CN102603311B - 一种钢厂中间包用干式渣线料及其制备方法 - Google Patents
一种钢厂中间包用干式渣线料及其制备方法 Download PDFInfo
- Publication number
- CN102603311B CN102603311B CN 201110261442 CN201110261442A CN102603311B CN 102603311 B CN102603311 B CN 102603311B CN 201110261442 CN201110261442 CN 201110261442 CN 201110261442 A CN201110261442 A CN 201110261442A CN 102603311 B CN102603311 B CN 102603311B
- Authority
- CN
- China
- Prior art keywords
- granularity
- weight
- sand
- line material
- slag line
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种钢厂中间包用干式渣线料及其制备方法。采用的技术方案是:由1mm<粒度≤3mm烧成橄榄石砂20~50%、粒度≤1mm烧成橄榄石砂10~25%、粒度≤1mm电熔镁砂10~25%、粒度≤0.088mm电熔镁砂10~25%、结合剂4~10%、添加剂5~15%、烧结剂0.5~2.5%制成。本发明主要适用于连铸中间包工作衬,可提高工作衬的高温抗侵蚀和抗渗透性,提高工作效益,降低永久衬的损坏,提高连浇时间,稳定性和耐用性能。
Description
技术领域
本发明涉及一种不定型耐火材料及其制备方法领域,特别涉及一种用于钢厂中间包的40小时干式渣线料及其制备方法。
背景技术
目前,用于钢铁浇注过程的中间包工作衬大都为普通干式料,都是以镁砂为主体原料,添加一些抗氧化剂,用固体树脂为结合剂,经混合而成的不定型散料。这种普通材料由于抗侵蚀性和渗透性强,在相当长的一段时间内一直发挥着重要作用,但是存在的问题是使用时间短。随着我国钢厂对各种优质钢种需求的急剧增加,冶金行业对各种耐火材料在冶金工艺过程中的稳定性和耐用性都有了新的要求。因此钢厂也越来越需要成本低,使用时间长,减少永久衬的损坏,提高连浇时间,稳定性,耐用性的钢厂中间包用渣线料。
发明内容
本发明的目的是提供一种成本低,高温抗侵蚀和抗渗透性强,使用时间可达40小时,可减少永久衬的损坏,提高连浇时间,稳定性和耐用性能的钢厂中间包用干式渣线料。
本发明的另一目的是提供一种生产工艺简单的上述钢厂中间包用干式渣线料的制备方法。
为了实现上述目的,本发明采用的技术方案是:一种钢厂中间包用干式渣线料由以下原料按重量百分比制成:
烧成橄榄石砂 1 mm<粒度≤3mm 20~50%
烧成橄榄石砂 粒度≤1mm 10~25%
电熔镁砂 粒度≤1mm 10~25%
电熔镁砂 粒度≤0.088mm 10~25%
结合剂 4~10%
添加剂 5~15%
烧结剂 0.5~2.5% 。
所述的结合剂是热固型树脂、乌洛托品和纤维素按重量比3 : 1~3 : 1~3的混合。
所述的添加剂是α- Al2O3、铝粉、镁铝尖晶石细粉和镁锆钛砂粉按重量比1 : 1~3 : 1~3 : 1~3的混合。
所述的烧结剂是硼砂、镁铁钙合成砂和固体硅酸钠按重量比1 : 1~3 : 1~3的混合。
上述的一种钢厂中间包用干式渣线料的制备方法如下:
1)按重量百分比将1 mm<粒度≤3 mm烧成橄榄石砂、粒度≤1mm烧成橄榄石砂和粒度≤1mm电熔镁砂放入混合机中,混合1~2分钟,再按重量百分比加入结合剂,混合1~3分钟;
2)按重量百分比加入添加剂和粒度≤0.088mm的电熔镁砂,混合1~3分钟;
3)按重量百分比加入烧结剂,混合3~5分钟。
本发明的有益效果是:烧成橄榄石砂是选用天然橄榄石矿,经高温竖窑煅烧而成的。电熔镁砂是以MgO含量为97%的轻烧氧化镁为原料,经压球、高温电熔等工艺生产而成。本发明所有原材料易得,价格低,明显降低了中间包耐材成本。主要适用于连铸中间包工作衬,可提高工作衬的高温抗侵蚀和抗渗透性,提高工作效益,降低永久衬的损坏,提高连浇时间,稳定性,耐用性能和价格明显优于目前的中包工作衬材料。
具体实施方式
实施例1 一种钢厂中间包用干式渣线料
(一)原料的配比如下:
烧成橄榄石砂 1 mm<粒度≤3mm 35%
烧成橄榄石砂 粒度≤1mm 17%
电熔镁砂 粒度≤1mm 16%
电熔镁砂 粒度≤0.088mm 15%
结合剂 6%
添加剂 10%
烧结剂 1.0% 。
所用的烧成橄榄石砂是选用天然橄榄石矿,经1600 ℃高温竖窑煅烧而成的烧成橄榄石砂。
结合剂是热固型树脂、乌洛托品和纤维素按重量比3 : 2 : 1的混合。
添加剂是α- Al2O3、铝粉、镁铝尖晶石细粉和镁锆钛砂粉按重量比1 : 2 : 2 : 2的混合。
烧结剂是硼砂、镁铁钙合成砂和固体硅酸钠按重量比1 : 2 : 2的混合。
(二)制备方法下:
1)按重量百分比将1 mm<粒度≤3 mm烧成橄榄石砂、粒度≤1mm烧成橄榄石砂和粒度≤1mm电熔镁砂放入混合机中,混合1~2分钟,再按重量百分比加入结合剂,混合1~3分钟;
2)按重量百分比加入添加剂和粒度≤0.088mm的电熔镁砂,混合1~3分钟;
3)按重量百分比加入烧结剂,混合3~5分钟。结果见表1。
实施例2 一种钢厂中间包用干式渣线料
(一)原料的配比如下:
烧成橄榄石砂 1 mm<粒度≤3mm 20%
烧成橄榄石砂 粒度≤1mm 10%
电熔镁砂 粒度≤1mm 25%
电熔镁砂 粒度≤0.088mm 25%
结合剂 4%
添加剂 14%
烧结剂 2% 。
所用的烧成橄榄石砂是选用天然橄榄石矿,经1600℃高温竖窑煅烧而成的烧成橄榄石砂。
结合剂是热固型树脂、乌洛托品和纤维素按重量比3 : 1 : 3的混合。
添加剂是α- Al2O3、铝粉、镁铝尖晶石细粉和镁锆钛砂粉按重量比1 : 1 : 1 : 1的混合。
烧结剂是硼砂、镁铁钙合成砂和固体硅酸钠按重量比1 : 1 : 1的混合。
(二)制备方法同实施例1,结果见表1。
实施例3 一种钢厂中间包用干式渣线料
(一)原料的配比如下:
烧成橄榄石砂 1 mm<粒度≤3mm 45%
烧成橄榄石砂 粒度≤1mm 19%
电熔镁砂 粒度≤1mm 10%
电熔镁砂 粒度≤0.088mm 10%
结合剂 10%
添加剂 5%
烧结剂 1% 。
所用的烧成橄榄石砂是选用天然橄榄石矿,经1600℃高温竖窑煅烧而成的烧成橄榄石砂。
结合剂是热固型树脂、乌洛托品和纤维素按重量比3 : 3 : 2的混合。
添加剂是α- Al2O3、铝粉、镁铝尖晶石细粉和镁锆钛砂粉按重量比1 : 3 : 3 : 3的混合。
烧结剂是硼砂、镁铁钙合成砂和固体硅酸钠按重量比1 : 3 : 3的混合。
(二)制备方法同实施例1,结果见表1。
表 1
Claims (2)
1.一种钢厂中间包用干式渣线料,其特征在于由以下原料按重量百分比制成:
烧成橄榄石砂 1 mm<粒度≤3mm 20~50%、
烧成橄榄石砂 粒度≤1mm 10~25%、
电熔镁砂 粒度≤1mm 10~25%、
电熔镁砂 粒度≤0.088mm 10~25%、
结合剂 4~10%、
添加剂 5~15%、
烧结剂 0.5~2.5%;
其中,
所述的结合剂是热固型树脂、乌洛托品和纤维素按重量比3 : 1~3 : 1~3的混合;
所述的添加剂是α- Al2O3、铝粉、镁铝尖晶石细粉和镁锆钛砂粉按重量比1 : 1~3 : 1~3 : 1~3的混合;
所述的烧结剂是硼砂、镁铁钙合成砂和固体硅酸钠按重量比1 : 1~3 : 1~3的混合。
2.权利要求1所述的一种钢厂中间包用干式渣线料的制备方法,其特征在于步骤如下:
1)按重量百分比将1 mm<粒度≤3 mm烧成橄榄石砂、粒度≤1mm烧成橄榄石砂和粒度≤1mm电熔镁砂放入混合机中,混合1~2分钟,再按重量百分比加入结合剂,混合1~3分钟;
2)按重量百分比加入添加剂和粒度≤0.088mm的电熔镁砂,混合1~3分钟;
3)按重量百分比加入烧结剂,混合3~5分钟。