建筑内墙涂料。本发明具有良好的技术性能，成本低，所用原材料天然无毒无危害，能够节约资源，保护环境，可广泛应用于各类建筑的内墙涂饰工程。
本发明的技术方案如下：
一种纯天然建筑内墙涂料，由以下重量份的原料混合而成：白水泥50~130份，石灰膏250~400份，明矾4.2~6.9份，老土10~20份，橡胶树汁0.1~0.8份，水60~90份。具体制备步骤为：首先将老土、明矾粉碎，然后将白水泥、石灰膏混合，投入搅拌机中，再将粉碎好的老土、明矾依次投入，均匀搅拌，再加入橡胶树汁均匀搅拌，最后搅拌出料后的混干固体状再经过加水的步骤，调制成纯天然建筑内墙涂料成品。
本发明有益的技术效果在于：
本发明所用原料中的白水泥为白色硅酸盐水泥的简称，石灰膏为熟石灰膏；老土是承载力较高的天然黄土，其主要成分是砂粒、黏土和少量方解石的混合物，质地均一，含多量钙质和黄土结核；橡胶树汁为海南岛的天然橡胶树汁。
在上述原料中，白水泥、石灰膏作为粘结剂；明矾作为凝固剂；老土抗压力较强，起到提高涂料面层抗压强度的作用，有一定抗辐射能力，还起到一定调色作用，调和涂料的炫白刺目感；橡胶树汁胶结作用强。
橡胶树汁作为胶结剂，橡胶汁具有良好的活性和胶结性能。除此之外，橡胶树汁为天然原料，无毒无味，价格低廉，符合循环经济和环境保护的要求。明矾作为胶结料，其有效成分是Al2O3、SO3，能够与水泥水化物进行反应，生成钙矾石，可加速水泥的水化和硬化。除此之外，明矾的防水作用提高了涂料的防水防腐的性能。白水泥作为粘结剂和防水剂，以硅酸钙为主要成份，铁度含量极少的硅酸盐熟料经漂白处理，加入适量的石膏磨细制成的白色硬性胶凝内材料,另外白水泥有一定防水作用，可以提高涂料的防水性能。石灰膏主要成分是Ca(OH)2，具有强碱性，能使细菌的蛋白质成分失去活性，对原料进行消毒,另外，石灰膏能增强混合物的和易性，使得涂料不易发散，保水性好抗压性较强。
本发明生产的纯天然内墙涂料不仅具有良好的阻燃性能，涂刷本发明产品的内墙光滑平整，无裂缝产生，且具有一定的抗压强度和保温性能。
具体实施方式
      本发明方法按照以下步骤实施：
（1）将老土、明矾用粉碎机粉碎成细微颗粒状。
（2）将白水泥、石灰膏混合，投入搅拌机中，再将粉碎好的老土、明矾按一定配比的量依次投入，然后加入橡胶树汁均匀搅拌。
（3）搅拌出料后的混干固体状再经过加水的步骤，调制成稠液体状成品。
本发明按照以下方法施工：
内墙清扫过后，当气温在2~10℃时提前5天在墙上洒水；气温在10~25℃时提前3天在墙上洒水；气温在25℃以上时提前1天在墙上洒水。第一遍用水泥混合砂浆打底（含泥量不超过5%），然后用本发明产品混合一定配比的水，通过砂浆机搅拌成腻子，进行内墙的粉刷打底，用2m长刮尺刮平，再用木垫平整（按国家砌筑施工规范GB503-2002执行，粉刷按照GB50210-2001规范执行）。
本发明产品实施例1至实施例4所用的原料重量份数见表1，单位为kg。
表1
实施例1~4所用的原料来源见表2所示。
表2 
Figure DEST_PATH_IMAGE003
根据国家标准GB/T9756-1955对实施例1进行检测，检测结果如表3所示。
表3
Figure DEST_PATH_IMAGE004
 

Claims (2)

1.一种纯天然建筑内墙涂料，其特征在于由以下重量份的原料混合而成：白水泥50~130份，石灰膏250~400份，明矾4.2~6.9份，老土10~20份，橡胶树汁0.1~0.8份，水60~90份。
2.根据权利要求1所述的纯天然建筑内墙涂料，其特征在于具体制备步骤为：首先将老土、明矾粉碎，然后将白水泥、石灰膏混合，投入搅拌机中，再将粉碎好的老土、明矾依次投入，均匀搅拌，再加入橡胶树汁均匀搅拌，最后搅拌出料后的混干固体状再经过加水的步骤，调制成纯天然建筑内墙涂料成品。
CN 201210079959 2012-03-26 2012-03-26 一种纯天然建筑内墙涂料 Active CN102617099B (zh)