CN102504728B - 一种建筑用速溶胶粉 - Google Patents
一种建筑用速溶胶粉 Download PDFInfo
- Publication number
- CN102504728B CN102504728B CN201110351629.7A CN201110351629A CN102504728B CN 102504728 B CN102504728 B CN 102504728B CN 201110351629 A CN201110351629 A CN 201110351629A CN 102504728 B CN102504728 B CN 102504728B
- Authority
- CN
- China
- Prior art keywords
- powder
- weight percent
- building
- glue powder
- dissolving glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种高强度、高耐水性、高粘度的高分子建筑用速溶胶粉。其包含瓜尔胶粉、聚氧化乙烯、高吸附树脂、憎水有机硅粉末和苯乙烯塑胶粉末，将上述组分按比例混合均匀后即可得到本发明所提供的建筑用胶粉，该胶粉具有高强度、高耐水性、高粘度，不含有害物质，便于运输存储等优点，可广泛用于建筑保温砂浆、粘结砂浆、抹面砂浆、内外墙腻子、涂料等。
Description
技术领域
本发明涉及一种建筑粘结材料，特别涉及一种用于砂浆、涂料或腻子的高强度高耐水高粘度多功能的速溶胶粉。
背景技术
在建筑领域，进行粘贴瓷砖时通常使用水泥砂浆，为了提高基层和瓷砖层之间的粘结强度，通常在水泥砂浆中掺加占水泥质量10-20％的107胶(聚乙烯醇缩甲醛)，然而采用这样传统的方法所配置的水泥砂浆或水泥浆粘结强度较低，收缩率大，耐温性、耐水性和抗冻性差，往往施工后不久，墙地砖就会出现开裂。脱落等现象。另外在室内外墙面的采用的涂料中，也使用107胶或308胶做粘合剂，这种粘合剂为稀乳状，加工运输仓储都非常不便利，成本高。且由于其中含甲醛，对人体危害巨大，特别不适用于内墙涂料。因此，就需要有一种粘结力强，耐水性强的粘合剂，同时该粘合剂还应该成本低，方便运输。
发明内容
本发明一个目的是提供一种高强度、高耐水性、高粘度的速溶胶粉。所述胶粉由瓜尔胶粉、聚氧化乙烯、高吸附树脂、憎水有机硅粉盒苯乙烯塑胶粉末混合而成。
本发明的另一个目的是提供一种高强度的建筑砂浆，所述砂浆包含上述的速溶胶粉。
本发明还可以提供一种建筑涂料，该涂料含有上述的速溶胶粉。
本发明采用的技术方案是：
一种高轻度速溶胶粉，包含下列组分：
瓜尔胶粉，10-20％重量百分比；
聚氧化乙烯，5-10％重量百分比；
高吸附树脂，15-25％重量百分比；
憎水有机硅粉末，20-30％重量百分；
苯乙烯塑胶粉末，30-40％重量百分比。
优选得，各组分的较佳含量：
瓜尔胶粉，12-16％重量百分比；
聚氧化乙烯，7-9％重量百分比；
高吸附树脂，18-22％重量百分比；
憎水有机硅粉末，22-26％重量百分。
苯乙烯塑胶粉末，32-36％重量百分比；
更进一步，各组分的最佳含量为：
瓜尔胶粉，14％重量百分比；
聚氧化乙烯，8％重量百分比；
高吸附树脂，20％重量百分比；
憎水有机硅粉末，24％重量百分比；
苯乙烯塑胶粉末，34％重量百分比。
将上述成分按重量比称取，混合均匀后即可得本发明所要保护的产品。
瓜尔胶是由天然瓜尔豆改性而成的一种性能较为特殊的植物胶，是一种半乳甘露聚糖结构。该胶具有以下特点；比较容易溶于水，PH值对瓜尔胶的性能基本上没有影响；在砂浆中使用瓜尔胶具有更高的施工性能，且对砂浆的凝结时间强度没有不利影响；瓜尔胶赋予砂浆更好的抗垂挂性、触变性和施工的滑爽性。
聚氧化乙烯(Polyethylene oxide)又称聚环氧乙烷，是一种具有水溶性和热塑性的非离子型线性高分子聚合物，它能够提高砂浆的抗流挂性并且能够增强砂浆的柔性。
高吸附树脂是近年来国内外广泛应用的一种高吸附高分子材料，它以吸附为特点，具有多孔立体结构，是近来高分子领域发展起来的一种多孔性树脂，由二乙烯苯等单体在甲苯等有机溶剂存在下，通过悬浮共聚法制得的鱼籽样小圆球。它使胶粉具有优异的保水性，提高施工性，延长胶粉的开放时间。
在胶粉中掺加憎水有机硅粉末能够使胶粉具有优异的憎水耐水性。
苯乙烯塑胶粉末能够使提高砂浆等的粘结力，提高砂浆的强度。
将上述组分按重量比混合后可得本发明所要求保护的胶粉，该胶粉为粉末状，在水中可以溶解。用编织袋加装内封包装后可以十分方便的运输仓储，经试验检测，该胶粉溶解后粘度、低温稳定性、附着力，干燥时间，粘接强度都符合国家标准。使用时，将本产品作为粘合剂与水泥涂料等按比例充分混合，即可得到性能优异的水泥砂浆、腻子或涂料。
与现有技术相比，本发明的胶粉具有如下优点：
1、高强度，高耐水性，高粘度；
2、比行业规定的乳胶粉同量条件下用量少，成本可以降低20％以上
3、不含有害物质，用在涂料中时对人体无害；
4、制成的砂浆粘结强度高、抗裂性强、干缩小且耐候性优良；
5、便于运输，便于储存。
此高分子高粘度多功能速溶胶粉可以广泛用于建筑保温砂浆、粘结砂浆、抹面砂浆、内外墙腻子、涂料等。
具体实施方式
实施例1：称取如下重量的组分：瓜尔胶粉10kg，聚氧化乙烯5kg，高吸附树脂15kg，憎水有机硅粉末30kg，苯乙烯塑胶粉末40kg，将上列组分均匀物理混合，即得100kg的胶粉。
实施例2：称取如下重量的组分：瓜尔胶粉12kg，聚氧化乙烯7kg，高吸附树脂18kg，憎水有机硅粉末25kg，苯乙烯塑胶粉末36kg，将上列组分均匀物理混合，即得100kg的胶粉。
实施例3：称取如下重量的组分：瓜尔胶粉14kg，聚氧化乙烯8kg，高吸附树脂20kg，憎水有机硅粉末24kg，苯乙烯塑胶粉末34kg，将上列组分均匀物理混合，即得100kg的胶粉。
实施例4：称取如下重量的组分：瓜尔胶粉16kg，聚氧化乙烯9kg，高吸附树脂21kg，憎水有机硅粉末22kg，苯乙烯塑胶粉末32kg，将上列组分均匀物理混合，即得100kg的胶粉。
实施例5：称取如下重量的组分：瓜尔胶粉18kg，聚氧化乙烯7kg，高吸附树脂25kg，憎水有机硅粉末20kg，苯乙烯塑胶粉末30kg，将上列组分均匀物理混合，即得100kg的胶粉。
实施例6：称取如下重量的组分：瓜尔胶粉20kg，聚氧化乙烯10kg，高吸附树脂20kg，憎水有机硅粉末20kg，苯乙烯塑胶粉末30kg，将上列组分均匀物理混合，即得100kg的胶粉。
在使用时根据需要将上述实施例中得到的胶粉添加到砂浆或涂料中，混合均匀后即可以使用。
Claims (6)
1.一种建筑用速溶胶粉，其特征在于，包含如下组分：
瓜尔胶粉，10-20％重量百分比；
聚氧化乙烯，5-10％重量百分比；
高吸附树脂，15-25％重量百分比；
憎水有机硅粉末，20-30％重量百分比；
苯乙烯塑胶粉末，30-40％重量百分比。
2.根据权利要求1所述的建筑用速溶胶粉，其特征在于所含的组分为：
瓜尔胶粉，12-16％重量百分比；
聚氧化乙烯，7-9％重量百分比；
高吸附树脂，18-22％重量百分比；
憎水有机硅粉末，22-26％重量百分比 ；
苯乙烯塑胶粉末，32-36％重量百分比 。
3.根据权利要求2所述的建筑用速溶胶粉，其特征在于所含的组分为：
瓜尔胶粉，14％重量百分比；
聚氧化乙烯，8％重量百分比；
高吸附树脂，20％重量百分比；
憎水有机硅粉末，24％重量百分比；
苯乙烯塑胶粉末，34％重量百分比。
4.一种制备权利要求1-3任一所述的建筑用速溶胶粉的方法，其特征在于，包含如下步骤：
a.按前述重量比称取各组分；
b.将称取好的各组分物理混合均匀即得需要的建筑用胶粉。
5.一种建筑砂浆，其特征在于包含权利要求1-3任一所述的建筑用速溶胶粉。
6.一种建筑用墙面涂料，其特征在于包含权利要求1-3任一所述的建筑用速溶胶粉。