CN102504655B - External wall temperature-change-resistant anti-oxidation color paint for factory - Google Patents
External wall temperature-change-resistant anti-oxidation color paint for factory Download PDFInfo
- Publication number
- CN102504655B CN102504655B CN201110366929.2A CN201110366929A CN102504655B CN 102504655 B CN102504655 B CN 102504655B CN 201110366929 A CN201110366929 A CN 201110366929A CN 102504655 B CN102504655 B CN 102504655B
- Authority
- CN
- China
- Prior art keywords
- percent
- paint
- factory
- change
- external wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses external wall temperature-change-resistant anti-oxidation color paint for a factory. The paint consists of the following ingredients in percentage by weights: 40 to 50 percent of polymer emulsion of styrene-acrylate copolymers, 5 to 8 percent of PbMoO4 pigments, 10 to 15 percent of phase change wax micro capsules, 6 to 8 percent of cobalt blue, 1 to 2 percent of dispersing agents, 10 to 20 percent of flaky aluminum powder and the balance water. The paint has the advantages that the application is wide, the paint can be used for anti-corrosion and erosion resistance and can be used at a certain temperature, the cost is low, and the paint is suitable for being used in different regions.
Description
Technical field
The present invention relates to a kind of coating, particularly relate to coating anticorrosion, anti-corrosion, resistance to certain temperature.
Background technology
Along with national economy and high-tech development, except universal, day by day urgent to the demand of speciality coating to the requirement of coating.In protective system, peroxide ethene coating, epoxypaint, oxygen sulfonated polyethylene coating etc. are all held concurrently or exist, but respectively have deficiency.Peroxide ethene coating came out at the beginning of the seventies, and this coating has certain preservative activity, but due to larger molecular weight, levelling property is undesirable, solid content is low, generally only has 14～18%, paint film density difference, and viscosity is also very low, only have 20～50 seconds, its sticking power is also bad, and paint film easily comes off.
In numerous functional paints, thermal insulation coatings is a kind of important hot functional paint, and its effect is that the object temperature change that various factors is caused is controlled, and object is had to overheated, cold provide protection excessively, has energy-saving and cost-reducing effect.At present thermal insulation coatings mainly adopt regulate coating absorption/radiation ratio, increase the mechanism such as thermal resistance and infrared radiation cooling and the pattern of coating, but exist in actual use overweight coating, temperature control effect be subject to the impact of atmosphere and dust, to the equal shortcoming of the temperature control effect of different-waveband.For the problems referred to above, people actively seek the thermal insulation coatings based on other mechanism and pattern.
Summary of the invention
For the deficiencies in the prior art, one of object of the present invention is to provide a kind of corrosion resistant coating, and it can protect the chemical resistance of general structure part in factory;
Another object of the present invention is to provide a kind of thermal insulation coatings, effectively solve factory heat up in summer too fast, the too fast problem of lowering the temperature winter, save energy, improves factory comfort level, is conducive to produce;
Three of object of the present invention is to improve the over-all properties of coating system, finds by research, and part pigment is reactive colors, with the process of emulsion film forming in, can there is part surface affine, Ligature, be conducive to improve the overall performance of film, that especially find is cobalt blue (CoAl
2o
3) can occur effectively to link with the polymer emulsion of styrene-propene acid copolymer, further improve film forming properties.
According to aforementioned object and other content, concrete coating of the present invention is composed as follows:
A kind of external wall temperature-change-resistant anti-oxidation color paint for factory, is made up of the component of following weight percent:
The polymer emulsion 40-50% of styrene-propene acid copolymer,
Flake aluminum 10-20%,
PbMoO
4pigment 5-8%,
Phase change paraffin microcapsule 10-15%
Cobalt blue 6-8%,
Dispersion agent 1-2%,
Surplus is water
The polymer emulsion of described styrene-propene acid copolymer, its solid content is 60%;
Described flake aluminum, its particle diameter is 100-240nm, more even in this particle size range, intensive, laminate structure is obvious, is conducive to stop the direct infiltration of corrosive medium.
Embodiment
Embodiment mono-
The polymer emulsion 50% of styrene-propene acid copolymer,
Flake aluminum 10%,
PbMoO
4pigment 5%,
Phase change paraffin microcapsule 15%
Cobalt blue 6%,
Dispersion agent 2%,
Surplus is water.
Embodiment 2:
The polymer emulsion 45% of styrene-propene acid copolymer,
Flake aluminum 15%,
PbMoO
4pigment 7%,
Phase change paraffin microcapsule 13%
Cobalt blue 8%,
Dispersion agent 1%,
Surplus is water.
By on above-mentioned coating coating and industrial building, compared with general ordinary plant coating, in factory, temperature reduces 3-5 degree Celsius, and factory building steel component has no corrosion, and coating integrity is good.
Coating of the present invention, has outstanding antiseptic property, also has temperature-control performance, especially cobalt blue simultaneously and has more promoted above performance with coordinating of emulsion, higher than independent any function, has a wide range of applications.
Applicant's statement, the present invention illustrates detailed process equipment and process flow process of the present invention by above-described embodiment, but the present invention is not limited to above-mentioned detailed process equipment and process flow process, do not mean that the present invention must rely on above-mentioned detailed process equipment and process flow process and could implement.Person of ordinary skill in the field should understand, any improvement in the present invention, and the selections of the equivalence replacement to the each raw material of product of the present invention and the interpolation of ancillary component, concrete mode etc., within all dropping on protection scope of the present invention and open scope.
Claims (2)
1. an external wall temperature-change-resistant anti-oxidation color paint for factory, is made up of the component of following weight percent:
The polymer emulsion 40-50% of styrene-propene acid copolymer,
Flake aluminum 10-20%, its particle diameter is 100-240nm,
PbMoO
4pigment 5-8%,
Phase change paraffin microcapsule 10-15%,
Cobalt blue 6-8%,
Dispersion agent 1-2%,
Surplus is water.
2. coating according to claim 1, is characterized in that, the polymer emulsion of described styrene-propene acid copolymer, and its solid content is 60%.