CN102504734A - 阻燃型环保万能胶及其制备方法 - Google Patents
阻燃型环保万能胶及其制备方法 Download PDFInfo
- Publication number
- CN102504734A CN102504734A CN2011103497493A CN201110349749A CN102504734A CN 102504734 A CN102504734 A CN 102504734A CN 2011103497493 A CN2011103497493 A CN 2011103497493A CN 201110349749 A CN201110349749 A CN 201110349749A CN 102504734 A CN102504734 A CN 102504734A
- Authority
- CN
- China
- Prior art keywords
- purpose adhesive
- flame
- parts
- friendly
- sbs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种阻燃型环保万能胶及其制备方法,其由SBS、萜烯树脂、碳九树脂、松香酯、磷酸酯、氯化石蜡、三氯乙烯、二氯甲烷、1,1-二氯乙烷等制成。本发明的万能胶遇明火不燃,粘接力强,施工方便,由国家固定灭火系统和耐火构件质量监督检验中心按GB8624-2006《建筑材料及制品燃烧性能分级》检测,燃烧性能达到A1级,为非易燃易爆品,其运输时不再受到限制。
Description
技术领域
本发明涉及一种阻燃型环保万能胶及其制备方法。
技术背景
万能胶是建筑装饰行业常用的一种胶粘剂,目前国内生产万能胶时使用的材料是:SBS、萜烯树脂、碳九树脂、松香、松香酯、6号溶剂油、120号汽油、甲苯、二甲苯、二氯乙烷、醋酸乙酯、丙酮、丁酮、环己烷等等,含有多种易燃易爆组分和对人体及环境有害的组分。
目前国内万能胶的生产厂家销售方式是:经过生产厂家、省级代理、市级代理、县级代理、分销商,最后到用户手中,从生产厂家到客户手中几经周折,需多次运输,而国家对运输易燃易爆品有明文规定,必须使用运输易燃易爆品专用车,并配备安全员押运,因经销商要货量少,不能整车运输,只好走物流零担,国内百分之九十九的物流都不具备易燃易爆品专用车,一旦发生意外火灾爆炸,就会造成车毁人亡,危及人身安全。在使用中因组分的挥发也会对环境和人身健康带来危害。因此开发阻燃型环保万能胶具有重要意义。
发明内容
本发明所要解决的技术问题是提供一种运输使用安全且对环境污染小的阻燃型环保万能胶。
本发明的另一个目的是提供上述阻燃型环保万能胶的制备方法。
本发明解决上述技术问题采取的技术方案:
一种阻燃型环保万能胶,其由如下重量份的组分制成:
SBS 13-14份
萜烯树脂 7-10份
碳九树脂 8-10份
松香酯 9-12份
磷酸酯 3-8份
氯化石蜡 5-8份
三氯乙烯 20- 25份
二氯甲烷 10-15份
1,1-二氯乙烷 20-25份。
制备上述万能胶的方法,其具体步骤如下:
(1)按比例称取各组分;
(2)将三氯乙烯、二氯甲烷和1,1-二氯乙烷20-25℃下加入封闭式反应釜,然后加入SBS,于1400转/分钟高速分散1小时使SBS溶解;
(3)加入萜烯树脂、碳九树脂和松香酯,于1400转/分钟高速分散1小时使其溶解;
(4)最后加入磷酸酯和氯化石蜡,1400转/分钟高速分散1小时,使其溶解即可。
本发明采用上述技术方案取得的有益效果:本发明的万能胶遇明火不燃,粘接力强,施工方便,由国家固定灭火系统和耐火构件质量监督检验中心按GB8624-2006《建筑材料及制品燃烧性能分级》对其进行了燃烧性能检测,检测结果见表1。
表1 检测结果汇总
由表1可见,本发明的万能胶燃烧性能达到A1级,为非易燃易爆品,其运输时不再受到限制。
本发明的万能胶没有使用苯、甲苯、二甲苯等有害溶剂,对使用人员及装修家庭的环保起到了积极作用。
具体实施方式
实施例1
一种阻燃型环保万能胶,其由如下重量份的组分制成:
SBS 13份
萜烯树脂 8份
碳九树脂 10份
松香酯 9份
三(2一氯丙基)磷酸酯 5份
氯化石蜡 8份
三氯乙烯 20份
二氯甲烷 13份
1,1-二氯乙烷 25份。
本实施例万能胶的制备方法:
(1)按比例称取各组分;
(2)将三氯乙烯、二氯甲烷和1,1-二氯乙烷于20-25℃下加入封闭式反应釜,然后加入SBS,于1400转/分钟高速分散1小时使SBS充分溶解;
(3)加入萜烯树脂、碳九树脂和松香酯,于1400转/分钟高速分散1小时使其充分溶解;
(4)最后加入三(2-氯丙基)磷酸酯和氯化石蜡,1400转/分钟高速分散1小时,使其完全溶解即可。
实施例2
一种阻燃型环保万能胶,其由如下重量份的组分制成:
SBS 14份
萜烯树脂 7份
碳九树脂 9份
松香酯 12份
磷酸三辛酯 3份
氯化石蜡 7份
三氯乙烯 25份
二氯甲烷 10份
1,1-二氯乙烷 23份。
本实施例万能胶的制备方法:
(1)按比例称取各组分;
(2)将三氯乙烯、二氯甲烷和1,1-二氯乙烷于20-25℃下加入封闭式反应釜,然后加入SBS,于1400转/分钟高速分散1小时使SBS充分溶解;
(3)加入萜烯树脂、碳九树脂和松香酯,于1400转/分钟高速分散1小时使其充分溶解;
(4)最后加入磷酸三辛酯和氯化石蜡,1400转/分钟高速分散1小时,使其完全溶解即可。
实施例3
一种阻燃型环保万能胶,其由如下重量份的组分制成:
SBS 13份
萜烯树脂 10份
碳九树脂 8份
松香酯 10份
四(2-氯乙基)亚乙基二磷酸酯 8份
氯化石蜡 5份
三氯乙烯 22份
二氯甲烷 15份
1,1-二氯乙烷 20份。
本实施例万能胶的制备方法:
(1)按比例称取各组分;
(2)将三氯乙烯、二氯甲烷和1,1-二氯乙烷于常温20-25℃下加入封闭式反应釜,然后加入SBS,于1400转/分钟高速分散1小时使SBS充分溶解;
(3)加入萜烯树脂、碳九树脂和松香酯,于1400转/分钟高速分散1小时使其充分溶解;
(4)最后加入四(2-氯乙基)亚乙基二磷酸酯和氯化石蜡,1400转/分钟高速分散1小时,使其完全溶解即可。
Claims (2)
1.一种阻燃型环保万能胶,其特征在于其由如下重量份的组分制成:
SBS 13-14份
萜烯树脂 7-10份
碳九树脂 8-10份
松香酯 9-12份
磷酸酯 3-8份
氯化石蜡 5-8份
三氯乙烯 20- 25份
二氯甲烷 10-15份
1,1-二氯乙烷 20-25份。
2.一种制备权利要求1所述万能胶的方法,其特征在于其具体步骤如下:
(1)按比例称取各组分;
(2)将三氯乙烯、二氯甲烷和1,1-二氯乙烷20-25℃下加入封闭式反应釜,然后加入SBS,于1400转/分钟高速分散1小时使SBS溶解;
(3)加入萜烯树脂、碳九树脂和松香酯,于1400转/分钟高速分散1小时使其溶解;
(4)最后加入磷酸酯和氯化石蜡,1400转/分钟高速分散1小时,使其溶解即可。