CN102561059A - Corduroy imitating fabric with perspective effect by inkjet printing

Info

Publication number: CN102561059A
Application number: CN2011104215155A
Authority: CN
Inventors: 王潮霞; 张冠峰; 陈丽; 张霞
Original assignee: Jiangnan University
Current assignee: Jiangnan University
Priority date: 2011-12-16
Filing date: 2011-12-16
Publication date: 2012-07-11
Anticipated expiration: 2031-12-16
Also published as: CN102561059B

Abstract

The invention discloses a production method of corduroy imitating fabric, which realizes a stereoscopic perspective effect of the fabric by local treatment of the fabric and inkjet printing, belonging to the field of textile and clothing. In the invention, an alkaline thickener is adopted to perform local treatment of the fabric so as to realize a stripe semi-transparent perspective effect of the fabric; and the pattern with a corduroy imitating effect is printed on the fabric after the local treatment by an inkjet printing method, so that the concave-convex visual effect of the fabric is more stereoscopic. The method has the advantages of novel idea, simple flow, outstanding stereoscopic effect and good reproducibility.

Description

A kind of inkjet printing has the imitative corduroy fabric of transparent effect

Technical field

The invention belongs to the textile garment field, be specifically related to adopt alkaline thickener to make fabric acquisition suede bar and translucent perspective striped imitate corduroy fine hair stereoeffect with inkjet printing alternately through PLATE SCREAM PRINTING or ROTARY SCREAM PRINTING mode.

Background technology

Corduroy is to cut the COTTON FABRIC of latitude napping, the vertical suede bar of surface formation, adopts filling-backed weave to knit system, and through the clipping arrangement, cloth cover is wick-like suede bar again.Corduroy fabric feel bullet is sliding soft, the suede bar clear mellow and full, gloss is soft even, abundant and wear-resisting, uses very extensively, can be used as autumn and winter coat, shoes and hats lining, also can be used as furniture decoration cloth, curtain, sofa fabric, artifacts, toy etc.Can form velour through flocking and additive method.The velour preparation method of known imitative corduroy is an electrostatic spinning, and the physical characteristic that there is a natural attraction between the sexes is bonded on the fabric fine hair to utilize the electric charge same sex to repel each other, and forms velour.

Stereoscopic printing is claimed foamed printing again, and early stage foamed printing adopts CBA, it and thermoplastic resin; Thickeners etc. are printed on the matrix after being made into foaming printing paste; Bake through high temperature, blowing agent is decomposed produce gas, in thermoplastic resin, form microvesicle.This stamp has been broken through the conventional planar stamp and has been had the stereoeffect as similar applique, flocking and the embroidery.The disclosed novel solid flocking of patent CN201979744U cloth has carried out foamed printing to flocking cloth base material, makes flocking cloth have strong third dimension, can enrich its color, increases attractive in appearance, pattern and style, enlarges its scope of application.On the disclosed flocked fabric of patent CN1375023 decalcomania and pattern of indentations are arranged, these patterns can create a kind of three-D grain picture, figure and pattern true to nature.

Inkjet printing is a kind of digitized process; Flower to pattern returns, overlaps chromatic number and color does not all have restriction; In theory, all patterns can carry out inkjet printing, but common decalcomania can only demonstrate plane effect; The pattern of process particular design can demonstrate under the inkjet technology condition and have relief visual effect, remedies the deficiency of plane pattern aspect level and third dimension.

Summary of the invention

The object of the invention is to provide a kind of production method of having an X-rayed imitative corduroy fine hair stereoeffect printed fabric; And this production method combined with inkjet technology; The fabric that preparation has imitative corduroy effect has solved the shortage stereovision that occurs in the prior art lining printing process, the shortcoming of stereoeffect.

A kind of inkjet printing has the production method of the imitative corduroy fabric of transparent effect, it is characterized in that said method comprising the steps of:

(1) alkaline thickener configuration: under stirring condition, 2-6 part sodium alginate is added in 84-88 part deionized water gradually, be stirred to the abundant swelling of sodium alginate, add 50g/L sodium hydroxide solution 8-12 part;

(2) fabric treating: adopt the alkaline thickener of above-mentioned preparation on dacron, to print the alternate striped of 1.0-4.0mm through PLATE SCREAM PRINTING or ROTARY SCREAM PRINTING mode, oven dry, in 90-110 ℃ of following decatize 5-15min, fully washing, oven dry;

(3) imitative corduroy design sketch design: design the pattern that alternate width of fringe and spacing distance are the imitative corduroy fine hair of having of 1.0-4.0mm stereoeffect according to corduroy suede bar specification commonly used;

(4) inkjet printing: adopting ink-jet printer is 25 ℃ in temperature; Relative humidity is 60%; Resolution ratio is under the condition of 720dpi; Select suitable color, the imitative corduroy matte effect space pattern of design is printed on the fabric after the above-mentioned processing, make that jog and the alkaline thickener fabric treated jog on the pattern is complementary.

Description of drawings

Fig. 1 is: the special fine fleece bar of design inkjet printing 1.0mm, Fig. 2 is: design inkjet printing fine fleece bar 1.8mm, Fig. 3 is: design inkjet printing medium staple bar 2.5mm, Fig. 4 is: design inkjet printing rug bar 4.0mm.

The specific embodiment

The present invention will be helped further to understand through following embodiment, but content of the present invention can not be limited.

Embodiment 1:

(1) alkaline thickener configuration: under stirring condition, 2 parts of sodium alginates are added in 86 parts of deionized waters gradually, be stirred to the abundant swelling of sodium alginate, add 12 parts of 50g/L sodium hydroxide solutions;

(2) fabric treating: adopt the alkaline thickener of above-mentioned preparation on dacron, to print 1.8mm striped alternately through the PLATE SCREAM PRINTING mode, oven dry, in 90 ℃ of following decatize 15min, fully washing, oven dry;

(3) imitative corduroy design sketch design: design the pattern that alternate width of fringe and spacing distance are the imitative corduroy fine hair of having of 1.8mm stereoeffect according to corduroy suede bar specification commonly used;

(4) inkjet printing: adopting ink-jet printer is 25 ℃ in temperature; Relative humidity is 60%; Resolution ratio is under the condition of 720dpi; Select buff, the imitative corduroy nap effect space pattern of design is printed on the dacron after the above-mentioned processing, make that jog and the alkaline thickener fabric treated jog on the pattern is complementary.

Embodiment 2:

(1) alkaline thickener configuration: under stirring condition, 4 parts of sodium alginates are added in 88 parts of deionized waters gradually, be stirred to the abundant swelling of sodium alginate, add 8 parts of 50g/L sodium hydroxide solutions;

(2) fabric treating: adopt the alkaline thickener of above-mentioned preparation on polyester-cotton fabric, to print 4.0mm striped alternately through the ROTARY SCREAM PRINTING mode, oven dry, in 102 ℃ of following decatize 10min, fully washing, oven dry;

(3) imitative corduroy design sketch design: design the pattern that alternate width of fringe and spacing distance are the imitative corduroy fine hair of having of 4.0mm stereoeffect according to corduroy suede bar specification commonly used;

(4) inkjet printing: adopting ink-jet printer is 25 ℃ in temperature; Relative humidity is 60%; Resolution ratio is under the condition of 720dpi; Select coffee-likely, the imitative corduroy nap effect space pattern of design is printed on the polyester-cotton fabric after the above-mentioned processing, make that jog and the alkaline thickener fabric treated jog on the pattern is complementary.

Claims

1. fabric comprises:

Adopt alkaline thickener to handle the striped transparent effect alternately of generation through PLATE SCREAM PRINTING or ROTARY SCREAM PRINTING mode;

Imitative corduroy fine hair stereoeffect through the inkjet printing generation;

Striped transparent effect and imitative corduroy fine hair stereoeffect jog alternately is complementary.

2. fabric as claimed in claim 1 makes fabric obtain translucent transparent effect through adopting alkaline thickener through PLATE SCREAM PRINTING or ROTARY SCREAM PRINTING fabric to be handled, and it is characterized in that adopting following processing step:

Alkalescence thickener configuration: under stirring condition, 2-6 part sodium alginate is added in 84-88 part deionized water gradually, be stirred to the sodium alginate complete swelling, add 50g/L sodium hydroxide solution 8-12 part;

Fabric treating: adopt the alkaline thickener of above-mentioned preparation on dacron, to print 1.0-4.0mm striped alternately through PLATE SCREAM PRINTING or ROTARY SCREAM PRINTING, oven dry, in 90-110 ℃ of following decatize 5-15min, fully washing, oven dry;

Described translucent transparent effect is to control through the consumption of control sodium hydroxide solution.

3. fabric as claimed in claim 1, wherein the characteristics through the inkjet technology impressing pattern are that imitative corduroy fine hair third dimension three-D grain effect pattern is presented on the fabric visually, make the striped alternately after alkaline thickener is handled more true to nature;

Described textile design color characteristic can be selected arbitrarily when inkjet printing;

Described fabric is dacron and BLENDED FABRIC thereof.