CN102468352A - 一种高阻隔柔性背膜 - Google Patents

一种高阻隔柔性背膜 Download PDF

Info

Publication number
CN102468352A
CN102468352A CN2010105323932A CN201010532393A CN102468352A CN 102468352 A CN102468352 A CN 102468352A CN 2010105323932 A CN2010105323932 A CN 2010105323932A CN 201010532393 A CN201010532393 A CN 201010532393A CN 102468352 A CN102468352 A CN 102468352A
Authority
CN
China
Prior art keywords
film
barrier
flexible
base material
notacoria
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010105323932A
Other languages
English (en)
Inventor
彭成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHAN MEIGE ENERGY TECHNOLOGY Co Ltd
Original Assignee
WUHAN MEIGE ENERGY TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHAN MEIGE ENERGY TECHNOLOGY Co Ltd filed Critical WUHAN MEIGE ENERGY TECHNOLOGY Co Ltd
Priority to CN2010105323932A priority Critical patent/CN102468352A/zh
Publication of CN102468352A publication Critical patent/CN102468352A/zh
Pending legal-status Critical Current

Abstract

本发明提供的一种高阻隔柔性背膜，主要包括基材膜、铝箔、抗紫外线涂层、保护膜层、粘胶层。铝箔两侧通过胶黏剂分别与基材膜进行复合，抗紫外线层可直接涂覆或溅射到复合膜外侧，在抗紫外线层上直接涂覆或复合一层保护膜层，在复合膜的内侧涂覆一层粘胶层，即可得到高阻隔柔性背膜。本发明中，选用铝箔作为中间层，其具有极好的阻隔性能，可以满足新兴的以CIGS、OPV等为代表的柔性化的薄膜太阳能产品的高阻隔要求，并且能反射光线达到提高太阳能转化效率的功效；此外，本发明主要采用复合工艺制备。本发明所制得的太阳能电池背膜有着极佳的阻隔性能和机械强度，能够很好的保护太阳能电池组件；本发明以复合工艺为主，生产工艺简单，并且各原材料的生产技术成熟、成本较低。所以本发明背膜的规模化产能较高，成本远低于目前市场上同类产品，并且背膜的柔韧性优势可更好的发挥薄膜太阳能电池的柔、薄等特性。

Description

一种高阻隔柔性背膜
技术领域
本发明涉及太阳能电池领域，尤其涉及一种柔性太阳能电池封装用的高阻隔柔性背膜。
背景技术
太阳能在可再生能源行业的地位举足轻重，是一种取之不尽、用之不竭的绿色能源。利用太阳能电池将太阳能转换成电能是很有效的利用途径，太阳能电池主要由表面封装层、EVA密封层、太阳能电池片和太阳能电池背膜层复合而成；其中表面封装层和背膜层的主要作用是提高太阳能电池的整体机械强度，和对外界环境中的水、氧、腐蚀性气液体等起到阻隔作用，以防止对太阳能电池产生的破坏。由于薄膜化太阳能的诸多优势，已经得到快速发展；但通常使用的高成本多晶硅太阳能产品对水汽的阻隔要求较低，然而新兴的以CIGS、OPV等为代表的柔性化薄膜太阳能产品对封装材料的阻隔要求较高，目前普遍使用的太阳能电池封装材料难以满足阻隔指标。本发明旨在提供一种高阻隔柔性背膜技术，以满足柔性薄膜太阳能产品对封装材料的高阻隔要求，进而真正实现薄膜太阳能电池的柔韧性优势，从而更好的拓展薄膜太阳能产品的发展领域，也利于光伏产品的快速普及。
发明内容
本发明主要是针对目前新兴的以CIGS、OPV等为代表的柔性薄膜太阳能产品封装背膜存在的问题与不足，改善现有技术后提出了一种高阻隔柔性背膜。
为了实现上述目的，本发明采用的技术方案如下：
本发明的高阻隔柔性背膜，主要包括基材膜、铝箔、抗紫外线涂层、保护膜层、粘胶层。所述的铝箔两侧通过胶黏剂分别与基材膜进行复合，所述的抗紫外线层可直接涂覆或溅射到复合膜外侧，所述的抗紫外线层上再涂覆或复合一层保护膜层，所述的复合膜的内侧涂覆一层粘胶层，即可得到高阻隔柔性背膜。
所述的高阻隔柔性背膜是一种柔韧性好、阻隔性高的封装背膜。
所述的基材膜是市场规模大、生产工艺成熟、成本较低的薄膜。
所述的基材膜I和基材膜II两者的基材和厚度的异同性，可以依据目标功能的要求做相应调整。
所述的基材膜I选用机械强度较高的薄膜，如PET，BOPA，GXP等，基材膜II选用热封强度较好的薄膜，如CPP，PE，BOPP等。
所述的基材膜可以经过常规的阻隔性无机涂层处理的薄膜，所述的无机涂层所用材料是从由金属氧化物或非金属氧化物或它们的氮化物(如Al2O3、SiO2、Si3N4)等任选一种或几种的组合。
所述的铝箔选用厚度为20um到60um的铝箔。
所述的胶黏剂选用聚氨酯胶黏剂，优选无溶剂型聚氨酯胶黏剂。
所述的抗紫外线层直接涂覆或溅射到基材膜I上。
所述的保护膜层选用含氟涂层或氟塑料薄膜，如PVF或PTFE等。
所述的粘胶层选用与EVA粘胶有较高粘接强度的粘胶。
本发明的优点及其显著效果：
由于本发明一种高阻隔柔性背膜的构成方式和采用的特殊胶黏剂，与目前市场上普遍采用的阻隔性封装膜相比，本发明的背膜具有如下优势：1.原材料基材薄膜、铝箔等的生产工艺相当成熟、市场供应充足、成本较低；2.采用铝箔与基材薄膜复合结构，具有更好的阻隔性能和机械强度，能够较好的阻隔水汽、氧气、腐蚀性气液体的对太阳能电池的损坏；同时由于铝箔的反光作用，还能够反射光线达到提高太阳能转化效率的功效；3.生产工艺以复合为主，所以本发明的生产速度快、产能高、制备成本低，且对环境无任何危害，属于零排放；4.本发明的封装膜质轻、膜薄、柔韧、可卷，易于再加工。此外，本发明的产品不仅应用于太阳能电池的封装，同时也适用于其他阻隔性封装行业。因此，本发明是一种通过提高现行阻隔性背膜技术含量增加经济效益的有效方法：本发明的高阻隔柔性背膜具有柔韧性好、阻隔性高、成本低、寿命长、适用范围较广、市场前景好等特点，能够开辟更多的应用领域，从而产生很高的经济效益。
附图说明
图1是本发明的高阻隔柔性背膜结构示意图。
图中：基材膜I(1)、铝箔(2)、基材膜II(3)、抗紫外线层(4)、保护膜层(5)和粘胶层(6)、临时保护膜(7)。
具体实施方式
以下结合附图和具体实施方式对本发明作进一步详细的说明。
实施例1
参见图1，一种高阻隔柔性背膜，包括基材膜I(1)、铝箔(2)、基材膜II(3)、抗紫外线层(4)、保护膜层(5)和粘胶层(6)、临时保护膜(7)，所述的基材膜I(1)、II(3)通过胶黏剂与铝箔(2)采用复合工艺制备成复合膜，所述的抗紫外线层(4)直接涂覆或溅射到基材膜I(1)的外侧，所述的保护膜层(5)涂覆或复合到抗紫外线层(4)上，所述的粘胶层(6)涂覆到基材膜II(3)上，所述的临时保护膜(7)粘贴在粘胶层(6)上，即可得到多重阻隔性能的柔性透明高阻隔封装膜。
作为优选，基材膜采用机械强度较高的塑料薄膜。
作为进一步的优选，基材膜采用供应充足、价格较低的薄膜。
作为进一步的优选，基材膜I(1)是机械强度较高的薄膜，如PET，BOPA，GXP等，基材膜II是热封强度较好的薄膜，如CPP，PE，BOPP等。
作为优选，铝箔(2)选用厚度为20um到60um的铝箔。
作为优选，胶黏剂选用铝塑复合膜专用的聚氨酯胶黏剂。
作为进一步的优选，胶黏剂优选无溶剂型聚氨酯胶黏剂。
作为优选，抗紫外线层(4)可选用具有一定硬度的抗紫外线膜。
作为进一步的优选，抗紫外线层(4)也可以通过胶黏剂与阻隔膜复合到一起。
作为优选，保护膜层(5)为一种含氟涂层或氟塑料薄膜，如PVF或PTFE等。
作为进一步的优选，保护膜层(5)可以选用压力敏感黏结型薄膜，直接施加压力复合到阻隔膜上。
作为优选，粘胶层(6)是一种常温下具有良好粘接性能的粘胶。
作为进一步的优选，粘胶层(6)是与EVA粘胶有较高粘接强度的粘胶。
作为优选，临时保护膜(7)在高阻隔柔性背膜使用时直接剥离即可。
以上所述仅为本发明的较佳实施方式，本发明的保护范围并不以上述实施方式为限，但凡本领域普通技术人员根据本发明所揭示内容所作的等效修饰或变化，皆应纳入权利要求书中记载的保护范围内。

Claims (8)

1.一种高阻隔柔性背膜，包括基材膜I(1)和基材膜II(3)、铝箔(2)、抗紫外线涂层(4)、保护膜层(5)、粘胶层(6)，主要采用复合工艺制备成复合膜。
2.根据权利要求1所述的一种高阻隔柔性背膜，其特征在于：所述的基材膜I(1)和基材膜II(3)两者的基材和厚度的异同性，可以依据目标功能的要求做相应调整。
3.根据权利要求1所述的一种高阻隔柔性背膜，其特征在于：所述的基材膜I(1)是机械强度较高的薄膜，如PET，BOPA，GXP等，基材膜II(3)是热封强度较好的薄膜，如CPP，PE，BOPP等。
4.根据权利要求1所述的一种高阻隔柔性背膜，其特征在于：所述的铝箔(2)选用厚度为20um到60um的铝箔。
5.根据权利要求1所述的一种高阻隔柔性背膜，其特征在于：所述的抗紫外线层(4)可直接涂覆或溅射到基材膜I(1)上。
6.根据权利要求1所述的一种高阻隔柔性背膜，其特征在于：所述的抗紫外线层(4)外再涂覆或复合一层保护膜层(5)。
7.根据权利要求1所述的一种高阻隔柔性背膜，其特征在于：所述的保护膜层(5)可选用含氟涂层或氟塑料薄膜，如PVF或PTFE等。
8.根据权利要求1所述的一种高阻隔柔性背膜，其特征在于：所述的基材膜II(3)的另一侧涂覆一层粘胶层(6)。
CN2010105323932A 2010-11-01 2010-11-01 一种高阻隔柔性背膜 Pending CN102468352A (zh)