CN102585740A - 一种环保型建筑胶粘剂及其制备方法 - Google Patents

一种环保型建筑胶粘剂及其制备方法 Download PDF

Info

Publication number
CN102585740A
CN102585740A CN2012100048622A CN201210004862A CN102585740A CN 102585740 A CN102585740 A CN 102585740A CN 2012100048622 A CN2012100048622 A CN 2012100048622A CN 201210004862 A CN201210004862 A CN 201210004862A CN 102585740 A CN102585740 A CN 102585740A
Authority
CN
China
Prior art keywords
minutes
water
minute
percent
borax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012100048622A
Other languages
English (en)
Other versions
CN102585740B (zh
Inventor
郭文录
张秀荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Saier Time Industry & Trade Co ltd
Original Assignee
Jiangsu University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu University of Science and Technology filed Critical Jiangsu University of Science and Technology
Priority to CN 201210004862 priority Critical patent/CN102585740B/zh
Publication of CN102585740A publication Critical patent/CN102585740A/zh
Application granted granted Critical
Publication of CN102585740B publication Critical patent/CN102585740B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种型环保型建筑胶粘剂，按质量百分含量由组分：1799聚乙烯醇为2～5％，丙烯酰胺为2～4％，聚丙烯酸钠为0.4～0.8％，羟乙基尿素为0.1～0.3％，硼砂为0.2～1.0％，KS25杀菌剂为0.03～0.12％，水为90.61～94.08％组成。制备时先将羟乙基尿素加5％的水溶解18-22分钟；将丙烯酰胺加5％的水溶解28-32分钟，搅拌8-12分钟备用；将聚丙烯酸钠和硼砂分别加4％和2％的水溶解备用；将剩余的水加入容器中加热至78℃-82℃，启动搅拌机，加入1799聚乙烯醇加热到88℃-92℃，保温搅拌45-50分钟后降温到85℃-88℃；将丙烯酰胺加入容器中，搅拌28-32分钟，加入羟乙基尿素和聚丙烯酸钠，搅拌18-22分钟，降温到58℃-62℃；加入硼砂，搅拌18-22分钟；降温到28℃-32℃加入KS25杀菌剂，搅拌13-17分钟，出胶装桶。

Description

一种环保型建筑胶粘剂及其制备方法
技术领域
本发明涉及一种环保型建筑胶粘剂及其制备方法，主要应用建筑装潢领域。
背景技术
近年来，随着人们生活水平的提高，建筑装潢市场对建筑胶粘剂量的需求越来越大，居住环保也成了人们关注的焦点。传统的107胶水、801胶水和901胶水等均因含有害物质，由于长期危害人们的身体健康，因而逐渐被市场淘汰。房子装修中的有害物质一直捆扰着人们。为了人们的身体健康，为杜绝胶水污染，研制一种环保型建筑胶粘剂实为当务之急。该胶粘剂环保，不含甲醛，无毒无害，黏结力强，成本低，施工方便，是传统胶粘剂的理想替代产品，建筑装潢领域需求量巨大，前景看好。
发明内容
本发明的目的是为了克服现有技术存在的缺陷，通过对1799聚乙烯醇与丙烯酰胺和聚丙烯酸钠、硼砂共聚、交联改性，提供一种不含甲醛，无毒无害，黏结力强，成本低，施工方便的环保型建筑胶粘剂，同时提供其制备方法。为了达到上述目的，本发明实现目的所采取的技术方案是：
一种环保型建筑胶粘剂，按质量百分含量由组分：1799聚乙烯醇为2～5％，丙烯酰胺为2～4％，聚丙烯酸钠为0.4～0.8％，羟乙基尿素为0.1～0.3％，硼砂为0.2～1.0％，KS25杀菌剂为0.03～0.12％，水为90.61～94.08％组成。
为了达到上述目的，本发明实现目的所采取的另一个技术方案是：所述一种环保型建筑胶粘剂的制备方法，包括如下步骤：
步骤1、将羟乙基尿素加5％的水溶解18-22分钟备用；将丙烯酰胺加5％的水溶解28-32分钟，启动搅拌机搅拌8-12分钟备用；将聚丙烯酸钠加4％的水溶解备用；硼砂加2％的水溶解备用；
步骤2、将剩余的74.61～78.08％水加入容器中，加热至78℃-82℃，启动搅拌机，加入1799聚乙烯醇，继续加热到88℃-92℃，保温搅拌45-50分钟，使聚乙烯醇彻底溶解，降温到85℃-88℃；
步骤3、将溶解的丙烯酰胺加入到容器中，搅拌28-32分钟，分别加入溶解好的羟乙基尿素和聚丙烯酸钠，搅拌18-22分钟，将温度降到58℃-62℃。
步骤4、加入溶解好的硼砂，搅拌18-22分钟；温度降到28℃-32℃，加入KS25杀菌剂，搅拌13-17分钟，出胶装桶。
本发明与现有技术相比较，所具备的优点和效果是：
本发明的胶粘剂具有环保，无毒，粘结力强，胶水透明，防水性能、稳定性好，存储期长，成本低，施工方便的优点。经检测各项性能指标产品达到GB18583-2001标准要求。本发明主要用于内墙调腻子，建筑装潢，是传统胶粘剂的理想替代品。胶粘剂成本190～210元/吨，市场销售价预计650元/吨，经济效益丰厚。
具体实施方式
结合具体实例说明本发明的技术方案。
实施例1
一、按质量百分比配组分
1799聚乙烯醇3.00％，丙烯酰胺2.00％，聚丙烯酸钠0.50％，羟乙基尿素0.10％，硼砂0.20％，KS25杀菌剂0.12％，自来水94.08％。
二、制备方法
步骤1、将羟乙基尿素加5％的水溶解18分钟备用；将丙烯酰胺加5％的水溶解28分钟，启动搅拌机搅拌8分钟备用；将聚丙烯酸钠加4％的水溶解备用；硼砂加2％的水溶解备用。
步骤2、将剩余的74.61～78.08％水加入容器中，加热至78℃，启动搅拌机，加入1799聚乙烯醇，继续加热到88℃，保温搅拌50分钟，使聚乙烯醇彻底溶解，降温到86℃。
步骤3、将溶解的丙烯酰胺加入到容器中，搅拌28分钟，分别加入溶解好的羟乙基尿素和聚丙烯酸钠，搅拌18分钟，将温度降到58℃。
步骤4、加入溶解好的硼砂，搅拌18分钟；温度降到28℃，加入KS25杀菌剂，搅拌13分钟，出胶水装桶。
实施例2
一、按质量百分比配组分
1799聚乙烯醇2.00％，丙烯酰胺3.00％，聚丙烯酸钠0.38％，羟乙基尿素0.20％，硼砂1.00％，KS25杀菌剂0.03％，自来水93.39％。
二、制备方法
步骤1、将羟乙基尿素加5％的水溶解19分钟备用；将丙烯酰胺加5％的水溶解29分钟，启动搅拌机搅拌9分钟备用；将聚丙烯酸钠加4％的水溶解备用；硼砂加2％的水溶解备用。
步骤2、将剩余的74.61～78.08％水加入容器中，加热至79℃，启动搅拌机，加入1799聚乙烯醇，继续加热到89℃，保温搅拌48分钟，使聚乙烯醇彻底溶解，降温到87℃。
步骤3、将溶解的丙烯酰胺加入到容器中，搅拌29分钟，分别加入溶解好的羟乙基尿素和聚丙烯酸钠，搅拌19分钟，将温度降到59℃。
步骤4、加入溶解好的硼砂，搅拌19分钟；温度降到29℃，加入KS25杀菌剂，搅拌14分钟，出胶水装桶。
实施例3
一、按质量百分比配组分
1799聚乙烯醇5.00％，丙烯酰胺2.00％，聚丙烯酸钠0.60％，羟乙基尿素0.30％，硼砂0.94％，KS25杀菌剂0.06％，自来水91.1％。
二、制备方法
步骤1、将羟乙基尿素加5％的水溶解20分钟备用；将丙烯酰胺加5％的水溶解30分钟，启动搅拌机搅拌10分钟备用；将聚丙烯酸钠加4％的水溶解备用；硼砂加2％的水溶解备用。
步骤2、将剩余的74.61～78.08％水加入容器中，加热至80℃，启动搅拌机，加入1799聚乙烯醇，继续加热到90℃，保温搅拌47分钟，使聚乙烯醇彻底溶解，降温到88℃。
步骤3、将溶解的丙烯酰胺加入到容器中，搅拌30分钟，分别加入溶解好的羟乙基尿素和聚丙烯酸钠，搅拌20分钟，将温度降到60℃。
步骤4、加入溶解好的硼砂，搅拌20分钟；温度降到30℃，加入KS25杀菌剂，搅拌15分钟，出胶水装桶。
实施例4
一、按质量百分比配组分
1799聚乙烯醇4.00％，丙烯酰胺4.00％，聚丙烯酸钠0.70％，羟乙基尿素0.20％，硼砂0.40％，KS25杀菌剂0.09％，自来水90.61％。
二、制备方法
步骤1、将羟乙基尿素加5％的水溶解21分钟备用；将丙烯酰胺加5％的水溶解31分钟，启动搅拌机搅拌11分钟备用；将聚丙烯酸钠加4％的水溶解备用；硼砂加2％的水溶解备用。
步骤2、将剩余的74.61～78.08％水加入容器中，加热至81℃，启动搅拌机，加入1799聚乙烯醇，继续加热到91℃，保温搅拌46分钟，使聚乙烯醇彻底溶解，降温到85℃。
步骤3、将溶解的丙烯酰胺加入到容器中，搅拌31分钟，分别加入溶解好的羟乙基尿素和聚丙烯酸钠，搅拌21分钟，将温度降到61℃。
步骤4、加入溶解好的硼砂，搅拌21分钟；温度降到31℃，加入KS25杀菌剂，搅拌16分钟，出胶水装桶。
实施例5
一、按质量百分比配组分
1799聚乙烯醇3.00％，丙烯酰胺3.00％，聚丙烯酸钠0.80％，羟乙基尿素0.20％，硼砂0.60％，KS25杀菌剂0.10％，自来水92.3％。
二、制备方法
步骤1、将羟乙基尿素加5％的水溶解22分钟备用；将丙烯酰胺加5％的水溶解32分钟，启动搅拌机搅拌12分钟备用；将聚丙烯酸钠加4％的水溶解备用；硼砂加2％的水溶解备用。
步骤2、将剩余的74.61～78.08％水加入容器中，加热至82℃，启动搅拌机，加入1799聚乙烯醇，继续加热到92℃，保温搅拌45分钟，使聚乙烯醇彻底溶解，降温到86℃。
步骤3、将溶解的丙烯酰胺加入到容器中，搅拌32分钟，分别加入溶解好的羟乙基尿素和聚丙烯酸钠，搅拌22分钟，将温度降到62℃。
步骤4、加入溶解好的硼砂，搅拌22分钟；温度降到32℃，加入KS25杀菌剂，搅拌17分钟，出胶水装桶。

Claims (2)

1.一种型环保型建筑胶粘剂，其特征是，按质量百分含量由组分：1799聚乙烯醇为2～5％，丙烯酰胺为2～4％，聚丙烯酸钠为0.4～0.8％，羟乙基尿素为0.1～0.3％，硼砂为0.2～1.0％，KS25杀菌剂为0.03～0.12％，水为90.61～94.08％组成。
2.一种如权利要求1所述的环保型建筑胶粘剂的制备方法，其特征是，包括如下步骤：
步骤1、将羟乙基尿素加5％的水溶解18-22分钟备用；将丙烯酰胺加5％的水溶解28-32分钟，启动搅拌机搅拌8-12分钟备用；将聚丙烯酸钠加4％的水溶解备用；硼砂加2％的水溶解备用；
步骤2、将剩余的74.61～78.08％水加入容器中，加热至78℃-82℃，启动搅拌机，加入1799聚乙烯醇，继续加热到88℃-92℃，保温搅拌45-50分钟，使聚乙烯醇彻底溶解，降温到85℃-88℃；
步骤3、将溶解的丙烯酰胺加入到容器中，搅拌28-32分钟，分别加入溶解好的羟乙基尿素和聚丙烯酸钠，搅拌18-22分钟，将温度降到58℃-62℃；
步骤4、加入溶解好的硼砂，搅拌18-22分钟；温度降到28℃-32℃，加入KS25杀菌剂，搅拌13-17分钟，出胶装桶。
CN 201210004862 2012-01-10 2012-01-10 一种环保型建筑胶粘剂及其制备方法 Expired - Fee Related CN102585740B (zh)