CN102605632A - Velvety composite filament wash-faded plus material - Google Patents
Velvety composite filament wash-faded plus material Download PDFInfo
- Publication number
- CN102605632A CN102605632A CN2012100740350A CN201210074035A CN102605632A CN 102605632 A CN102605632 A CN 102605632A CN 2012100740350 A CN2012100740350 A CN 2012100740350A CN 201210074035 A CN201210074035 A CN 201210074035A CN 102605632 A CN102605632 A CN 102605632A
- Authority
- CN
- China
- Prior art keywords
- lining
- wash
- weight portion
- washing
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a velvety composite filament wash-faded plus material. The plus material comprises a bottom fabric layer consisting of polyester and nylon composite fibers and cotton fibers, and a wash-faded layer coated on the surface of the bottom fabric layer, wherein the wash-faded layer is formed by scraping a layer of wash-faded slurry on the surface of the bottom fabric layer; and the wash-faded slurry is prepared by the following components in parts by weight: 10 parts of water-base resin, 90 parts of water, 2.5 parts of PTF thickening agent, 0 to 0.3 part of poly aziridine crosslinking agent, 0.2 to 0.3 part of organic silicon flatting agent, 0.1 to 0.2 part of polyether defoamer and 3 to 6 parts of water-based environment-friendly color paste. The plus material has a soft, plump and compact hand feeling; the surface has uniform, stable, velvety and comfortable fluff condition, and has high moisture permeability; simultaneously, by combining with a wash-faded style, the composite filament plus material is environment-friendly and non-toxic; moreover, the wash-faded effect is uniform, durable and stable; and the plus material has rinsing and scrubbing resistance, and cannot be whitened and misted after being washed for a plurality of times.
Description
Technical field
The present invention relates to a kind of lining, particularly a kind of velvet compound silk is washed and is taken off lining.
Background technology
At present, existing compound silk lining is generally directly weaved and is formed by washing the cotton three kinds of fibers of brocade, and the loose not consolidation of feel does not have bony, and because three kinds of fiber materials differ, the surperficial sanding uniformity and velvet are undesirable; And existing washing taken off lining three kinds of technologies probably arranged: 1. pure coating process; 2. liquid curing technology; 3. reduction adds coating process, and three's washing process is complicated, and the difficult control of batch difference exists not anti-rinsing behind the ready-made clothes, and brushing fastness is poor, inadequate natural endowments such as photooxidation resistant fastness difference, and the washing style is difficult to lasting stability, and dying of part material can't pass through environmental protection tests.
Summary of the invention
Main purpose of the present invention is the shortcoming that overcomes prior art; A kind of soft, plentiful consolidation is provided, and surperficial sanding situation is uniform and stable, and velvet is comfortable; Have good moisture permeability, wash the velvet compound silk that takes off effect lasting stability and environment-protecting asepsis and wash and take off lining.
The present invention adopts following technical scheme:
A kind of velvet compound silk is washed and is taken off lining; This lining includes to be weaved the bottom cloth layer that forms and be coated on washing of bottom cloth layer surface by polyester-nylon complex fiber and cotton fiber and takes off layer; Said wash take off layer on bottom cloth layer surface blade coating one deck wash that the boil off material forms, the said boil off material of washing is formed by 10 weight portion water-based resins, 90 weight parts waters, 2.5 weight portion PTF thickeners, 0～0.3 weight portion polyaziridine crosslinking agent, 0.2～0.3 weight portion organosilicon levelling agent, 0.1～0.2 weight portion polyether antifoam agent and 3～6 weight portion water-based environmental protection mill base manufacturings.
Said bottom cloth layer is a warp thread with the polyester-nylon complex fiber, is one with the cotton fiber for the weft yarn interlacing.
The said boil off material of washing adds the stirring of PTF thickener more while stirring and processed in 20～30 minutes for after earlier water-base resin, water, polyaziridine crosslinking agent, organosilicon levelling agent, polyether antifoam agent and aqueous, environmental protective mill base being passed through the simple mixing and stirring of mixer.
Said water-base resin adopts modification acrylate.
The pH value of said water is 6～7.
A kind of velvet compound silk is washed the production method that takes off lining, may further comprise the steps:
1. sanding is carried out the carbon element sanding to the bottom cloth layer surface and is handled;
2. open fibre, lining that will be after sanding is 10% NaOH solution through concentration, utilizes the hydrolysis principle of ester class, and lining is opened fine the processing, makes a polyester-nylon complex fiber become many, removes residual NaOH through ultrasonic washing then;
3. coating; The sanding face blade coating one deck that to open the bottom cloth layer behind the fibre through coating machine is washed the boil off material by what 10 weight portion water-based resins, 90 weight parts waters, 2.5 weight portion PTF thickeners, 0～0.3 weight portion polyaziridine crosslinking agent, 0.2～0.3 weight portion organosilicon levelling agent, 0.1～0.2 weight portion polyether antifoam agent and 3～6 weight portion water-based environmental protection mill base manufacturings formed; Hyperthermia drying solidifies it fully then;
4. washing is carried out leaven washing technology with the lining after the coating, promptly obtains having behind the flush away part pigment washing taking off washing of style and taking off lining.
During hyperthermia drying, bake out temperature is 130 ℃～150 ℃.
The neutral high temperature ferment of said leaven washing process using at 40 ℃～45 ℃, is washed under the condition of pH=8.
Can know that by the above-mentioned description of this invention compared with prior art, the present invention has following beneficial effect:
1. bottom cloth layer is weaved by polyester-nylon complex fiber and cotton fiber and is formed, and after the carbon element sanding is handled, opens fibre, makes the soft and plentiful consolidation of lining, and surperficial sanding situation is uniform and stable, and velvet is comfortable, also has good moisture permeability simultaneously;
2. adopt novel boil off material and the new coating washed to wash and take off technology, the compound silk lining taken off style and combines with washing, environment-protecting asepsis, and wash take off effect evenly, lasting stability, anti-rinsing is scrubbed, repeatedly washing can not whitened and grown dim;
3. it is lower to wash in the boil off material solid content, and lining does not almost have the glue sense after the coating, so lining has been able to keep stronger surperficial velvet.
Description of drawings
Fig. 1 is the structural representation of the specific embodiment of the invention.
Among the figure: 1. bottom cloth layer, 2. wash and take off layer.
The specific embodiment
Below through the specific embodiment the present invention is done further description.
With reference to Fig. 1; A kind of velvet compound silk is washed and is taken off lining; This lining includes to be weaved the bottom cloth layer 1 that forms and be coated on washing of bottom cloth layer 1 surface by polyester-nylon complex fiber and cotton fiber and takes off layer 2; Said washing taken off layer 2 the boil off material formed in order to wash at bottom cloth layer 1 surperficial blade coating one deck; Said wash the boil off material for 10 weight portion modification acrylates, 90 weight portion pH values be 6～7 water, 0.3 weight portion polyaziridine crosslinking agent, 0.3 weight portion organosilicon levelling agent, 0.2 weight portion polyether antifoam agent and 5 weight portion water-based environmental protection mill bases through after the simple mixing and stirring of mixer, add the stirring of 2.5 weight portion PTF thickeners more while stirring and processed in 20～30 minutes.Because it is lower to wash in the boil off material solid content, lining does not almost have the glue sense after the coating, so lining has been able to keep stronger surperficial velvet, simultaneously, this wash take off the lining environment-protecting asepsis and wash take off effect evenly, lasting stability.Said bottom cloth layer 1 is a warp thread with the polyester-nylon complex fiber, is one with the cotton fiber for the weft yarn interlacing.
With reference to Fig. 1, a kind of velvet compound silk is washed the production method that takes off lining, may further comprise the steps:
1. conventional husky shelling hair has been abandoned in sanding, the present invention, the carbon element sanding is carried out on bottom cloth layer 1 surface handled, and can grind thin weak point and uniform and stable fine hair, and velvet is comfortable;
2. open fibre; Lining that will be after sanding is 10% NaOH solution through concentration, utilizes the hydrolysis principle of ester class, and lining is opened fine the processing; Make a polyester-nylon complex fiber become many; The feel of the lining soft consolidation that just becomes like this, and have good sucting wet air permeability, remove residual NaOH through ultrasonic washing then;
3. coating; The sanding face blade coating one deck that to open the bottom cloth layer 1 behind the fibre through coating machine by 10 weight portion water-based resins, 90 weight portion pH values be 6～7 water, 2.5 weight portion PTF thickeners, 0.3 weight portion polyaziridine crosslinking agent, 0.3 weight portion organosilicon levelling agent, 0.2 weight portion polyether antifoam agent and 5 weight portion water-based environmental protection mill bases mix make form wash the boil off material; Hyperthermia drying then; It is solidified fully, and bake out temperature is 130 ℃～150 ℃;
4. washing is carried out leaven washing technology with the lining after the coating, promptly obtains having behind the flush away part pigment washing taking off washing of style and taking off lining; In order to enhance productivity, the present invention adopts neutral high temperature ferment, at 40 ℃～45 ℃; Wash under the condition of pH=8; Should be before adding ferment earlier with PH test paper adjustment pH value, the water body meta-acid can add the soda ash neutralization, and the inclined to one side alkali of water body can add glacial acetic acid or citric acid neutralization.
The velvet compound silk that obtains through above-mentioned technology washes that to take off the lining performance indications following:
1. regain: 6%
2. air penetrability: positive greater than 35mm/s, reverse side is greater than 25mm/s
3. content of formaldehyde: zero
4. azo dyes content: zero
5. plumbous mercury cadmium antimony selenium arsenic barium chromium content: zero
6. the variable color of soaping: 4-5 level
Above-mentionedly be merely a specific embodiment of the present invention, but design concept of the present invention is not limited thereto, allly utilizes this design that the present invention is carried out the change of unsubstantiality, all should belong to the behavior of invading protection domain of the present invention.
Claims (8)
1. a velvet compound silk is washed and is taken off lining; It is characterized in that: this lining includes to be weaved the bottom cloth layer that forms and be coated on washing of bottom cloth layer surface by polyester-nylon complex fiber and cotton fiber and takes off layer; Said wash take off layer on bottom cloth layer surface blade coating one deck wash that the boil off material forms, the said boil off material of washing is formed by 10 weight portion water-based resins, 90 weight parts waters, 2.5 weight portion PTF thickeners, 0～0.3 weight portion polyaziridine crosslinking agent, 0.2～0.3 weight portion organosilicon levelling agent, 0.1～0.2 weight portion polyether antifoam agent and 3～6 weight portion water-based environmental protection mill base manufacturings.
2. a kind of velvet compound silk as claimed in claim 1 is washed and taken off lining, it is characterized in that: said bottom cloth layer is a warp thread with the polyester-nylon complex fiber, is one with the cotton fiber for the weft yarn interlacing.
3. a kind of velvet compound silk as claimed in claim 1 is washed and is taken off lining; It is characterized in that: the said boil off material of washing adds the stirring of PTF thickener more while stirring and processed in 20～30 minutes for after earlier water-base resin, water, polyaziridine crosslinking agent, organosilicon levelling agent, polyether antifoam agent and aqueous, environmental protective mill base being passed through the simple mixing and stirring of mixer.
4. a kind of velvet compound silk as claimed in claim 3 is washed and taken off lining, it is characterized in that: said water-base resin adopts modification acrylate.
5. a kind of velvet compound silk as claimed in claim 1 is washed and taken off lining, it is characterized in that: the pH value of said water is 6～7.
6. wash the production method that takes off lining like the described velvet compound silk of claim 1 to 5 for one kind, it is characterized in that: may further comprise the steps:
1. sanding is carried out the carbon element sanding to the bottom cloth layer surface and is handled;
2. open fibre, lining that will be after sanding is 10% NaOH solution through concentration, utilizes the hydrolysis principle of ester class, and lining is opened fine the processing, makes a polyester-nylon complex fiber become many, removes residual NaOH through ultrasonic washing then;
3. coating; The sanding face blade coating one deck that to open the bottom cloth layer behind the fibre through coating machine is washed the boil off material by what 10 weight portion water-based resins, 90 weight parts waters, 2.5 weight portion PTF thickeners, 0～0.3 weight portion polyaziridine crosslinking agent, 0.2～0.3 weight portion organosilicon levelling agent, 0.1～0.2 weight portion polyether antifoam agent and 3～6 weight portion water-based environmental protection mill base manufacturings formed; Hyperthermia drying solidifies it fully then;
4. washing is carried out leaven washing technology with the lining after the coating, promptly obtains having behind the flush away part pigment washing taking off washing of style and taking off lining.
7. a kind of velvet compound silk as claimed in claim 6 is washed the production method that takes off lining, it is characterized in that: during hyperthermia drying, bake out temperature is 130 ℃～150 ℃.
8. a kind of velvet compound silk as claimed in claim 6 is washed the production method that takes off lining, it is characterized in that: the neutral high temperature ferment of said leaven washing process using, at 40 ℃～45 ℃, wash under the condition of pH=8.