CN104230299B - 一种无机生态墙泥干粉及其生产方法 - Google Patents
一种无机生态墙泥干粉及其生产方法 Download PDFInfo
- Publication number
- CN104230299B CN104230299B CN201410464318.5A CN201410464318A CN104230299B CN 104230299 B CN104230299 B CN 104230299B CN 201410464318 A CN201410464318 A CN 201410464318A CN 104230299 B CN104230299 B CN 104230299B
- Authority
- CN
- China
- Prior art keywords
- shell
- carry out
- dry powder
- ecological wall
- wall mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种无机生态墙泥干粉,其按重量百分比计,包括以下组分:贝壳30-40%、硅藻土15-25%、脱硫石膏8-15%、硅酸钠盐5-10%、碳酸钙20-30%、木质短纤维1-5%、纤维素0.2-1%、氧化铁颜料0.5-3%、石英砂10-20%。生产时,首先将贝壳用水冲洗干净,晾干后,进行烘干粉碎,粉碎后用分级筛进行颗粒分级处理,并将分级好的粉料包装,进行备用;然后将粉碎好的贝壳原料投入到搅拌机,接着在投入贝壳原料的搅拌机中按上述比例逐一投入硅藻土、硅酸钠盐、脱硫石膏、碳酸钙、木质短纤维、纤维素、氧化铁颜料和石英砂,投入结束后,搅拌15-30分钟,使之充分搅拌均匀,将搅拌均匀的生态墙泥干粉进行计量灌装,即得成品。
Description
技术领域
本发明涉及一种新型建筑装修材料,具体地说,涉及一种无机生态墙泥干粉及其生产方法。
背景技术
内墙墙面装饰是每个家庭住宅在装饰中最重要的组成部分,并且每个家庭住宅在装饰时都期望通过环保型的室内墙面材料来达到美观和环保的要求。
长期以来,内墙墙面装饰基本上都在使用大白粉,801胶水与乳胶涂料、墙纸等材料进行施工。由于以上材料因自身储存条件受到限制的原因,生产过程中在胶水、乳胶涂料中均不同程度地添加了防腐性材料,这些防腐性材料在施工完工后均不同程度地向空气中释放甲醛等有害气体,这些气体在污染着空气的同时,也给人体带来了伤害。
目前,随着人们对环保要求认识的提高,以上大白粉,胶水、乳胶涂料与墙纸等装饰材料,已远远不能满足人们的需求,均不能长久地应用于室内装饰。因此,需要一种新的环保材料来满足当下需求。
发明内容
本发明的目的是提供一种由贝壳粉为主要原料的无机生态墙泥干粉。
本发明的另一目的是提供一种无机生态墙泥干粉的生产方法。
本发明采用的技术方案是:
一种无机生态墙泥干粉,其按重量百分比计,包括以下组分:贝壳30-40%、硅藻土15-25%、脱硫石膏8-15%、硅酸钠盐5-10%、碳酸钙20-30%、木质短纤维1-5%、纤维素0.2-1%、氧化铁颜料0.5-3%、石英砂10-20%。生产时,首先将贝壳用水冲洗干净,晾干后,进行烘干粉碎,粉碎后用分级筛进行颗粒分级处理,并将分级好的粉料包装,进行备用;然后将粉碎好的贝壳原料投入到搅拌机,接着在投入贝壳原料的搅拌机中按上述比例逐一投入硅藻土、硅酸钠盐、脱硫石膏、碳酸钙、木质短纤维、纤维素、氧化铁颜料和石英砂,投入结束后,搅拌15-30分钟,使之充分搅拌均匀,将搅拌均匀的生态墙泥干粉进行计量灌装,即得成品。
本发明最主要的特点是采用了贝壳材料,进行二次加工使用,变废为宝,同时不采用化学物质原材料,产品中不含有挥发性有机化合物(VOC),游离甲醛、苯、及可溶性重金属。在施工过程中,采用清水为助剂,不需要使用胶水,产品施工成膜后,并具有隔热、吸音、防霉等功能、并能净化室内甲醛的释放,有效地净化室内环境,是一种真正地绿色环保节能的专用室内装修材料。
采用以上组分及生产方法制作的生态墙泥干粉成品,产品性能均能达到GB18582-2008《室内装修材料内墙涂料中有害物质限量》标准与JC/T1074-2008《室内空气净化功能涂覆材料净化性能》标准;样品经过测试,参数如下表:
本发明的优点:
(1)采用贝壳为主要原料,变废为宝,减少使用天然矿石原料,保护自然环境。
(2)产品施工成膜后能有效地去除空气中的甲醛、苯、氨、VOC等有害物质及宠物、吸烟、垃圾所产生的异味,保持空气清新。
(3)采用硅酸钠盐材料,增强产品的透气性,能有效地调节室内空气中的水分,即墙面可吸收或释放水分,使室内空气保持清爽感觉。
(4)所有原材料均采用无机材料,在达到1000℃时均不燃烧,耐高温,不会产生有害气体,因其中硅藻土的材料成分中特有的多孔结构,起到保温、隔热、吸音等效果。
(5)通过纯手工操作,可创造出各种写意的艺术纹理,既有观赏性又有功能性效果,效果如泥土一样,亲近自然,返璞归真,有较强的艺术感染力,使人置身于大自然中的效果。
具体实施方式
实施例1
一种无机生态墙泥干粉,其按重量百分比计,包括以下组分:贝壳40%、硅藻土15%、脱硫石膏8%、硅酸钠盐5.3%、碳酸钙20%、木质短纤维1%、纤维素0.2%、氧化铁颜料0.5%、石英砂10%。生产时,首先将贝壳用水冲洗干净,晾干后,进行烘干粉碎(粉碎目数为200),粉碎后用分级筛进行颗粒分级处理,并将分级好的粉料包装,进行备用;然后将粉碎好的贝壳原料投入到搅拌机,接着在投入贝壳原料的搅拌机中按上述比例逐一投入硅藻土、硅酸钠盐、脱硫石膏、碳酸钙、木质短纤维、纤维素、氧化铁颜料和石英砂,投入结束后,搅拌15分钟,使之充分搅拌均匀,将搅拌均匀的生态墙泥干粉进行计量灌装,即得成品。
实施例2
一种无机生态墙泥干粉,其按重量百分比计,包括以下组分:贝壳30%、硅藻土20%、脱硫石膏8%、硅酸钠盐10%、碳酸钙20%、木质短纤维1%、纤维素0.5%、氧化铁颜料0.5%、石英砂10%。生产时,首先将贝壳用水冲洗干净,晾干后,进行烘干粉碎(粉碎目数为400),粉碎后用分级筛进行颗粒分级处理,并将分级好的粉料包装,进行备用;然后将粉碎好的贝壳原料投入到搅拌机,接着在投入贝壳原料的搅拌机中按上述比例逐一投入硅藻土、硅酸钠盐、脱硫石膏、碳酸钙、木质短纤维、纤维素、氧化铁颜料和石英砂,投入结束后,搅拌15分钟,使之充分搅拌均匀,将搅拌均匀的生态墙泥干粉进行计量灌装,即得成品。
实施例3
一种无机生态墙泥干粉,其按重量百分比计,包括以下组分:贝壳30%、硅藻土15%、脱硫石膏10%、硅酸钠盐8%、碳酸钙20%、木质短纤维5%、纤维素1%、氧化铁颜料1%、石英砂10%。生产时,首先将贝壳用水冲洗干净,晾干后,进行烘干粉碎(粉碎目数为300),粉碎后用分级筛进行颗粒分级处理,并将分级好的粉料包装,进行备用;然后将粉碎好的贝壳原料投入到搅拌机,接着在投入贝壳原料的搅拌机中按上述比例逐一投入硅藻土、硅酸钠盐、脱硫石膏、碳酸钙、木质短纤维、纤维素、氧化铁颜料和石英砂,投入结束后,搅拌20分钟,使之充分搅拌均匀,将搅拌均匀的生态墙泥干粉进行计量灌装,即得成品。
实施例4
一种无机生态墙泥干粉,其按重量百分比计,包括以下组分:贝壳30%、硅藻土20%、脱硫石膏8%、硅酸钠盐5%、碳酸钙20%、木质短纤维2%、纤维素0.3%、氧化铁颜料0.7%、石英砂14%。生产时,首先将贝壳用水冲洗干净,晾干后,进行烘干粉碎(粉碎目数为200),粉碎后用分级筛进行颗粒分级处理,并将分级好的粉料包装,进行备用;然后将粉碎好的贝壳原料投入到搅拌机,接着在投入贝壳原料的搅拌机中按上述比例逐一投入硅藻土、硅酸钠盐、脱硫石膏、碳酸钙、木质短纤维、纤维素、氧化铁颜料和石英砂,投入结束后,搅拌30分钟,使之充分搅拌均匀,将搅拌均匀的生态墙泥干粉进行计量灌装,即得成品。
Claims (2)
1.一种无机生态墙泥干粉,其特征在于:其按重量百分比计,包括以下组分:
贝壳30-40%
硅藻土15-25%
脱硫石膏8-15%
硅酸钠盐5-10%
碳酸钙20-30%
木质短纤维1-5%
纤维素0.2-1%
氧化铁颜料0.5-3%
石英砂10-20%。
2.如权利要求1所述的一种无机生态墙泥干粉,其特征在于:其生产方法如下,首先将贝壳用水冲洗干净,晾干后,进行烘干粉碎,粉碎后用分级筛进行颗粒分级处理,并将分级好的粉料包装,进行备用;然后将粉碎好的贝壳原料投入到搅拌机,接着在投入贝壳原料的搅拌机中按比例和顺序逐一投入硅藻土、硅酸钠盐、脱硫石膏、碳酸钙、木质短纤维、纤维素、氧化铁颜料和石英砂,投入结束后,搅拌15-30分钟,使之充分搅拌均匀,将搅拌均匀的生态墙泥干粉进行计量灌装,即得成品。