A kind of low stimulation nial polish
Technical field
The invention belongs to the cosmetics technical field, relate to a kind of nial polish, particularly a kind of is the low stimulation nial polish of primary raw material with alcohols solvent and pure dissolubility film former.
Background technology
Nial polish belongs to the big series products of one in the color make-up series, has to beautify the function of modifying fingernail, and the nial polish of people's use at present is divided into esters solvent type nial polish and water-based nail polish.
Esters solvent type nial polish is a solvent with esters such as ethyl acetate, butyl acetates, ester dissolubility film former, and to draw oronain hectorite and hydration Silicon stone etc. be the thickening suspending agent in department, is equipped with additives such as plasticizer, pigment and essence and mixes and form.Such is filled a prescription, and allotment is proper can to obtain high glaze, strong adhesive force and strong water-proof nial polish.But there is following shortcoming: 1, have penetrating odor, can cause uncomfortable after strong pungent abnormal smells from the patient sucks; 2, use the back bigger to the fingernail and the skin irritation of human body, life-time service has bigger injury; 3, contact chemical fibre class medicated clothing and general plastics all can cause the dissolubility corrosion.
Water-based nail polish mixes with additives such as water, waterborne film-forming agent, pigment and essence and forms.Such prescription allotment is proper can obtain low abnormal smells from the patient, low irritant, high glaze, can the corrosive nial polish of dissolubility to chemical fibre clothes and plastics, but have following shortcoming: 1, poor water resistance, meet the water capacity and be prone to come off; 2, adhesive force is bad, and there is a big difference with esters solvent type nial polish ratio; 3, nial polish surface, dry back can be returned sticking.
Summary of the invention
The objective of the invention is to the existing the problems referred to above of existing nial polish, is the low stimulation nial polish that primary raw material is prepared from and proposed a kind of with alcohols solvent and pure dissolubility film former.
The object of the invention can be realized through following technical proposal: a kind of low stimulation nial polish is characterized in that this nial polish is formed (parts by weight) by following composition and proportioning:
Alcohols solvent: 30-85;
Alcohol dissolubility film former: 10-40;
Plasticizer: 1-10;
Thickening, suspending agent: 1-10;
Pigment: 0-5;
Essence: 0-5;
Solvent except that alcohols: 0-30.
This is low, and to stimulate nial polish be main with alcohols solvent and pure dissolubility film former, is equipped with additives such as thickening agent, suspending agent, plasticizer, pigment and essence again and mixes and form.Alcohols solvent wherein plays each component in the dissolving prescription, regulates the effect of drying time; Add essence and make this nial polish have fragrance, thickening agent, suspending agent come the suspended solid component.Film former plays the effect that film forming improves adhesive force; Dissolubility by weight in above-mentioned alcohols solvent all is classified as pure dissolubility film former above 5% film former; Because esters solvent is stronger than alcohols solvent dissolubility, thus the present invention about especially surely in esters solvent dissolving simultaneously again can be in alcohols solvent dissolubility also be defined as pure dissolubility film former greater than 5% film former.
In above-mentioned a kind of low stimulation nial polish, described alcohols solvent is a molecular weight less than low first alcohols of 103.
In above-mentioned a kind of low stimulation nial polish, described alcohols solvent is a kind of in ethanol, normal propyl alcohol, isopropyl alcohol, n-butyl alcohol and the isobutanol or several kinds mixture wherein.
In above-mentioned a kind of low stimulation nial polish, described pure dissolubility film former is a kind of in modified rosin resin, novolac resin, Lauxite, acrylate copolymer, polyamide, polyurethane resin, alkyd resins, polyvinyl alcohol, polyvinyl butyral resin, polyvinylpyrrolidone, NC Nitroncellulose, cellulose acetate and the acetate butyrate fiber or several kinds mixture wherein.
In above-mentioned a kind of low stimulation nial polish, described except that alcohols solvent be deionized water and/or esters solvent.
Compared with prior art, this low nial polish that stimulates has the following advantages:
1, low abnormal smells from the patient has only light alcohols taste, adds the fragrance that can also obtain similar perfume behind the various essence.
2, less to the fingernail and the skin irritation of human body.
3, contact chemical fibre class medicated clothing and plastics can not cause the dissolubility corrosion.
4, excellent in water resistance.
5, adhesive force is suitable with esters solvent type nial polish.
6, nial polish surface, dry back can not returned sticking.
7, surface gloss is suitable with esters solvent type nial polish.
The specific embodiment
Below be specific embodiment of the present invention, technical scheme of the present invention is done further to describe, but the present invention be not limited to these embodiment.
Embodiment 1
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process red nail oil.
Embodiment 2
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process the yellow nial polish of band rose.
Embodiment 3
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process the blue nial polish of band rose.
Embodiment 4
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process band NINGMENGXIANG white nial polish.
Embodiment 5
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process transparent nail polish.
Embodiment 6
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process the black nial polish.
Embodiment 7
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process red nail oil.
Embodiment 8
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process red nail oil.
Embodiment 9
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process red nail oil.
Embodiment 10
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process the black nial polish.
Embodiment 11
In the present embodiment, low stimulation nial polish of the present invention is made up of following composition:
More than after each composition weighing the high-speed stirred mix homogeneously process the black nial polish.
It is good that the various nial polish that is prepared from through above-mentioned embodiment all has surface gloss; Zest less with contact chemical fibre class medicated clothing and plastics and can not cause the corrosive characteristics of dissolubility; In addition, its adhesive force, resistance to water are also all more outstanding, make people in the pursuit while to U.S.A; Reduce negative effect to greatest extent, improved quality of the life.
Specific embodiment described herein only is that the present invention's spirit is illustrated.Person of ordinary skill in the field of the present invention can make various modifications or replenishes or adopt similar mode to substitute described specific embodiment, but can't depart from spirit of the present invention or surmount the defined scope of appended claims.