CN102516701A - 纳米TiO2增强的ABS料 - Google Patents

纳米TiO2增强的ABS料 Download PDF

Info

Publication number
CN102516701A
CN102516701A CN2011104090592A CN201110409059A CN102516701A CN 102516701 A CN102516701 A CN 102516701A CN 2011104090592 A CN2011104090592 A CN 2011104090592A CN 201110409059 A CN201110409059 A CN 201110409059A CN 102516701 A CN102516701 A CN 102516701A
Authority
CN
China
Prior art keywords
weight parts
parts
abs material
nano
tio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104090592A
Other languages
English (en)
Inventor
费近峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUJIANG MINGFENG POLYURETHANE PRODUCT CO Ltd
Original Assignee
WUJIANG MINGFENG POLYURETHANE PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG MINGFENG POLYURETHANE PRODUCT CO Ltd filed Critical WUJIANG MINGFENG POLYURETHANE PRODUCT CO Ltd
Priority to CN2011104090592A priority Critical patent/CN102516701A/zh
Publication of CN102516701A publication Critical patent/CN102516701A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种纳米TiO2增强的ABS料，其特征在于包括以重量份计的以下组份：ABS料100份、外润滑剂硬脂酸镁0.5-1.5份、内润滑剂EBA0.1-1.0份、氯化聚乙烯1-5份、滑石粉0.5-1.5份、抗紫外线剂1-5份、阻燃剂1-15份、改性剂10-25份、硅烷偶联剂1-30份、纳米TiO2 1-15份、微晶纤维素1-5份。本发明制得的ABS料具有优良的耐热耐候性、尺寸稳定性和耐冲击性能。主要应用于通讯器材、家用电器、汽车、电脑等部件。

Description

纳米TiO2增强的ABS料
技术领域
本发明涉及一种ABS，属于塑料领域。
背景技术
ABS(Acrylonitrile Butadiene Styrene)树脂是丙烯腈、丁二烯、苯乙烯的三种成分组成的一群耐冲击性热塑性树脂的总称。是树脂相、橡胶相的两相不均匀聚合物，树脂相的组成、橡胶相的组成以及比例、橡胶与树脂界面的相容性以及接枝率等因素都会影响树脂的性能。
发明内容
本发明所要解决的技术问题是提供一种纳米TiO2增强的ABS料。
为解决上述技术问题，本发明是这样实现的：
一种纳米TiO2增强的ABS料，其特征在于包括以重量份计的以下组份：ABS料100份、外润滑剂硬脂酸镁0.5-1.5份、内润滑剂EBA0.1-1.0份、氯化聚乙烯1-5份、滑石粉0.5-1.5份、抗紫外线剂1-5份、阻燃剂1-15份、改性剂10-25份、硅烷偶联剂1-30份、纳米TiO21-15份、微晶纤维素1-5份。
前述的纳米TiO2增强的ABS料，其特征在于包括以重量份计的以下组份：ABS料100份、外润滑剂硬脂酸镁0.5-1.5份、内润滑剂EBA 0.1-1.0份、氯化聚乙烯1-5份、滑石粉0.5-1.5份、抗紫外线剂1-4份、阻燃剂5-15份、改性剂10-15份、硅烷偶联剂5-15份、纳米TiO21-10份、微晶纤维素1-2份。
纳米TiO2增强的ABS料将所有组份混合后，干燥，挤出造粒、注射成型获得。
硅油在体系中可以降低摩擦系数，增加制品的耐磨性；但硅油与ABS料的相容性较差，滑石粉可以改善硅油在ABS树脂中的分散性，增加制品的硬度。
内外润滑剂硬脂酸镁、EBA加入可以提高材料的流动性能，但会降低力学性能；ABS中含有大量的丁二烯双键，易于被氧化，热稳定性差，抗紫外线剂可以改善ABS的耐候性；阻燃剂为氢氧化铝、三聚氰胺之任一种或两者的混合物，氢氧化铝为发烟抑制剂，与三聚氰胺混合后，其中因为两者混合后能发挥协同作用，改善了ABS料的阻燃性能，阻燃剂较佳为两者等重量的混合物；添加阻燃剂后降低了ABS料的拉伸强度和冲击强度，阻燃剂用量大于15％，拉伸强度和冲击强度下降加速，小于5％，阻燃效果有限；偶联剂可以的ABS的表面处理，改善其与其他组份的融合性能。纳米TiO2在材料的结晶过程中发挥了成核剂的作用，导致生成的晶体减小，从而提高材料的冲击强大。
本发明有以下积极的效果：本发明制得的ABS料具有优良的耐热耐候性、尺寸稳定性和耐冲击性能。主要应用于通讯器材、家用电器、汽车、电脑等部件。
具体实施方式
下面结合具体实施方式对本发明做进一步的详细说明。
本发明所采用材料均购自国药集团化学试剂有限公司。
实施例1
一种纳米TiO2增强的ABS料，包括以重量份计的以下组份：ABS料100份、硬脂酸镁0.5份、EBA0.1份、氯化聚乙烯1份、滑石粉0.5份、抗紫外线剂1份、阻燃剂1份、改性剂10份、硅烷偶联剂1份、纳米TiO25份、微晶纤维素1份。
纳米TiO2增强的ABS料将所有组份混合后，干燥，挤出造粒、注射成型获得。
实施例2
纳米TiO2增强的ABS料，包括以重量份计的以下组份：ABS料100份、硬脂酸镁1.5份、EBA 1.0份、氯化聚乙烯5份、滑石粉1.5份、抗紫外线剂4份、阻燃剂15份、改性剂15份、硅烷偶联剂15份、纳米TiO210份、微晶纤维素2份。将所有组份混合后，干燥，挤出造粒、注射成型获得。
实施例3
纳米TiO2增强的ABS料，包括以重量份计的以下组份：ABS料100份、硬脂酸镁1.0份、EBA 0.5份、氯化聚乙烯2份、滑石粉1.0份、抗紫外线剂2份、阻燃剂10份、改性剂15份、硅烷偶联剂25份、纳米TiO210份、微晶纤维素5份。将所有组份混合后，干燥，挤出造粒、注射成型获得。
实施例4
纳米TiO2增强的ABS料，包括以重量份计的以下组份：ABS料100份、硬脂酸镁1.2份、EBA 0.8份、氯化聚乙烯3份、滑石粉0.8份、抗紫外线剂3份、阻燃剂5份、改性剂12份、硅烷偶联剂8份、纳米TiO29份、微晶纤维素3份。
实施例所制备得到的纳米TiO2增强的ABS料的性能说明以及与国内同类泡沫性能的比较结果如表1所示：
表1
 实施例1  实施例2  实施例3  对照例
  密度/kg·m-3   151.2   89.3   112.3   ≤250
  拉伸强度/MPa   0.11   0.13   0.12   ≥0.15
  25％压缩强度/MPa   0.112   0.098   0.105   0.13±0.08
  断裂伸长率％   41.2   56.0   47.3   ≥20
上述具体实施方式不以任何形式限制本发明的技术方案，凡是采用等同替换或等效变换的方式所获得的技术方案均落在本发明的保护范围。

Claims (2)

1.一种纳米TiO2增强的ABS料，其特征在于包括以重量份计的以下组份：ABS料 100份、外润滑剂 硬脂酸镁 0.5-1.5份、内润滑剂EBA 0.1-1.0份、氯化聚乙烯1-5份、滑石粉0.5-1.5份、抗紫外线剂1-5份、阻燃剂 1-15份、改性剂10-25份、硅烷偶联剂1-30份、纳米TiO2  1-15份、微晶纤维素1-5份。
2.根据权利要求1所述的纳米TiO2增强的ABS料，其特征在于包括以重量份计的以下组份：ABS料 100份、外润滑剂 硬脂酸镁 0.5-1.5份、内润滑剂EBA 0.1-1.0份、氯化聚乙烯1-5份、滑石粉0.5-1.5份、抗紫外线剂1-4份、阻燃剂 5-15份、改性剂10-15份、硅烷偶联剂5-15份、纳米TiO2  1-10份、微晶纤维素1-2份。
CN2011104090592A 2011-12-12 2011-12-12 纳米TiO2增强的ABS料 Pending CN102516701A (zh)