CN102543325B - 绝缘子的制备方法 - Google Patents
绝缘子的制备方法 Download PDFInfo
- Publication number
- CN102543325B CN102543325B CN201010611808.5A CN201010611808A CN102543325B CN 102543325 B CN102543325 B CN 102543325B CN 201010611808 A CN201010611808 A CN 201010611808A CN 102543325 B CN102543325 B CN 102543325B
- Authority
- CN
- China
- Prior art keywords
- insulator
- glass fiber
- framework
- demoulding
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种绝缘子的制备方法，包括以下步骤：a.将玻璃纤维束制成与绝缘子形状相配合的三维立体骨架，表面是玻璃纤维布，浸润环氧树脂；b.待开始凝固时，在表面均匀涂抹含陶瓷粉或玻璃粉的树脂放入绝缘子模具中；d.加温定型，固化后脱模，制成绝缘子。本发明制成的一体式的绝缘子，省去了将伞裙一个个依次套装在绝缘子芯棒上的工序，节省了人力，而且用此工艺制出的绝缘子，自重小，电气性能和机械性能较好。不管是用此工艺制成的空心绝缘子还是实心绝缘子，均具有较好的电气性能和机械性能，而且自身重量较轻。适合户外高压输电线路的使用。
Description
技术领域
本发明属于绝缘子领域，具体的说是涉及一种绝缘子的制备方法。
背景技术
通常户外使用的高压支柱绝缘子一般是瓷棒绝缘子，绝缘子伞裙有瓷伞裙也有玻璃钢伞裙，还有是玻璃伞裙。随着科技水平的不断提高，人们对电站电器设备提出了更高的要求。对于电站用复合支柱绝缘子不仅要求具有较高的绝缘性能及各种电气性能，还要能承受运行中常受到导线的重力和张力、风力、覆冰重量、绝缘子自重、导线振动、设备操作机械力、短路电动力、地震和其他机械力的作用。复合绝缘子是由多片伞裙套设在瓷绝缘芯棒上，瓷绝缘子，表层的机械强度较差，易发生裂缝，从而毁坏绝缘子，而且自重较大。玻璃绝缘子和玻璃钢绝缘子的表层机械强度高，使表面不易发生裂缝，但是自身较重。因此不论是瓷伞裙绝缘子、玻璃伞裙绝缘还是玻璃钢伞裙绝缘子，其自身重量较大，在运行过程中会影响到绝缘子的机械性能，同时还会波及到运行中导线的正常使用。而且目前的绝缘子伞裙是一个个依次套在绝缘子芯棒上，然后用绝缘胶粘接，工艺比较复杂。
发明内容
本发明的目的就在于提供一种制作工艺简单的绝缘子的制备方法，用此方法制出的绝缘子是一体的，且自重大幅降低。
本发明的目的可通过以下技术方案来实现：
一种绝缘子的制备方法，包括以下步骤：
a.将玻璃纤维束制成与绝缘子形状相配合的三维立体骨架，表面是玻璃纤维布，浸润环氧树脂，
b. 待开始凝固时，在表面均匀涂抹含陶瓷粉或玻璃粉的树脂，放入绝缘子模具中；
d.加温定型，固化后脱模，制成绝缘子。
上述绝缘子的制备方法，在步骤b后面加一步骤c. 在模具中心插入脱模管；所述步骤d. 加温定型，固化后拔出脱膜管，再脱模，制成空心绝缘子。
上述绝缘子的制作方法，在步骤b后面加一步骤c.在模具中间植入挤压的玻璃钢棒；所述步骤d. 加温定型，玻璃钢棒与绝缘子固化为一体，脱模，制成实心绝缘子。
上述绝缘子的制作方法，所述步骤c的玻璃钢棒的制作方法如下：将玻璃纤维束拧成麻花状，浸润环氧树脂，拉挤成实心绝缘子芯棒。
本发明是用玻璃纤维束制成与绝缘子形状相配合的三维立体骨架，表面是玻璃纤维布，浸润环氧树脂，在模具中固化脱模制成的一体式的绝缘子，省去了将伞裙一个个依次套装在绝缘子芯棒上的工序，节省了人力，而且用此工艺制出的绝缘子，自重小，电气性能和机械性能较好。不管是用此工艺制成的空心绝缘子还是实心绝缘子，均具有较好的电气性能和机械性能，而且自身重量较轻。适合户外高压输电线路的使用。
具体实施方式
实施例１：
空心绝缘子的制备方法，包括以下步骤：
a.将玻璃纤维束制成与绝缘子形状相配合的三维立体骨架，表面是玻璃纤维布，浸润环氧树脂，
b.待开始凝固时，在表面均匀涂抹含陶瓷粉或玻璃粉的树脂，放入绝缘子模具中；
c.在模具中心插入脱模管；
d.加温定型，固化后拔出脱膜管，再脱模，制成空心绝缘子。
实施例２：
实心绝缘子的制备方法，包括以下步骤：
a.将玻璃纤维束制成与绝缘子形状相配合的三维立体骨架，表面是玻璃纤维布，浸润环氧树脂，
b.待开始凝固时，在表面均匀涂抹含陶瓷粉或玻璃粉的树脂，放入绝缘子模具中；
c. 玻璃钢棒的制作方法：将玻璃纤维束拧成麻花状，浸润环氧树脂，拉挤成实心绝缘子芯棒；
d. 在模具中间植入挤压的玻璃钢棒，加温定型，玻璃钢棒与绝缘子固化为一体，脱模，制成实心绝缘子。
Claims (4)
1.一种绝缘子的制备方法，包括以下步骤：
a.将玻璃纤维束制成与绝缘子形状相配合的三维立体骨架，表面是玻璃纤维布，浸润环氧树脂，
b. 待开始凝固时，在表面均匀涂抹含陶瓷粉或玻璃粉的树脂，放入绝缘子模具中；
d.加温定型，固化后脱模，制成绝缘子。
2.根据权利要求１所述的绝缘子的制备方法，其特征在于：在步骤b后、步骤d前加一步骤c. 在模具中心插入脱模管；所述步骤d.固化后拔出脱膜管，再脱模，制成空心绝缘子。
3.根据权利要求１所述的绝缘子的制作方法，其特征在于：在步骤b后面步骤d前加一步骤c.在模具中间植入挤压的玻璃钢棒；所述步骤d.玻璃钢棒与绝缘子固化为一体，制成实心绝缘子。
4.根据权利要求３所述的绝缘子的制作方法，其特征在于：所述步骤c的玻璃钢棒的制作方法如下：将玻璃纤维束拧成麻花状，浸润环氧树脂，拉挤成实心绝缘子芯棒。