CN102489596B - Hot bulging method for forming rectangular titanium alloy rolled ring into special-shaped ring - Google Patents
Hot bulging method for forming rectangular titanium alloy rolled ring into special-shaped ring Download PDFInfo
- Publication number
- CN102489596B CN102489596B CN201110377628.XA CN201110377628A CN102489596B CN 102489596 B CN102489596 B CN 102489596B CN 201110377628 A CN201110377628 A CN 201110377628A CN 102489596 B CN102489596 B CN 102489596B
- Authority
- CN
- China
- Prior art keywords
- bulging
- special
- shaped ring
- time
- ring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a hot bulging method for forming a rectangular titanium alloy rolled ring into a special-shaped ring; the hot bulging method comprises the following steps of: sleeving a heated rectangular titanium alloy rolled ring at the periphery of a preheated bulging block of a bulging machine, starting the bulging machine so that the bulging block extrudes the rolled ring along the radial direction on the surface of the inner circumference of the rolled ring till the deformation amount of the rolled ring is 10%-12%, and the rolled ring is formed into a special-shaped ring blank, thereby completing primary bulging, and then leading the special-shaped ring blank to rotate by 45 degrees along a central axis to complete primary rotation; and afterwards, according to the operation, carrying out secondary bulging with 0.9%-1.5% of deformation amount and secondary rotation, third bulging with 0.9%-1.5% of deformation amount and third rotation, and fourth bulging with 0.5%-1% of deformation amount on the special-shaped ring blank, thereby obtaining the special-shaped ring. The dimensional accuracy of the special-shaped ring can reach 0.1%-0.2% of the corresponding dimension; and the special-shaped ring is mainly applied to the fields of aerospace and the like.
Description
Technical field
The present invention relates to a kind of expanding method of ring, the method that particularly to have related to titanium alloy straight-flanked ring rolled piece hot expansion forming be special-shaped ring.
Background technology
Titanium alloy straight-flanked ring rolled piece (referring to that longitudinal section is the looping mill rolling part of square-section) or special-shaped ring rolled piece (referring to that longitudinal section is the looping mill rolling part of non-rectangular cross-section) adopt after looping mill rolling, owing to being subject to the impact of rolling mill practice and equipment limitation, its dimensional accuracy is generally not high; The in the situation that only more satisfactory at ring shape of rolling piece and equipment performance being more excellent, its dimensional accuracy just can reach 3 ‰ of corresponding size～5 ‰ (3/1000ths to 5/1000ths), and the looping mill rolling part after rolling is because stress is larger, if control the even defect such as cracking of bad easy generation warpage, distortion in following process operation.
On February 18th, 2009, disclosed Chinese invention patent description CN101367104A disclosed a kind of shroud ring, this process is by peripheral hardware high-pressure pump and make the highly pressurised liquid of its generation by the passage in high pressure cylinder, then via the passage subtracting in power post in mould part, inject fixing upper prod cast and mobile lower prod cast and the enclosure space of retaining ring formation, make retaining ring that plastic deformation occur under the effect of fluid pressure and carry out bulging retaining ring, to reach strengthening retaining ring, improve the object of retaining ring forming accuracy, from this patent specification accompanying drawing, can find out that described retaining ring is rectangle ring.The method is owing to being that flexible contact by the inner peripheral surface of liquid and ring carrys out cold expanding shape rectangle ring, therefore, can only be applicable to the little material of some resistances of deformation, its Main Function is strengthening ring, for the larger material of resistance of deformation titanium alloy and become special-shaped ring inapplicable rectangle ring bulging for example; And the method is for the also disclosure in detail of dimensional accuracy how to improve ring by bulging, just broadly draw and can reach the object that improves retaining ring forming accuracy, the method can not solve the low problem of looping mill rolling part dimensional accuracy existing in prior art.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of bulging piece that adopts and realizes the method that the hot expansion forming of titanium alloy straight-flanked ring rolled piece is special-shaped ring, the method is carried out bulging by a large deformation and continuous three small deformations to described titanium alloy straight-flanked ring rolled piece, has obtained the high bulging abnormity ring of dimensional accuracy.
For solving the problems of the technologies described above, the method that the hot expansion forming of titanium alloy straight-flanked ring rolled piece of the present invention is special-shaped ring, its technical scheme comprises the following steps:
Shape expanding machine is provided, and this shape expanding machine is mainly comprised of mandrel slide block, radial slider, bulging piece, workbench and guide rail; Described mandrel slide block is conical and is sleeved in radial slider and coordinates with the taper inner peripheral surface of radial slider, and can in radial slider, move up and down vertically extruding radial slide block; Described radial slider is 12 secter pats that separate, and is arranged on the guide rail of shape expanding machine and can radially moves around along guide rail, is installed with respectively bulging piece on the outer circumference surface of each secter pat, forms a toroidal when each secter pat closes up together with bulging piece; When described mandrel slide block moves down vertically in described radial slider, can make each radial slider radially synchronizing moving diffusion make bulging piece reach the object of bulging ring, when described mandrel slide block moves up vertically in radial slider shape expanding machine can drive each radial slider radially synchronizing moving close up and make bulging piece depart from the ring after bulging; On the workbench of this shape expanding machine, can drive in addition ring deflector roll along central axis rotation on this workbench;
The titanium alloy straight-flanked ring rolled piece cover that is heated to 920 ℃～950 ℃ is put into shape expanding machine, its inner ring surface is enclosed within through being preheating to the outer circumference surface periphery of the bulging piece of 260 ℃～320 ℃, the outer circumference surface of described bulging piece has and the inner peripheral surface of the special-shaped ring of the final expansion forming consistent shape that matches, now, radial slider is in closing up state;
Starting shape expanding machine applies axial tension F to mandrel slide block and it is moved down vertically and make the radially synchronizing moving diffusion of each radial slider along the endoporus conical surface extruding radial slide block of described radial slider, the bulging piece being contained on radial slider outer circumference surface radially pushes this straight-flanked ring rolled piece from the inner circumferential surface of straight-flanked ring rolled piece, straight-flanked ring rolled piece generation dimension of inner and outer diameters expands and wall thickness reduction plastic deformation is special-shaped ring base, completes bulging for the first time; In this Bulging Process, the bulging temperature of described straight-flanked ring rolled piece is 920 ℃～950 ℃, and the bulging time is 25s～40s, and the dwell time is 20s～23s, and bulging deflection is 10%～12%;
Shape expanding machine drives mandrel slide block to move up vertically in radial slider, and drive radial slider radially synchronizing moving close up and make bulging piece depart from the special-shaped ring base after bulging, deflector roll on the workbench of startup shape expanding machine makes it drive described special-shaped ring base along 45 ° of central axis rotations, completes the rotation for the first time of special-shaped ring base;
By the operation of above-mentioned bulging for the first time, the special-shaped ring base through after bulging is for the first time carried out to bulging for the second time, in this Bulging Process, the bulging temperature of described special-shaped ring base is 900 ℃～920 ℃, the bulging time is 15s～25s, dwell time is 10s～13s, and bulging deflection is 0.9%～1.5%;
Operation by above-mentioned rotation is for the first time rotated for the second time to the special-shaped ring base through after bulging for the second time, this rotation, and described special-shaped ring base rotates 45 ° in the same way again with direction of rotation for the first time;
By the operation of above-mentioned bulging for the first time, the special-shaped ring base through after bulging is for the second time carried out to bulging for the third time, in this Bulging Process, the bulging temperature of described special-shaped ring base is 870 ℃～900 ℃, the bulging time is 15s～25s, dwell time is 10s～13s, and bulging deflection is 0.9%～1.5%;
Operation by above-mentioned rotation is for the first time rotated for the third time to the special-shaped ring base through after bulging for the second time, this rotation, and described special-shaped ring base rotates 45 ° in the same way again with direction of rotation for the first time;
By the operation of above-mentioned bulging for the first time, the special-shaped ring base through after bulging is for the third time carried out to bulging the 4th time, in this Bulging Process, the bulging temperature of described special-shaped ring base is 850 ℃～870 ℃, the bulging time is 20s～30s, dwell time is 15s～18s, and bulging deflection is 0.5%～1%;
After bulging finishes, the mandrel slide block that moves up, closes up radial slider, takes out the special-shaped ring after bulging.
The titanium alloy that the above-mentioned titanium alloy preferred material trade mark is TC4.
The axial tension F that described shape expanding machine applies mandrel slide block is calculated as follows definite:
F=ξ×σ
0.2×S
In formula:
ξ---shape expanding machine bulge coefficient, the present invention gets 1.26～1.52;
σ
0.2---the yield strength of titanium alloy material (MPa) at bulging temperature, TC4 alloy is got 270MPa～450MPa;
Longitudinal section area (the mm of S---straight-flanked ring rolled piece or special-shaped ring base
2).
The bulging size of described special-shaped ring under hot be calculative determination as follows:
D=D
0(1+β
t)+d
In formula:
The internal diameter size (mm) of D---special-shaped ring under hot;
D
0---the final products internal diameter size (mm) of special-shaped ring under cold conditions;
β
t---the temperature compensation coefficient (%) of alloy material at bulging temperature, TC4 alloy gets 0.4%～1%;
D---bulging becomes the springback capacity (mm) of internal diameter size after special-shaped ring, and TC4 alloy is got 1mm～5mm.
The special-shaped ring that adopts the method for the invention expansion forming, its internal diameter size scope is Φ 400mm～Φ 4500mm, wall thickness is 10mm～200mm, is highly 40mm～750mm.
Compared with prior art, beneficial effect of the present invention is as follows:
The present invention carries out rigidity by the bulging piece on shape expanding machine and titanium alloy straight-flanked ring rolled piece and contacts that to carry out direct expansion forming be special-shaped ring, can carry out bulging to the larger difficult wrought titanium alloy material of resistance of deformation, and can obtain needed bulging size and be conducive to improve dimensional accuracy.
The present invention is by being heated to titanium straight-flanked ring rolled piece, the aximal deformation value of employing 10%～12% is once deformed into special-shaped ring base straight-flanked ring rolled piece bulging, by three small deformation amounts, special-shaped ring base expansion forming, be special-shaped ring again, and by selecting the suitable technological parameters such as bulging temperature, bulging time and dwell time, can not make a significant impact the tissue of looping mill rolling part, there will not be spalling phenomenon, can also make the springback capacity of looping mill rolling part after each bulging or special-shaped ring base less; And pass through 45 ° of three rotating Vortexes of described special-shaped ring base in Bulging Process, the vestige that gap in the time of can eliminating bulging piece and radially spread bulging between adjacent bulging piece forms special-shaped ring base inner peripheral surface, thus be conducive to carrying out smoothly and obtaining the special-shaped ring of bulging that dimensional accuracy is higher of Bulging Process; In whole Bulging Process, because bulging piece can be measured the springback capacity of internal diameter size after the situation of change of special-shaped ring base internal diameter size and each bulging in real time, and measurement data is sent in time on the display of shape expanding machine, thereby when bulging, can accurately control the bulging size of special-shaped ring rolled piece.In sum, adopt the special-shaped ring rolled piece of the method for the invention bulging can obtain the final products size that dimensional accuracy is higher.
In Bulging Process, axial tension F mandrel slide block being applied due to shape expanding machine is the yield strength (σ by material at the bulge coefficient (ξ) of shape expanding machine, bulging temperature
0.2) and the longitudinal section area (S) of straight-flanked ring rolled piece or special-shaped ring base determine, therefore, can be for different shape expanding machines and different materials, the looping mill rolling part of size or the size that special-shaped ring base is determined axial tension F, make looping mill rolling part stressed more even more reasonable in Bulging Process, can guarantee carrying out smoothly of Bulging Process, avoid exerting oneself excessive cause spalling or exert oneself too smallly cause swollen motionless phenomenon to occur.
The hot bulging internal diameter size (D) of the special-shaped ring after described bulging is by special-shaped ring final products internal diameter size (D under cold conditions after bulging
0), the temperature compensation coefficient (β of alloy material at bulging temperature
t) and bulging become the springback capacity (d) of internal diameter size after special-shaped ring to carry out calculative determination, thereby when bulging, can accurately control the thermal state sizes of special-shaped ring, and the high cold conditions size of the cooling rear acquisition dimensional accuracy of the special-shaped ring after bulging is the final products size of special-shaped ring after bulging.
The titanium alloy bulging abnormity ring that the trade mark of take is TC4 is example, and the cold conditions size of this alloy abnormity ring after bulging is final products sizes after testing, and the dimensional accuracy of its internal diameter, wall thickness and height has reached respectively 1 ‰ of corresponding size～2 ‰; , there is not marked change in the interior tissue of this alloy abnormity ring after testing, and without defects such as distortion, warpages.
Accompanying drawing explanation
Below in conjunction with the drawings and specific embodiments, the present invention is described in further detail.
Fig. 1 is that straight-flanked ring rolled piece is along the profilograph of its center line.
Fig. 2 is the structure diagram of shape expanding machine.
Fig. 3 is the installation schematic diagram of straight-flanked ring rolled piece.
Fig. 4 is the process schematic diagram that the hot expansion forming of straight-flanked ring rolled piece is special-shaped ring.
Fig. 5 is the schematic diagram that bulging piece departs from the special-shaped ring after bulging.
Fig. 6 is that special-shaped ring after bulging is along the profilograph of its center line.
The specific embodiment
Implement the method that the hot expansion forming of titanium alloy straight-flanked ring rolled piece of the present invention is special-shaped ring the equipment such as shape expanding machine, forge furnace, manipulator need to be provided.The titanium alloy that China's material trademark of take is below TC4 describes the specific embodiment of the method in detail as example:
The main chemical elements content (percentage by weight) of this alloy is: containing Al amount 5.50～6.80%, V content 3.50～4.50%, containing Fe amount≤0.30%, C content≤0.10%, containing N amount≤0.05%, containing H amount≤0.015%, containing O amount≤0.20%, other elements add up to≤0.30, surplus is Ti.
For implement hot expanding method of the present invention shape expanding machine structure diagram as shown in Figure 2, this shape expanding machine is mainly comprised of mandrel slide block 1, radial slider 2, bulging piece 3, workbench 4 and guide rail 5.Mandrel slide block 1 is conical and is sleeved in radial slider 2 and coordinates with the taper inner peripheral surface of radial slider 2, and mandrel slide block 1 can be driven and in radial slider 2, be moved up and down vertically and extruding radial slide block 2 by the hydraulic cylinder of shape expanding machine; Radial slider 2 is arranged on the guide rail 5 of shape expanding machine and can radially moves around along guide rail 5, radial slider 2 is overlooked direction from Fig. 2 and is seen it is 12 secter pat shapes of separating, on the outer circumference surface of each secter pat, be installed with respectively bulging piece 3, when each secter pat closes up, can form a toroidal together with bulging piece 3; When mandrel slide block 1 moves down vertically in radial slider 2, can make each radial slider 2 radially synchronizing moving diffusion make bulging piece 3 reach the object of bulging ring, when mandrel slide block 1 moves up vertically in radial slider 2 shape expanding machine can drive each radial slider 2 radially synchronizing moving close up and make bulging piece 3 depart from the ring after bulgings, bulging piece 3 has real-time measurement ring internal diameter size and measurement data is sent to the function on the display of shape expanding machine in Bulging Process; In addition, on the workbench 4 of this shape expanding machine, can drive in addition ring deflector roll (not shown) along central axis rotation on this workbench.
The processing step that this alloy is special-shaped ring from the hot expansion forming of straight-flanked ring rolled piece is as follows:
Step 1: installation.
As shown in Figure 3, first the bulging piece 3 on shape expanding machine is preheating to 260 ℃～320 ℃, after TC4 alloy straight-flanked ring rolled piece 10 being more as shown in Figure 1 heated to 920 ℃～950 ℃, cover is put into shape expanding machine, make its inner ring surface be enclosed within the outer circumference surface periphery of bulging piece 3, the outer circumference surface of bulging piece 3 has and the consistent shape that matches of the inner peripheral surface of the special-shaped ring 20 of final expansion forming as shown in Figure 6, its bottom surface lie in workbench 4 above, now, radial slider 2 is in closing up state.During installation, the shipment of workpiece mainly completes by Robot actions.
Step 2: bulging for the first time.
As shown in Figure 4, starting shape expanding machine makes its mandrel slide block 1 axially move down along it, mandrel slide block 1 makes the radially synchronizing moving diffusion of each radial slider 2 along its taper surface extruding radial slide block 2 radial slider 2 is interior, the outer circumference surface of the bulging piece 3 in radial slider 2 is along the inner circumferential surface extruding straight-flanked ring rolled piece 10 of straight-flanked ring rolled piece 10, make straight-flanked ring rolled piece 10 from inner circumferential surface to external peripheral surface, be subject to the radial compression power from bulging piece 3, cause the inner peripheral surface of straight-flanked ring rolled piece 10 radially to expand, in straight-flanked ring rolled piece 10 occurs, outside dimension expands, the plastic deformation of wall thickness reduction, straight-flanked ring rolled piece 10 by bulging piece 3 for the first time bulging be deformed into special-shaped ring base 15.During bulging, the hydraulic cylinder of shape expanding machine applies axial tension F to mandrel slide block 1, and the bulging temperature of straight-flanked ring rolled piece 10 is 920 ℃～950 ℃, and the bulging time is 25s～40s, and the dwell time is 20s～23s, and the bulging deflection of straight-flanked ring rolled piece 10 is 10%～12%.
The described bulging time refers to the time after straight-flanked ring rolled piece 10 is finished to bulging by bulging from the beginning; The described dwell time refers to after straight-flanked ring rolled piece 10 is reached deflection by bulging and no longer deforms and remain to the time that bulging finishes always.
Step 3: rotation for the first time.
As shown in Figure 5, make shape expanding machine drive mandrel slide block 1 to move up vertically in radial slider 2, and drive radial slider 2 radially synchronizing moving close up and make bulging piece 3 depart from the special-shaped ring base 15 after bulgings, start deflector roll on the workbench 4 of shape expanding machine make its drive special-shaped ring base 15 on this workbench along central axis clockwise or be rotated counterclockwise 45 °, thereby complete the rotation for the first time of special-shaped ring base 15.
Step 4: bulging for the second time.
The Bulging Process of repeating step 1 makes 3 pairs of special-shaped ring bases of bulging piece 15 carry out bulging for the second time, during bulging, the hydraulic cylinder of shape expanding machine applies axial tension F to mandrel slide block 1, the bulging temperature of special-shaped ring base 15 is 900 ℃～920 ℃, the bulging time is 15s～25s, dwell time is 10s～13s, and the bulging deflection of special-shaped ring base 15 is 0.9%～1.5%.
Step 5: rotation for the second time.
Repeating step 3, makes the deflector roll driving ring rolled piece 10 of shape expanding machine and direction of rotation for the first time rotate in the same way 45 ° again, thereby completes the rotation for the second time of special-shaped ring base 15.
Step 6: bulging for the third time.
The Bulging Process of repeating step 1 makes 3 pairs of special-shaped ring bases of bulging piece 15 carry out bulging for the third time, during bulging, the hydraulic cylinder of shape expanding machine applies axial tension F to mandrel slide block 1, the bulging temperature of special-shaped ring base 15 is 870 ℃～900 ℃, the bulging time is 15s～25s, dwell time is 10s～13s, and the bulging deflection of special-shaped ring base 15 is 0.9%～1.5%.
Step 7: rotation for the third time.
Repeating step 3, makes the deflector roll of shape expanding machine drive special-shaped ring base 15 and direction of rotation for the second time to rotate in the same way 45 ° again, thereby completes the rotation for the third time of special-shaped ring base 15.
Step 6: the 4th bulging.
The Bulging Process of repeating step 1 makes 3 pairs of special-shaped ring bases of bulging piece 15 carry out the 4th bulging to make its final distortion be configured as special-shaped ring 20, during bulging, the hydraulic cylinder of shape expanding machine applies axial tension F to mandrel slide block 1, the bulging temperature of special-shaped ring base 15 is 850 ℃～870 ℃, the bulging time is 20s～30s, dwell time is 15s～18s, and the bulging deflection of special-shaped ring base 15 is 0.5%～1%.
After four times bulging finishes, the mandrel slide block 1 that moves up, closes up radial slider 2 and makes bulging piece 3 depart from special-shaped ring 20, thereby take out special-shaped ring 20 with manipulator, completes Bulging Process.
Described straight-flanked ring rolled piece 10 or special-shaped ring base 15 are in Bulging Process, and described axial tension F is calculated as follows:
F=ξ×σ
0.2×S
In formula:
ξ---shape expanding machine bulge coefficient, the present invention gets 1.26～1.52;
σ
0.2---the yield strength of titanium alloy material (MPa) at bulging temperature, the present invention gets 270MPa～450MPa;
Longitudinal section area (the mm of S---straight-flanked ring rolled piece 10 or special-shaped ring base 15
2);
The computational methods of the bulging deflection of described straight-flanked ring rolled piece 10 are: the bulging deflection=central diameter size of looping mill rolling part 10 (or special-shaped ring base 15) before [the central diameter size of straight-flanked ring rolled piece 10 (or special-shaped ring base 15) before the central diameter size-bulging of straight-flanked ring rolled piece 10 after bulging (or special-shaped ring base 15))]/bulging * 100%.
The central diameter size of described straight-flanked ring rolled piece 10 (or special-shaped ring base 15)=(outside dimension of internal diameter size+straight-flanked ring rolled piece 10 (or special-shaped ring base 15) of straight-flanked ring rolled piece 10 (or special-shaped ring base 15)) ÷ 2
For guaranteeing that straight-flanked ring rolled piece 10 can access the final size of product requirement after expansion forming abnormity ring 20, special-shaped ring 20 is calculated as follows at the bulging size under hot:
D=D
0(1+β
t)+d
In formula:
The internal diameter size (mm) of D---special-shaped ring 20 under hot;
D
0---special-shaped ring 20 is through the final products internal diameter size (mm) under cold conditions;
β
t---the temperature compensation coefficient (%) of alloy material at bulging temperature, the temperature compensation coefficient for different materials under different temperatures is different, and the present invention gets 0.4%～1%;
D---bulging becomes the springback capacity (mm) of special-shaped ring 20 rear internal diameter sizes, and the present invention gets 1mm～5mm.
Above-mentioned size is as the criterion to be out of shape maximum size when calculating, and the size while calculating for the present invention refers to the size of the big end surface bottom face of straight-flanked ring rolled piece 10 or special-shaped ring base 15
The alloy special-shaped titanium ring that adopts said method bulging, its internal diameter size scope is: Φ 400mm～Φ 4500mm, wall thickness is 10mm～200mm, is highly 40mm～750mm.
The present invention is not limited to above-mentioned special-shaped ring rolled piece 20, for the special-shaped ring rolled piece of different cross section, as long as corresponding the outer circumference surface shape of bulging piece 3 is processed into the shape consistent with the shape of the inner peripheral surface of special-shaped ring rolled piece, adopt method of the present invention just can bulging to go out the special-shaped ring rolled piece of different cross section.
Claims (5)
1. the method that the hot expansion forming of titanium alloy straight-flanked ring rolled piece is special-shaped ring, is characterized in that, comprises the following steps:
Shape expanding machine is provided, and this shape expanding machine is mainly comprised of mandrel slide block, radial slider, bulging piece, workbench and guide rail; Described mandrel slide block is conical and is sleeved in radial slider and coordinates with the taper inner peripheral surface of radial slider, and can in radial slider, move up and down vertically extruding radial slide block; Described radial slider is 12 secter pats that separate, and is arranged on the guide rail of shape expanding machine and can radially moves around along guide rail, is installed with respectively bulging piece on the outer circumference surface of each secter pat, forms a toroidal when each secter pat closes up together with bulging piece; When described mandrel slide block moves down vertically in described radial slider, can make each radial slider radially synchronizing moving diffusion make bulging piece reach the object of bulging ring, when described mandrel slide block moves up vertically in radial slider shape expanding machine can drive each radial slider radially synchronizing moving close up and make bulging piece depart from the ring after bulging; On the workbench of this shape expanding machine, can drive in addition ring deflector roll along central axis rotation on this workbench;
The titanium alloy straight-flanked ring rolled piece cover that is heated to 920 ℃～950 ℃ is put into shape expanding machine, its inner ring surface is enclosed within through being preheating to the outer circumference surface periphery of the bulging piece of 260 ℃～320 ℃, the outer circumference surface of described bulging piece has and the inner peripheral surface of the special-shaped ring of the final expansion forming consistent shape that matches, now, radial slider is in closing up state;
Starting shape expanding machine applies axial tension F to mandrel slide block and it is moved down vertically and make the radially synchronizing moving diffusion of each radial slider along the endoporus conical surface extruding radial slide block of described radial slider, the bulging piece being contained on radial slider outer circumference surface radially pushes this straight-flanked ring rolled piece from the inner circumferential surface of straight-flanked ring rolled piece, straight-flanked ring rolled piece generation dimension of inner and outer diameters expands and wall thickness reduction plastic deformation is special-shaped ring base, completes bulging for the first time; In this Bulging Process, the bulging temperature of described straight-flanked ring rolled piece is 920 ℃～950 ℃, and the bulging time is 25s～40s, and the dwell time is 20s～23s, and bulging deflection is 10%～12%;
Shape expanding machine drives mandrel slide block to move up vertically in radial slider, and drive radial slider radially synchronizing moving close up and make bulging piece depart from the special-shaped ring base after bulging, deflector roll on the workbench of startup shape expanding machine makes it drive described special-shaped ring base along 45 ° of central axis rotations, completes the rotation for the first time of special-shaped ring base;
By the operation of above-mentioned bulging for the first time, the special-shaped ring base through after bulging is for the first time carried out to bulging for the second time, in this Bulging Process, the bulging temperature of described special-shaped ring base is 900 ℃～920 ℃, the bulging time is 15s～25s, dwell time is 10s～13s, and bulging deflection is 0.9%1.5%;
Operation by above-mentioned rotation is for the first time rotated for the second time to the special-shaped ring base through after bulging for the second time, this rotation, and described special-shaped ring base rotates 45 ° in the same way again with direction of rotation for the first time;
By the operation of above-mentioned bulging for the first time, the special-shaped ring base through after bulging is for the second time carried out to bulging for the third time, in this Bulging Process, the bulging temperature of described special-shaped ring base is 870 ℃～900 ℃, the bulging time is 15s～25s, dwell time is 10s～13s, and bulging deflection is 0.9%～1.5%;
Operation by above-mentioned rotation is for the first time rotated for the third time to the special-shaped ring base through after bulging for the second time, this rotation, and described special-shaped ring base rotates 45 ° in the same way again with direction of rotation for the first time;
By the operation of above-mentioned bulging for the first time, the special-shaped ring base through after bulging is for the third time carried out to bulging the 4th time, in this Bulging Process, the bulging temperature of described special-shaped ring base is 850 ℃～870 ℃, the bulging time is 20s～30s, dwell time is 15s～18s, and bulging deflection is 0.5%～1%;
After bulging finishes, the mandrel slide block that moves up, closes up radial slider, takes out the special-shaped ring after bulging.
2. the method that the hot expansion forming of straight-flanked ring rolled piece according to claim 1 is special-shaped ring, is characterized in that: described titanium alloy is TC4.
3. the method that the hot expansion forming of straight-flanked ring rolled piece according to claim 2 is special-shaped ring, is characterized in that: the axial tension F that described shape expanding machine applies mandrel slide block is calculated as follows definite:
F=ξ×σ
0.2×S
In formula:
ξ-shape expanding machine bulge coefficient, gets 1.26～1.52;
σ
0.2the yield strength MPa of titanium alloy material at-bulging temperature, TC4 alloy is got 270MPa～450MPa;
The longitudinal section area mm of S-straight-flanked ring rolled piece or special-shaped ring base
2.
4. the method that the hot expansion forming of straight-flanked ring rolled piece according to claim 2 is special-shaped ring, is characterized in that: the bulging size of described special-shaped ring under hot be calculative determination as follows:
D=D
0(1+β
t)+d
In formula:
The internal diameter size mm of D-special-shaped ring under hot;
D
0the final products internal diameter size mm of-special-shaped ring under cold conditions;
β
tthe temperature compensation coefficient % of-alloy material at bulging temperature, TC4 alloy gets 0.4%～1%;
D-bulging becomes the springback capacity mm of internal diameter size after special-shaped ring, and TC4 alloy is got 1mm～5mm.
5. the method that the hot expansion forming of straight-flanked ring rolled piece according to claim 1 and 2 is special-shaped ring, it is characterized in that: the special-shaped ring of described expansion forming, its internal diameter size scope is Φ 400mm～Φ 4500mm, and wall thickness is 10mm～200mm, is highly 40mm～750mm.