CN102503516A - 免烧碎石形凹凸棒河底淤泥陶粒 - Google Patents

免烧碎石形凹凸棒河底淤泥陶粒 Download PDF

Info

Publication number
CN102503516A
CN102503516A CN2011103523638A CN201110352363A CN102503516A CN 102503516 A CN102503516 A CN 102503516A CN 2011103523638 A CN2011103523638 A CN 2011103523638A CN 201110352363 A CN201110352363 A CN 201110352363A CN 102503516 A CN102503516 A CN 102503516A
Authority
CN
China
Prior art keywords
ceramsite
irregularly
attapulgite
bed
silt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011103523638A
Other languages
English (en)
Other versions
CN102503516B (zh
Inventor
许庆华
金白云
徐志伟
许盛英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Haode Anti-Corrosion Equipment Co., Ltd.
Original Assignee
许庆华
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 许庆华 filed Critical 许庆华
Priority to CN2011103523638A priority Critical patent/CN102503516B/zh
Publication of CN102503516A publication Critical patent/CN102503516A/zh
Application granted granted Critical
Publication of CN102503516B publication Critical patent/CN102503516B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种免烧碎石形凹凸棒河底淤泥陶粒，其技术方案的要点是，免烧碎石形凹凸棒河底淤泥陶粒由高粘凹凸棒石粘土粉、凹凸棒石粘土尾矿粉、膨润土尾矿粉、河底淤泥、水泥和膨胀珍珠岩粉组成。将免烧碎石形凹凸棒河底淤泥陶粒的配料经过混合、造粒、养护、粉碎和筛分后包装为免烧碎石形凹凸棒河底淤泥陶粒。免烧碎石形凹凸棒河底淤泥陶粒为不规则形状的颗粒，颗粒内部有细微气孔，是一种强度高、导热系数低、化学稳定性好、耐久性和保温隔音性能好的建筑陶粒。综合利用河底淤泥和尾矿生产免烧碎石形凹凸棒河底淤泥陶粒，有利于提高资源利用率，变废为宝，保护环境，免烧碎石形凹凸棒河底淤泥陶粒适用于生产混凝土保温砌块和保温隔音材料。

Description

免烧碎石形凹凸棒河底淤泥陶粒
技术领域
本发明涉及陶粒，具体涉及一种免烧碎石形凹凸棒河底淤泥陶粒。
背景技术
我国为治理景观水体水质恶化而采取的疏浚工程产生的疏浚河底淤泥量日益增加，由于河底淤泥含水率大于75％，组成成分复杂，容易产生二次污染，处置不当将对环境造成极为不利的影响，因而对疏浚河底淤泥的处理和处置就成了人们普遍关注的问题。
河底淤泥的可塑性较好，有利于生产凹凸棒河底淤泥陶粒，但是河底淤泥含水率较大，通常降低河底淤泥含水率的方法是进行浓缩和干化处理，需要消耗大量的能源，直接影响到河底淤泥陶粒的生产成本和质量。
我国矿产资源80％为共伴生矿，大量有价值资源存留于尾矿之中，尾矿堆存需要占用大量土地。很多尾矿库超期或超负荷使用，甚至违规操作，使尾矿库存在极大安全隐患，对周边地区人民的财产和生命安全造成严重威胁。
发明内容
本发明的目的是克服现有技术中不足之处，提供一种免烧碎石形凹凸棒河底淤泥陶粒。
免烧碎石形凹凸棒河底淤泥陶粒由高粘凹凸棒石粘土粉、凹凸棒石粘土尾矿粉、膨润土尾矿粉、河底淤泥、水泥和膨胀珍珠岩粉组成。
免烧碎石形凹凸棒河底淤泥陶粒的生产方法：将免烧碎石形凹凸棒河底淤泥陶粒的配料经过混合、造粒、养护、粉碎和筛分后包装为免烧碎石形凹凸棒河底淤泥陶粒。
凹凸棒石粘土是一种层链状结构的含水富镁铝硅酸盐粘土矿物，凹凸棒石粘土土质细腻，吸水性强，湿时具粘性和可塑性，有利于原料之间的粘结，能提高免烧碎石形凹凸棒河底淤泥陶粒砂的颗粒强度、附着力和孔隙率。
高粘凹凸棒石粘土粉是指取28.0g凹凸棒石粘土粉试样，加入高速搅拌机的悬浮液杯中，再加入372g水，将悬浮液杯置于高速搅拌机上，在11000转/分钟的转速下搅拌20分钟，再将经过高速搅拌试样悬浮液倒入250ml的烧杯中，使用NDJ-1型旋转粘度计进行测试其悬浮液的粘度，测试粘度值≥2200 mPa·s的凹凸棒石粘土粉为高粘凹凸棒石粘土粉，本发明选用的高粘凹凸棒石粘土粉颗粒细度≤0.074毫米。
膨润土吸水性强，具有可塑性和黏结性，用于本发明能提高免烧碎石形凹凸棒河底淤泥陶粒的颗粒强度。
凹凸棒石粘土和膨润土在开采过程中会混杂有一定量的碎石和泥土，无法进行筛分，作为一种尾矿抛弃，造成大量的资源浪费，本发明将凹凸棒石粘土尾矿和膨润土尾矿分别粉碎为尾矿粉，颗粒细度≤0.15毫米。
河底淤泥含水率大于75％，很难进行干燥处理，由于河底淤泥可塑性较好，将高粘凹凸棒石粘土粉、凹凸棒石粘土尾矿粉、膨润土尾矿粉、水泥、膨胀珍珠岩粉和河底淤泥混合后，混合物的含水量可以快速下降到20％以下，本发明选用的河底淤泥颗粒细度≤0.15毫米。
本发明采用水泥标号≥42.5的普通硅酸盐水泥。
膨胀珍珠岩颗粒呈白色或浅灰色，内部含有蜂窝状结构，用于制作绝热、吸音、防火等制品，本发明选用的膨胀珍珠岩粉颗粒细度≤0.15毫米。
本发明通过下述技术方案予以实现：
1、免烧碎石形凹凸棒河底淤泥陶粒的配料按重量百分比由下列组分组成：高粘凹凸棒石粘土粉1～10％、凹凸棒石粘土尾矿粉5～25％、膨润土尾矿粉5～20％、河底淤泥45～65％、水泥5～20％和膨胀珍珠岩粉1～10％。
2、免烧碎石形凹凸棒河底淤泥陶粒的生产方法：⑴将免烧碎石形凹凸棒河底淤泥陶粒的配料加入搅拌机中混合后输入挤压造粒机造粒，颗粒直径控制在10～25毫米，颗粒长度控制在20～40毫米；⑵将造粒后的颗粒运到混凝土养护室内进行水泥制品的常规养护28天；⑶将养护后的颗粒输入破碎机中粉碎为碎石形颗粒并进行筛分，颗粒细度控制在1～10毫米，包装为免烧碎石形凹凸棒河底淤泥陶粒。
筛分是为了除去免烧碎石形凹凸棒河底淤泥陶粒在养护和粉碎过程中产生的碎屑。
使用免烧碎石形凹凸棒河底淤泥陶粒的生产方法生产陶粒，具有速度快、成品率高、产量大、养护方法简单、生产成本低廉和易于推广应用的特点。
免烧碎石形凹凸棒河底淤泥陶粒为不规则形状的颗粒，颗粒内部有细微气孔，是一种强度高、导热系数低、化学稳定性好、耐久性和保温隔音性能好的建筑陶粒。
本发明综合利用河底淤泥和尾矿生产免烧碎石形凹凸棒河底淤泥陶粒，有利于提高资源利用率，变废为宝，还能减少占用土地，保护环境和净化环境，可谓一举多得。
免烧碎石形凹凸棒河底淤泥陶粒适用于生产混凝土保温砌块和保温隔音材料。
具体实施方式
下面结合实施例对本发明作进一步的描述： 
1、免烧碎石形凹凸棒河底淤泥陶粒的配料按重量百分比由下列组分组成：高粘凹凸棒石粘土粉3％、凹凸棒石粘土尾矿粉18％、膨润土尾矿粉10％、河底淤泥50％、水泥15％和膨胀珍珠岩粉4％。
2、免烧碎石形凹凸棒河底淤泥陶粒的生产方法：⑴将免烧碎石形凹凸棒河底淤泥陶粒的配料加入搅拌机中混合后输入挤压造粒机造粒，颗粒直径控制在15毫米，颗粒长度控制在30～40毫米；⑵将造粒后的颗粒运到混凝土养护室内进行水泥制品的常规养护28天；⑶将养护后的颗粒输入破碎机中粉碎为碎石形颗粒并进行筛分，颗粒细度控制在2～5毫米，包装为免烧碎石形凹凸棒河底淤泥陶粒。

Claims (1)

1.一种免烧碎石形凹凸棒河底淤泥陶粒，其特征在于，免烧碎石形凹凸棒河底淤泥陶粒的配料按重量百分比由下列组分组成：高粘凹凸棒石粘土粉1～10％、凹凸棒石粘土尾矿粉5～25％、膨润土尾矿粉5～20％、河底淤泥45～65％、水泥5～20％和膨胀珍珠岩粉1～10％；
所述免烧碎石形凹凸棒河底淤泥陶粒的生产方法：⑴将免烧碎石形凹凸棒河底淤泥陶粒的配料加入搅拌机中混合后输入挤压造粒机造粒，颗粒直径控制在10～25毫米，颗粒长度控制在20～40毫米；⑵将造粒后的颗粒运到混凝土养护室内进行水泥制品的常规养护28天；⑶将养护后的颗粒输入破碎机中粉碎为碎石形颗粒并进行筛分，颗粒细度控制在1～10毫米，包装为免烧碎石形凹凸棒河底淤泥陶粒。
CN2011103523638A 2011-11-10 2011-11-10 免烧碎石形凹凸棒河底淤泥陶粒 Active CN102503516B (zh)