CN102525116A - Stone table surface with glass fiber sandwich structure and manufacturing method of stone table surface - Google Patents
Stone table surface with glass fiber sandwich structure and manufacturing method of stone table surface Download PDFInfo
- Publication number
- CN102525116A CN102525116A CN2010106189061A CN201010618906A CN102525116A CN 102525116 A CN102525116 A CN 102525116A CN 2010106189061 A CN2010106189061 A CN 2010106189061A CN 201010618906 A CN201010618906 A CN 201010618906A CN 102525116 A CN102525116 A CN 102525116A
- Authority
- CN
- China
- Prior art keywords
- layer
- material layer
- adhesive
- glass fabric
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a stone table surface with a glass fiber sandwich structure and a manufacturing method of the stone table surface. The stone table surface comprises a bordering material layer, a stone thin plate layer, a glass fiber fabric reinforcing layer, a core material layer and a glass steel plate layer, wherein the stone thin plate layer is adhered to the bordering material layer; the core material layer is positioned between the glass fiber fabric reinforcing layer and the glass steel plate layer; the glass steel plate layer is adhered to the core material layer and the bordering material layer through an adhesive agent; one surface of the glass fiber fabric reinforcing layer is fully adhered to the inner side surfaces of the stone thin plate layer and the bordering material layer through the adhesive agent; and the other surface of the glass fiber fabric reinforcing layer is adhered to the core material layer through the adhesive agent. The stone table surface is simple and firm in structure and good in integral mechanical property; and the quality problems that the bordering material layer deforms, cracks, and generates air bubbles easily and the like are effectively solved.
Description
Technical field
The present invention relates to the Stone table top technical field, particularly relate to a kind of Stone table top and process thereof of glass sandwich.
Background technology
The Stone table top of our common various patterns adopts materials such as timber, plastics, metal to process mostly at present; The desktop of processing by homogenous material; Rot easily outdoor like the timber desktop, Plastic table top corrosion easily is aging, metal desktop not only heaviness but also easy-to-rust; Therefore, the Stone table top of sandwich is able to extensive use.
The Stone table top of the sandwich that prior art adopts is through elder generation adhesive to be coated on the sandwich composite plate of finished product, and then bonding desktop surrounding edge material layer, is processed into Stone table top at last.This processing technology because the strength of materials of center sandwich is low, through large-area bonding after; The product distortion is big, bubble is many, bonding force descends, and causes desktop surrounding edge material layer easy of crack, the phenomenon that drops; Especially out of doors the desktop that uses; Because the temperature difference is big, makes used storeroom temperature deformation coefficient differ greatly, thereby causes quality problems such as splitting appears in desktop surrounding edge more easily.
Therefore, to deficiency of the prior art, needing badly provides a kind of simple in structure, firm, durable Stone table top with sandwich and process thereof.
Summary of the invention
The objective of the invention is to avoid weak point of the prior art and a kind of Stone table top and process thereof of simple in structure, firm, durable glass sandwich are provided.
The object of the invention is realized through following technical measures:
A kind of Stone table top of glass sandwich is provided; Include surrounding edge material layer, thin slabstone layer, glass fabric enhancement Layer, core layer and fiberglass flaggy; Said thin slabstone layer and said surrounding edge material layer are bonding; Said core layer is between said glass fabric enhancement Layer and said fiberglass flaggy; Said fiberglass flaggy and said core layer, said surrounding edge material layer are bonding through adhesive, and the one side of said glass fabric enhancement Layer is bonding fully through adhesive with the inner surface of said thin slabstone layer, said surrounding edge material layer, and it is bonding that the another side of said glass fabric enhancement Layer and said core layer pass through adhesive.
Wherein, the said glass fabric enhancement Layer glass fabric that is one deck or multilayer.
Wherein, said glass fabric extends to the upper end of said surrounding edge material layer.
Wherein, said core layer is cellular material or slight expanded material.
Wherein, said adhesive is unsaturated-resin, epoxy resin or polyurethane resin.
A kind of process of making Stone table top is provided, includes following steps:
Steps A: the desktop that thin slabstone need be spliced into required pattern according to drawing on workbench; With adhesive that surrounding edge material layer and thin slabstone is bonding then; After treating that adhesive solidifies, inject an amount of adhesive in the inboard of thin slabstone, surrounding edge material layer, and adhesive is scrawled evenly;
Step B: put into the glass fabric that cuts in advance, said glass fabric extends to the upper end of surrounding edge material layer always, and the inner surface of glass fabric and thin slabstone, surrounding edge material layer is bonding fully, with pressure roller glass fabric is flattened then;
Step C: glass fabric injects an amount of adhesive, and scrawles evenly, puts into core then, makes core and glass fabric bonding;
Step D: on pre-processed glass epoxy, scrawle an amount of adhesive uniformly, then glass epoxy is buckled in the top of core, and applies suitable pressure, adhesive is solidified;
Step e: the Stone table top polishing of making is machined to finished product.
Wherein, among the step B, said glass fabric is one deck or multilayer.
Wherein, among the step D, said glass epoxy covers the surrounding edge material layer fully.
Beneficial effect of the present invention:
The Stone table top of a kind of glass sandwich of the present invention; Include surrounding edge material layer, thin slabstone layer, glass fabric enhancement Layer, core layer and fiberglass flaggy; Said thin slabstone layer and said surrounding edge material layer are bonding; Said core layer is between said glass fabric enhancement Layer and said fiberglass flaggy; Said fiberglass flaggy and said core layer, said surrounding edge material layer are bonding through adhesive, and the one side of said glass fabric enhancement Layer is bonding fully through adhesive with the inner surface of said thin slabstone layer, said surrounding edge material layer, and it is bonding that the another side of said glass fabric enhancement Layer and said core layer pass through adhesive.Adopt said structure; The glass fabric of enhancement Layer extends to the upper end of surrounding edge material layer always; Make surrounding edge rim charge, glass fabric, core layer and glass epoxy bonding as a whole through adhesive; Improved integrally-built mechanical property greatly, firm and durable efficiently solves the surrounding edge material layer and occurs being out of shape, splits, produces quality problems such as bubble easily more.
Description of drawings
Utilize accompanying drawing that the present invention is described further, but the embodiment in the accompanying drawing does not constitute any restriction of the present invention.
Fig. 1 is the structural representation of the Stone table top with sandwich of prior art.
Fig. 2 is the structural representation of the Stone table top of a kind of glass sandwich of the present invention.
Fig. 3 is the cross-sectional view of Fig. 2.
Include among Fig. 1 to Fig. 3:
Surrounding edge material layer 1, thin slabstone layer 2, glass fabric enhancement Layer 3;
Core layer 4, fiberglass flaggy 5, sandwich composite plate 6.
The specific embodiment
Below in conjunction with accompanying drawing technical scheme of the present invention is described.
Embodiment 1
The Stone table top with sandwich of prior art; As shown in Figure 1; Include surrounding edge material layer 1, thin slabstone layer 2, sandwich composite plate 6; Processing method is through elder generation adhesive to be coated on the sandwich composite plate 6 of finished product, and then bonding surrounding edge material layer 1, is processed into Stone table top at last.Adopt this structure because center material intensity is low, through large-area bonding after, the product distortion is big, bubble is many, bonding force decline, causes desktop surrounding edge easy of crack, the phenomenon that drops.
The Stone table top of a kind of glass sandwich of the present invention as shown in Figures 2 and 3; Include surrounding edge material layer 1, thin slabstone layer 2, glass fabric enhancement Layer 3, core layer 4 and fiberglass flaggy 5; Thin slabstone layer 2 is bonding with surrounding edge material layer 1; Core layer 4 is between said glass fabric enhancement Layer 3 and fiberglass flaggy 5, and fiberglass flaggy 5 and core layer 4, surrounding edge material layer 1 are bonding through adhesive.
Concrete, core layer 4 is cellular material or slight expanded material, adopts this low-density material can effectively reduce the weight of Stone table top.
In the present embodiment, the one side of glass fabric enhancement Layer 3 is bonding fully through adhesive with the inner surface of thin slabstone layer 2, surrounding edge material layer 1, and the another side of glass fabric enhancement Layer 3 and core layer 4 are bonding through adhesive.
Concrete, glass fabric enhancement Layer 3 is the glass fabric of one deck or multilayer, glass fabric extends to the upper end of surrounding edge material layer 1 always.Adopt this structure; Pass through adhesive; Glass fabric and surrounding edge rim charge 1, core layer 4 and fiberglass flaggy 5 are bonding as a whole, have improved integrally-built mechanical property greatly, efficiently solve surrounding edge material layer 1 and occur being out of shape, splitting, produce quality problems such as bubble easily.
In the present embodiment, adhesive can adopt unsaturated-resin, epoxy resin or polyurethane resin according to different cores.
Steps A: the desktop that thin slabstone need be spliced into required pattern according to drawing on workbench; With adhesive that surrounding edge material layer and thin slabstone is bonding then; After treating that adhesive solidifies, inject an amount of adhesive in the inboard of thin slabstone, surrounding edge material layer, and adhesive is scrawled evenly;
Step B: put into the glass fabric that cuts in advance, said glass fabric extends to the upper end of surrounding edge material layer always, and the inner surface of glass fabric and thin slabstone, surrounding edge material layer is bonding fully, with pressure roller glass fabric is flattened then;
Concrete, the glass fabric among the step B is one deck or multilayer.
Step C: glass fabric injects an amount of adhesive, and scrawles evenly, puts into core then, makes core and glass fabric bonding;
Step D: on pre-processed glass epoxy, scrawle an amount of adhesive uniformly, then glass epoxy is buckled in the top of core, and applies suitable pressure, adhesive is solidified.
Concrete, glass epoxy covers the surrounding edge material layer fully.
Step e: the Stone table top polishing of making is machined to finished product.
Process of the present invention, has been avoided the bonding bonding force decline that causes of large tracts of land and the phenomenon that the surrounding edge material layer splits, drops occurred surrounding edge material layer, core and thin slabstone integrated bond through adopting glass fabric as enhancement Layer.Stone table top through above-mentioned process is made is simple in structure, more firm, durable.
Should be noted that at last; Above embodiment is only in order to technical scheme of the present invention to be described but not to the restriction of protection domain of the present invention; Although the present invention has been done detailed description with reference to preferred embodiment; Those of ordinary skill in the art should be appreciated that and can make amendment or be equal to replacement technical scheme of the present invention, and do not break away from the essence and the scope of technical scheme of the present invention.
Claims (8)
1. the Stone table top of a glass sandwich; It is characterized in that: include surrounding edge material layer, thin slabstone layer, glass fabric enhancement Layer, core layer and fiberglass flaggy; Said thin slabstone layer and said surrounding edge material layer are bonding; Said core layer is between said glass fabric enhancement Layer and said fiberglass flaggy; Said fiberglass flaggy and said core layer, said surrounding edge material layer are bonding through adhesive; The one side of said glass fabric enhancement Layer is bonding fully through adhesive with the inner surface of said thin slabstone layer, said surrounding edge material layer, and the another side of said glass fabric enhancement Layer and said core layer are bonding through adhesive.
2. the Stone table top of a kind of glass sandwich according to claim 1 is characterized in that: said glass fabric enhancement Layer is the glass fabric of one deck or multilayer.
3. the Stone table top of a kind of glass sandwich according to claim 2 is characterized in that: said glass fabric extends to the upper end of said surrounding edge material layer.
4. the Stone table top of a kind of glass sandwich according to claim 1 is characterized in that: said core layer is cellular material or slight expanded material.
5. the Stone table top of a kind of glass sandwich according to claim 1 is characterized in that: said adhesive is unsaturated-resin, epoxy resin or polyurethane resin.
6. process of making the described Stone table top of claim 1 is characterized in that: include following steps:
Steps A: the desktop that thin slabstone need be spliced into required pattern according to drawing on workbench; With adhesive that surrounding edge material layer and thin slabstone is bonding then; After treating that adhesive solidifies, inject an amount of adhesive in the inboard of thin slabstone, surrounding edge material layer, and adhesive is scrawled evenly;
Step B: put into the glass fabric that cuts in advance, said glass fabric extends to the upper end of surrounding edge material layer always, and the inner surface of glass fabric and thin slabstone, surrounding edge material layer is bonding fully, with pressure roller glass fabric is flattened then;
Step C: glass fabric injects an amount of adhesive, and scrawles evenly, puts into core then, makes core and glass fabric bonding;
Step D: on pre-processed glass epoxy, scrawle an amount of adhesive uniformly, then glass epoxy is buckled in the top of core, and applies suitable pressure, adhesive is solidified;
Step e: the Stone table top polishing of making is machined to finished product.
7. process according to claim 6 is characterized in that: among the step B, said glass fabric is one deck or multilayer.
8. process according to claim 6 is characterized in that: among the step D, said glass epoxy covers the surrounding edge material layer fully.