CN102464844A - 一种氧化铝填充改性ptfe类树脂 - Google Patents
一种氧化铝填充改性ptfe类树脂 Download PDFInfo
- Publication number
- CN102464844A CN102464844A CN2010105390212A CN201010539021A CN102464844A CN 102464844 A CN102464844 A CN 102464844A CN 2010105390212 A CN2010105390212 A CN 2010105390212A CN 201010539021 A CN201010539021 A CN 201010539021A CN 102464844 A CN102464844 A CN 102464844A
- Authority
- CN
- China
- Prior art keywords
- alumina
- ptfe
- ptfe resin
- modified ptfe
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及高分子材料技术领域，是一种氧化铝填充改性PTFE类树脂。本氧化铝填充改性PTFE类树脂由PTFE类树脂、氧化铝、颜料，经过低、高速混合，模压成型、自由烧结、机加工制得。本氧化铝填充改性PTFE，具有优良的耐磨性、阻燃效果，抗压缩性能，抗蠕变性能和更低的生产成本，可广泛适用于制造各种载荷类制品，比如：食品化工造纸、纺织机械轴承、活塞环、导向环、机床导轨和桥梁滑块等；耐高温耐腐蚀制品，如：化工容器等。
Description
技术领域
本发明涉及高分子材料技术领域，是一种氧化铝填充改性PTFE类树脂。
背景技术
聚四氟乙烯作为特种工程塑料家族的一员担负着功能性新材料的使命，具有优良的电绝缘性、化学稳定性、耐腐蚀性，是当今世界上耐腐蚀性能最佳材料之一，除熔融金属钠和液氟外，能耐其它一切化学药品，在王水中煮沸也不起变化，广泛应用于各种需要抗酸碱和有机溶剂的领域、密封性、高润滑不粘性、电绝缘性和良好的抗老化耐力、耐温优异，能在+250℃至-180℃的温度下长期工作。同时，聚四氟乙烯也有一定缺点：不耐磨、易蠕变、抗压缩性差等等。
发明内容
本发明的目的在于克服现有技术的不足，提供一种极大改善了耐磨性、阻燃性，抗压缩性，抗蠕变性能的改性PTFE类树脂。
发明是通过以下技术方案来实现的：
一种氧化铝填充改性PTFE类树脂，其特征在于：其组分及重量份数分别为：
PTFE类树脂 100份；
氧化铝 5～50份；
颜料 0.3～5份。
而且，所述的一种氧化铝填充改性PTFE类树脂，其特征在于：所述的PTFE类树脂选自平均粒径15～45微米的PTFE悬浮聚合树脂、PTFE回收料粉碎树脂的一种或几种。
而且，所述的一种氧化铝填充改性PTFE类树脂，其特征在于：所述的氧化铝是一种直径在5-40微米之间的粉体。
而且，所述的一种氧化铝填充改性PTFE类树脂，其特征在于：所述的颜料为炭黑、钛白粉、酞菁蓝、酞菁绿、铁红、咯铬黄中的一种或几种。
本发明的特点是：
1.本氧化铝填充改性PTFE类树脂，具有优良的耐磨性、抗压缩性和抗蠕变性能，广泛适用于制造各种载荷类制品，比如：食品化工造纸、纺织机械轴承、活塞环、导向环、机床导轨和桥梁滑块等。
2.本氧化铝填充改性PTFE类树脂，具有良好的阻燃性，可用于制造各种需要阻燃、耐高温的制品。
具体实施方式
本发明通过以下实施例进一步详述，下述实施例是说明性的，不是限定性的，不能以下述实施例来限定本发明的保护范围。
实施例：耐高温耐腐蚀PTFE容器
PTFE 100kg
氧化铝 40kg
钛白粉 0.3kg。
将PTFE树脂、氧化铝、钛白粉依次放入高混机，首先低速混合1-2分钟，然后高速混合1-2分钟后放料，得到混配料。将混配料通过强制加料法加入到模具中，用四柱液压机压制成型，在380℃的温度下自由烧结成型材，最后通过加工中心加工成容器。
Claims (4)
1.一种氧化铝增强PTFE类树脂，其特征在于：其组分及重量份数分别为：
PTFE类树脂 100份；
氧化铝 5～50份；
颜料 0.3～5份。
2.根据权利要求1所述的一种氧化铝增强PTFE类树脂，其特征在于：所述的PTFE类树脂选自平均粒径15～45微米的PTFE悬浮聚合树脂、PTFE回收料粉碎树脂的一种或几种。
3.根据权利要求1所述的一种氧化铝增强PTFE类树脂，其特征在于：所述的氧化铝是一种直径在5-40微米之间的粉体。
4.根据权利要求1所述的一种氧化铝增强PTFE类树脂，其特征在于：所述的颜料为炭黑、钛白粉、酞菁蓝、酞菁绿、铁红、咯铬黄中的一种或几种。