CN102531510B - 一种高硬度石膏香薰工艺品及其制备方法 - Google Patents

一种高硬度石膏香薰工艺品及其制备方法 Download PDF

Info

Publication number
CN102531510B
CN102531510B CN201110419590.8A CN201110419590A CN102531510B CN 102531510 B CN102531510 B CN 102531510B CN 201110419590 A CN201110419590 A CN 201110419590A CN 102531510 B CN102531510 B CN 102531510B
Authority
CN
China
Prior art keywords
gypsum
hardness
artwork
modified resin
kaolin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201110419590.8A
Other languages
English (en)
Other versions
CN102531510A (zh
Inventor
陈索斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO JINWANG APPLIED CHEMISTRY CO Ltd
Original Assignee
QINGDAO JINWANG APPLIED CHEMISTRY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO JINWANG APPLIED CHEMISTRY CO Ltd filed Critical QINGDAO JINWANG APPLIED CHEMISTRY CO Ltd
Priority to CN201110419590.8A priority Critical patent/CN102531510B/zh
Publication of CN102531510A publication Critical patent/CN102531510A/zh
Application granted granted Critical
Publication of CN102531510B publication Critical patent/CN102531510B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高硬度石膏香薰工艺品及其制备方法；本发明通过改善石膏制品的内部孔径的面积和石膏的密度，在传统香薰石膏制作配方和工艺的基础上，通过添加高效助剂，改进了原配方和工艺的几个突出的缺陷；本发明涉及的添加剂为分散剂、高岭土、高分子改性树脂等，通过添加高效硅氧烷水性分散剂，利用它的粘黏和膨胀的特性，使原CaSO4-2H2O结构更加紧密，提高了产品的硬度；通过添加高白度和高粒度的烧结高岭土，起到了增白剂的效果，提高了产品的白度；通过添加DH高分子改性树脂，由于其结构紧密含有活性基团，可进一步固化线型结构聚合物，并且具有憎水特性，所以使制作过程更加便于操作，有效地避免了气泡的干扰。

Description

一种高硬度石膏香薰工艺品及其制备方法
技术领域
本发明涉及一种石膏香薰工艺品及其制备方法，尤其是涉及一种高硬度石膏香薰工艺品及其制备方法，属于日常生活用品领域。
背景技术
现有的香熏产品在使用时为了达到香熏的效果，往往需要加热或者点燃，这样一方面限制了其使用场所，另一方面在加热或点燃后香精挥发速度较快，限制了使用的时间，而加热后的烟雾往往又会污染墙面，同时加热或燃烧这样的方式也带来了安全隐患。随着人们生活的多元化及生活品质的提高，需要更简便实用、香味持久、安全卫生的香熏产品。目前市场上也有作为香薰的石膏制品，但其存在留香时间短，表面粗糙且容易掉粉的缺陷。
发明内容
针对现有技术存在的不足，本发明所要解决的技术问题是，提供一种高硬度石膏香薰工艺品及其制备方法，解决了现有香薰石膏制品的留香时间短，表面粗糙且容易掉粉的问题。
为解决上述技术问题，本发明采取的技术方案是，一种高硬度石膏香薰工艺品，由以下重量比的原料制成：石膏粉CaSO4.2H2O74.5％，水20.5-21％，烧结高岭土3％，硅氧烷水性分散剂1％，DH高分子改性树脂0.5-1％。
上述高硬度石膏香薰工艺品的制备方法，包括下列步骤：
(1)按上述配方比例称取石膏粉CaSO4.2H2O和DH高分子改性树脂，将其充分混合，备用；
(2)按配方比例称取水和硅氧烷水性分散剂，将其充分混合，备用；
(3)将步骤(1)和(2)的混合物搅拌混合为膏状物；
(4)向步骤(3)中的膏状物按配方比例添加烧结高岭土后再混合均匀，倾倒在模具中成型；
(5)自然晾干即可。
本发明通过改善石膏制品的内部孔径的面积和石膏的密度，在传统香薰石膏制作配方和工艺的基础上，通过添加高效助剂，改进了原配方和工艺的几个突出的缺陷；本发明涉及的添加剂为分散剂、高岭土、高分子改性树脂等，通过添加高效硅氧烷水性分散剂，利用它的粘黏和膨胀的特性，使原CaSO4.2H2O结构更加紧密，提高了产品的硬度；通过添加高白度和高粒度的烧结高岭土，起到了增白剂的效果，提高了产品的白度；通过添加DH高分子改性树脂，由于其结构紧密含有活性基团，可进一步固化线型结构聚合物，并且具有憎水特性，所以使制作过程更加便于操作，有效地避免了气泡的干扰；本发明的石膏香薰工艺品具有硬度高、白度高、表面光滑不掉粉和留香时间长的特点，制作工艺简单。
具体实施方式
实施例1
本发明为一种高硬度石膏香薰工艺品，由以下重量比的原料制成：石膏粉CaSO4.2H2O74.5％，水20.5％，烧结高岭土3％，硅氧烷水性分散剂1％，DH高分子改性树脂1％。
上述高硬度石膏香薰工艺品的制备方法，包括下列步骤：
(1)按上述配方比例称取石膏粉CaSO4.2H2O和DH高分子改性树脂，将其充分混合，备用，通过添加DH高分子改性树脂，由于其结构紧密含有活性基团，可进一步固化线型结构聚合物，并且具有憎水特性，所以使制作过程更加便于操作，有效地避免了气泡的干扰；
(2)按配方比例称取水和硅氧烷水性分散剂，将其充分混合，备用，通过添加高效硅氧烷水性分散剂，利用它的粘黏和膨胀的特性，使原CaSO4.2H2O结构更加紧密，提高了产品的硬度；
(3)将步骤(1)和(2)的混合物搅拌混合为膏状物；
(4)向步骤(3)中的膏状物按配方比例添加烧结高岭土后再混合均匀，倾倒在模具中成型，通过添加高白度和高粒度的烧结高岭土，起到了增白剂的效果，提高了产品的白度；
(5)自然晾干即可。
实施例2
本实施例与实施例1中相同的部分不再累述，区别在于：一种高硬度石膏香薰工艺品，由以下重量比的原料制成：石膏粉CaSO4.2H2O74.5％，水21％，烧结高岭土3％，硅氧烷水性分散剂1％，DH高分子改性树脂0.5％。
以上所述，仅是对本发明的较佳实施例而已，并非是对本发明做其他形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例。但是，凡是未脱离本发明方案内容，依据本发明的技术实质对以上实施例所做的任何简单修改、等同变化与改型，仍属于本发明的保护范围。

Claims (2)

1.一种高硬度石膏香薰工艺品，其特征在于：由以下重量比的原料制成：石膏粉CaSO4·2H2O 74.5％，水20.5-21％，烧结高岭土3％，硅氧烷水性分散剂1％，DH高分子改性树脂0.5-1％。
2.根据权利要求1所述的高硬度石膏香薰工艺品的制备方法，包括下列步骤：
(1)按上述配方比例称取石膏粉CaSO4·2H2O 和DH高分子改性树脂，将其充分混合，备用；
(2)按配方比例称取水和硅氧烷水性分散剂，将其充分混合，备用；
(3)将步骤(1)和(2)的混合物搅拌混合为膏状物；
(4)向步骤(3)中的膏状物按配方比例添加烧结高岭土后再混合均匀，倾倒在模具中成型；
(5)自然晾干即可。
CN201110419590.8A 2011-12-15 2011-12-15 一种高硬度石膏香薰工艺品及其制备方法 Active CN102531510B (zh)