CN102603258A - 耐水嵌缝石膏粉及其制备方法 - Google Patents
耐水嵌缝石膏粉及其制备方法 Download PDFInfo
- Publication number
- CN102603258A CN102603258A CN2011103060250A CN201110306025A CN102603258A CN 102603258 A CN102603258 A CN 102603258A CN 2011103060250 A CN2011103060250 A CN 2011103060250A CN 201110306025 A CN201110306025 A CN 201110306025A CN 102603258 A CN102603258 A CN 102603258A
- Authority
- CN
- China
- Prior art keywords
- water
- filleting
- terra alba
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐水嵌缝石膏粉及其制备方法，其组分按重量比为：β石膏7500-8500份，石灰石1500-2500份，缓凝剂1-10份，纤维素100-200份，有机硅粉20-80份。制备方法，包括将β石膏、石灰石制成粒度≤200μm的细粉；将制成的细粉与其他组分按比例加入混料机中混料5-10min，混匀。本发明耐水嵌缝石膏具有施工性能和耐水性能好，粘结强度高、耐蚀性强等优点。
Description
技术领域
本发明属于建筑装饰材料这一技术领域，特别涉及一种耐水型石膏粉及其制备方法。
背景技术
目前石膏制品广泛用于建筑工程中，如室内隔墙板，装饰板等，由于普通石膏板受潮后强度大大降低，极易翘曲变形，严重影响装饰效果，因此目前使用的石膏板一般为耐水纸面石膏板，但目前作为耐水纸面石膏板嵌缝处理用普通嵌缝石膏粉耐水性能差，影响石膏板之间缝隙的强度，易出现开裂，色泽不匹配，影响后期装饰整体效果，与耐水纸面石膏板接缝处理不相适宜，耐水耐碱性异常和浸水后粘结强度差，极不适宜在潮湿环境下施工。
发明内容
针对现有技术的不足，本发明的目的提供一种施工性能好，耐水性能强的耐水嵌缝石膏粉，以解决现有技术普通嵌缝石膏粉耐水性能差，与耐水纸面石膏板接缝处理不相适宜的问题，本发明的另一目的是提供该耐水嵌缝石膏粉的制备方法。
本发明通过以下方式实现：
一种耐水嵌缝石膏粉，其组分按重量比为：β石膏7500-8500份，石灰石1500-2500份，缓凝剂1-10份，纤维素100-200份，有机硅粉20-80份；所述缓凝剂为plast retard PE缓凝剂，所述纤维素为HPMC15000纤维素，所述有机硅粉为Elotex Seal80有机硅粉；所述耐水嵌缝石膏粉其组分还含有按重量比为10-50份的酞菁绿G。
一种耐水嵌缝石膏粉的制备方法，包括以下步骤：
A、将β石膏、石灰石制成粒度≤200μm的细粉；
B、将A步骤制成的细粉与其他组分按比例加入混料机中混料5-10min，混匀。
本发明运用了β石膏粉、石灰石和其他添加剂按特定的配比制成耐水嵌缝石膏，具有施工性能和耐水性能好，粘结强度高、耐蚀性强等优点。解决了现有仅普通嵌缝材料应用于耐水纸面石膏板表面接缝产生的技术问题。
经大量试验证明，酞菁绿G作为绿色颜料，使耐水嵌缝石膏粉具有稳定的绿色色泽，与耐水纸面石膏板表面颜色相一致，且对耐水嵌缝石膏粉的使用性能不产生不利影响，非常适用于室内建材装饰装修行业规范。
具体实施方式
实施例1
一种耐水嵌缝石膏粉，其组分及含量见表1，其中：
plast retard PE缓凝剂，生产厂家为意大利Sicit公司。
HPMC15000纤维素，生产厂家为Hercules天普化工公司。
Elotex Seal80有机硅粉，生产厂家为国民淀粉化学公司。
一种耐水嵌缝石膏粉的制备方法，包括以下步骤：
A、将β石膏、石灰石制成粒度≤200μm的细粉；
B、将A步骤制成的细粉与其他组分按比例加入混料机中混料5-10min，混匀。
实施例2～8
一种耐水嵌缝石膏粉的组分及含量见表1，制备方法同实施例1
对比例
一种普通嵌缝石膏粉的组分及含量见表2，制备方法同实施例1
对实施例1～8以及对比例制备的石膏粉进行抽样，测试结果见表3。从表3中可以看出，实施例均能满足耐水嵌缝石膏粉的要求，用批号实施例1制得的石膏粉进行嵌缝处理，施工性能好，耐水耐碱性能优良。
表1：实施例1～8耐水嵌缝石膏粉的组分及含量
表2：对比例普通嵌缝石膏粉的组分及含量
表3：耐水嵌缝石膏粉物理化学性能
Claims (4)
1.一种耐水嵌缝石膏粉，其组分按重量比为：β石膏7500-8500份，石灰石1500-2500份，缓凝剂1-10份，纤维素100-200份，有机硅粉20-80份。
2.如权利要求1所述的耐水嵌缝石膏粉，其特征在于：所述缓凝剂为plast retard PE缓凝剂，所述纤维素为HPMC15000纤维素，所述有机硅粉为Elotex Seal80有机硅粉。
3.如权利要求3所述的耐水嵌缝石膏粉，其特征在于：其组分还含有按重量比为10-50份的酞菁绿G。
4.如权利要求1-3任一项所述的耐水嵌缝石膏粉的制备方法，其特征在于包括以下步骤：
A、将β石膏、石灰石制成粒度≤200μm的细粉；
B、将A步骤制成的细粉与其他组分按比例加入混料机中混料5-10min，混匀。