CN102561583A - 一种温室后墙用保温墙板 - Google Patents
一种温室后墙用保温墙板 Download PDFInfo
- Publication number
- CN102561583A CN102561583A CN201210049156XA CN201210049156A CN102561583A CN 102561583 A CN102561583 A CN 102561583A CN 201210049156X A CN201210049156X A CN 201210049156XA CN 201210049156 A CN201210049156 A CN 201210049156A CN 102561583 A CN102561583 A CN 102561583A
- Authority
- CN
- China
- Prior art keywords
- layer
- wall
- heat preservation
- greenhouse
- insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及到一种温室后墙用保温墙板,有5层的层状结构,中间一层为中心板层,厚度5~10mm;中心板层的上下两层为保温层,厚度10~20mm;保温层的上下两层为阻燃层,厚度5~10mm。所述的中心板层用铝合金、木塑、铝塑、聚苯泡沫颗粒一次性压制而成;所述的保温层由两块泡沫塑料板材组成,通过粘合材料层粘合而成;所述阻燃层由氯化镁、氧化镁、膨胀蛭石、粘合剂、乳化剂组成。温室后墙用保温墙板具有制作简单,墙体具有强度高,保温效果好和阻燃性能高等优点。
Description
技术领域
本发明涉及到一种建筑板材复合材料领域,特别涉及到温室后墙用保温材料。
背景技术
目前市场上大部分温室后墙只是停留在对强度的重视方面,没有解决保温功能,从而造成温室内热量散发比较快,需要加大供暖量,从而造成燃料资源的浪费。并且即使有些温室的建筑材料注重了它的保温功能,但是存在不能阻燃的缺陷。所以制造既保温又阻燃的温室用建筑墙板具有很重要的意义。
发明内容
针对现有技术存在的上述缺陷,本发明的目的在于提供一种保温性、阻燃性、防火性强的轻质保温墙板。
为实现上述目的,本发明采用的技术方案:一种温室后墙用保温墙板,其有5层的层状结构,中间一层为中心板层,厚度5~10mm;中心板层的上下两层为保温层,厚度10~20mm;保温层的上下两层为阻燃层,厚度5~10mm。
所述的中心板层用铝合金、木塑、铝塑、聚苯泡沫颗粒一次性压制而成,其中各组分的质量比为铝合金:木塑:铝塑:聚苯泡沫颗粒=0.25~0.36:1~1.4:0.5~0.7:2.3~2.7。
所述的保温层由两块泡沫塑料板材组成,通过粘合材料层粘合而成。
所述阻燃层的组成重量配比为:氯化镁50~55kg、氧化镁4~5kg、膨胀蛭石40~43kg,粘合剂160~170kg、乳化剂1~1.4kg。
所述的粘合材料层的配制原料由苛性白云石(CaO·MgO)、Na3PO4、MgCl2、SiO2组成,各原料的配比为:苛性白云石(CaO·MgO):Na3PO4:MgCl2:SiO2=2~2.3:0.05~0.07:0.11~0.13:2.0~2.3。
所述的粘合剂为美国红魔胶。
采用上述技术方案的有益效果是:温室后墙用保温墙板采用一层中心板层、两层保温层、两层阻燃层, 五层组合成一体,集防火、防水、轻质、高强、耐污染于一体,具体而言:
1:温室后墙用保温墙板的中心板层是以回收隔热材料-聚苯泡沫颗粒为主要原材料,另外配以铝合金、木塑、铝塑组成,使墙板单位面积重量低于传统的保温轻质墙板,但抗冲击性能、抗折强度比其它轻质墙板要高;
2:温室后墙用保温墙板的保温层由两块泡沫塑料板材通过粘合材料层粘合而成,其中泡沫层有利于获得质量轻的板材,同时更能提高隔热的性能,苛性白云石中MgO的活性高,易生成起主要强度作用的5Mg(OH)2.3MgCl2.8H2O,水化时几乎无Mg(OH)2伴成,同时苛性白云石中的CaO也具有一定的活性,水化生成物并非惰性填料,对强度也有一定的贡献;
3:温室后墙用保温墙板的阻燃层主要由膨胀蛭石与粘合剂混合而成,故本发明温室后墙用保温墙板防火、防潮、隔热、重量轻的作用。
附图说明
下面结合附图对本发明的具体实施例作进一步详细的说明。
图1 为温室后墙用保温墙板的结构示意图。
具体实施方式
如图1所示的温室后墙用保温墙板,其有5层的层状结构,中间一层为中心板层1,厚度5~10mm;中心板层的上下两层为保温层2,厚度10~20mm;保温层的上下两层为阻燃层3,厚度5~10mm。
所述的温室后墙用保温墙板的组成配方见下面。
温室后墙用保温墙板的实施例1为:
所述的中心板层用铝合金、木塑、铝塑、聚苯泡沫颗粒一次性压制而成,其中各组分的质量比为铝合金:木塑:铝塑:聚苯泡沫颗粒=0.25:1.2:0.5:2.5。
所述的保温层由两块泡沫塑料板材组成,通过粘合材料层粘合而成。
所述阻燃层的组成重量配比为:氯化镁50kg、氧化镁4kg、膨胀蛭石40kg,粘合剂170kg、乳化剂1kg。
所述的粘合材料层的配制原料由苛性白云石(CaO·MgO)、Na3PO4、MgCl2、SiO2组成,各原料的配比为:苛性白云石(CaO·MgO):Na3PO4:MgCl2:SiO2=2:0.07:0.11:2.0。
所述的粘合剂为美国红魔胶。
温室后墙用保温墙板的实施例2为:
所述的中心板层用铝合金、木塑、铝塑、聚苯泡沫颗粒一次性压制而成,其中各组分的质量比为铝合金:木塑:铝塑:聚苯泡沫颗粒=0.31:1:0.6:2.3。
所述的保温层由两块泡沫塑料板材组成,通过粘合材料层粘合而成。
所述阻燃层的组成重量配比为:氯化镁53kg、氧化镁4.5kg、膨胀蛭石42kg,粘合剂160kg、乳化剂1.2kg。
所述的粘合材料层的配制原料由苛性白云石(CaO·MgO)、Na3PO4、MgCl2、SiO2组成,各原料的配比为:苛性白云石(CaO·MgO):Na3PO4:MgCl2:SiO2=2.2:0.06:0.12:2.2。
所述的粘合剂为美国红魔胶。
温室后墙用保温墙板的实施例3为:
所述的中心板层用铝合金、木塑、铝塑、聚苯泡沫颗粒一次性压制而成,其中各组分的质量比为铝合金:木塑:铝塑:聚苯泡沫颗粒=0.36:1.4:0.7:2.7。
所述的保温层由两块泡沫塑料板材组成,通过粘合材料层粘合而成。
所述阻燃层的组成重量配比为:氯化镁55kg、氧化镁5kg、膨胀蛭石43kg,粘合剂165kg、乳化剂1.4kg。
所述的粘合材料层的配制原料由苛性白云石(CaO·MgO)、Na3PO4、MgCl2、SiO2组成,各原料的配比为:苛性白云石(CaO·MgO):Na3PO4:MgCl2:SiO2=2.3:0.05:0.13:2.3。
所述的粘合剂为美国红魔胶。
Claims (3)
1.一种温室后墙用保温墙板,其特征在于:有5层的层状结构,中间一层为中心板层,厚度5~10mm;中心板层的上下两层为保温层,厚度10~20mm;保温层的上下两层为阻燃层,厚度5~10mm;所述的中心板层用铝合金、木塑、铝塑、聚苯泡沫颗粒一次性压制而成,其中各组分的质量比为铝合金:木塑:铝塑:聚苯泡沫颗粒=0.25~0.36:1~1.4:0.5~0.7:2.3~2.7;所述的保温层由两块泡沫塑料板材组成,通过粘合材料层粘合而成;所述阻燃层由氯化镁、氧化镁、膨胀蛭石、粘合剂、乳化剂组成;其阻燃层的组成重量配比为:氯化镁50~55kg、氧化镁4~5kg、膨胀蛭石40~43kg、粘合剂160~170kg、乳化剂1~1.4kg。
2.根据权利1要求所述的温室后墙用保温墙板,其特征在于:所述的粘合材料层的配制原料由苛性白云石(CaO·MgO)、Na3PO4、MgCl2、SiO2组成,各原料的质量比为:苛性白云石(CaO·MgO):Na3PO4:MgCl2:SiO2=2~2.3:0.05~0.07:0.11~0.13:2.0~2.3。
3.根据权利1要求所述的温室后墙用保温墙板,其特征在于:所述的粘合剂为美国红魔胶。