CN102492962A - 一种碲电解液的配制方法 - Google Patents

一种碲电解液的配制方法 Download PDF

Info

Publication number
CN102492962A
CN102492962A CN2011104461446A CN201110446144A CN102492962A CN 102492962 A CN102492962 A CN 102492962A CN 2011104461446 A CN2011104461446 A CN 2011104461446A CN 201110446144 A CN201110446144 A CN 201110446144A CN 102492962 A CN102492962 A CN 102492962A
Authority
CN
China
Prior art keywords
tellurium
sodium hydroxide
electrolytic solution
electrolyte
solid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104461446A
Other languages
English (en)
Inventor
赵科湘
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuzhou Keneng New Material Co Ltd
Original Assignee
Zhuzhou Keneng New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuzhou Keneng New Material Co Ltd filed Critical Zhuzhou Keneng New Material Co Ltd
Priority to CN2011104461446A priority Critical patent/CN102492962A/zh
Publication of CN102492962A publication Critical patent/CN102492962A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种碲电解液的配制方法。本发明的目的在于提供一种碲电解液的配制方法。本发明的特征在于以下步骤：A、在造液罐中将二氧化碲、氢氧化钠与纯水按重量固液比1∶0.5∶5混合，加热至80℃，搅拌后使二氧化碲溶解，氢氧化钠的加入量为每公斤二氧化碲加入0.5公斤氢氧化钠，得到初始碲电解液；B、将步骤A得到的初始碲电解液依次加入固体草酸钠、固体碘化钾，经溶解后，即制得最终碲电解液。所述的二氧化碲的纯度为99.99％。所述的氢氧化钠的纯度为99.99％。本发明主要用作配制生产99.995％以上高纯碲的电解液。

Description

一种碲电解液的配制方法
技术领域
本发明涉及一种电解液的配制方法，尤其涉及一种碲电解液的配制方法。
背景技术
碲消费量的80％是在冶金工业中应用：钢和铜合金加入少量碲，能改善其切削加工性能并增加硬度；在白口铸铁中碲被用作碳化物稳定剂，使表面坚固耐磨；含少量碲的铅，可提高材料的耐蚀性、耐磨性和强度，用作海底电缆的护套；铅中加入碲能增加铅的硬度，用来制作电池极板和印刷铅字。碲可用作石油裂解催化剂的添加剂以及制取乙二醇的催化剂。氧化碲用作玻璃的着色剂。高纯碲可作温差电材料的合金组分。碲化铋为良好的制冷材料。碲和若干碲化物是半导体材料。超纯碲单晶是新型的红外材料。
碲主要用来添加到钢材中以增加延性，电镀液中的光亮剂、石油裂化的催化剂、玻璃着色材料，以及添加到铅中增加它的强度和耐蚀性。碲和它的化合物又是一种半导体材料。。
从98％粗碲提纯到99.99％碲的过程主要是电解，而电解液的杂质含量是电解过程是否能产出合格产品的关键。由于粗碲电解过程中阳极所含的杂质元素如Se、Pb等容易在电解液中累积，造成电解阴极析出物杂质含量高而导致产品不合格。现有的电解液配方主要是加入了氢氧化钠，提高溶液的导电性，同时提高氢氧根的过电位，但是电位接近的难以去除，并且导致杂质在电解液中富集，需重新配制新电解液，而配制新的电解液所需时间长且费用高。
发明内容
本发明的目的在于提供一种碲电解液的配制方法，以解决上述问题。
为实现上述目的，本发明的技术解决方案是：一种碲电解液的配制方法，其特征在于以下步骤：
A、在造液罐中将二氧化碲、氢氧化钠与纯水按重量固液比1∶0.5∶5混合，加热至80℃，搅拌后使二氧化碲溶解，氢氧化钠的加入量为每公斤二氧化碲加入0.5公斤氢氧化钠，得到初始碲电解液；
B、将步骤A得到的初始碲电解液依次加入固体草酸钠、固体碘化钾，经溶解后，即制得最终碲电解液。
所述的二氧化碲的纯度为99.99％。
所述的氢氧化钠的纯度为99.99％。
本发明的有益效果是：本发明具有电解生产时电解液中残留杂质低，碲电解液使用时间长，电解液中碲损失小，成品中杂质含量低的优点，适用生产需要。
生产30天后本发明的电解液与老配方电解液的比较
Figure BDA0000125832500000021
具体实施方式
下面结合实施例对本发明及其具体实施方式作进一步详细说明。
本发明的特征在于以下步骤：
A、在造液罐中将二氧化碲、氢氧化钠与纯水按重量固液比1∶0.5∶5混合，加热至80℃，搅拌后使二氧化碲溶解，氢氧化钠的加入量为每公斤二氧化碲加入0.5公斤氢氧化钠，得到初始碲电解液；
B、将步骤A得到的初始碲电解液依次加入固体草酸钠、固体碘化钾，经溶解后，即制得最终碲电解液。
所述的二氧化碲的纯度为99.99％。
所述的氢氧化钠纯度为99.99％。
以下给出本发明的实施例：
实例1
将纯度为99.99％的二氧化碲1000克加纯度为99.99％的氢氧化钠500克，再加入纯水5kg，在容器中80℃下溶解后，得到浓度为200克/升的初始碲电解液；然后，依次加入固体草酸钠200克、固体碘化钾20克、溶解后即得最终的碲电解液。
实例2
将纯度为99.99％的二氧化碲500克加纯度为99.99％的氢氧化钠250克，再加入纯水2.5kg，在容器中80℃下溶解后，得到浓度为200克/升的初始碲电解液；然后，依次加入固体草酸钠100克、固体碘化钾10克、溶解后即得最终的碲电解液。其余同实例1。
实例3
将纯度为99.99％的二氧化碲250克加纯度为99.99％的氢氧化钠125克，再加入纯水1.25kg，在容器中80℃下溶解后，得到浓度为200克/升的初始碲电解液；然后，依次加入固体草酸钠50克、固体碘化钾5克、溶解后即得最终的碲电解液。其余同实例1。

Claims (3)

1.一种碲电解液的配制方法，其特征在于以下步骤：
A、在造液罐中将二氧化碲、氢氧化钠与纯水按重量固液比1∶0.5∶5混合，加热至80℃，搅拌后使二氧化碲溶解，氢氧化钠的加入量为每公斤二氧化碲加入0.5公斤氢氧化钠，得到初始碲电解液；
B、将步骤A得到的初始碲电解液依次加入固体草酸钠、固体碘化钾，经溶解后，即制得最终碲电解液。
2.按权利要求1所述的配制方法，其特征在于所述的二氧化碲的纯度为99.99％。
3.按权利要求1所述的配制方法，其特征在于所述的氢氧化钠的纯度为99.99％。
CN2011104461446A 2011-12-28 2011-12-28 一种碲电解液的配制方法 Pending CN102492962A (zh)