CN102516982B - Illuminating lamp, blended powder for illuminating lamp thereof and its production method - Google Patents
Illuminating lamp, blended powder for illuminating lamp thereof and its production method Download PDFInfo
- Publication number
- CN102516982B CN102516982B CN201110336347.XA CN201110336347A CN102516982B CN 102516982 B CN102516982 B CN 102516982B CN 201110336347 A CN201110336347 A CN 201110336347A CN 102516982 B CN102516982 B CN 102516982B
- Authority
- CN
- China
- Prior art keywords
- deionized water
- polyethylene oxide
- lighting
- powder
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a production method of blended powder for an illuminating lamp, which comprises the following steps: adding 5Kg phosphor in 900ml 20% of alumina dispersion solution and 600ml deionized water, milling in a ball mill; adding 800ml 7% of polyethylene oxide sol and stirring, then adding 1000ml 7% of polyethylene oxide sol, 20ml dispersant and 100ml 0.5% of surfactant and then stirring.
Description
Technical field
The present invention relates to lighting technical field, a kind of lighting be especially set, lighting join powder and preparation method thereof.
Background technology
In electrodeless lamp bulb, be coated with fluorescent material at glass bulb inwall and pipe outer wall.In the coating of fluorescent material, need to join powder processing to fluorescent material, fluorescent material can be coated on the tube wall of Glass tubing, and in baking oven, the Glass tubing of dusting be carried out to baking powder.Therefore, in prior art to the joining meal component and join powder method and improved higher requirement of fluorescent material, to meet good illuminating effect.
Summary of the invention
For above defect, what the present invention proposes a kind of lighting joins powder and preparation method thereof, joins powder and is coated on bulb and can realizes good illuminating effect.
For achieving the above object, the present invention is achieved through the following technical solutions:
Lighting join a powder making method, comprise the following steps:
20% alumina fluid dispersion and the deionized water 600ml that in 5Kg fluorescent material, add 900ml carry out ball milling in ball mill;
Add the 7% polyethylene oxide glue of 800ml to stir;
Add again 7% of 1000ml to stir according to 5 ‰ surfactant solns of oxyethane glue, 20ml dispersion agent and 100ml.
Lighting join a powder, its component and content are very:
Fluorescent material, at 5Kg;
20% alumina fluid dispersion, 900ml;
7% polyethylene oxide glue, 1800ml;
Dispersion agent, 20ml;
5 ‰ surfactant solns, 100ml;
Deionized water, 600ml.
A kind of lighting, adopts above-mentioned lighting to join powder.
Preferably, lighting is Non-polarized lamp.
Compared with prior art, the present invention has following beneficial effect: what the present invention proposes a kind of lighting joins powder and preparation method thereof, joins powder and is coated on bulb and can realizes good illuminating effect.
Embodiment
The powder of joining that the present invention proposes a kind of lighting, its component and content are:
Fluorescent material, at 5Kg;
20% alumina fluid dispersion, 900ml;
7% polyethylene oxide glue, 1800ml;
Dispersion agent, 20ml;
5 ‰ surfactant solns, 100ml;
Deionized water, 600ml.
The preformulation operation of in the present invention, joining powder comprises:
1, aluminum oxide and deionized water by weight disperse stir, be made into 20% alumina fluid dispersion, stirred for several hour, quiet put stand-by.The high speed agitator that preferably adopts high scissors, it has good dispersion effect.
2, polyethylene oxide and deionized water, by weight disperseing stirring, are made into 7% polyethylene oxide glue.Stirring velocity can be first quick and back slow, and churning time 10h is to solution without particle, transparent, and as also having particulate matter need extend churning time, quiet putting after bubble collapse used.
3, tensio-active agent and deionized water dilute in proportion, are made into 5 ‰ surfactant soln, stir 3-5h quiet put stand-by.
According to the material of above-mentioned preformulation, can carry out the powder of joining of lighting, its making method comprises the following steps:
20% alumina fluid dispersion and the deionized water 600ml that in 5Kg fluorescent material, add 900ml carry out ball milling in ball mill; In mechanical milling process, depending on fluorescent material situation, ball milling powder wants seeking time to carry out ball milling on demand, and non-ball milling powder stirs;
Add the 7% polyethylene oxide glue of 800ml to stir;
Add again 7% of 1000ml to stir according to 5 ‰ surfactant solns of oxyethane glue, 20ml dispersion agent and 100ml.
What the present invention proposes a kind of lighting joins powder and preparation method thereof, joins powder and is coated on bulb and can realizes good illuminating effect.
The invention allows for a kind of lighting, adopt the powder of joining of above-mentioned lighting.
Preferably, lighting is Non-polarized lamp.
The present invention is carried out to exemplary description above; obvious realization of the present invention is not subject to the restrictions described above; as long as the various improvement that adopted method design of the present invention and technical scheme to carry out; or without improving, design of the present invention and technical scheme are directly applied to other occasion, all in protection scope of the present invention.
Claims (4)
- Lighting join a powder making method, it is characterized in that, comprise the following steps:20% alumina fluid dispersion and the deionized water 600ml that in 5Kg fluorescent material, add 900ml carry out ball milling in ball mill; Wherein, 20% alumina fluid dispersion adopts high speed agitator stirring to obtain in aluminum oxide and deionized water by weight;Add the 7% polyethylene oxide glue of 800ml to stir; Wherein, described 7% polyethylene oxide glue is made into polyethylene oxide and deionized water by weight disperseing to stir;Add again 5 ‰ surfactant solns of 7% polyethylene oxide glue, 20ml dispersion agent and the 100ml of 1000ml to stir; Wherein, described 5 ‰ surfactant solns dilute tensio-active agent and deionized water to be made in proportion.
- Lighting join a powder, it is characterized in that, its component and content are:Fluorescent material, 5Kg;20% alumina fluid dispersion, 900ml;7% polyethylene oxide glue, 1800ml;Dispersion agent, 20ml;5 ‰ surfactant solns, 100ml;Deionized water, 600ml;The powder of joining of described lighting is prepared by the following method:20% alumina fluid dispersion and the deionized water 600ml that in 5Kg fluorescent material, add 900ml carry out ball milling in ball mill; Wherein, 20% alumina fluid dispersion adopts high speed agitator stirring to obtain in aluminum oxide and deionized water by weight;Add the 7% polyethylene oxide glue of 800ml to stir; Wherein, described 7% polyethylene oxide glue is made into polyethylene oxide and deionized water by weight disperseing to stir;Add again 5 ‰ surfactant solns of 7% polyethylene oxide glue, 20ml dispersion agent and the 100ml of 1000ml to stir; Wherein, described 5 ‰ surfactant solns dilute tensio-active agent and deionized water to be made in proportion.
- 3. a lighting, is characterized in that, adopts the powder of joining of lighting claimed in claim 2.
- 4. lighting as claimed in claim 3, is characterized in that, described lighting is Non-polarized lamp.